CN103215727A - Production technique of superfine cloth - Google Patents
Production technique of superfine cloth Download PDFInfo
- Publication number
- CN103215727A CN103215727A CN2013101626605A CN201310162660A CN103215727A CN 103215727 A CN103215727 A CN 103215727A CN 2013101626605 A CN2013101626605 A CN 2013101626605A CN 201310162660 A CN201310162660 A CN 201310162660A CN 103215727 A CN103215727 A CN 103215727A
- Authority
- CN
- China
- Prior art keywords
- cloth
- yarn
- ultra
- material manufacturing
- manufacturing technique
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a production technique of superfine cloth. The production technique includes that (1) according to appearance requirements of the surface of the cloth, cloth yarn meeting the requirements is selected; (2) a certain number of warps are ordered, even in breadth and wound on a warp beam of a warping machine in parallel according to the specified length; (3) multiple single yarn is combined through a doubler winder and then wound to a tube; (4) a layer of sizing agent is adhered to the periphery of each warp through a sizing machine, after drying, a size agent film is formed on each warp, hairiness is appressed, yarn is smooth and wear-resistant, and the other part of the sizing agent soaks into yarn layers; and (5) through matched motion of a weaving machine, wefts and the warps are interwoven together to form the textile meeting technique requirements. The cloth produced through the production technique is long in service life and ultrastrong in water absorbing force, and surface abrasion can not be caused in use. Dustfall is small, ion release quantity is small, and compared with wiping effect of a common wiping cloth, the wiping effect of the cloth is higher by over 10 times.
Description
Technical field
The present invention relates to a kind of ultra-fine cloth material manufacturing technique.
Background technology
Ultra-fine cloth is develop fibre in differentiation rapidly a kind of, is called as the synthetic fiber of a new generation, is a kind of textile raw material of high-quality, high-tech, typical case's representative of the shin-gosen that to be chemical fibre develop to high-tech, high emulation direction.Be to be made into by super superfine and tough and tensile fiber, have superpower institutional framework, soft tough and tensile characteristic is neither damaged the advantage that working substance and low dust fall hang down ion concentration.
Summary of the invention
The invention provides a kind of new ultra-fine cloth material manufacturing technique.
Major technique of the present invention thes contents are as follows:
A kind of ultra-fine cloth material manufacturing technique may further comprise the steps:
(1), according to the appearance requirement on cloth surface, select to adapt to the cloth yarn that requires;
(2), warping;
Warp thread length in accordance with regulations with certain radical puts in order, and fabric width is even, be wound on abreast warping machines on axle;
(3), sizing;
To adhere to one deck sizing agent around the warp thread with Sizing machines, the oven dry back forms serous coat, makes filoplume paste volt, and yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
(4), doubling;
To starch good yarn according to the total quantity of warps of fabric and become required beam of a loom with warp rebeaming machine;
(5), weave;
By weaving the routing motion of machine,, form the fabric of technological requirement with weft yarn and warp thread weave in.
Cloth yarn in the above-mentioned steps (1) is 20D nylon+20D terylene.
The following setting of parameter of warping machines in the above-mentioned steps (2):
A, the speed of a motor vehicle: 170m/min;
B, move back and separate tension force: 1 of tension link, tension force scale: little 1 quarter, pressure plate: 2;
C, coiling tension: 6kg, last item roller pressure: 2.2kg.
The following setting of parameter of Sizing machines in the above-mentioned steps (3):
A, the speed of a motor vehicle: 120m/min;
B, first baking oven, 140 degree, second baking oven, 140 degree, slurry temperature 38 degree, wax temperature 84 degree.
The following setting of parameter of warp rebeaming machine in the above-mentioned steps (4):
A, the speed of a motor vehicle: 40m/min;
B, batch a width of cloth: 170cm;
C, move back and separate tension force: 12kg;
D, coiling tension: 90kg;
E, tapering: 3%, tapered: 200%, select single magnetic.
Weave the following setting of parameter of machine in the above-mentioned steps (5):
A, the speed of a motor vehicle: 450m/min;
B, preceding 45 degree of the back rest, tension force: 1500N.
Sizing agent is for comprising in the above-mentioned steps (4):
Vinyl alcohol condensate: 35.5-43.5%
Propenyl condensate: 10.4%-46.4%
Starch: 4-8.9%
Sodium carboxymethylcellulose: 0-50%
Ethylene oxide adduct: 0.1-5%.
By technique scheme, the present invention has following advantage at least: long service life, water absorbing force superpower (imitative silk) can not cause surface abrasion during use.The dust fall amount is few, and the ion emission is few, and wiping effect is higher more than 10 times than general cleaning wiping cloth.
The specific embodiment of the present invention is provided in detail by following examples.
The specific embodiment
Reach technological means and the effect that predetermined goal of the invention is taked for further setting forth the present invention, below in conjunction with preferred embodiment, to its specific embodiment, structure, feature and the effect thereof that foundation the present invention proposes, describe in detail as after.
A kind of ultra-fine cloth material manufacturing technique may further comprise the steps:
(1), according to the appearance requirement on cloth surface, select to adapt to the cloth yarn that requires;
(2), warping;
Warp thread length in accordance with regulations with certain radical puts in order, and fabric width is even, be wound on abreast warping machines on axle;
(3), sizing;
To adhere to one deck sizing agent around the warp thread with Sizing machines, the oven dry back forms serous coat, makes filoplume paste volt, and yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
(4), doubling;
To starch good yarn according to the total quantity of warps of fabric and become required beam of a loom with warp rebeaming machine;
(5), weave;
By weaving the routing motion of machine,, form the fabric of technological requirement with weft yarn and warp thread weave in.
Cloth yarn in the above-mentioned steps (1) is 20D nylon+20D terylene.
The following setting of parameter of warping machines in the above-mentioned steps (2):
A, the speed of a motor vehicle: 170m/min;
B, move back and separate tension force: 1 of tension link, tension force scale: little 1 quarter, pressure plate: 2;
C, coiling tension: 6kg, last item roller pressure: 2.2kg.
The following setting of parameter of Sizing machines in the above-mentioned steps (3):
A, the speed of a motor vehicle: 120m/min;
B, first baking oven, 140 degree, second baking oven, 140 degree, slurry temperature 38 degree, wax temperature 84 degree.
The following setting of parameter of warp rebeaming machine in the above-mentioned steps (4):
A, the speed of a motor vehicle: 40m/min;
B, batch a width of cloth: 170cm;
C, move back and separate tension force: 12kg;
D, coiling tension: 90kg;
E, tapering: 3%, tapered: 200%, select single magnetic.
Weave the following setting of parameter of machine in the above-mentioned steps (5):
A, the speed of a motor vehicle: 450m/min;
B, preceding 45 degree of the back rest, tension force: 1500N.
Sizing agent is for comprising in the above-mentioned steps (4):
Vinyl alcohol condensate: 35.5-43.5%
Propenyl condensate: 10.4%-46.4%
Starch: 4-8.9%
Sodium carboxymethylcellulose: 0-50%
Ethylene oxide adduct: 0.1-5%.
The above, it only is preferred embodiment of the present invention, be not that the present invention is done any pro forma restriction, though the present invention discloses as above with preferred embodiment, yet be not in order to limit the present invention, any those skilled in the art, in not breaking away from the technical solution of the present invention scope, when the technology contents that can utilize above-mentioned announcement is made a little change or is modified to the equivalent embodiment of equivalent variations, in every case be the content that does not break away from technical solution of the present invention, according to technical spirit of the present invention to any simple modification that above embodiment did, equivalent variations and modification all still belong in the scope of technical solution of the present invention.
Claims (7)
1. ultra-fine cloth material manufacturing technique is characterized in that may further comprise the steps:
(1), according to the appearance requirement on cloth surface, select to adapt to the cloth yarn that requires;
(2), warping;
Warp thread length in accordance with regulations with certain radical puts in order, and fabric width is even, be wound on abreast warping machines on axle;
(3), sizing;
To adhere to one deck sizing agent around the warp thread with Sizing machines, the oven dry back forms serous coat, makes filoplume paste volt, and yarn is smooth and wear-resisting, and sizing agent another part is impregnated into layer inside, impels its cohesive force of inter-adhesive increase between fiber, improves the fracture strength of yarn;
(4), doubling;
To starch good yarn according to the total quantity of warps of fabric and become required beam of a loom with warp rebeaming machine;
(5), weave;
By weaving the routing motion of machine,, form the fabric of technological requirement with weft yarn and warp thread weave in.
2. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: the cloth yarn in the described step (1) is 20D nylon+20D terylene.
3. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: the following setting of parameter of warping machines in the described step (2):
3a, the speed of a motor vehicle: 170m/min;
3b, move back and separate tension force: 1 of tension link, tension force scale: little 1 quarter, pressure plate: 2;
3c, coiling tension: 6kg, last item roller pressure: 2.2kg.
4. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: the following setting of parameter of Sizing machines in the described step (3):
4a, the speed of a motor vehicle: 120m/min;
4b, first baking oven, 140 degree, second baking oven, 140 degree, slurry temperature 38 degree, wax temperature 84 degree.
5. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: the following setting of parameter of warp rebeaming machine in the described step (4):
5a, the speed of a motor vehicle: 40m/min;
5b, batch a width of cloth: 170cm;
5c, move back and separate tension force: 12kg;
5d, coiling tension: 90kg;
5e, tapering: 3%, tapered: 200%, select single magnetic.
6. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: the following setting of parameter of weaving machine in the described step (5):
5a, the speed of a motor vehicle: 450m/min;
5b, preceding 45 degree of the back rest, tension force: 1500N.
7. a kind of ultra-fine cloth material manufacturing technique according to claim 1 is characterized in that: sizing agent is for comprising in the described step (4):
Vinyl alcohol condensate: 35.5-43.5%
Propenyl condensate: 10.4%-46.4%
Starch: 4-8.9%
Sodium carboxymethylcellulose: 0-50%
Ethylene oxide adduct: 0.1-5%.