CN103173085A - 一种防污涂料 - Google Patents

一种防污涂料 Download PDF

Info

Publication number
CN103173085A
CN103173085A CN 201310088042 CN201310088042A CN103173085A CN 103173085 A CN103173085 A CN 103173085A CN 201310088042 CN201310088042 CN 201310088042 CN 201310088042 A CN201310088042 A CN 201310088042A CN 103173085 A CN103173085 A CN 103173085A
Authority
CN
China
Prior art keywords
antifouling paint
agent
paint according
solvent
superpolymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201310088042
Other languages
English (en)
Inventor
吴旭明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NINGBO SANLI NEW MATERIALS CO Ltd
Original Assignee
NINGBO SANLI NEW MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGBO SANLI NEW MATERIALS CO Ltd filed Critical NINGBO SANLI NEW MATERIALS CO Ltd
Priority to CN 201310088042 priority Critical patent/CN103173085A/zh
Publication of CN103173085A publication Critical patent/CN103173085A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防污涂料，其特征在于：所述防污涂料按重量百分比以如下成份组成而成，不含锡降阻高聚物30％-50％，毒料20％-40％，辅助基料2％-5％，颜料5％-10％，溶剂10％-20％和助剂4％-7％，本发明毒量低，不危害海洋环境，与防锈涂料配合，使得船体的物理性能优良，涂膜光滑平整，降阻性能良好，磨蚀速率均匀，节能降耗。

Description

一种防污涂料
技术领域
本发明涉及一种防污涂料。
背景技术
海洋中有许多生物会附着于船底和海洋水下设备，这些附着生物对船舶和海洋水下设施危害巨大，它们显著增加船体质量，增大航行阻力，影响船舶航速，从而增加燃料消耗。防污涂料采用汞、砷等化合物为毒料，对海洋环境的污染大，严重影响海生物生长繁殖，甚至引起遗传变异。
发明内容
本发明要解决的技术问题是提供一种长效防污和降阻节能的特点，同时符合环境保护要求的防污涂料。
为解决以上技术问题，本发明采用以下技术方案来实现的：一种防污涂料，所述防污涂料按重量百分比以如下成份组成而成，
不含锡降阻高聚物  30％-50％
毒料  20％-40％
辅助基料  2％-5％
颜料  5％-10％
溶剂  10％-20％
助剂  4％-7％
进一步地，所述不含锡降阻高聚物内有聚丙烯酸树脂为基料。
进一步地，所述毒料由氧化亚铜、铜粉以及低毒有机防污剂的一种或几种组成。
进一步地，所述辅助基料由松香、沥青和氯化橡胶的一种或几种组成。
进一步地，所述颜料为氧化锌或滑石粉。
进一步地，所述溶剂为混合溶剂。
进一步地，所述助剂为增塑剂和触变剂。
进一步地，所述增塑剂按百分比配比为3％-5％，触变剂按百分比配比为1％-1.5％。
所述的防污涂料的制备方法，该防污涂料的制备方法如下：
1)按重量百分比将不含锡降阻高聚物30％-50％、毒料20％-40％和溶剂10％-20％放置在容器内混合，并逐渐加热至70度，得混合物；
2)将步骤1的混合物放置在容器内，按重量百分比将辅助基料2％-5％、颜料5％-10％和助剂4％-7％依次加入到混合物内，在加入时需搅拌，完成后得防污涂料。
本发明的有益效果是：实海渗毒率控制合理稳定，与防锈涂料配套好，物理性能优良，涂膜光滑平整，降阻性能良好，磨蚀速率均匀，节能降耗，属医学微毒级，不危害海洋环境，且防污时效长。
具体实施方式
本发明的一种防污涂料，所述防污涂料按重量百分比以如下成份组成而成，
不含锡降阻高聚物  30％-50％
毒料  20％-40％
辅助基料  2％-5％
颜料  5％-10％
溶剂  10％-20％
助剂  4％-7％
其中，所述不含锡降阻高聚物内有聚丙烯酸树脂为基料。
所述毒料由氧化亚铜、铜粉以及低毒有机防污剂的一种或几种组成，本实施例中，选用铜粉，铜粉在生产及涂装过程中对人体无毒。
所述辅助基料由松香、沥青和氯化橡胶的一种或几种组成，本实施例中，选用松香。
所述颜料为氧化锌或滑石粉，本实施例中，选用滑石粉，滑石粉可以改善沉淀柱，使涂料产品贮存稳定。
所述溶剂为混合溶剂。
所述助剂为增塑剂和触变剂。
所述增塑剂按百分比配比为3％-5％，触变剂按百分比配比为1％-1.5％。
所述的防污涂料的制备方法，该防污涂料的制备方法如下：
1)按重量百分比将不含锡降阻高聚物40％、毒料30％和溶剂15％放置在容器内混合，并逐渐加热至70度，得混合物；
2)将步骤1的混合物放置在容器内，按重量百分比将辅助基料2％、颜料8％和助剂5％依次加入到混合物内，在加入时需搅拌，完成后得防污涂料。
本发明的有益效果是：实海渗毒率控制合理稳定，与防锈涂料配套好，物理性能优良，涂膜光滑平整，降阻性能良好，磨蚀速率均匀，节能降耗，属医学微毒级，不危害海洋环境，且防污时效长。
显然，本领域的技术人员可以对本发明进行各种改动和变型而不脱离本发明的精神和范围。这样，倘若对本发明的这些修改和变型属于本发明权利要求及其等同技术的范围之内，则本发明也意图包含这些改动和变型在内。

Claims (9)

1.一种防污涂料，其特征在于：所述防污涂料按重量百分比以如下成份组成而成，
不含锡降阻高聚物 30％-50％
毒料 20％-40％
辅助基料 2％-5％
颜料 5％-10％
溶剂 10％-20％
助剂 4％-7％
2.根据权利要求1所述的防污涂料，其特征在于：所述不含锡降阻高聚物内有聚丙烯酸树脂为基料。
3.根据权利要求1所述的防污涂料，其特征在于：所述毒料由氧化亚铜、铜粉以及低毒有机防污剂的一种或几种组成。
4.根据权利要求1所述的防污涂料，其特征在于：所述辅助基料由松香、沥青和氯化橡胶的一种或几种组成。
5.根据权利要求1所述的防污涂料，其特征在于：所述颜料为氧化锌或滑石粉。
6.根据权利要求1所述的防污涂料，其特征在于：所述溶剂为混合溶剂。
7.根据权利要求1所述的防污涂料，其特征在于：所述助剂为增塑剂和触变剂。
8.根据权利要求7所述的防污涂料，其特征在于：所述增塑剂按百分比配比为3％-5％，触变剂按百分比配比为1％-1.5％。
9.一种如权利要求1-8所述的防污涂料的制备方法，其特征在于：该防污涂料的制备方法如下：
1)按重量百分比将不含锡降阻高聚物30％-50％、毒料20％-40％和溶剂10％-20％放置在容器内混合，并逐渐加热至70度，得混合物；
2)将步骤1的混合物放置在容器内，按重量百分比将辅助基料2％-5％、颜料5％-10％和助剂4％-7％依次加入到混合物内，在加入时需搅拌，完成后得防污涂料。
CN 201310088042 2013-03-07 2013-03-07 一种防污涂料 Pending CN103173085A (zh)