CN103173870A - 一种以稻秸秆为原料制备天然纤维素纤维的制备方法 - Google Patents

一种以稻秸秆为原料制备天然纤维素纤维的制备方法 Download PDF

Info

Publication number
CN103173870A
CN103173870A CN2013100605086A CN201310060508A CN103173870A CN 103173870 A CN103173870 A CN 103173870A CN 2013100605086 A CN2013100605086 A CN 2013100605086A CN 201310060508 A CN201310060508 A CN 201310060508A CN 103173870 A CN103173870 A CN 103173870A
Authority
CN
China
Prior art keywords
rice straw
straw fiber
humidification
condition
raw
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013100605086A
Other languages
English (en)
Inventor
陈夕方
陈华芳
陈静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DANYANG CHAOCHAO GARMENT Co Ltd
Original Assignee
DANYANG CHAOCHAO GARMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DANYANG CHAOCHAO GARMENT Co Ltd filed Critical DANYANG CHAOCHAO GARMENT Co Ltd
Priority to CN2013100605086A priority Critical patent/CN103173870A/zh
Publication of CN103173870A publication Critical patent/CN103173870A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种以稻秸秆为原料制备天然纤维素纤维的制备方法,包括以下步骤:预处理,机械碾压,碱处理,双氧水处理,软化处理,加湿焖放,梳理。本发明以稻秸秆为原料,用以制备天然纤维素纤维,解决稻秸秆在纺织工业中作为纺织原料应用较少的问题,且我国水稻资源丰富,资源循环利用,不仅能够减少我国因水稻的稻秸秆利用不当造成环境污染的问题,而且节能,资源利用率较高。

Description

一种以稻秸秆为原料制备天然纤维素纤维的制备方法
技术领域
[0001] 本发明属于纺织技术领域,具体涉及一种以稻秸杆为原料制备天然纤维素纤维的制备方法。
背景技术
[0002] 我国是一个农业大国,拥有较多的水稻资源,国内水稻的分布也较为广泛。我国秸杆每年产量达7亿,水稻属于禾本科植物,其中稻秸杆约占27.5%,而丰富的稻秸杆资源在我国的利用率却很低。稻秸杆是天然的再生性高分子资源,可以对其资源化利用,开发出环境友好的绿色产品。
发明内容
[0003] 本发明所要解决的技术问题是提供一种以稻秸杆为原料制备天然纤维素纤维的制备方法,解决稻秸杆在纺织工业中作为纺织原料应用较少的问题。
[0004] 为解决上述技术问题,本发明提供了一种以稻秸杆为原料制备天然纤维素纤维的制备方法,依次包括以下步骤:
(1)预处理:将稻秸杆和水按质量比1:20-40混合,在温度70-90°C的条件下,处理l-2h ;
(2)机械碾压:将预处理的稻秸杆进行机械碾压1-3遍,碾压后进行水洗;
(3)碱处理:将水洗后的稻秸杆放入质量浓度为10-30g/L的氢氧化钠溶液中,在温度为80-100°C的条件下处理l_3h,处理得到稻秸杆纤维,然后将其取出并水洗;
(4)双氧水处理:将碱处理后的稻秸杆纤维放入2-6g/L的双氧水溶液中,在温度50-600C的条件下处理5-15min,然后将稻秸杆纤维取出,并水洗;
(5)软化处理:按质量比1:10-30,称取稻秸杆纤维及质量浓度为4-8g/L的纤维素软化齐U,并将稻秸杆纤维放入溶液中,在温度60-80°C的条件下处理30-60min,然后取出脱水烘干;
(6)加湿焖放:将软化处理后的稻秸杆纤维进行均匀加湿,稻秸杆纤维与水的质量比为1:0.5-1.5,加湿后焖放 12-24h ;
(7)梳理:将加湿焖放后的稻秸杆纤维,在梳理机上梳理1-3遍,即制得稻秸杆天然纤维素纤维。
[0005] 本发明的技术效果:本发明以稻秸杆为原料,用以制备天然纤维素纤维,解决稻秸杆在纺织工业中作为纺织原料应用较少的问题,且我国水稻资源丰富,资源循环利用,不仅能够减少我国因水稻的稻秸杆利用不当造成环境污染的问题,而且节能,资源利用率较高。
具体实施方式
[0006] 实施例1
本实施例的以稻秸杆为原料制备天然纤维素纤维的制备方法,依次包括以下步骤:(1)预处理:将稻秸杆和水按质量比1:20混合,在温度70°C的条件下,处理2h ;
(2)机械碾压:将预处理的稻秸杆进行机械碾压2遍,碾压后进行水洗;
(3)碱处理:将水洗后的稻秸杆放入质量浓度为10g/L的氢氧化钠溶液中,在温度为80°C的条件下处理2h,处理得到稻秸杆纤维,然后将其取出并水洗;
(4)双氧水处理:将碱处理后的稻秸杆纤维放入2g/L的双氧水溶液中,在温度50°C的条件下处理lOmin,然后将稻秸杆纤维取出,并水洗;
(5)软化处理:按质量比1:10,称取稻秸杆纤维及质量浓度为4g/L的纤维素软化剂,并将稻秸杆纤维放入溶液中,在温度80°C的条件下处理30min,然后取出脱水烘干;
(6)加湿焖放:将软化处理后的稻秸杆纤维进行均匀加湿,稻秸杆纤维与水的质量比为I:0.5,加湿后烟放12h ;
(7)梳理:将加湿焖放后的稻秸杆纤维,在梳理机上梳理2遍,即制得稻秸杆天然纤维素纤维。
[0007] 实施例2
本实施例的以稻秸杆为原料制备天然纤维素纤维的制备方法,依次包括以下步骤:
(1)预处理:将稻秸杆和水按质量比1:30混合,在温度80°C的条件下,处理Ih ;
(2)机械碾压:将预处理的稻秸杆进行机械碾压3遍,碾压后进行水洗;
(3)碱处理:将水洗后的稻秸杆放入质量浓度为20g/L的氢氧化钠溶液中,在温度为100°C的条件下处理2h,处理得到稻秸杆纤维,然后将其取出并水洗;
(4)双氧水处理:将碱处理后的稻秸杆纤维放入6g/L的双氧水溶液中,在温度60°C的条件下处理5min,然后将稻秸杆纤维取出,并水洗;
(5)软化处理:按质量比1:20,称取稻秸杆纤维及质量浓度为6g/L的纤维素软化剂,并将稻秸杆纤维放入溶液中,在温度70°C的条件下处理45min,然后取出脱水烘干;
(6)加湿焖放:将软化处理后的稻秸杆纤维进行均匀加湿,稻秸杆纤维与水的质量比为1:1,加湿后烟放18h ;
(7)梳理:将加湿焖放后的稻秸杆纤维,在梳理机上梳理3遍,即制得稻秸杆天然纤维素纤维。
[0008] 实施例3
本实施例的以稻秸杆为原料制备天然纤维素纤维的制备方法,依次包括以下步骤:
(1)预处理:将稻秸杆和水按质量比1: 40混合,在温度90°C的条件下,处理Ih ;
(2)机械碾压:将预处理的稻秸杆进行机械碾压3遍,碾压后进行水洗;
(3)碱处理:将水洗后的稻秸杆放入质量浓度为30g/L的氢氧化钠溶液中,在温度为90°C的条件下处理3h,处理得到稻秸杆纤维,然后将其取出并水洗;
(4)双氧水处理:将碱处理后的稻秸杆纤维放入6g/L的双氧水溶液中,在温度60°C的条件下处理15min,然后将稻秸杆纤维取出,并水洗;
(5)软化处理:按质量比1:30,称取稻秸杆纤维及质量浓度为8g/L的纤维素软化剂,并将稻秸杆纤维放入溶液中,在温度80°C的条件下处理60min,然后取出脱水烘干;
(6)加湿焖放:将软化处理后的稻秸杆纤维进行均匀加湿,稻秸杆纤维与水的质量比为I: 1.5,加湿后烟放24h ;
(7)梳理:将加湿焖放后的稻秸杆纤维,在梳理机上梳理3遍,即制得稻秸杆天然纤维素纤维。

Claims (1)

1.一种以稻秸杆为原料制备天然纤维素纤维的制备方法,其特征在于依次包括以下步骤: (1)预处理:将稻秸杆和水按质量比1:20-40混合,在温度70-90°C的条件下,处理l-2h ; (2)机械碾压:将预处理的稻秸杆进行机械碾压1-3遍,碾压后进行水洗; (3)碱处理:将水洗后的稻秸杆放入质量浓度为10-30g/L的氢氧化钠溶液中,在温度为80-100°C的条件下处理l_3h,处理得到稻秸杆纤维,然后将其取出并水洗; (4)双氧水处理:将碱处理后的稻秸杆纤维放入2-6g/L的双氧水溶液中,在温度50-600C的条件下处理5-15min,然后将稻秸杆纤维取出,并水洗; (5)软化处理:按质量比1:10-30,称取稻秸杆纤维及质量浓度为4-8g/L的纤维素软化齐U,并将稻秸杆纤维放入溶液中,在温度60-80°C的条件下处理30-60min,然后取出脱水烘干; (6)加湿焖放:将软化处理后的稻秸杆纤维进行均匀加湿,稻秸杆纤维与水的质量比为1:0.5-1.5,加湿后焖放 12-24h ; (7)梳理:将加湿焖放后的稻秸杆纤维,在梳理机上梳理1-3遍。
CN2013100605086A 2013-02-27 2013-02-27 一种以稻秸秆为原料制备天然纤维素纤维的制备方法 Pending CN103173870A (zh)