CN103145211A - 氧化锰改性硅藻土从电解锌漂洗废水中回收Zn2+的方法 - Google Patents
氧化锰改性硅藻土从电解锌漂洗废水中回收Zn2+的方法 Download PDFInfo
- Publication number
- CN103145211A CN103145211A CN2013101174044A CN201310117404A CN103145211A CN 103145211 A CN103145211 A CN 103145211A CN 2013101174044 A CN2013101174044 A CN 2013101174044A CN 201310117404 A CN201310117404 A CN 201310117404A CN 103145211 A CN103145211 A CN 103145211A
- Authority
- CN
- China
- Prior art keywords
- solution
- concentration
- standing
- electrolytic zinc
- waste water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用氧化锰改性硅藻土从电解锌漂洗废水中回收Zn2+的方法。（1）取15g硅藻土精土加入到50mL浓度为4-4.2mol/L的NaOH溶液中，振荡，然后除去上层溶液；再加入100mL浓度为2-2.1mol/L的MnCl2溶液，调pH至1-2，静置，搅拌，静置，除去上清液；（2）在步骤（1）所得溶液中加入25mL浓度为2-2.1mol/L的MnCl2溶液，搅拌，静置；（3）重复步骤（2），去掉上清液，洗涤至中性，固液分离，烘干，粉碎，制备出吸附剂；（4）将10mL浓度为1g/L的吸附剂放入250mL具塞锥形瓶中，加入100mLpH值为6.54-6.60的含Zn2+电解锌漂洗废水溶液，吸附时间60-65分钟，吸附温度25-30℃，振荡至吸附平衡。本发明从电解锌漂洗废水中回收Zn2+，提高了回收率。
Description
技术领域
本发明涉及了一种用氧化锰改性硅藻土从电解锌漂洗废水中回收Zn2+的方法。
背景技术
含Zn2+的废水主要来源于冶金、电镀、电池和固体垃圾填埋场的渗滤液。重金属离子的废水排放到环境中，只能改变其形态或被转移、稀释和积累，却不能被降解，因而危害极大。铅及其化合物对人体的很多系统都有副作用。
硅藻土是一种生物成因的硅质沉积岩，主要由硅藻类遗骸经硅化固结而成的沉积矿。但是天然的硅藻土吸附容量小，往往需要对硅藻土进行改性。因此，研究采用具有吸附能力的氧化锰对硅藻土改性，研究氧化锰改性硅藻土对重金属离子Zn2+的回收，从电解锌漂洗废水中回收Zn2+，提高回收率，有效利用我国的矿产资源，对有价金属的回收，类似的新工艺设计和开发的研究具有十分重大的现实意义，在技术、学术和工业经济上具有诸多好处。同时也符合当前国家产业政策。
发明内容
本发明涉及了一种用氧化锰改性硅藻土从电解锌漂洗废水中回收Zn2+的方法。
具体步骤为：
（1）取15g硅藻土精土（提纯后）加入到50 mL浓度为4-4.2mol/L的NaOH溶液中，在90-95℃温度下振荡100-120分钟，然后除去上层溶液；再加入100mL浓度为2-2.1mol/L的MnCl2溶液，用HCl（分析纯）调pH至1-2，静置120分钟，搅拌60分钟，然后静置24小时，除去上清液；
（2）在步骤（1）所得溶液中加入25mL浓度为2-2.1mol/L的MnCl2溶液，搅拌，静置。
（3）在步骤（2）所得溶液中加入25mL浓度为2-2.1mol/L的MnCl2溶液，搅拌，静置，去掉上清液，用纯水洗涤至中性，离心使固液分离，取固体在105℃下烘干，粉碎过200目筛子，制备出吸附剂。
（4）将10mL浓度为1g/L的步骤（3）所得的吸附剂放入250mL具塞锥形瓶中，加入100mL pH值为6.54-6.60的含Zn2+电解锌漂洗废水溶液，吸附时间60-65分钟，吸附温度25-30℃，加盖后在回旋式水浴恒温振荡器中以150r/min的转速振荡至吸附平衡。
(5)将步骤（4）所得溶液用0.45μm滤膜过滤到10mL离心管中，用火焰原子吸收分光光度法测定滤液中Zn2+的质量浓度；Zn2+的回收率达到89-92%。
本发明从电解锌漂洗废水中回收Zn2+，提高了回收率，有效利用我国的矿产资源，对有价金属的回收，在技术、学术和工业经济上具有诸多好处。同时也符合当前国家产业政策。
附图说明
图1为本发明实施例硅藻土精土的扫描电镜图。
图2为本发明实施例氧化锰改性硅藻土的扫描电镜图。
具体实施方式
实施例：
（1）取15g硅藻土精土（提纯后）加入到50 mL浓度为4mol/L的NaOH溶液中，在90℃温度下振荡100分钟，然后除去上层溶液；再加入100mL浓度为2mol/L的MnCl2溶液，用HCl（分析纯）调pH至1.5，静置120分钟，搅拌60分钟，然后静置24小时，除去上清液；
（2）在步骤（1）所得溶液中加入25mL浓度为2mol/L的MnCl2溶液，搅拌，静置。
（3）在步骤（2）所得溶液中加入25mL浓度为2mol/L的MnCl2溶液，搅拌，静置，去掉上清液，用纯水洗涤至中性，离心使固液分离，取固体在105℃下烘干，粉碎过200目筛子，制备出吸附剂。
（4）将10mL浓度为1g/L的步骤（3）所得的吸附剂放入250mL具塞锥形瓶中，加入100mL pH值为6.54的含Zn2+电解锌漂洗废水溶液，吸附时间60分钟，吸附温度25℃，加盖后在回旋式水浴恒温振荡器中以150r/min的转速振荡至吸附平衡。
(5)将步骤（4）所得溶液用0.45μm滤膜过滤到10mL离心管中，用火焰原子吸收分光光度法测定滤液中Zn2+的质量浓度;Zn2+的回收率达到90%。
Claims (1)
1.一种用氧化锰改性硅藻土从电解锌漂洗废水中回收Zn2+的方法，其特征在于具体步骤为：
（1）取15g硅藻土精土加入到50 mL浓度为4-4.2mol/L的NaOH溶液中，在90-95℃温度下振荡100-120分钟，然后除去上层溶液；再加入100mL浓度为2-2.1mol/L的MnCl2溶液，用分析纯HCl调pH至1-2，静置120分钟，搅拌60分钟，然后静置24小时，除去上清液；
（2）在步骤（1）所得溶液中加入25mL浓度为2-2.1mol/L的MnCl2溶液，搅拌，静置；
（3）在步骤（2）所得溶液中加入25mL浓度为2-2.1mol/L的MnCl2溶液，搅拌，静置，去掉上清液，用纯水洗涤至中性，离心使固液分离，取固体在105℃下烘干，粉碎过200目筛子，制备出吸附剂；
（4）将10mL浓度为1g/L的步骤（3）所得的吸附剂放入250mL具塞锥形瓶中，加入100mL pH值为6.54-6.60的含Zn2+电解锌漂洗废水溶液，吸附时间60-65分钟，吸附温度25-30℃，加盖后在回旋式水浴恒温振荡器中以150r/min的转速振荡至吸附平衡。