CN103173139A - 一种尿醛树脂-氯丁橡胶胶黏剂及其制备方法 - Google Patents

一种尿醛树脂-氯丁橡胶胶黏剂及其制备方法 Download PDF

Info

Publication number
CN103173139A
CN103173139A CN2013100599390A CN201310059939A CN103173139A CN 103173139 A CN103173139 A CN 103173139A CN 2013100599390 A CN2013100599390 A CN 2013100599390A CN 201310059939 A CN201310059939 A CN 201310059939A CN 103173139 A CN103173139 A CN 103173139A
Authority
CN
China
Prior art keywords
parts
chloroprene rubber
ureaformaldehyde resin
precondensed ureaformaldehyde
adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013100599390A
Other languages
English (en)
Other versions
CN103173139B (zh
Inventor
徐冉阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Huibang paint Co., Ltd
Original Assignee
ANHUI MINGZHU PIGMENT TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI MINGZHU PIGMENT TECHNOLOGY Co Ltd filed Critical ANHUI MINGZHU PIGMENT TECHNOLOGY Co Ltd
Priority to CN201310059939.0A priority Critical patent/CN103173139B/zh
Publication of CN103173139A publication Critical patent/CN103173139A/zh
Application granted granted Critical
Publication of CN103173139B publication Critical patent/CN103173139B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种尿醛树脂-氯丁橡胶胶黏剂，包括以下重量份的原料：苯乙烯100-120、乙酸乙酯100-150、氯丁橡胶CR121 20-25、二甲苯15-20、4,4'-二苯基甲烷二异氰酸酯1-2、聚异丁烯8-12、3-氨丙基三甲氧基硅烷2-3、聚四氢呋喃醚二醇2-3、尿醛树脂15-20、二茂铁1-2、丁基橡胶CBK139 5-10、环氧油酸丁酯2-4等。本发明胶黏剂具有优良的耐热性、耐水性，粘结强度高，耐水防潮，贮存稳定性好，环保性好，使用效果好且方便、应用范围广，适用于人造革、合成革、塑料、尼龙、有机玻璃的粘合，也适用于制鞋行业。

Description

一种尿醛树脂-氯丁橡胶胶黏剂及其制备方法
技术领域
本发明涉及一种尿醛树脂-氯丁橡胶胶黏剂及其制备方法，属于化工技术领域。
背景技术
氯丁橡胶是一种被大量生产的合成橡胶化合物，制作的胶黏剂应用范围广。氯丁橡胶的结构比较规整，又有极性较大的氯原子，故结晶性高，其在室温下就有较好的粘接性能和较大的内聚强度，非常适宜作胶黏剂，氯丁胶黏剂特性是：初始粘力大、粘接强度高、耐久性好、胶层柔韧，弹性良好，耐冲击与振动，有较好的耐油、耐水、耐碱、耐酸、耐溶剂性能，对多种材料都有较好的粘接性，使用方便，价格低廉，但耐热性较差，耐水性不佳，贮存稳定性差。为了克服传统的氯丁胶黏剂耐热性较差，耐水性不佳，贮存稳定性差，毒性大等缺点，通过改进配方，加入尿醛树脂等其他原料，从而生产出一种新型尿醛树脂-氯丁橡胶胶黏剂。
发明内容
本发明的目的是提供一种具有优良的耐热性、耐水性和贮存稳定性的尿醛树脂-氯丁橡胶胶黏剂及其制备方法。
本发明采用的技术方案如下：  
    一种尿醛树脂-氯丁橡胶胶黏剂，由下列重量份的原料制成：苯乙烯100-120、乙酸乙酯100-150、氯丁橡胶CR121 20-25、二甲苯15-20、4,4'-二苯基甲烷二异氰酸酯1-2、聚异丁烯8-12、3-氨丙基三甲氧基硅烷2-3、聚四氢呋喃醚二醇2-3、尿醛树脂15-20、二茂铁1-2、丁基橡胶CBK139 5-10、环氧油酸丁酯2-4、甲基丙烯酸正丁酯3-5、硫磺0.5-1、硬脂酸钙1-2、氧化锌1-2、二甲基二巯基乙酸异辛酯锡1-2、纳米陶土10-15、纳米二氧化硅20-25、钛酸酯偶联剂TMC-TTS 1-2、过氧化二异丙苯1-2、促进剂CBS 0.5-1.5、促进剂Na-22 0.1-0.2、防老剂ODA 1-2、防老剂RD 1-2、交联剂 TAIC 1-2、改性淀粉2-4。
    所述的改性淀粉由以下步骤制得：向玉米干淀粉中8-12%的三聚磷酸钠、5-10%的木质素、4-6%的草木灰、20-30%的水，充分混合均匀，将其干燥至含水量5-10%，加入膨化罐后在140-160℃加热2-3h，将产物冷却、干燥、粉碎后加入挤压机中经螺旋加热而糊化、膨胀，干燥、粉碎后，研磨成粉末即可。
    尿醛树脂-氯丁橡胶胶黏剂的制备方法，包括以下步骤：
    （1）将氯丁橡胶CR121、二甲苯、4,4’-二苯基甲烷二异氰酸酯、聚异丁烯、3-氨丙基三甲氧基硅烷、聚四氢呋喃醚二醇、尿醛树脂、二茂铁、丁基橡胶CBK139混合，在100-120℃下反应1-2h；
    （2）将其它物料与反应物混合，搅拌30-40min，得到成品，包装即可。
    本发明的有益效果：
 本发明通过三聚磷酸、木质素和草木灰对玉米淀粉进行改性，提高了其胶合强度和耐水性，从而可以明显改善尿醛树脂-氯丁橡胶胶黏剂的粘接强度和耐水性,并具有成本低,效果优良的特点。本发明胶黏剂具有优良的耐热性、耐水性，粘结强度高，耐水防潮，贮存稳定性好，环保性好，使用效果好且方便、应用范围广，适用于人造革、合成革、塑料、尼龙、有机玻璃的粘合，也适用于制鞋行业。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例    
    一种尿醛树脂-氯丁橡胶胶黏剂，由下列重量份的原料制成：苯乙烯105份、乙酸乙酯120份、氯丁橡胶CR121 25份、二甲苯18份、4,4'-二苯基甲烷二异氰酸酯1.6份、聚异丁烯10份、3-氨丙基三甲氧基硅烷2.5份、聚四氢呋喃醚二醇2份、尿醛树脂18份、二茂铁1.8份、丁基橡胶CBK139 6份、环氧油酸丁酯3份、甲基丙烯酸正丁酯4份、硫磺0.6份、硬脂酸钙1.5份、氧化锌1.2份、二甲基二巯基乙酸异辛酯锡1.6份、纳米陶土12份、纳米二氧化硅24份、钛酸酯偶联剂TMC-TTS 1.5份、过氧化二异丙苯2份、促进剂CBS 0.8份、促进剂Na-22 0.15份、防老剂ODA 1.5份、防老剂RD 1.5份、交联剂 TAIC 1.6份、改性淀粉3份。
    其中，所述的改性淀粉由以下步骤制得：向玉米干淀粉中10%的三聚磷酸钠、8%的木质素、5%的草木灰、25%的水，充分混合均匀，将其干燥至含水量6%，加入膨化罐后在150℃加热3h，将产物冷却、干燥、粉碎后加入挤压机中经螺旋加热而糊化、膨胀，干燥、粉碎后，研磨成粉末即可。
    尿醛树脂-氯丁橡胶胶黏剂的制备方法，包括以下步骤：
（1）将氯丁橡胶CR121、二甲苯、4,4’-二苯基甲烷二异氰酸酯、聚异丁烯、3-氨丙基三甲氧基硅烷、聚四氢呋喃醚二醇、尿醛树脂、二茂铁、丁基橡胶CBK139混合，在105℃下反应2h；
（2）将其它物料与反应物混合，搅拌40min，得到成品，包装即可。
    本实施例制得的尿醛树脂-氯丁橡胶胶黏剂的主要性能如下表1。
表1
耐水，在水中浸泡12个月，剥离强度下降5%。

Claims (3)

1.一种尿醛树脂-氯丁橡胶胶黏剂，其特征在于，由下列重量份的原料制成：苯乙烯100-120、乙酸乙酯100-150、氯丁橡胶CR121 20-25、二甲苯15-20、4,4'-二苯基甲烷二异氰酸酯1-2、聚异丁烯8-12、3-氨丙基三甲氧基硅烷2-3、聚四氢呋喃醚二醇2-3、尿醛树脂15-20、二茂铁1-2、丁基橡胶CBK139 5-10、环氧油酸丁酯2-4、甲基丙烯酸正丁酯3-5、硫磺0.5-1、硬脂酸钙1-2、氧化锌1-2、二甲基二巯基乙酸异辛酯锡1-2、纳米陶土10-15、纳米二氧化硅20-25、钛酸酯偶联剂TMC-TTS 1-2、过氧化二异丙苯1-2、促进剂CBS 0.5-1.5、促进剂Na-22 0.1-0.2、防老剂ODA 1-2、防老剂RD 1-2、交联剂 TAIC 1-2、改性淀粉2-4。
2.根据权利要求1所述的尿醛树脂-氯丁橡胶胶黏剂，其特征在于，所述的改性淀粉由以下步骤制得：向玉米干淀粉中8-12%的三聚磷酸钠、5-10%的木质素、4-6%的草木灰、20-30%的水，充分混合均匀，将其干燥至含水量5-10%，加入膨化罐后在140-160℃加热2-3h，将产物冷却、干燥、粉碎后加入挤压机中经螺旋加热而糊化、膨胀，干燥、粉碎后，研磨成粉末即可。
3.一种如权利要求1所述的尿醛树脂-氯丁橡胶胶黏剂的制备方法，其特征在于包括以下步骤：
    （1）将氯丁橡胶CR121、二甲苯、4,4’-二苯基甲烷二异氰酸酯、聚异丁烯、3-氨丙基三甲氧基硅烷、聚四氢呋喃醚二醇、尿醛树脂、二茂铁、丁基橡胶CBK139混合，在100-120℃下反应1-2h；
    （2）将其它物料与反应物混合，搅拌30-40min，得到成品，包装即可。
CN201310059939.0A 2013-02-26 2013-02-26 一种尿醛树脂-氯丁橡胶胶黏剂及其制备方法 Active CN103173139B (zh)