CN103231053A - 冷等静压用制备钼板坯模具 - Google Patents
冷等静压用制备钼板坯模具 Download PDFInfo
- Publication number
- CN103231053A CN103231053A CN2013101285278A CN201310128527A CN103231053A CN 103231053 A CN103231053 A CN 103231053A CN 2013101285278 A CN2013101285278 A CN 2013101285278A CN 201310128527 A CN201310128527 A CN 201310128527A CN 103231053 A CN103231053 A CN 103231053A
- Authority
- CN
- China
- Prior art keywords
- rubber
- frame
- molybdenum
- plate
- isostatic cool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开的冷等静压用制备钼板坯模具,包括一端设有开口的橡胶护套,橡胶护套的内部设置有压坯橡胶板框组件,橡胶护套的开口处用锁紧扣组件锁紧密封。本发明的冷等静压用制备钼板坯模具结构简单,操作容易,适合于各种尺寸的钼板坯的压制,并且所使用的都是常见材料,制造成本低,使用本发明的模具能够很好地提升钼板坯的成品率,降低了钼板坯的制造成本,带来良好的经济效益。
Description
技术领域
本发明属于制备钼板模具技术领域,具体涉及一种冷等静压用制备钼板坯模具。
背景技术
目前压制钼板坯主要有两种方式,一种是油压机压制、一种是冷等静压压制。
油压机制备钼压坯时采用钢模具进行压制,其工艺特点是:外形尺寸规整,钼压坯只能单向受力或双向受力,对设备的工作压力要求较高,受设备性能和模具限制,只能压制3kg以下压坯。
冷等静压是指在室温条件下进行的压制成型技术,通常采用橡胶作为包裹材料,以液体作为压力传导介质,压制钼粉压坯时的工作压力范围在150~250MPa,其目的在于为下一步烧结制备压坯。
冷等静压压制钼压坯时采用橡胶模具进行压制,具有不受外形、规格、重量限制的特点,并且压制过程中钼压坯是六面均匀受力,钼压坯密度均匀。然而现有冷等静压的橡胶模具强度不够,易造成压坯外形不够规整,尺寸不准确,导致成品率下降、加工成本上升、盈利水平下降。
发明内容
本发明的目的在于提供一种冷等静压用制备钼板坯模具,解决了现有技术中由于模具在压制过程中发生形变,导致最终制得的钼板坯外形不够规整、尺寸不准确的问题。
本发明所采用的技术方案是:冷等静压用制备钼板坯模具,包括一端设有开口的橡胶护套,橡胶护套的内部设置有压坯橡胶板框组件,橡胶护套的开口处用锁紧扣组件锁紧密封。
本发明的特点还在于,
压坯橡胶板框组件包括两端开口的橡胶板框、橡胶底板以及橡胶上压板,橡胶底板和橡胶上压板分别套合于橡胶板框的下端和上端开口;橡胶上压板上设置有第一把手,橡胶板框的四个侧面上分别沿与相应侧面平行方向设置有若干个第一通孔,每个第一通孔中都插入有加固杆。
每根加固杆的长度与其所在橡胶板框的侧面的长度相适应。
还包括装粉装置,装粉装置进一步包括矩形的边框,边框的底部连接有底板,底板上设置有若干个第二通孔,边框的一组对边分别设置有连接板,每个连接板上设置有第二把手,边框套合于橡胶板框的上端开口中。
第二通孔为直径是5~6mm的圆形孔。
锁紧扣组件包括一个U形杆,U形杆的开口端连接有挡片,U形杆的两个自由端穿过挡片并分别连接有锁紧螺母,橡胶护套的开口聚拢后,置于挡片与U形杆所形成的开孔内。
本发明的有益效果是:本发明的冷等静压用制备钼板坯模具结构简单,操作容易,适合于各种尺寸的钼板坯的压制,并且所使用的都是常见材料,制造成本低,使用本发明的模具能够很好地提升钼板坯的成品率,降低了钼板坯的制造成本,带来良好的经济效益。
附图说明
图1是本发明的冷等静压用制备钼板坯模具的结构示意图;
图2是本发明的冷等静压用制备钼板坯模具中压坯橡胶板框组件的分解结构示意图;
图3是本发明冷等静压用制备钼板坯模具装粉时的使用状态图;
图4是本发明冷等静压用制备钼板坯模具中装粉装置的结构示意图;
图5是本发明冷等静压用制备钼板坯模具中锁紧扣组件的结构示意图。
图中,1.压坯橡胶板框组件,2.橡胶护套,3.锁紧扣组件,4.装粉装置,101.橡胶板框,102.橡胶底板,103.橡胶上压板,104.第一通孔,105.加固杆,106.第一把手,301.U形杆,302.挡片,303.锁紧螺母,304.开孔,401.边框,402.连接板,403.第二把手,404.底板,405.第二通孔。
具体实施方式
下面结合具体实施方式对本发明进行详细说明。
本发明的冷等静压用制备钼板坯模具的结构如图1所示,包括一端设有开口的橡胶护套2,橡胶护套2的内部设置有压坯橡胶板框组件1,橡胶护套2的开口处用锁紧扣组件3锁紧密封。
如图2所示,压坯橡胶板框组件1包括两端开口的橡胶板框101、橡胶底板102以及橡胶上压板103,橡胶底板102和橡胶上压板103分别套合于橡胶板框101的下端和上端开口;橡胶上压板103上设置有第一把手106,橡胶板框101的四个侧面上分别沿与相应侧面平行方向设置有若干个第一通孔104,每个第一通孔104中都插入有加固杆105。
每根加固杆105的长度与其所在橡胶板框101的侧面的长度相适应。
如图3所示,本发明的冷等静压用制备钼板坯模具还包括装粉装置4,装粉装置4的结构如图4所示,包括矩形的边框401,边框401的底部连接有底板404,底板404上设置有若干个第二通孔405,边框401的一组对边分别设置有连接板402,每个连接板402上设置有第二把手403,边框401套合于橡胶板框101的上端开口中。
第二通孔405为直径是5~6mm的圆形孔。
如图5所示,锁紧扣组件3包括一个U形杆301,U形杆301的开口端连接有挡片302,U形杆301的两个自由端穿过挡片302并分别连接有锁紧螺母303,橡胶护套2的开口聚拢后,置于挡片302与U形杆301所形成的开孔304内。
工作时,先将压坯橡胶板框1的橡胶上压板103取出,再将装粉装置4的底部套合入橡胶板框1中,向装粉装置4中倒入钼粉,通过振动使得钼粉从底板404的第二通孔405中进入压坯橡胶板框组件1中,然后再取出装粉装置4,并将橡胶上压板103放置于橡胶板框101上,压紧,将压坯橡胶板框1放入橡胶护套2中,再将橡胶护套2的开口聚拢后塞入锁紧扣组件3的U形杆中,安装挡片302,最后再用锁紧螺母303将橡胶护套2的开口端锁紧密封。
由于在橡胶板框1中插入了加固杆105,使得模具在钼板坯的压制过程中不易变形,保证了最终压板坯的尺寸较为规整,并且本发明的模具可以根据需要设计成不同的尺寸,以满足不同尺寸的钼板坯压制的需要。
通过上述方式,本发明解决了现有技术中由于模具在压制过程中发生形变,导致最终制得的钼板坯外形不够规整、尺寸不准确的问题。并且本发明的冷等静压用制备钼板坯模具结构简单,操作容易,适合于各种尺寸的钼板坯的压制,并且所使用的都是常见材料,制造成本低,使用本发明的模具能够很好地提升钼板坯的成品率,降低了钼板坯的制造成本,带来良好的经济效益。
Claims (6)
1.冷等静压用制备钼板坯模具,其特征在于,包括一端设有开口的橡胶护套(2),所述橡胶护套(2)的内部设置有压坯橡胶板框组件(1),所述橡胶护套(2)的开口处用锁紧扣组件(3)锁紧密封。
2.如权利要求1所述的冷等静压用制备钼板坯模具,其特征在于,所述压坯橡胶板框组件(1)包括两端开口的橡胶板框(101)、橡胶底板(102)以及橡胶上压板(103),所述橡胶底板(102)和所述橡胶上压板(103)分别套合于所述橡胶板框(101)的下端和上端开口;所述橡胶上压板(103)上设置有第一把手(106),所述橡胶板框(101)的四个侧面上分别沿与相应侧面平行方向设置有若干个第一通孔(104),所述每个第一通孔(104)中都插入有加固杆(105)。
3.如权利要求2所述的冷等静压用制备钼板坯模具,其特征在于,所述每根加固杆(105)的长度与其所在橡胶板框(101)的侧面的长度相适应。
4.如权利要求2所述的冷等静压用制备钼板坯模具,其特征在于,还包括装粉装置(4),所述装粉装置(4)进一步包括矩形的边框(401),所述边框(401)的底部连接有底板(404),所述底板(404)上设置有若干个第二通孔(405),所述边框(401)的一组对边上分别设置有连接板(402),所述每个连接板(402)上设置有第二把手(403),所述边框(401)套合于所述橡胶板框(101)的上端开口中。
5.如权利要求4所述的冷等静压用制备钼板坯模具,其特征在于,所述第二通孔(405)为直径是5~6mm的圆形孔。
6.如权利要求1~5任意一项所述的冷等静压用制备钼板坯模具,其特征在于,所述锁紧扣组件(3)包括一个U形杆(301),所述U形杆(301)的开口端连接有挡片(302),所述U形杆(301)的两个自由端穿过所述挡片(302)并分别连接有锁紧螺母(303),所述橡胶护套(2)的开口聚拢后,置于所述挡片(302)与所述U形杆(301)所形成的开孔(304)内。