CN103144455A - Material for ink-jet imaging and preparation method thereof - Google Patents
Material for ink-jet imaging and preparation method thereof Download PDFInfo
- Publication number
- CN103144455A CN103144455A CN2013100592917A CN201310059291A CN103144455A CN 103144455 A CN103144455 A CN 103144455A CN 2013100592917 A CN2013100592917 A CN 2013100592917A CN 201310059291 A CN201310059291 A CN 201310059291A CN 103144455 A CN103144455 A CN 103144455A
- Authority
- CN
- China
- Prior art keywords
- particle
- particle base
- preparation
- image forming
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a material for ink-jet imaging and a preparation method of the material. The method comprises the following steps of: screening a white marble particle material, a quartz sand particle material or a transparent glass sand particle material to obtain a particle base material with the particle size of 40-120 meshes; adding a polyvinyl acetate adhesive into the particle base material; fully mixing the adhesive with the particle base material; spraying the mixture of the particle base material and the adhesive to a white cloth through a specially made high pressure jet device with a special nozzle; curing the adhesive by means of ultraviolet radiation so that the particle base material is firmly adhered to the cloth to function as an image bearing body, and printing an image in a digital form to an imaging material which takes the white cloth as a substrate and the particle base material as a coating through a modified color ink-jet printer. The obtained image not only has the clearness and vividness advantages of a traditional planer imaging material, but also has the stereoscopic sensations of an oil painting and a relief painting and the texture of natural stone, as well as is the harmonious unity of natural materials and a modern ink-jet printing technology.
Description
Technical field
The present invention relates to a kind of for air brushing image forming material and preparation method thereof.
Background technology
Along with the development that the personage draws a portrait, the imaging techniques such as landscape is realistic, decorations colored drawing make rapid progress, image forming material has become to lead the pushing hands of variation.The output body of tradition imaging technique is main body mainly with color printer, and the supporting body of graph image is mainly with plain paper, offset printing printing paper, wooden boards, fibrous material such as cloth, fiber crops, silk etc.Clear true to nature by the image effect that these materials obtain, but shortcoming is without stereoeffect, and mostly image is that air brushing on the plane of outer surface, easily causes aesthetic and visual fatigue.
Summary of the invention
The present invention seeks to disclose a kind of for air brushing image forming material and preparation method thereof; with the supporting body of this image forming material as image; color painting printer by transformation prints to digital format-pattern on image forming material take calico as base material, take the particle base material as coating; the image that obtains not only has the advantage clear true to nature of conventional planar image forming material; the third dimension of oil painting, relief painting and the texture of lithotome are more arranged, and have advantages of clear more true to nature than traditional prints works.
The technology used in the present invention is as follows:
A kind of preparation method for the air brushing image forming material, step is as follows:
(1) processing base material and particle base-material:
Cutting needs the white cloth of size, be fixed and fully launch smooth, as the base material of particle base-material; Screening particle base-material particle diameter more than or equal to 40 orders less than or equal to 120 orders; Described particle base-material is white jade stone granulate, quartz sand or clear glass sand;
(2) preparation particle base-material glue batch mixing
Particle base-material and polyvinyl acetate glue stick that screening is good are pressed the weight proportion of 10: 2, by high-speed dispersion equipment, fully mix, and obtain particle base-material glue batch mixing, and be stand-by;
(3) spraying and moulding
Use high-pressure spraying machine, particle base-material glue batch mixing is sprayed on white cloth equably, then dried 28-30 minute under 40-42 ℃ of drying baker, make the particle base-material be attached to securely on cloth; Acquisition can be carried the image forming material of image.
The present invention also has following feature:
1, the rotating speed of described preparation particle base-material glue batch mixing step high speed dispersing apparatus is 280 rev/mins, incorporation time 10-15 minute.
2, in described spraying and forming step, a moulding is accomplished in spraying, adopts in a zigzag and sweeps rifle, and spray tip is apart from 20 centimeters, cloth substrate layer, and spray gun pressure is 0.4MPA, and the spray tip diameter is 0.14mm-0.22mm.
3, a kind of a kind of preparation method for the air brushing image forming material as above makes is used for the air brushing image forming material.
the air brushing image forming material that said method obtains is exported image file by the color inkjet printer of special debugging, obtain rich texture, color is true to nature, the image of image definition, and have natural, pseudo-classic highest quality effect, and, due to white marble quality particle, quartz sand, these granular materials majorities such as clear glass sand are the multiaspect cubes, and polyhedral smooth surface is smooth-going, so its meeting reflect visible light line under different angles, therefore, after imaging, remove to appreciate this air brushing image in different angles, the capital obtains different visual effects, image is in multi-angle, multiposition point is glittering, vivid, ornamental, artistry is high.In addition, surperficial slim and sexy, the height of the image works after air brushing rise and fall, and use this image forming material as the decorated wall surface large tracts of land, and the irregularity on its distinctive surface can also play the effect that absorbs noise.The preparation method of image forming material of the present invention is drawn materials conveniently, and manufacture craft is simple and easy to control.
The specific embodiment
The present invention is described further for example for the below:
Embodiment 1
In the present invention be at first the white cloth of size cutting certain size of image works as required as basic material, the white cloth size of cutting be larger than after imaging size so that deburring process; White cloth must fully launch and utilize bail with it nail at the wood-based plate face, keep smooth, and make white cloth integral body that some tension be arranged.Its less important preparation particle base-material; adopt white marble rock land particle, quartz sand or clear glass sand particle; utilize 40 purpose vibrating screen panels to obtain the particle of uniform particle diameter, particle is crossed conference and is caused image distortion, and particle is too small can not well embody stereoeffect again.The particle base-material that screening is good and polyvinyl acetate glue stick, fully mix by high-speed dispersion equipment according to the weight ratio ratio of 10: 2, obtain particle base-material glue batch mixing, and the good fluidity of glue batch mixing is suitable for spraying.The rotating speed of high speed dispersion is advisable with 280 rev/mins, and too low mixing is even not, and too high meeting makes the particle polyhedral surface become crude, affects the image flash effect, and incorporation time got final product in 15 minutes.Adopt customized, spray gun spraying glue batch mixing that conform to particle base-material particle diameter in the present invention, the spray tip diameter is 0.22mm, and a moulding is accomplished in spraying, adopts in a zigzag and sweeps rifle, and spray tip is apart from 20 centimeters, cloth substrate layer, and spray gun pressure is 0.4MPA.After grain coating sprays, then oven dry 30 minutes under 38 ℃ of drying bakers, after solidifying coating can anti--30 variations in temperature of ℃-+60 ℃.And the colorless adhesive that solidifies is transparent, can not affect the color and luster of image.Use the ink-jet printer of transformation, and adjustment charging rate, 4-5 hour drying time when the image baking temperature that prints is 0-10 ℃, 3-4 hour drying time when baking temperature is 11-20 ℃, 2-3 hour drying time when baking temperature is 21-30 ℃, 1-1.5 hour drying time when baking temperature is 31-40 ℃.Can be to the deburring of image works and mounting after the printing ink transformation.
Embodiment 2
In the present invention be at first the white cloth of size cutting certain size of image works as required as basic material, the white cloth size of cutting be larger than after imaging size so that deburring process; White cloth must fully launch and utilize bail with it nail at the wood-based plate face, keep smooth, and make white cloth integral body that some tension be arranged.Its less important preparation particle base-material; adopt white marble rock land particle, quartz sand or clear glass sand particle; utilize 120 purpose vibrating screen panels to obtain the particle of uniform particle diameter, particle is crossed conference and is caused image distortion, and particle is too small can not well embody stereoeffect again.The particle base-material that screening is good and polyvinyl acetate glue stick, fully mix by high-speed dispersion equipment according to the weight ratio ratio of 10: 2, obtain particle base-material glue batch mixing, and the good fluidity of glue batch mixing is suitable for spraying.The rotating speed of high speed dispersion is advisable with 280 rev/mins, and too low mixing is even not, and too high meeting makes the particle polyhedral surface become crude, affects the image flash effect, and incorporation time got final product in 10 minutes.Because the order number of particle base-material is fixed on certain limit; adopt customized, spray gun spraying glue batch mixing that conform to particle base-material particle diameter in the present invention, a moulding is accomplished in spraying, adopts and sweeps in a zigzag rifle; spray tip is apart from 20 centimeters, cloth substrate layer, and spray gun pressure is 0.4MPA.The spray tip diameter is after the 0.14mm. grain coating sprays, then oven dry 28 minutes under 40 ℃ of drying bakers, after solidifying coating can anti--30 variations in temperature of ℃-+60 ℃.And the colorless adhesive that solidifies is transparent, can not affect the color and luster of image.Use the ink-jet printer of transformation, and adjustment charging rate, 4-5 hour drying time when the image baking temperature that prints is 0-10 ℃, 3-4 hour drying time when baking temperature is 11-20 ℃, 2-3 hour drying time when baking temperature is 21-30 ℃, 1-1.5 hour drying time when baking temperature is 31-40 ℃.Can be to the deburring of image works and mounting after the printing ink transformation.Obtain the image printing works, have advantages of that not only the traditional prints works are clear true to nature, more obtain strong modelling effect, novel free from vulgarity, image is glittering, and is vivid, and visual impact is strong, sees for a long time and does not mind.
Claims (4)
1. a preparation method that is used for the air brushing image forming material, is characterized in that, step is as follows:
(1) processing base material and particle base-material:
Cutting needs the white cloth of size, be fixed and fully launch smooth, as the base material of particle base-material; Screening particle base-material particle diameter more than or equal to 40 orders less than or equal to 120 orders; Described particle base-material is white jade stone granulate, quartz sand or clear glass sand;
(2) preparation particle base-material glue batch mixing
Particle base-material and polyvinyl acetate glue stick that screening is good are pressed the weight proportion of 10: 2, by high-speed dispersion equipment, fully mix, and obtain particle base-material glue batch mixing, and be stand-by;
(3) spraying and moulding
Use high-pressure spraying machine, particle base-material glue batch mixing is sprayed on white cloth equably, then dried 28-30 minute in 40-42 ℃ of drying baker, make the particle base-material be attached to securely on cloth; Acquisition can be carried the image forming material of image.
2. a kind of preparation method for the air brushing image forming material according to claim 1, it is characterized in that: the rotating speed of described preparation particle base-material glue batch mixing step high speed dispersing apparatus is 280 rev/mins, incorporation time 10-15 minute.
3. a kind of preparation method for the air brushing image forming material according to claim 1, it is characterized in that: in described spraying and forming step, a moulding is accomplished in spraying, adopt and sweep in a zigzag rifle, spray tip is apart from 20 centimeters, cloth substrate layer, spray gun pressure is 0.4MPA, and the spray tip diameter is 0.14mm-0.22mm.
4. the described a kind of preparation method for the air brushing image forming material of any one makes is used for the air brushing image forming material.