CN103205839B - Production process of plaid cloth - Google Patents
Production process of plaid cloth Download PDFInfo
- Publication number
- CN103205839B CN103205839B CN201310162676.6A CN201310162676A CN103205839B CN 103205839 B CN103205839 B CN 103205839B CN 201310162676 A CN201310162676 A CN 201310162676A CN 103205839 B CN103205839 B CN 103205839B
- Authority
- CN
- China
- Prior art keywords
- sizing
- yarns
- yarn
- machine
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a production process of plaid cloth. The production process comprises the following steps of: (1) choosing required cloth yarns which meet the appearance requirement of the surface of the cloth; (2) sequencing a certain quantity of wrap yarns according to the required length to ensure the evenness of the breadth, and winding on a wrap shaft of a warping machine in parallel; (3) combining a plurality of single yarns by using a doubler winder and winding to be a bobbin; (4) adhering a layer of sizing agents around the wrap yarns by using a sizing machine, drying to form a serosa to ensure that hairs are sticky, the yarns are smooth and abrasion-resistant and the other part of the sizing agents are soaked into the yarn layers; and (5) interweaving weft yarns and wrap yarns together through matching motion of a weaving machine to form a fabric which meets technological requirements. The plaid cloth produced by the process is high in tearing and breaking strength and has a wide application prospect, and parachutes and paragliders manufactured by the production process can meet the requirements on various industries of aerospace, military industries, sports and the like.
Description
Technical field
The present invention relates to a kind of plaids production technology.
Background technology
Plaids are paragliders, the main cloth of parachute, be characterized in lightweight, intensity is high, feel is softer.Current plaids are mainly used in above army's parachute, but it is torn, and fracture strength does not also reach corresponding requirement, and the requirement for plaids quality process optimization is extremely urgent.
Summary of the invention
Tear to reach plaids, the requirement of fracture strength, the invention provides a kind of new plaids production technology.
Main technical content of the present invention is as follows:
A kind of plaids production technology comprises the following steps:
(1), according to the appearance requirement of design on fabric surface, the cloth yarn adapting to require is selected;
(2), warping;
By the length of the warp thread of certain radical by regulation, put in order, fabric width is even, is wound on abreast in the warp beam of warping machines;
(3), sizing;
With Sizing machines by adhering to one deck sizing agent around warp thread, form serous coat after oven dry, make filoplume paste volt, yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
(4), doubling;
With warp rebeaming machine by the yarn the starched beam of a loom according to the total quantity of warps of fabric and needed for becoming;
(5), weave;
By the routing motion of Weaving-machine, by weft yarn together with warp yarns, the fabric that formation process requires.
In above-mentioned steps (2), the parameter of warping machines is arranged as follows:
A, the speed of a motor vehicle: 170m/min;
B, move back solution tension force: tension link 1, tension scale: little 1 quarter, pressure plate: 2;
C, coiling tension: 9kg, last item roller pressure: 2.2kg.
In above-mentioned steps (4), the parameter of warp rebeaming machine is arranged as follows:
A, the speed of a motor vehicle: 40m/min;
B, batch a width: 170cm;
C, move back solution tension force: 12kg;
D, coiling tension: 90kg;
E, tapering: 3%, tapered: 200%, select single magnetic.
In above-mentioned steps (3), the parameter of Sizing machines is arranged as follows:
A, the speed of a motor vehicle: 180m/min;
B, move back solution tension force: 9kg, coiling tension: 12kg;
C, temperature: slurry temperature: 38 degree, baking oven high temperature: 140 degree, low temperature: 130 degree;
D, elongation strain: 8g;
E, after oil, rotating speed scale set: 0.4rmp.
In above-mentioned steps (5), the parameter of Weaving-machine is arranged as follows:
A, the speed of a motor vehicle: 450m/min;
Before b, the back rest 45 degree, tension force: 1500N.
In above-mentioned steps (4), sizing agent is acrylate based copolymer, and its solid content is 20 ± 0.5%, PH is 6.5-7.5, midge amount is 4kg/km, the rate of sizing is 11%.
By technique scheme, the present invention at least has following advantages: the plaids that this production technology is produced have stronger tearing, fracture strength, the parachute made and paraglider can meet the requirement of the industry-by-industries such as Aero-Space, military project, physical culture completely, are with a wide range of applications.
The specific embodiment of the present invention is provided in detail by following examples.
Detailed description of the invention
For further setting forth the present invention for the technological means reaching predetermined goal of the invention and take and effect, below in conjunction with preferred embodiment, to its detailed description of the invention proposed according to the present invention, structure, feature and effect thereof, be described in detail as follows.
A kind of plaids production technology comprises the following steps:
(1), according to the appearance requirement of design on fabric surface, the cloth yarn adapting to require is selected;
(2), warping;
By the length of the warp thread of certain radical by regulation, put in order, fabric width is even, is wound on abreast in the warp beam of warping machines;
(3), sizing;
With Sizing machines by adhering to one deck sizing agent around warp thread, form serous coat after oven dry, make filoplume paste volt, yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
(4), doubling;
With warp rebeaming machine by the yarn the starched beam of a loom according to the total quantity of warps of fabric and needed for becoming;
(5), weave;
By the routing motion of Weaving-machine, by weft yarn together with warp yarns, the fabric that formation process requires.
In above-mentioned steps (2), the parameter of warping machines is arranged as follows:
A, the speed of a motor vehicle: 170m/min;
B, move back solution tension force: tension link 1, tension scale: little 1 quarter, pressure plate: 2;
C, coiling tension: 9kg, last item roller pressure: 2.2kg.
In above-mentioned steps (4), the parameter of warp rebeaming machine is arranged as follows:
A, the speed of a motor vehicle: 40m/min;
B, batch a width: 170cm;
C, move back solution tension force: 12kg;
D, coiling tension: 90kg;
E, tapering: 3%, tapered: 200%, select single magnetic.
In above-mentioned steps (3), the parameter of Sizing machines is arranged as follows:
A, the speed of a motor vehicle: 180m/min;
B, move back solution tension force: 9kg, coiling tension: 12kg;
C, temperature: slurry temperature: 38 degree, baking oven high temperature: 140 degree, low temperature: 130 degree;
D, elongation strain: 8g;
E, after oil, rotating speed scale set: 0.4rmp.
In above-mentioned steps (5), the parameter of Weaving-machine is arranged as follows:
A, the speed of a motor vehicle: 450m/min;
Before b, the back rest 45 degree, tension force: 1500N.
In above-mentioned steps (4), sizing agent is acrylate based copolymer, and its solid content is 20 ± 0.5%, PH is 6.5-7.5, midge amount is 4kg/km, the rate of sizing is 11%.
Plaids of the present invention can reach following technical parameter:
Ultimate strength/(N):
Radial>=800, broadwise>=400(mass area ratio>=200g/m
2);
Radial>=400, broadwise>=400(mass area ratio < 200g/m
2).
The above, it is only preferred embodiment of the present invention, not any pro forma restriction is done to the present invention, although the present invention discloses as above with preferred embodiment, but and be not used to limit the present invention, any those skilled in the art, do not departing within the scope of technical solution of the present invention, make a little change when the technology contents of above-mentioned announcement can be utilized or be modified to the Equivalent embodiments of equivalent variations, in every case be the content not departing from technical solution of the present invention, according to any simple modification that technical spirit of the present invention is done above embodiment, equivalent variations and modification, all still belong in the scope of technical solution of the present invention.
Claims (1)
1. a plaids production technology, is characterized in that comprising the following steps:
(1), according to the appearance requirement of design on fabric surface, the cloth yarn adapting to require is selected;
(2), warping;
By the length of the warp thread of certain radical by regulation, put in order, fabric width is even, is wound on abreast in the warp beam of warping machines;
The parameter of described warping machines is arranged as follows:
2a, the speed of a motor vehicle: 170m/min;
2b, move back solution tension force: tension link 1, pressure plate: 2;
2c, coiling tension: 9kg, last item roller pressure: 2.2kg;
(3), sizing;
With Sizing machines by adhering to one deck sizing agent around warp thread, form serous coat after oven dry, make filoplume paste volt, yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
Described sizing agent is acrylate based copolymer, and its solid content is 20 ± 0.5%, PH is 6.5-7.5, midge amount is 4kg/km, the rate of sizing is 11%;
The parameter of Sizing machines is arranged as follows:
3a, the speed of a motor vehicle: 180m/min;
3b, move back solution tension force: 9kg, coiling tension: 12kg;
3c, temperature: slurry temperature: 38 degree, baking oven high temperature: 140 degree, low temperature: 130 degree;
3d, elongation strain: 8g;
3e, after oil, rotating speed scale set: 0.4rmp;
(4), doubling;
With warp rebeaming machine by the yarn the starched beam of a loom according to the total quantity of warps of fabric and needed for becoming;
The parameter of described warp rebeaming machine is arranged as follows:
4a, the speed of a motor vehicle: 40m/min;
4b, batch a width: 170cm;
4c, move back solution tension force: 12kg;
4d, coiling tension: 90kg;
4e, tapering: 3%, tapered: 200%, select single magnetic;
(5), weave;
By the routing motion of Weaving-machine, by weft yarn together with warp yarns, the fabric that formation process requires;
The parameter of Weaving-machine is arranged as follows:
5a, the speed of a motor vehicle: 450m/min;
5b, tension force: 1500N.