CN102212926A - Warp-weft heterochromatic fabric with washing effect and production method thereof - Google Patents
Warp-weft heterochromatic fabric with washing effect and production method thereof Download PDFInfo
- Publication number
- CN102212926A CN102212926A CN201110168787.9A CN201110168787A CN102212926A CN 102212926 A CN102212926 A CN 102212926A CN 201110168787 A CN201110168787 A CN 201110168787A CN 102212926 A CN102212926 A CN 102212926A
- Authority
- CN
- China
- Prior art keywords
- raw material
- fabric
- heterochromatic
- washing effect
- latitude
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a warp-weft heterochromatic fabric with washing effect and a production method thereof. Super light terylene low stretch yarns serving as a raw material A and cationic modified terylene low stretch yarns serving as a raw material B are blown by high-speed compressed air and deformed and compounded to form warps A, and the warps A are arranged; blended yarns of cationic modified terylene serving as a raw material C and viscous staple fibers serving as a raw material D are used as wefts A, and the wefts A are arranged; and combined tissues or twill tissues are adopted in the fabric. 8 healds are adopted for sequential healding; the reed count is No. 10; 3 warps/reeds are interwoven; and the operation amplitude is 180 centimeters. Different composite knot numbers are achieved by combining and selecting the yarns consisting of different fibers and adopting different winding speeds of the warps A in the high-speed compressed air blowing, deforming and compounding process; after dyeing finishing, the surface of the fabric shows irregular vertical stripes with unequal lengths, and the phenomenon is called as the washing effect; and the warp-weft heterochromatic fabric with the washing effect produced according to the process flows has rich colors and soft luster and is draping, stiff and smooth.
Description
Technical field
The present invention relates to heterochromatic fabric of longitude and latitude and production method thereof, especially relate to a kind of heterochromatic fabric of washing effect longitude and latitude and production method thereof.
Background technology
In recent years, the appearance that weaving tec fiber and fibre in differentiation emerge in an endless stream, the exploitation of textile product be variation day by day also, and the heterochromatic fabric of longitude and latitude is succinct, natural, plain and liked by the consumer with it all the time.
The heterochromatic fabric of common longitude and latitude is a dominant hue with black warp-wise and white broadwise mostly, or also some fabric is a dominant hue with white warp-wise and black broadwise, be that color is single on the whole, with low uncertainty, and the super appearance that the light low elastic polyester filament is arranged, broken this general layout, super the light low elastic polyester filament is arranged is main characteristic with the superbright flash of light.On the high-speed compressed air compounding machine and positive after the modified dacron low-stretch yarn is jointly compound, form irregular compound knot effect, produced the visual impact of washing through dyeing, the appearance of washing effect has also embodied the active sensation that flows of fabric, grain cross uses cellulose fibre, and the soft cunning of lining feel is suitable.The heterochromatic fabric of a kind of washing effect longitude and latitude is exactly that above-mentioned several fibers are organically combined, and forms by certain characteristics of combination weaving.
Summary of the invention
The object of the present invention is to provide a kind of have washing heterochromatic fabric of effect longitude and latitude and production method thereof.
The present invention solves the technical scheme that its technical problem is taked:
One, the heterochromatic fabric of a kind of washing effect longitude and latitude:
The present invention with the A raw material super have light low elastic polyester filament and B raw material sun from the modified dacron low-stretch yarn blow through high-speed compressed air the spray distortion compound after as the first warp, warp thread arrangement: first; With C raw material sun from modified dacron and with the blended yarn of D raw material viscose staple fibre as the first latitude, weft yarn arrangement: first, fabric adopts united organization or twill-weave.
Two, the heterochromatic manufacturing method of fabrics of a kind of washing effect longitude and latitude:
The step of this method is as follows:
1) apolegamy of raw material:
The A raw material: 17.78 Tex surpass the light low elastic polyester filament;
B raw material: the cation-modified low elastic polyester filament of 16.67 Tex;
C raw material: cation-modified polyester staple fiber;
D raw material: viscose staple fibre;
2) selection of composite junction subnumber and twist factor:
The control of composite junction subnumber is the selection of the convoluting speed of reel-motor, and first is through adopting 17.78 Tex
A raw material and 16.67 Tex B raw materials blow the spray distortion through high-speed compressed air, and then first is through being 34.45 Tex, the composite junction subnumber be chosen as 60～80/meter;
It is the single thread that 65/35 ratio blending becomes 23.5 Tex by mass percentage that the first latitude adopts C raw material and D raw material, and twist factor is 435～485;
3) fabric product basic specification:
Gait and adopt 8 along wearing;
Porter: 10# penetrates: 3 organizine/reeds, the last gate width of cloth: 180cm;
4) product process flow:
(1) weave processing process:
Warp thread: ingredient inspection → twist thread → warping → gait, denting →;
Weft yarn: ingredient inspection → twist thread → rewinding →;
Warp thread and weft yarn are weaved in the lump then;
(2) back finishing process flow process:
Grey cloth check → debatching margin to seam → preshrunk → dyeing → pine baking → typing → jar steaming → check → clot warehouse-in.
By four kinds of fibrous yarn combination being selected for use and first adopts different coiling speeds to reach different composite junction subnumbers through reel-motor in blow the spray deforming process through high-speed compressed air, after the dyeing arrangement, fabric face presents the irregular vertical striped that is uneven in length (this kind phenomenon is called the washing effect), and the heterochromatic fabric color of producing according to the said goods technological process of washing effect longitude and latitude enriches, color and luster is soft, fabric dangles well-pressed.
The beneficial effect that the present invention has is:
The present invention is by selecting for use the fibrous material combination of difference, and according to selected product process flow, the heterochromatic manufacturing method of fabrics color of a kind of washing effect longitude and latitude of production is abundant, color and luster is soft, washing is effective.
Description of drawings
Fig. 1 is a kind of fabric united organization figure of the present invention.
Fig. 2 is another kind of fabric twill-weave figure of the present invention.
The specific embodiment
Select following A, B, four kinds of raw materials of C, D:
The A raw material: 17.78 Tex surpass the light low elastic polyester filament;
B raw material: the cation-modified low elastic polyester filament of 16.67 Tex;
C raw material: cation-modified polyester staple fiber;
D raw material: viscose staple fibre.
Embodiment 1:
Adopt four kinds of raw materials of A, B, C, D of said ratio.
The first warp: it is compound to adopt two A raw materials and B raw material to blow spray distortion through high-speed compressed air, and then first is 17.78Tex through fineness, and the reel-motor coiling speed is selected 300 meters/minute, and the composite junction subnumber is selected 80/meter;
The first latitude: adopting mass percent is that 65 C raw material and mass percent are to add the suitable twist again after 35 the D raw material blending, and then the first latitude is 23.5 Tex;
Last machine is selected porter 10# for use, penetrates: 3 organizine/reeds, and the last gate width of cloth: 180cm gaits and adopts 8 along wearing; Line version organization chart is selected shown in Figure 1.After the dyed back arrangement of the fabric of weaving was handled, the A stock chart revealed and stays white effect, and the washing effect appears in the compound back of A raw material and B raw material, and the cloth cover color is soft, and is well arranged, illustrates that weaving with dyeing is to meet the fabric requirement.
Embodiment 2:
Adopt four kinds of raw materials of A, B, C, D of said ratio.
The first warp: adopt two A raw materials and B raw material to blow the spray distortion through high-speed compressed air, then first is 17.78Tex through fineness, and the reel-motor coiling speed is selected 315 meters/minute, and the composite junction subnumber is selected 70/meter;
The first latitude: adopting mass percent is that 65 C raw material and mass percent are to add the suitable twist again after 35 the D raw material blending, and then the first latitude is 23.5 Tex;
Last machine is selected porter 10# for use, penetrates: 3 organizine/reeds, and the last gate width of cloth: 180cm gaits and adopts 8 along wearing; Line version organization chart is selected shown in Figure 2.After the dyed back arrangement of the fabric of weaving was handled, the A stock chart revealed and stays white effect, and the washing effect appears in the compound back of A raw material and B raw material, and the cloth cover color is soft, and is well arranged, illustrates that weaving with dyeing is to meet the fabric requirement.
Embodiment 3:
Adopt four kinds of raw materials of A, B, C, D of said ratio.
The first warp: adopt two A raw materials and B raw material to blow the spray distortion through high-speed compressed air, then first is 17.78Tex through fineness, and the reel-motor coiling speed is selected 330 meters/minute, and the composite junction subnumber is selected 60/meter;
The first latitude: adopting mass percent is that 65 C raw material and mass percent are to add the suitable twist again after 35 the D raw material blending, and then the first latitude is 23.5 Tex;
Last machine is selected porter 10# for use, penetrates: 3 organizine/reeds, and the last gate width of cloth: 180cm gaits and adopts 8 along wearing; Line version organization chart is selected shown in Figure 2.After the dyed back arrangement of the fabric of weaving was handled, the A stock chart revealed and stays white effect, and the washing effect appears in the compound back of A raw material and B raw material, and the cloth cover color is soft, and is well arranged, illustrates that weaving with dyeing is to meet the fabric requirement.
Claims (3)
1. one kind has washing effect longitude and latitude heterochromatic fabric, it is characterized in that: with the A raw material super have light low elastic polyester filament and B raw material sun from the modified dacron low-stretch yarn blow through high-speed compressed air the spray distortion compound after as the first warp, warp thread arrangement: first; With C raw material sun from modified dacron and with the blended yarn of D raw material viscose staple fibre as the first latitude, weft yarn arrangement: first, fabric adopts united organization or twill-weave.
2. one kind has the heterochromatic manufacturing method of fabrics of washing effect longitude and latitude, it is characterized in that its step is as follows:
1) apolegamy of raw material:
The A raw material: 17.78 Tex surpass the light low elastic polyester filament;
B raw material: the cation-modified low elastic polyester filament of 16.67 Tex;
C raw material: cation-modified polyester staple fiber;
D raw material: viscose staple fibre;
2) selection of composite junction subnumber and twist factor:
The control of composite junction subnumber is that the convoluting speed of reel-motor selects, and first is blown the spray distortion through adopting 17.78 Tex A raw materials and 16.67 Tex B raw materials through high-speed compressed air, and then first is through being 34.45 Tex, the composite junction subnumber be chosen as 60～80/meter;
It is the single thread that 65/35 ratio blending becomes 23.5 Tex by mass percentage that the first latitude adopts C raw material and D raw material, and twist factor is 435～485;
3) fabric product basic specification:
Gait and adopt 8 along wearing;
Porter: 10# penetrates: 3 organizine/reeds, the last gate width of cloth: 180cm;
4) product process flow:
(1) weave processing process:
Warp thread: ingredient inspection → twist thread → warping → gait, denting →;
Weft yarn: ingredient inspection → twist thread → rewinding →;
Warp thread and weft yarn are weaved in the lump then;
(2) back finishing process flow process:
Grey cloth check → debatching margin to seam → preshrunk → dyeing → pine baking → typing → jar steaming → check → clot warehouse-in.
3. a kind of heterochromatic manufacturing method of fabrics of washing effect longitude and latitude that has according to claim 2, it is characterized in that: by four kinds of fibrous yarn combination being selected for use and first adopts different coiling speeds to reach different composite junction subnumbers through reel-motor in blow the spray deforming process through high-speed compressed air, after the dyeing arrangement, fabric face presents the irregular vertical striped that is uneven in length, and the heterochromatic fabric color of producing according to the said goods technological process of washing effect longitude and latitude enriches, color and luster is soft, fabric dangles well-pressed.