CN103184549A - 一种锦纶6粗旦丝的生产方法 - Google Patents

一种锦纶6粗旦丝的生产方法 Download PDF

Info

Publication number
CN103184549A
CN103184549A CN 201110451759 CN201110451759A CN103184549A CN 103184549 A CN103184549 A CN 103184549A CN 201110451759 CN201110451759 CN 201110451759 CN 201110451759 A CN201110451759 A CN 201110451759A CN 103184549 A CN103184549 A CN 103184549A
Authority
CN
China
Prior art keywords
production method
nylon
thick denier
denier yarn
slice
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110451759
Other languages
English (en)
Inventor
田永圣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG MEIMING POLYAMIDE Co Ltd
Original Assignee
NANTONG MEIMING POLYAMIDE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG MEIMING POLYAMIDE Co Ltd filed Critical NANTONG MEIMING POLYAMIDE Co Ltd
Priority to CN 201110451759 priority Critical patent/CN103184549A/zh
Publication of CN103184549A publication Critical patent/CN103184549A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种锦纶6粗旦丝的生产方法,包括以下步骤:以锦纶6切片为原料,分别经过切片料斗、螺杆挤压机、纺丝箱体、冷却室、油嘴上油,再通过冷拉伸辊、热辊定型和网络器,最后进行卷绕,所说的纺丝箱体内的温度为255-260摄氏度;所说的卷绕速度为4300m/min;所说的热定型温度为170摄氏度。本发明的锦纶6粗旦丝的生产方法,具有如下技术效果:能够生产出单丝纤度超过9dtex的粗旦长丝,产品质量稳定。

Description

一种锦纶6粗旦丝的生产方法
技术领域
    本发明涉及一种锦纶6粗旦丝的生产方法,属于化纤技术领域。
背景技术
随着锦纶6长丝技术的发展,具有新型特征的纤维博得了广大消费者的青睐,其利润空间大,市场广阔,因此,具有很好的市场前景。
锦纶6粗旦丝可以用于箱包、帐篷、花边和装饰布等领域,因此具有广泛的应用前景。
目前尚未有适合锦纶6粗旦丝的生产方法。
发明内容
本发明的目的是克服现有技术的不足之处,提供一种锦纶6粗旦丝的生产方法。
本发明的锦纶6粗旦丝的生产方法,包括以下步骤:以锦纶6切片为原料,分别经过切片料斗、螺杆挤压机、纺丝箱体、冷却室、油嘴上油,再通过冷拉伸辊、热辊定型和网络器,最后进行卷绕,
所说的纺丝箱体内的温度为255-260摄氏度。
所说的卷绕速度为4300m/min。
所说的热定型温度为170摄氏度。
本发明的锦纶6粗旦丝的生产方法,具有如下技术效果:能够生产出单丝纤度超过9dtex的粗旦长丝,产品质量稳定。
具体实施方式
实施例1
本实施例的锦纶6粗旦丝的生产方法,包括以下步骤:以锦纶6切片为原料,分别经过切片料斗、螺杆挤压机、纺丝箱体、冷却室、油嘴上油,再通过冷拉伸辊、热辊定型和网络器,最后进行卷绕。纺丝箱体内的温度为255-260摄氏度。卷绕速度为4300m/min。热定型温度为170摄氏度。

Claims (1)

1.锦纶6粗旦丝的生产方法,包括以下步骤:以锦纶6切片为原料,分别经过切片料斗、螺杆挤压机、纺丝箱体、冷却室、油嘴上油,再通过冷拉伸辊、热辊定型和网络器,最后进行卷绕,
其特征在于,
所说的纺丝箱体内的温度为255-260摄氏度;
所说的卷绕速度为4300m/min;
所说的热定型温度为170摄氏度。
CN 201110451759 2011-12-30 2011-12-30 一种锦纶6粗旦丝的生产方法 Pending CN103184549A (zh)