CN103132068A - 一种三价铬浓缩蓝白钝化剂以及用蓝白钝化剂钝化的方法 - Google Patents

一种三价铬浓缩蓝白钝化剂以及用蓝白钝化剂钝化的方法 Download PDF

Info

Publication number
CN103132068A
CN103132068A CN2011103864115A CN201110386411A CN103132068A CN 103132068 A CN103132068 A CN 103132068A CN 2011103864115 A CN2011103864115 A CN 2011103864115A CN 201110386411 A CN201110386411 A CN 201110386411A CN 103132068 A CN103132068 A CN 103132068A
Authority
CN
China
Prior art keywords
product
passivation
trivalent chromium
passivant
bright blue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103864115A
Other languages
English (en)
Inventor
孙启良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHONGQING DIANSHI METAL SURFACE TREATMENT Co Ltd
Original Assignee
CHONGQING DIANSHI METAL SURFACE TREATMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHONGQING DIANSHI METAL SURFACE TREATMENT Co Ltd filed Critical CHONGQING DIANSHI METAL SURFACE TREATMENT Co Ltd
Priority to CN2011103864115A priority Critical patent/CN103132068A/zh
Publication of CN103132068A publication Critical patent/CN103132068A/zh
Pending legal-status Critical Current

Abstract

本发明属于钝化处理领域，公开了一种三价铬浓缩蓝白钝化剂，主要由以下成分制成：氯化铬：8-50g/L、硫酸铝钾：10-60g/L、偏钒酸铵：3-10g/L、硝酸钴：3-20g/L、偶联剂：8-15ml/L、希土元素：0.5-5g/L；还公开了一种用三价铬浓缩蓝白钝化剂钝化的方法，主要包括以下步骤：首先在产品表面镀锌，用水洗产品，再用浓盐酸活化产品，再用水洗产品；然后用蓝白钝化剂钝化处理产品，用水洗产品，再用热水封闭，最后烘干产品；本发明的目的在于提供一种更加环保、工艺容限宽，易于操作、稳定性好成膜牢，消耗少，成本低的三价铬浓缩蓝白钝化剂以及用蓝白钝化剂钝化的方法。

Description

一种三价铬浓缩蓝白钝化剂以及用蓝白钝化剂钝化的方法
技术领域
本发明涉及钝化处理领域， 尤其涉及一种三价铬浓缩蓝白钝化剂以及用蓝白钝化剂钝化的方法。
背景技术
目前市场上的钝化剂多为包含有六价铬，不利于环境的保护，同时用这种钝化剂钝化处理时工艺容限较窄，需要加温，对PH值有特殊的要求，工艺流程复杂，不易于操作控制，同时成品，稳定性差，而腐蚀和抗碰撞能力较差。
发明内容
为了解决上述技术问题，本发明的目的在于提供一种更加环保、工艺容限宽，易于操作、稳定性好成膜牢，消耗少，成本低的三价铬浓缩蓝白钝化剂以及用蓝白钝化剂钝化的方法。
本发明的完整技术方案是，一种三价铬浓缩蓝白钝化剂，主要由以下成分制成：氯化铬：8-50g/L、硫酸铝钾：10-60g/L、偏钒酸铵：3-10g/L、硝酸钴：3-20g/L、偶联剂：8-15ml/L、希土元素：0.5-5g/L。
所述钝化剂的PH值为2.5-4。
一种用三价铬浓缩蓝白钝化剂钝化的方法，主要包括以下步骤：
首先在产品表面镀锌，用水洗产品，再用浓盐酸活化产品，再用水洗产品；
然后用蓝白钝化剂钝化处理产品，用水洗产品，再用热水封闭，最后烘干产品。
其特征在于，所述热水封闭的温度为50-60度。
所述烘干产品的温度为小于60度。
所述钝化处理中钝化液的温度为40-50度。
所述钝化处理的时间为40-60秒。
由上可见，本发明与现在技术相比有如下有益效果：不含六价铬，本产品采用国际最先进的三价铬，不含六价铬，属新一代环保型产品；工艺容限宽，本产品于进口同类产品相比，不需要加温，对HP值无特殊要求。工艺流程简单，易于操作控制，稳定性好，成膜牢，蓝白色钝化膜均匀，致密，牢固，具有良好的耐腐蚀和抗碰撞能力，消耗少，成本低，本产品处理镀件效率高，消耗少，成本较同类产品大大降低。
具体实施方式
下面将通过具体实施例来详细说明本发明，在此本发明的示意性实施例以及说明用来解释本发明，但并不作为对本发明的限定。
实施例1：
本实施例一种三价铬浓缩蓝白钝化剂，主要由以下成分制成：氯化铬：8-50g/L、硫酸铝钾：10-60g/L、偏钒酸铵：3-10g/L、硝酸钴：3-20g/L、偶联剂：8-15ml/L、希土元素：0.5-5g/L，钝化剂的PH值为2.5-4。 
一种用三价铬浓缩蓝白钝化剂钝化的方法，主要包括以下步骤：
首先在产品表面镀锌，用水洗产品，再用浓盐酸活化产品（浓盐酸5-10ml/L，室温，10秒），再用水洗产品；
然后用蓝白钝化剂钝化处理产品，钝化液的温度为40-50度，钝化处理的时间为40-60秒，用水洗产品，再用热水封闭，热水封闭的温度为50-60度，最后烘干产品，烘干产品的温度为小于60度。
由上可见，不含六价铬，本产品采用国际最先进的三价铬，不含六价铬，属新一代环保型产品；工艺容限宽，本产品于进口同类产品相比，不需要加温，对HP值无特殊要求。工艺流程简单，易于操作控制，稳定性好，成膜牢，蓝白色钝化膜均匀，致密，牢固，具有良好的耐腐蚀和抗碰撞能力，消耗少，成本低，本产品处理镀件效率高，消耗少，成本较同类产品大大降低；钝化封闭二合一，整个工艺维护适当时，氯化钾镀锌钝化膜层耐中性盐雾试验可达72小时以上，而无氰碱性镀锌纯化膜层可达48小时以上；龙门式直线型电镀生产线适用于镀铜、铬、锌、吕氧化、磷化、塑料电镀及其他先进工艺要求，并可根据用户需要满足各种电镀中的功能性和装饰性要求。
整线结构合理、外形美观、操作方便、并可根据客户要求设计全自动和半自动两种操作，电脑可编程序控制的全自动操作系统可用屏幕显示，稳定性高。 
以上对本发明实施例所提供的技术方案进行了详细介绍，本文中应用了具体个例对本发明实施例的原理以及实施方式进行了阐述，以上实施例的说明只适用于帮助理解本发明实施例的原理；同时，对于本领域的一般技术人员，依据本发明实施例，在具体实施方式以及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。

Claims (7)

1.一种三价铬浓缩蓝白钝化剂，其特征在于，主要由以下成分制成：氯化铬：8-50g/L、硫酸铝钾：10-60g/L、偏钒酸铵：3-10g/L、硝酸钴：3-20g/L、偶联剂：8-15ml/L、希土元素：0.5-5g/L。
2.根据权利要求1所述的一种三价铬浓缩蓝白钝化剂，其特征在于，所述钝化剂的PH值为2.5-4。
3.一种用三价铬浓缩蓝白钝化剂钝化的方法，其特征在于，主要包括以下步骤：
首先在产品表面镀锌，用水洗产品，再用浓盐酸活化产品，再用水洗产品；
然后用蓝白钝化剂钝化处理产品，用水洗产品，再用热水封闭，最后烘干产品。
4.根据权利要求3所述的一种用三价铬浓缩蓝白钝化剂钝化的方法，其特征在于，所述热水封闭的温度为50-60度。
5.根据权利要求3所述的一种用三价铬浓缩蓝白钝化剂钝化的方法，所述烘干产品的温度为小于60度。
6.根据权利要求3所述的一种用三价铬浓缩蓝白钝化剂钝化的方法，所述钝化处理中钝化液的温度为40-50度。
7.根据权利要求3所述的一种用三价铬浓缩蓝白钝化剂钝化的方法，所述钝化处理的时间为40-60秒。
CN2011103864115A 2011-11-29 2011-11-29 一种三价铬浓缩蓝白钝化剂以及用蓝白钝化剂钝化的方法 Pending CN103132068A (zh)