CN103193741A - 光固化顺酐桐油丙烯酸树脂及其制备方法 - Google Patents
光固化顺酐桐油丙烯酸树脂及其制备方法 Download PDFInfo
- Publication number
- CN103193741A CN103193741A CN201310107502XA CN201310107502A CN103193741A CN 103193741 A CN103193741 A CN 103193741A CN 201310107502X A CN201310107502X A CN 201310107502XA CN 201310107502 A CN201310107502 A CN 201310107502A CN 103193741 A CN103193741 A CN 103193741A
- Authority
- CN
- China
- Prior art keywords
- acid
- tung oil
- maleic anhydride
- photocurable
- acrylic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了光固化顺酐或富马酸桐油丙烯酸树脂及其制备方法,其技术解决方案如下:本产品由1mol桐油酸、2mol顺丁烯二酸酐(或富马酸)和4~5mol羟基丙烯酸单体组成。先将桐油采用高压水解以获取α-桐油酸,然后采用顺丁烯二酸酐或富马酸与α-桐油酸共轭双键进行加成反应,生成顺或反丁烯二酸化桐油酸,再用丙烯酸羟乙酯(HEA)或丙烯酸羟丙酯(HPA)或甲基丙烯酸羟乙酯(HEMA)或甲基丙烯酸羟丙酯(HPMA)与之进行酯化反应,得到几种4~5官能度的高活性顺丁烯二酸酐化桐油五丙烯酸光固化树脂。该产品具有环保、无溶剂、耐水解等特性,且漆膜具有优异的硬度与柔韧性。由于使用可再生资源取代部分石化产品,经该产品涂装工件废弃后,其漆膜易于降解,不会像纯化学涂膜对环境造成危害。该树脂加入光引发剂后,可制备光固化各类涂料、油墨等。
Description
技术领域
本发明属于一种UV用合成树脂。
背景技术
众所周知,目前广泛使用之UV树脂由聚合物单体与预聚体组成,都有强烈刺激性、腐蚀性、毒性,各个企业在不断提升UV涂料性能的同时并没有太多相应的降低其危害性的措施。经检索相关的专利技术,在该方面相应的专利技术并不多,因此特提出该方案。该方案旨在降低UV树脂对人体的危害性,并使用可再生资源取代部分石油产品,经该产品涂装之工件在废弃后可进行降解,而不像纯化学涂膜那样对环境造成伤害。
发明内容
本发明的目的就在于针对上述现有技术的缺陷而提供一种能够降低UV树脂对人体的危害,并降低UV涂料涂膜在废弃后对环境造成的危害的光固化顺酐(或富马酸)桐油丙烯酸树脂及其制备方法。
其技术解决方案如下:本产品由1mol桐油酸、2mol顺丁烯二酸酐(或富马酸)和4~5mol羟基丙烯酸单体组成。先将桐油采用高压水解以获取α-桐油酸,然后采用顺丁烯二酸酐(或富马酸)与α-桐油酸共轭双键进行加成反应,生成顺(或反)丁烯二酸化桐油酸,再用丙烯酸羟乙酯(HEA)或丙烯酸羟丙酯(HPA)或甲基丙烯酸羟乙酯(HEMA)或甲基丙烯酸羟丙酯(HPMA)与之进行酯化反应,得到几种4~5官能度的高活性顺丁烯二酸酐化桐油五丙烯酸光固化树脂。
该产品具有环保、无溶剂、耐水解等特性,且漆膜具有优异的硬度与柔韧性。由于使用可再生资源取代部分石化产品,经该产品涂装工件废弃后,其漆膜易于降解,不会像纯化学涂膜对环境造成危害。该树脂加入光引发剂后,可制备光固化各类涂料、油墨等。
具体实施方式
1、 先将桐油采用高压水解以获取α-桐油酸。
2、 采用2mol顺丁烯二酸酐(或富马酸)与1molα-桐油酸共轭双键进行加成反应,反应温度为200~240℃,则可生成顺(或反)丁烯二酸化桐油酸。
3、 再用4~5mol丙烯酸羟乙酯(HEA)或丙烯酸羟丙酯(HPA)或甲基丙烯酸羟乙酯(HEMA)或甲基丙烯酸羟丙酯(HPMA)与加成后桐油酸进行酯化反应,反应温度为160~200℃,待反应完全后,得到几种4~5官能度的高活性顺丁烯二酸酐化桐油五丙烯酸光固化树脂。
Claims (2)
1.光固化顺酐或富马酸桐油丙烯酸树脂,其特征在于是由1mol桐油酸、2mol顺丁烯二酸酐或富马酸和4~5mol羟基丙烯酸单体组成。
2.一种制备如权利要求1所述的光固化顺酐或富马酸桐油丙烯酸树脂的方法,先将桐油采用高压水解以获取α-桐油酸,然后采用顺丁烯二酸酐或富马酸与α-桐油酸共轭双键进行加成反应,生成顺或反丁烯二酸化桐油酸,再用丙烯酸羟乙酯或丙烯酸羟丙酯或甲基丙烯酸羟乙酯或甲基丙烯酸羟丙酯与之进行酯化反应,得到几种4~5官能度的高活性顺丁烯二酸酐化桐油五丙烯酸光固化树脂。