CN106739745A - A kind of new 3D printing match volume decoration painting and preparation method thereof - Google Patents
A kind of new 3D printing match volume decoration painting and preparation method thereof Download PDFInfo
- Publication number
- CN106739745A CN106739745A CN201611076863.2A CN201611076863A CN106739745A CN 106739745 A CN106739745 A CN 106739745A CN 201611076863 A CN201611076863 A CN 201611076863A CN 106739745 A CN106739745 A CN 106739745A
- Authority
- CN
- China
- Prior art keywords
- parts
- chalk
- preparation
- printing
- decoration painting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of new 3D printing match volume decoration painting and preparation method thereof, substrate surface is cleaned, dried；Prepared chalk particle in high speed dispersor is put into after the raw material mixing that chalk will be prepared；Chalk is extruded from nozzle on substrate surface, by being superimposed individual layer chalk, carries out three-dimensional printing treatment, obtain chalk bed die；Color ink is carried out by 3D printer using color ink on chalk bed die and sprays moulding, obtain moulding product, then moulding product are put into vacuum drying chamber carries out solidifying and setting, obtains semi-finished product；Under ultra violet lamp, curing process is carried out to semi-finished product, packaging obtains finished product after taking-up.3D printing method low production cost that the present invention is used, technique is simple and easy to operate, be conducive to scale of mass production, and make decoration painting new style, third dimension is strong and can effectively lift home decoration quality, be convenient for carrying ornaments not cracky.
Description
Technical field
The present invention relates to decorative art field, and in particular to a kind of new 3D printing match volume decoration painting and its making side
Method.
Background technology
With progress, expanding economy and the raising of quality of life of society and human thought, requirement of the people to decorating
Improve constantly, the field of decoration is also constantly expanding, and has developed the decorative painting of various cultural connotations and style characteristic.At present
The decoration painting of the pure print pattern of in the market shows slightly stiff, and printing effect is dumb, it is difficult to enter high-end decoration painting market, and right
For decoration painting outlet, the decoration painting of most of pure print pattern is eliminated by European ＆ American Market, and order is few, and profit is low,
And cannot meet the market demand.And decoration painting in the market is mostly bulky, it is only suitable for outdoor large exhibition
Position put.In order to meet visual demand and tactile demand of the market for decoration painting, decoration is decorated with variform at present, used
Raw material and preparation method are also not quite similar, and the demand of the decoration painting with stereoeffect is growing.
Printing technique is one kind of rapid shaping technique, and it is a kind of based on mathematical model file, with powdered
Metal or plastics etc. can jointing material, come the technology of constructed object by way of successively printing.Printable product has concavo-convex
Handle effect is also 3D printing.
Chinese patent CN201510448510.X discloses the resin picture of 3D printing, prepares its apparatus and method, and 3D beats
The resin picture of print includes the picture that the transparent material matrix being made through 3D printing, the pigment that is embedded in matrix are made through 3D printing
Body；The equipment for preparing resin picture includes mould and 3D printer, and matrix print cartridge and pigment print cartridge, matrix are provided with 3D printer
The matrix ink of transparent material is loaded with print cartridge, the pigment inks that pigment is made are loaded with pigment print cartridge；Mould has an opening
Upward accommodating chamber, the print area of 3D printer is provided with the fixture of the bottom of fixing mould；3D printer is deposited including model
Storage unit, model storage unit internal memory contains the data of 3D models.But method, the mistake of the undisclosed 3D printing resin picture of the patent
Journey and technical parameter.
Chinese patent CN201410059278.6 discloses the manufacturing process of a kind of plane and stereo decorative picture product, obtains
The plane picture of the decoration painting of pre- making is taken, close shot object image and background object image in the plane picture of decoration painting is separated；Beat
Print background object image, obtains comprising only the 2D plane pictures of background objects；3D printing is realized to close shot object image using 3D printing method
Operation, obtains the 3D printing physical model containing close shot thing containing equal proportion；The 3D printing reality for having close shot thing is described in identification
Body Model and the joint portion of the 2D plane pictures for describing the thing that has powerful connections, soil is mended by 3D printing entity mould on joint portion using AB moulding
Type is repaired with 2D plane pictures, and 3D printing physical model is adhesively fixed with 2D plane pictures；To the 2D planes after fixation
Draw and 3D printing physical model carries out colouring operation, making forms plane and stereo decorative picture product.But use the patent
The decoration painting background that preparation method makes is separated with close shot image, easy to fall off, so as to cause picture incompleteness, the quality of decoration painting
It is low.
Therefore need that a kind of production cost is relatively low, technique is simple and easy to operate, be conducive to the 3D printing of scale of mass production to make
The method of stereo decorative picture, and be made stereo decorative picture new style, third dimension is strong and can effectively lift household dress
Ornaments matter, it is convenient for carrying ornaments not cracky.
The content of the invention
The present invention is regarding to the issue above, there is provided a kind of new 3D printing match volume decoration painting and preparation method thereof.
The present invention the used technical scheme that solves the above problems is：
A kind of preparation method of new 3D printing match volume decoration painting, comprises the following steps：
Step S01, pre-treatment：Substrate surface is cleaned, carried out under 35 °C ~ 40 °C of temperature conditionss drying and processing 2h ~
5h；
Step S02, chalk allotment：Raw material phenol formaldehyde epoxy vinyl ester resin, thermosetting phenolic resin, the polyamides of chalk will be prepared
Polyimide resin, nano grade titanium white powder, butyl acetate, caprolactam, lignin acid, carboxymethylcellulose calcium, hydroxythiophenol, poly- methyl
Methyl acrylate, puts into high speed dispersor after material is mixed, and is first disperseed with the rotating speed of 1300r/min ~ 1700r/min
1.5min ~ 4min, then disperses 3min ~ 6min with the rotating speed of 3000r/min ~ 5500r/min, then with 6000r/min ~ 8000r/
The rotating speed dispersion 8min ~ 15min of min, is obtained the chalk particle that granularity is for 2 μm ~ 5 μm；
Step S03, bed die printing：Chalk is extruded from nozzle on substrate surface using 3D printer, is 32 according to color depth
Color composition, by being superimposed individual layer chalk, carry out three-dimensional printing treatment 30min ~ 50min, the distance of nozzle and base material is 3cm
~ 6cm, the extruded velocity of nozzle is 30mm/s ~ 40mm/s, and the rate travel of nozzle is 0.1mm/s ~ 3mm/s, photoelectricity position indicator
Position error≤0.5mm, the accuracy of manufacture is 3 μm ~ 5 μm, obtains the chalk bed die of decoration painting；
Step S04, color ink printing：On the chalk bed die of the decoration painting obtained in step S03 using viscosity be 3000mPa s ~
The color ink of 20000mPa s carries out color ink and sprays moulding by 3D printer, obtains moulding product, is then 45 °C ~ 60 °C in temperature
Under conditions of, moulding product are put into carries out solidifying and setting 60min ~ 80min in vacuum drying chamber, obtain semi-finished product；
Step S05, ultraviolet curing：Under 800W ~ 2500W ultra violet lamps, the semi-finished product to being processed through step S04 are consolidated
Change treatment 10s ~ 45s, packaging obtains finished product after taking-up.
Further, in step S01, base material is cardboard, leather board, wood plank, acrylic board, metallic plate, ceramic wafer, glass
Any one in glass plate, fiberboard, cement plate.
Further, base material is plane or micro- curved surface.
Further, the curvature of micro- curved surface is 0.005m-1~0.01m-1。
Further, in step S01, cleaning is specially：To substrate surface with concentration for 45% ~ 60% ethanol solution is carried out
Wipe.
Further, in step S02, the raw material and its weight portion for preparing chalk are：Phenol formaldehyde epoxy vinyl ester resin 34
Part ~ 38 parts, 20 parts ~ 25 parts of thermosetting phenolic resin, 10 parts ~ 15 parts of polyamide, 32 parts ~ 40 parts of nano grade titanium white powder, vinegar
10 parts ~ 16 parts of acid butyl ester, 1.6 parts ~ 3.2 parts of caprolactam, lignin acid 0.3 part ~ 0.6 part, carboxymethylcellulose calcium 0.5 part ~ 1
Part, 0.1 part ~ 0.3 part of hydroxythiophenol, 0.15 part ~ 0.3 part of polymethyl methacrylate.
Further, the raw material and its weight portion for preparing chalk are optimized for：Phenol formaldehyde epoxy vinyl ester resin 35 parts ~ 37
Part, 22 parts ~ 24 parts of thermosetting phenolic resin, 10 parts ~ 13 parts of polyamide, 35 parts ~ 40 parts of nano grade titanium white powder, butyl acetate
12 parts ~ 15 parts, 1.8 parts ~ 2.5 parts of caprolactam, lignin acid 0.3 part ~ 0.5 part, 0.6 part ~ 0.8 part of carboxymethylcellulose calcium, hydroxyl
0.1 part ~ 0.2 part of base benzenethiol, 0.2 part ~ 0.3 part of polymethyl methacrylate.
Further, in step S03, the thickness of individual layer chalk is 15 μm ~ 25 μm.
Further, in step S04, the pressure of vacuum drying chamber is 0.3MPa ~ 0.6MPa during the solidifying and setting.
It is that a kind of new 3D printing match volume decoration painting is provided, using above-mentioned according to another goal of the invention of the invention
Preparation method is made.
It is an advantage of the invention that：
1. the present invention uses a kind of new 3D printing technique, and bed die is made by homemade chalk, discloses bed die and color ink
Manufacturing process, the process and product of this technology be novel especially, enriches the market of decoration painting, and method simplify, production
Environment optimization, effectively improves production efficiency, is conducive to scale volume production；
2. the decoration painting that the present invention makes is made using environmental-protecting material, reusable edible, and new style, third dimension be strong and energy
Effectively lift home decoration, beautification life, compact is slim and graceful, surface texture is clear, texture good, and be convenient for carrying ornaments, no
Cracky, compensate for the vacancy of this field interior trim picture of interior home decoration；
3. the present invention allotment chalk material it is environmentally friendly, simple for production, for 3D printing technique when, do bed die it is formability thereof it is good, make
Type sharpness of border, stereoeffect are good, and bed die is tasteless, will not do harm to huamn body when doing decoration painting indoor placement；
4. the obtained decoration painting of the present invention can make of various base materials, have a wide range of application, and produce the decoration of various texture and level
Effect is drawn, the requirement in different consumption groups and different decorated styles and place is met.
Brief description of the drawings
Constitute the part of this specification, show embodiment party of the invention for further understanding accompanying drawing of the invention
Case, and be used for illustrating preparation flow of the invention together with specification.In the accompanying drawings：
Fig. 1 is the manufacturing process schematic diagram of new 3D printing match volume decoration painting in the present invention.
Specific embodiment
Embodiments of the invention are described in detail below in conjunction with accompanying drawing, but the present invention can be defined by the claims
Multitude of different ways with covering is implemented.
Embodiment 1
A kind of preparation method of new 3D printing match volume decoration painting, comprises the following steps：
Step S01, pre-treatment：Glass plate substrate surface to plane is wiped with the ethanol solution that concentration is 45%, at 35 °C
Temperature conditionss under carry out drying and processing 2h.
Step S02, chalk allotment：34 parts of raw material phenol formaldehyde epoxy vinyl ester resin, the thermosetting phenolic of chalk will be prepared
20 parts of resin, 10 parts of polyamide, 32 parts of nano grade titanium white powder, 10 parts of butyl acetate, 1.6 parts of caprolactam, lignin acid
0.3 part, 0.5 part of carboxymethylcellulose calcium, 0.1 part of hydroxythiophenol, 0.15 part of polymethyl methacrylate, after material is mixed throw
Enter in high speed dispersor, 1.5min is first disperseed with the rotating speed of 1300r/min, 3min is then disperseed with the rotating speed of 3000r/min, then
8min is disperseed with the rotating speed of 6000r/min, prepared granularity is 2 μm of chalk particle.Obtained chalk viscosity is 40s, tinting strength, tinting power
It is 95%, adhesive force is 95%, gloss is 70%.
Step S03, bed die printing：Chalk is extruded from nozzle on substrate surface using 3D printer, is according to color depth
The color composition of 32, by being superimposed individual layer chalk, the thickness of individual layer chalk is 15 μm, carries out three-dimensional printing treatment 30min, spray
Mouth is 3cm with the distance of base material, and the extruded velocity of nozzle is 30mm/s, and the rate travel of nozzle is 0.1mm/s, photoelectricity position indicator
Position error be 0.5mm, the accuracy of manufacture be 3 μm, obtain the chalk bed die of decoration painting.
Step S04, color ink printing：It is 3000mPa s that viscosity is used on the chalk bed die of the decoration painting obtained in step S03
Color ink by 3D printer carry out color ink spray moulding, obtain moulding product, then temperature be 45 °C under conditions of, by moulding
Product carry out solidifying and setting 60min in being put into the vacuum drying chamber that pressure is 0.3MPa, obtain semi-finished product.
Step S05, ultraviolet curing：Under 800W ultra violet lamps, the semi-finished product to being processed through step S04 solidify
Treatment 10s, packaging obtains finished product after taking-up.
Embodiment 2
A kind of preparation method of new 3D printing match volume decoration painting, comprises the following steps：
Step S01, pre-treatment：Fiberboard substrate surface to plane is wiped with the ethanol solution that concentration is 60%, at 40 °C
Temperature conditionss under carry out drying and processing 5h.
Step S02, chalk allotment：38 parts of raw material phenol formaldehyde epoxy vinyl ester resin, the thermosetting phenolic of chalk will be prepared
25 parts of resin, 15 parts of polyamide, 40 parts of nano grade titanium white powder, 16 parts of butyl acetate, 3.2 parts of caprolactam, lignin acid
0.6 part, 1 part of carboxymethylcellulose calcium, 0.3 part of hydroxythiophenol, 0.3 part of polymethyl methacrylate, after material is mixed put into
In high speed dispersor, 4min is first disperseed with the rotating speed of 1700r/min, then with the rotating speed dispersion 6min of 5500r/min, then with
The rotating speed dispersion 15min of 8000r/min, prepared granularity is 5 μm of chalk particle.Obtained chalk viscosity is 55s, and tinting strength, tinting power is
99.5%, adhesive force is 99.5%, and gloss is 90%.
Step S03, bed die printing：Chalk is extruded from nozzle on substrate surface using 3D printer, is according to color depth
The color composition of 32, by being superimposed individual layer chalk, the thickness of individual layer chalk is 25 μm, carries out three-dimensional printing treatment 50min, spray
Mouth is 6cm with the distance of base material, and the extruded velocity of nozzle is 40mm/s, and the rate travel of nozzle is 3mm/s, photoelectricity position indicator
Position error is 0.4mm, and the accuracy of manufacture is 5 μm, obtains the chalk bed die of decoration painting.
Step S04, color ink printing：It is 20000mPa that viscosity is used on the chalk bed die of the decoration painting obtained in step S03
The color ink of s carries out color ink and sprays moulding by 3D printer, obtains moulding product, under conditions of being then 60 °C in temperature, will make
Type product carry out solidifying and setting 80min in being put into the vacuum drying chamber that pressure is 0.6MPa, obtain semi-finished product.
Step S05, ultraviolet curing：Under 2500W ultra violet lamps, the semi-finished product to being processed through step S04 are consolidated
Change treatment 45s, packaging obtains finished product after taking-up.
Embodiment 3
A kind of preparation method of new 3D printing match volume decoration painting, comprises the following steps：
Step S01, pre-treatment：Acrylic board substrate surface to plane is wiped with the ethanol solution that concentration is 53%,
Drying and processing 3.5h is carried out under 38 °C of temperature conditionss.
Step S02, chalk allotment：36 parts of raw material phenol formaldehyde epoxy vinyl ester resin, the thermosetting phenolic of chalk will be prepared
43 parts of resin, 13 parts of polyamide, 36 parts of nano grade titanium white powder, 13 parts of butyl acetate, 2.4 parts of caprolactam, lignin acid
0.45 part, 0.75 part of carboxymethylcellulose calcium, 0.2 part of hydroxythiophenol, 0.23 part of polymethyl methacrylate, after material is mixed
In input high speed dispersor, 2.7min is first disperseed with the rotating speed of 1500r/min, then disperseed with the rotating speed of 4300r/min
4.5min, then 12min is disperseed with the rotating speed of 7000r/min, prepared granularity is 3.5 μm of chalk particle.Obtained chalk viscosity
It is 47s, tinting strength, tinting power is 97%, and adhesive force is 97%, and gloss is 80%.
Step S03, bed die printing：Chalk is extruded from nozzle on substrate surface using 3D printer, is according to color depth
The color composition of 32, by being superimposed individual layer chalk, the thickness of individual layer chalk is 20 μm, carries out three-dimensional printing treatment 40min, spray
Mouth is 4.5cm with the distance of base material, and the extruded velocity of nozzle is 35mm/s, and the rate travel of nozzle is 1.5mm/s, photoelectricity positioning
The position error of instrument is 0.1mm, and the accuracy of manufacture is 4 μm, obtains the chalk bed die of decoration painting.
Step S04, color ink printing：It is 11500mPa that viscosity is used on the chalk bed die of the decoration painting obtained in step S03
The color ink of s carries out color ink and sprays moulding by 3D printer, obtains moulding product, under conditions of being then 53 °C in temperature, will make
Type product carry out solidifying and setting 70min in being put into the vacuum drying chamber that pressure is 0.45MPa, obtain semi-finished product.
Step S05, ultraviolet curing：Under 1150W ultra violet lamps, the semi-finished product to being processed through step S04 are consolidated
Change treatment 28s, packaging obtains finished product after taking-up.
Embodiment 4
A kind of preparation method of new 3D printing match volume decoration painting, comprises the following steps：
Step S01, pre-treatment：It is 0.005m to curvature-1Micro- curved surface metal plate substrate surface concentration be 48% ethanol
Solution is wiped, and drying and processing 3h is carried out under 36 °C of temperature conditionss.
Step S02, chalk allotment：35 parts of raw material phenol formaldehyde epoxy vinyl ester resin, the thermosetting phenolic of chalk will be prepared
22 parts of resin, 10 parts of polyamide, 35 parts of nano grade titanium white powder, 12 parts of butyl acetate, 1.8 parts of caprolactam, lignin acid
0.3 part, 0.6 part of carboxymethylcellulose calcium, 0.1 part of hydroxythiophenol, 0.2 part of polymethyl methacrylate, after material is mixed throw
Enter in high speed dispersor, 2min is first disperseed with the rotating speed of 1400r/min, 3.5min is then disperseed with the rotating speed of 3600r/min, then
10min is disperseed with the rotating speed of 6500r/min, prepared granularity is 3 μm of chalk particle.Obtained chalk viscosity is 43s, tinting strength, tinting power
It is 96%, adhesive force is 96%, gloss is 75%.
Step S03, bed die printing：Chalk is extruded from nozzle on substrate surface using 3D printer, is according to color depth
The color composition of 32, by being superimposed individual layer chalk, the thickness of individual layer chalk is 17 μm, carries out three-dimensional printing treatment 35min, spray
Mouth is 4cm with the distance of base material, and the extruded velocity of nozzle is 33mm/s, and the rate travel of nozzle is 1mm/s, photoelectricity position indicator
Position error is 0.2mm, and the accuracy of manufacture is 3.5 μm, obtains the chalk bed die of decoration painting.
Step S04, color ink printing：It is 8000mPa s that viscosity is used on the chalk bed die of the decoration painting obtained in step S03
Color ink by 3D printer carry out color ink spray moulding, obtain moulding product, then temperature be 47 °C under conditions of, by moulding
Product carry out solidifying and setting 65min in being put into the vacuum drying chamber that pressure is 0.4MPa, obtain semi-finished product.
Step S05, ultraviolet curing：Under 1400W ultra violet lamps, the semi-finished product to being processed through step S04 are consolidated
Change treatment 38s, packaging obtains finished product after taking-up.
Embodiment 5
A kind of preparation method of new 3D printing match volume decoration painting, comprises the following steps：
Step S01, pre-treatment：It is 0.01m to curvature-1Micro- curved surface leather board substrate surface concentration be 55% ethanol
Solution is wiped, and drying and processing 4h is carried out under 38 °C of temperature conditionss.
Step S02, chalk allotment：37 parts of raw material phenol formaldehyde epoxy vinyl ester resin, the thermosetting phenolic of chalk will be prepared
24 parts of resin, 13 parts of polyamide, 40 parts of nano grade titanium white powder, 15 parts of butyl acetate, 2.5 parts of caprolactam, lignin acid
0.5 part, 0.8 part of carboxymethylcellulose calcium, 0.2 part of hydroxythiophenol, 0.3 part of polymethyl methacrylate, after material is mixed throw
Enter in high speed dispersor, 3.5min is first disperseed with the rotating speed of 1600r/min, 5min is then disperseed with the rotating speed of 5000r/min, then
14min is disperseed with the rotating speed of 7500r/min, prepared granularity is 4 μm of chalk particle.Obtained chalk viscosity is 52s, tinting strength, tinting power
It is 98%, adhesive force is 98%, gloss is 85%.
Step S03, bed die printing：Chalk is extruded from nozzle on substrate surface using 3D printer, is according to color depth
The color composition of 32, by being superimposed individual layer chalk, the thickness of individual layer chalk is 22 μm, carries out three-dimensional printing treatment 45min, spray
Mouth is 5cm with the distance of base material, and the extruded velocity of nozzle is 38mm/s, and the rate travel of nozzle is 2.5mm/s, photoelectricity position indicator
Position error be 0.3mm, the accuracy of manufacture be 4.5 μm, obtain the chalk bed die of decoration painting.
Step S04, color ink printing：It is 15000mPa that viscosity is used on the chalk bed die of the decoration painting obtained in step S03
The color ink of s carries out color ink and sprays moulding by 3D printer, obtains moulding product, under conditions of being then 58 °C in temperature, will make
Type product carry out solidifying and setting 75min in being put into the vacuum drying chamber that pressure is 0.5MPa, obtain semi-finished product.
Step S05, ultraviolet curing：Under 2000W ultra violet lamps, the semi-finished product to being processed through step S04 are consolidated
Change treatment 18s, packaging obtains finished product after taking-up.
The preferred embodiments of the present invention are these are only, is not intended to limit the invention, for those skilled in the art
For member, the present invention can have various modifications and variations.All any modifications within the spirit and principles in the present invention, made,
Equivalent, improvement etc., should be included within the scope of the present invention.
Claims (10)
1. a kind of preparation method of new 3D printing match volume decoration painting, it is characterised in that comprise the following steps：
Step S01, pre-treatment：Substrate surface is cleaned, carried out under 35 °C ~ 40 °C of temperature conditionss drying and processing 2h ~
5h；
Step S02, chalk allotment：Raw material phenol formaldehyde epoxy vinyl ester resin, thermosetting phenolic resin, the polyamides of chalk will be prepared
Polyimide resin, nano grade titanium white powder, butyl acetate, caprolactam, lignin acid, carboxymethylcellulose calcium, hydroxythiophenol, poly- methyl
Methyl acrylate, puts into high speed dispersor after material is mixed, and is first disperseed with the rotating speed of 1300r/min ~ 1700r/min
1.5min ~ 4min, then disperses 3min ~ 6min with the rotating speed of 3000r/min ~ 5500r/min, then with 6000r/min ~ 8000r/
The rotating speed dispersion 8min ~ 15min of min, is obtained the chalk particle that granularity is for 2 μm ~ 5 μm；
Step S03, bed die printing：Chalk is extruded from nozzle on substrate surface using 3D printer, is 32 according to color depth
Color composition, by being superimposed individual layer chalk, carry out three-dimensional printing treatment 30min ~ 50min, the distance of nozzle and base material is 3cm
~ 6cm, the extruded velocity of nozzle is 30mm/s ~ 40mm/s, and the rate travel of nozzle is 0.1mm/s ~ 3mm/s, photoelectricity position indicator
Position error≤0.5mm, the accuracy of manufacture is 3 μm ~ 5 μm, obtains the chalk bed die of decoration painting；
Step S04, color ink printing：On the chalk bed die of the decoration painting obtained in step S03 using viscosity be 3000mPa s ~
The color ink of 20000mPa s carries out color ink and sprays moulding by 3D printer, obtains moulding product, is then 45 °C ~ 60 °C in temperature
Under conditions of, moulding product are put into carries out solidifying and setting 60min ~ 80min in vacuum drying chamber, obtain semi-finished product；
Step S05, ultraviolet curing：Under 800W ~ 2500W ultra violet lamps, the semi-finished product to being processed through step S04 are consolidated
Change treatment 10s ~ 45s, packaging obtains finished product after taking-up.
2. preparation method according to claim 1, it is characterised in that in step S01, the base material be cardboard, leather board,
Any one in wood plank, acrylic board, metallic plate, ceramic wafer, glass plate, fiberboard, cement plate.
3. preparation method according to claim 2, it is characterised in that the base material is plane or micro- curved surface.
4. preparation method according to claim 3, it is characterised in that the curvature of micro- curved surface is 0.005m-1~0.01m-1。
5. preparation method according to claim 1, it is characterised in that in step S01, the cleaning is specially：To base material
Surface is with concentration for 45% ~ 60% ethanol solution is wiped.
6. preparation method according to claim 1, it is characterised in that in step S02, the raw material for preparing chalk and its
Weight portion is：34 parts ~ 38 parts of phenol formaldehyde epoxy vinyl ester resin, 20 parts ~ 25 parts of thermosetting phenolic resin, 10 parts of polyamide
~ 15 parts, 32 parts ~ 40 parts of nano grade titanium white powder, 10 parts ~ 16 parts of butyl acetate, 1.6 parts ~ 3.2 parts of caprolactam, lignin acid 0.3
Part ~ 0.6 part, 0.5 part ~ 1 part of carboxymethylcellulose calcium, 0.1 part ~ 0.3 part of hydroxythiophenol, 0.15 part of polymethyl methacrylate ~
0.3 part.
7. preparation method according to claim 6, it is characterised in that the raw material for preparing chalk and its weight portion optimize
For：35 parts ~ 37 parts of phenol formaldehyde epoxy vinyl ester resin, 22 parts ~ 24 parts of thermosetting phenolic resin, 10 parts ~ 13 parts of polyamide,
35 parts ~ 40 parts of nano grade titanium white powder, 12 parts ~ 15 parts of butyl acetate, 1.8 parts ~ 2.5 parts of caprolactam, lignin acid 0.3 part ~ 0.5
Part, 0.6 part ~ 0.8 part of carboxymethylcellulose calcium, 0.1 part ~ 0.2 part of hydroxythiophenol, 0.2 part ~ 0.3 part of polymethyl methacrylate.
8. preparation method according to claim 1, it is characterised in that in step S03, the thickness of the individual layer chalk is 15
μm~25μm。
9. preparation method according to claim 1, it is characterised in that in step S04, is vacuum dried during the solidifying and setting
The pressure of case is 0.3MPa ~ 0.6MPa.
10. a kind of new 3D printing match volume decoration painting, it is characterised in that using any one of claim 1 ~ 9
Preparation method is made.