CN103215727B - A kind of production technique of superfine cloth - Google Patents
A kind of production technique of superfine cloth Download PDFInfo
- Publication number
- CN103215727B CN103215727B CN201310162660.5A CN201310162660A CN103215727B CN 103215727 B CN103215727 B CN 103215727B CN 201310162660 A CN201310162660 A CN 201310162660A CN 103215727 B CN103215727 B CN 103215727B
- Authority
- CN
- China
- Prior art keywords
- cloth
- yarn
- superfine
- fabric
- warp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of production technique of superfine cloth to comprise the following steps: (1), appearance requirement according to design on fabric surface, select the cloth yarn adapting to require; (2), by the length of the warp thread of certain radical by regulation, put in order, fabric width is even, is wound on abreast in the warp beam of warping machines; (3) bobbin is wound into after, also being closed by many single thread with doubling winder; (4), with Sizing machines by adhering to one deck sizing agent around warp thread, form serous coat after oven dry, make filoplume paste volt, yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside; (5), by the routing motion of Weaving-machine, by weft yarn together with warp yarns, the fabric that formation process requires.This explained hereafter cloth long service life out, water absorbing force is superpower, can not cause surface abrasion during use.Dust fall amount is few, and ion emission is few, and wiping effect is higher than general cleaning wiping cloth more than 10 times.
Description
Technical field
The present invention relates to a kind of production technique of superfine cloth.
Background technology
Superfine cloth is the one developing fibre in differentiation rapidly, and being called as the synthetic fiber of a new generation, is the textile raw material of a kind of high-quality, high-tech, is the Typical Representative of chemical fibre to the shin-gosen of high-tech, high emulationization future development.Be be made into by the fiber that super is thin and tough and tensile, there is superpower institutional framework, soft tough and tensile characteristic, neither damage the advantage of working substance and the low ion concentration of low dust fall.
Summary of the invention
The invention provides a kind of new production technique of superfine cloth.
Main technical content of the present invention is as follows:
A kind of production technique of superfine cloth, comprises the following steps:
(1), according to the appearance requirement of design on fabric surface, the cloth yarn adapting to require is selected;
(2), warping;
By the length of the warp thread of certain radical by regulation, put in order, fabric width is even, is wound on abreast in the warp beam of warping machines;
(3), sizing;
With Sizing machines by adhering to one deck sizing agent around warp thread, form serous coat after oven dry, make filoplume paste volt, yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
(4), doubling;
With warp rebeaming machine by the yarn the starched beam of a loom according to the total quantity of warps of fabric and needed for becoming;
(5), weave;
By the routing motion of Weaving-machine, by weft yarn together with warp yarns, the fabric that formation process requires.
Cloth yarn in above-mentioned steps (1) is 20D nylon+20D terylene.
In above-mentioned steps (2), the parameter of warping machines is arranged as follows:
A, the speed of a motor vehicle: 170m/min;
B, move back solution tension force: tension link 1, tension scale: little 1 quarter, pressure plate: 2;
C, coiling tension: 6kg, last item roller pressure: 2.2kg.
In above-mentioned steps (3), the parameter of Sizing machines is arranged as follows:
A, the speed of a motor vehicle: 120m/min;
B, 140 degree, the first baking oven, 140 degree, the second baking oven, slurry temperature 38 degree, wax temperature 84 degree.
In above-mentioned steps (4), the parameter of warp rebeaming machine is arranged as follows:
A, the speed of a motor vehicle: 40m/min;
B, batch a width: 170cm;
C, move back solution tension force: 12kg;
D, coiling tension: 90kg;
E, tapering: 3%, tapered: 200%, select single magnetic.
In above-mentioned steps (5), the parameter of Weaving-machine is arranged as follows:
A, the speed of a motor vehicle: 450m/min;
Before b, the back rest 45 degree, tension force: 1500N.
In above-mentioned steps (4), sizing agent is for comprising:
Vinyl alcohol condensate: 35.5-43.5%
Propenyl condensate: 10.4%-46.4%
Starch: 4-8.9%
Sodium carboxymethylcellulose: 0-50%
Ethylene oxide adduct: 0.1-5%.
By technique scheme, the present invention at least has following advantages: long service life, and water absorbing force superpower (imitative silk), can not cause surface abrasion during use.Dust fall amount is few, and ion emission is few, and wiping effect is higher than general cleaning wiping cloth more than 10 times.
The specific embodiment of the present invention is provided in detail by following examples.
Detailed description of the invention
For further setting forth the present invention for the technological means reaching predetermined goal of the invention and take and effect, below in conjunction with preferred embodiment, to its detailed description of the invention proposed according to the present invention, structure, feature and effect thereof, be described in detail as follows.
A kind of production technique of superfine cloth, comprises the following steps:
(1), according to the appearance requirement of design on fabric surface, the cloth yarn adapting to require is selected;
(2), warping;
By the length of the warp thread of certain radical by regulation, put in order, fabric width is even, is wound on abreast in the warp beam of warping machines;
(3), sizing;
With Sizing machines by adhering to one deck sizing agent around warp thread, form serous coat after oven dry, make filoplume paste volt, yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
(4), doubling;
With warp rebeaming machine by the yarn the starched beam of a loom according to the total quantity of warps of fabric and needed for becoming;
(5), weave;
By the routing motion of Weaving-machine, by weft yarn together with warp yarns, the fabric that formation process requires.
Cloth yarn in above-mentioned steps (1) is 20D nylon+20D terylene.
In above-mentioned steps (2), the parameter of warping machines is arranged as follows:
A, the speed of a motor vehicle: 170m/min;
B, move back solution tension force: tension link 1, tension scale: little 1 quarter, pressure plate: 2;
C, coiling tension: 6kg, last item roller pressure: 2.2kg.
In above-mentioned steps (3), the parameter of Sizing machines is arranged as follows:
A, the speed of a motor vehicle: 120m/min;
B, 140 degree, the first baking oven, 140 degree, the second baking oven, slurry temperature 38 degree, wax temperature 84 degree.
In above-mentioned steps (4), the parameter of warp rebeaming machine is arranged as follows:
A, the speed of a motor vehicle: 40m/min;
B, batch a width: 170cm;
C, move back solution tension force: 12kg;
D, coiling tension: 90kg;
E, tapering: 3%, tapered: 200%, select single magnetic.
In above-mentioned steps (5), the parameter of Weaving-machine is arranged as follows:
A, the speed of a motor vehicle: 450m/min;
Before b, the back rest 45 degree, tension force: 1500N.
In above-mentioned steps (4), sizing agent is for comprising:
Vinyl alcohol condensate: 35.5-43.5%
Propenyl condensate: 10.4%-46.4%
Starch: 4-8.9%
Sodium carboxymethylcellulose: 0-50%
Ethylene oxide adduct: 0.1-5%.
The above, it is only preferred embodiment of the present invention, not any pro forma restriction is done to the present invention, although the present invention discloses as above with preferred embodiment, but and be not used to limit the present invention, any those skilled in the art, do not departing within the scope of technical solution of the present invention, make a little change when the technology contents of above-mentioned announcement can be utilized or be modified to the Equivalent embodiments of equivalent variations, in every case be the content not departing from technical solution of the present invention, according to any simple modification that technical spirit of the present invention is done above embodiment, equivalent variations and modification, all still belong in the scope of technical solution of the present invention.
Claims (4)
1. a production technique of superfine cloth, is characterized in that comprising the following steps:
(1), according to the appearance requirement of design on fabric surface, the cloth yarn adapting to require is selected;
(2), warping;
By the length of the warp thread of certain radical by regulation, put in order, fabric width is even, is wound on abreast in the warp beam of warping machines;
(3), sizing;
With Sizing machines by adhering to one deck sizing agent around warp thread, form serous coat after oven dry, make filoplume paste volt, yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
(4), doubling;
With warp rebeaming machine by the yarn the starched beam of a loom according to the total quantity of warps of fabric and needed for becoming;
(5), weave;
By the routing motion of Weaving-machine, by weft yarn together with warp yarns, the fabric that formation process requires;
In described step (3), sizing agent comprises:
Vinyl alcohol condensate: 35.5-43.5%
Propenyl condensate: 10.4%-46.4%
Starch: 4-8.9%
Sodium carboxymethylcellulose: 0-50%
Ethylene oxide adduct: 0.1-5%,
In described step (2), the parameter of warping machines is arranged as follows:
A, the speed of a motor vehicle: 170m/min;
B, move back solution tension force: tension link 1, pressure plate: 2;
C, coiling tension: 6kg, last item roller pressure: 2.2kg.
2. a kind of production technique of superfine cloth according to claim 1, is characterized in that: the cloth yarn in described step (1) is 20D nylon+20D terylene.
3. a kind of production technique of superfine cloth according to claim 1, is characterized in that: in described step (3), the parameter of Sizing machines is arranged as follows:
3a, the speed of a motor vehicle: 120m/min;
3b, 140 DEG C, the first baking oven, 140 DEG C, the second baking oven, slurry temperature 38 DEG C, wax temperature 84 DEG C.
4. a kind of production technique of superfine cloth according to claim 1, is characterized in that: in described step (5), the parameter of Weaving-machine is arranged as follows:
5a, the speed of a motor vehicle: 450m/min;
5b, tension force: 1500N.