CN103215728A - Manufacturing technology of cloth like paper - Google Patents
Manufacturing technology of cloth like paper Download PDFInfo
- Publication number
- CN103215728A CN103215728A CN2013101626802A CN201310162680A CN103215728A CN 103215728 A CN103215728 A CN 103215728A CN 2013101626802 A CN2013101626802 A CN 2013101626802A CN 201310162680 A CN201310162680 A CN 201310162680A CN 103215728 A CN103215728 A CN 103215728A
- Authority
- CN
- China
- Prior art keywords
- cloth
- yarn
- warp
- material manufacturing
- manufacturing technique
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to manufacturing technology of cloth like paper. The manufacturing technology comprises the following steps: firstly, cloth yarn meeting a requirement is selected according to the appearance requirement for the surface of the cloth; secondly, a certain number of strands of warp are arranged in order based on specified length and wound on a beam of a warping machine in parallel, wherein breadth of the warp is even; thirdly, a plurality of strands of single yarn are combined to be wound into a tube by a doubler winder; fourthly, a layer of a sizing agent is adhered to the periphery of the warp by a sizing machining, the layer of sizing agent is dried and form a size membrane, hairiness is adhered, the warp is smooth and wear-resistant, and the other part of the sizing agent is permeated into a yarn layer; and fifthly, weft and warp are interwoven together through coordination movement of a weaving machine so as to form fabric required by the technology. The cloth manufactured by the technology not only has an appearance style like paper, but also has good rebound resilience and air and moisture permeating performance, and original parameters of tear resistance, color fastness, folding resistance, wear resistance and the like are still not changed.
Description
Technical field
The present invention relates to a kind of paper sense cloth material manufacturing technique.
Background technology
Paper sense cloth is meant in order to make common lining possess particular appearance style and elastic handfeel, under the prerequisite that does not change the original institutional framework of lining, by the coating processing common lining is processed into the lining with paper sense of touch, this lining is except that possessing paper sense appearance style, also possess good resilience and saturating vapour poisture-penetrability simultaneously, parameters such as the original anti tear degree of lining, COLOR FASTNESS, anti-folding wear intensity all can be still constant, and this lining can be widely used in dress ornaments such as jacket, blouse, Casual Wear, down jackets, sportswear.
Summary of the invention
In order to reach the requirement of paper sense cloth, the invention provides a kind of new paper sense cloth material manufacturing technique.
Major technique of the present invention thes contents are as follows:
A kind of paper sense cloth material manufacturing technique may further comprise the steps:
(1), according to the appearance requirement on cloth surface, select to adapt to the cloth yarn that requires;
(2), warping;
Warp thread length in accordance with regulations with certain radical puts in order, and fabric width is even, be wound on abreast warping machines on axle;
(3), sizing;
To adhere to one deck sizing agent around the warp thread with Sizing machines, the oven dry back forms serous coat, makes filoplume paste volt, and yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
(4), doubling;
To starch good yarn according to the total quantity of warps of fabric and become required beam of a loom with warp rebeaming machine;
(5), weave;
By weaving the routing motion of machine,, form the fabric of technological requirement with weft yarn and warp thread weave in;
(6), coating;
On fabric, coat paper sense coating glue.
Cloth yarn in the above-mentioned steps (1) is 20D nylon+20D terylene.
The following setting of parameter of warping machines in the above-mentioned steps (2):
A, the speed of a motor vehicle: 170m/min;
B, move back and separate tension force: 1 of tension link, tension force scale: little 1 quarter, pressure plate: 2;
C, coiling tension: 5kg, last item roller pressure: 2.2kg.
The following setting of parameter of warp rebeaming machine in the above-mentioned steps (4):
A, the speed of a motor vehicle: 40m/min;
B, batch a width of cloth: 170cm;
C, move back and separate tension force: 12kg;
D, coiling tension: 90kg;
E, tapering: 3%, tapered: 200%, select single magnetic.
The following setting of parameter of Sizing machines in the above-mentioned steps (3):
A, the speed of a motor vehicle: 50m/min;
B, first baking oven, 140 degree, second baking oven, 140 degree, slurry temperature 38 degree, wax temperature 84 degree.
Weave the following setting of parameter of machine in the above-mentioned steps (5):
A, the speed of a motor vehicle: 400m/min;
B, preceding 45 degree of the back rest, tension force: 1500N.
Sizing agent is for comprising in the above-mentioned steps (4):
Vinyl alcohol condensate: 35.5-43.5%
Propenyl condensate: 10.4%-46.4%
Starch: 4-8.9%
Sodium carboxymethylcellulose: 0-50%.
By technique scheme, the present invention has following advantage at least: the cloth of this explained hereafter is except that possessing paper sense appearance style, also possess good resilience and saturating vapour poisture-penetrability simultaneously, parameters such as the original anti tear degree of lining, COLOR FASTNESS, anti-folding wear intensity all can be still constant.
The specific embodiment of the present invention is provided in detail by following examples.
The specific embodiment
Reach technological means and the effect that predetermined goal of the invention is taked for further setting forth the present invention, below in conjunction with preferred embodiment, to its specific embodiment, structure, feature and the effect thereof that foundation the present invention proposes, describe in detail as after.
A kind of paper sense cloth material manufacturing technique may further comprise the steps:
(1), according to the appearance requirement on cloth surface, select to adapt to the cloth yarn that requires;
(2), warping;
Warp thread length in accordance with regulations with certain radical puts in order, and fabric width is even, be wound on abreast warping machines on axle;
(3), sizing;
To adhere to one deck sizing agent around the warp thread with Sizing machines, the oven dry back forms serous coat, makes filoplume paste volt, and yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
(4), doubling;
To starch good yarn according to the total quantity of warps of fabric and become required beam of a loom with warp rebeaming machine;
(5), weave;
By weaving the routing motion of machine,, form the fabric of technological requirement with weft yarn and warp thread weave in;
(6), coating;
On fabric, coat paper sense coating glue.
Cloth yarn in the above-mentioned steps (1) is 20D nylon+20D terylene.
The following setting of parameter of warping machines in the above-mentioned steps (2):
A, the speed of a motor vehicle: 170m/min;
B, move back and separate tension force: 1 of tension link, tension force scale: little 1 quarter, pressure plate: 2;
C, coiling tension: 5kg, last item roller pressure: 2.2kg.
The following setting of parameter of warp rebeaming machine in the above-mentioned steps (4):
A, the speed of a motor vehicle: 40m/min;
B, batch a width of cloth: 170cm;
C, move back and separate tension force: 12kg;
D, coiling tension: 90kg;
E, tapering: 3%, tapered: 200%, select single magnetic.
The following setting of parameter of Sizing machines in the above-mentioned steps (3):
A, the speed of a motor vehicle: 50m/min;
B, first baking oven, 140 degree, second baking oven, 140 degree, slurry temperature 38 degree, wax temperature 84 degree.
Weave the following setting of parameter of machine in the above-mentioned steps (5):
A, the speed of a motor vehicle: 400m/min;
B, preceding 45 degree of the back rest, tension force: 1500N.
Sizing agent is for comprising in the above-mentioned steps (4):
Vinyl alcohol condensate: 35.5-43.5%
Propenyl condensate: 10.4%-46.4%
Starch: 4-8.9%
Sodium carboxymethylcellulose: 0-50%.
The above, it only is preferred embodiment of the present invention, be not that the present invention is done any pro forma restriction, though the present invention discloses as above with preferred embodiment, yet be not in order to limit the present invention, any those skilled in the art, in not breaking away from the technical solution of the present invention scope, when the technology contents that can utilize above-mentioned announcement is made a little change or is modified to the equivalent embodiment of equivalent variations, in every case be the content that does not break away from technical solution of the present invention, according to technical spirit of the present invention to any simple modification that above embodiment did, equivalent variations and modification all still belong in the scope of technical solution of the present invention.
Claims (7)
1. paper sense cloth material manufacturing technique is characterized in that may further comprise the steps:
(1), according to the appearance requirement on cloth surface, select to adapt to the cloth yarn that requires;
(2), warping;
Warp thread length in accordance with regulations with certain radical puts in order, and fabric width is even, be wound on abreast warping machines on axle;
(3), sizing;
To adhere to one deck sizing agent around the warp thread with Sizing machines, the oven dry back forms serous coat, makes filoplume paste volt, and yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
(4), doubling;
To starch good yarn according to the total quantity of warps of fabric and become required beam of a loom with warp rebeaming machine;
(5), weave;
By weaving the routing motion of machine,, form the fabric of technological requirement with weft yarn and warp thread weave in;
(6), coating;
On fabric, coat paper sense coating glue.
2. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: the cloth yarn in the described step (1) is 20D nylon+20D terylene.
3. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: the following setting of parameter of warping machines in the described step (2):
3a, the speed of a motor vehicle: 170m/min;
3b, move back and separate tension force: 1 of tension link, tension force scale: little 1 quarter, pressure plate: 2;
3c, coiling tension: 5kg, last item roller pressure: 2.2kg.
4. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: the following setting of parameter of warp rebeaming machine in the described step (4):
4a, the speed of a motor vehicle: 40m/min;
4b, batch a width of cloth: 170cm;
4c, move back and separate tension force: 12kg;
4d, coiling tension: 90kg;
4e, tapering: 3%, tapered: 200%, select single magnetic.
5. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: the following setting of parameter of Sizing machines in the described step (3):
5a, the speed of a motor vehicle: 50m/min;
5b, first baking oven, 140 degree, second baking oven, 140 degree, slurry temperature 38 degree, wax temperature 84 degree.
6. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: the following setting of parameter of weaving machine in the described step (5):
6a, the speed of a motor vehicle: 400m/min;
6b, preceding 45 degree of the back rest, tension force: 1500N.
7. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: sizing agent is for comprising in the described step (4):
Vinyl alcohol condensate: 35.5-43.5%
Propenyl condensate: 10.4%-46.4%
Starch: 4-8.9%
Sodium carboxymethylcellulose: 0-50%.