CN103130438A - 一种多用途助磨剂 - Google Patents
一种多用途助磨剂 Download PDFInfo
- Publication number
- CN103130438A CN103130438A CN2013100540293A CN201310054029A CN103130438A CN 103130438 A CN103130438 A CN 103130438A CN 2013100540293 A CN2013100540293 A CN 2013100540293A CN 201310054029 A CN201310054029 A CN 201310054029A CN 103130438 A CN103130438 A CN 103130438A
- Authority
- CN
- China
- Prior art keywords
- grinding aid
- grinding
- usage
- aid
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种多用途助磨剂,解决了普通助磨剂用途单一、功能单一、性能不完整的问题,其特点是组合物按下述组分按重量百分比制备而成:甲酸钙聚合体:25-30%,十二胺:5-10%,十二烷基多苷:5-8%,分散剂M-13:10-15%,海藻酸钠:7-15%,磁化水:35%,与现有技术相比,具有用途广泛,可广泛用于硅酸盐水泥、水煤浆、矿渣、高岭土、膨润土、方解石、硅灰石、石英、铅锌矿等领域;采用甲酸钙聚合体作为增强助磨原料,与其它各分散剂复合,可以大幅度降低三乙醇胺的用量,降低了生产成本,助磨效果更加显著的优点,适应于非金属矿物助磨应用。
Description
技术领域
本发明涉及一种多用途助磨剂,属于冶金粉磨技术领域,适应于非金属矿物〔如各种规格型号的硅酸盐水泥、水煤浆、矿渣、高岭土、膨润土、方解石、硅灰石、炉渣等〕、金属矿物〔如石英、铅锌矿〕等粉磨过程中应用。
技术背景
出于节约能源和资源的消耗,提高有效矿物的利用率,增加有效矿物产率的目的。助磨剂的研制工作发展很快,尤其是水泥助磨剂,在世界各国已被广泛的使用。助磨剂的作用是一种机械力化学现象。添加助磨剂,使物料颗粒的表面自由能和晶格畸变程度减小,促使颗粒软化;助磨剂吸附在颗粒表面上能平衡因粉碎而产生的不饱和价键,防止颗粒再度聚结,从而抑制粉碎逆过程的进行。以上两者均可加速粉碎,产生助磨作用。
目前,助磨剂的用途单一、功能单一,均在硅酸盐水泥生产中的球磨机干磨过程使用,而不能应用到湿磨中,也很少能应用到碾磨、振动磨中。不能广泛的应用到更多的非金属矿、金属矿的粉磨过程。由于目前国内生产的水泥助磨剂所采用的材料均以醇胺类、尿素、硫酸盐、磷酸盐、高分子聚合物为主,生产成本较大,用途单一、功能单一,如中国发明专利CN1059411C、CN1220977A,由于加入量较大,经济成本较高,用途单一,难以在非金属矿,金属矿等较大范围使用。
发明内容
本发明的目的就是为了克服以上不足,针对现有水泥助磨剂用途单一、功能单一、配伍技术单一,提供一种不但是一种良好的水泥助磨剂,还可以作为水煤浆、矿渣、高岭土、膨润土、方解石、硅灰石、炉渣、石英、铅锌矿等非金属矿物、金属矿物的助磨剂。针对现有传统的水泥助磨剂只能应用到球磨机的干磨中,本发明提供的多功能助磨剂,不仅适用球磨机干磨,同时还适用于球磨机、碾磨、振动磨等磨矿机的干磨、湿磨中的一种多用途助磨剂。
本发明的主要技术方案上这样实现的,所述的一种多用途助磨剂,其特征在于由质量配比化工原料:甲酸钙聚合体:25-30%,多功能复合助磨分散剂:35-40%,磁化水:35%混溶后组成液体状多功能助磨剂。
所述的一种多用途助磨剂甲酸钙聚合体,多功能复合助磨分散剂、磁化水等在使用前提前制备,包括下述步骤:(1)、甲酸钙聚合体配伍与生产工艺:配伍:甲酸钙:25%,亚硝酸钠:23%,三乙醇胺:15%,磁化水:37%
所述的一种多用途助磨剂甲酸钙聚合体生产工艺:是在加热罐中加入自来水或地下水,升温至90-95℃,加入甲酸钙搅拌、溶解、混均,加入亚硝酸钠搅拌、溶解、混均,加入三乙醇胺,维持90-95℃,连续搅拌2-3h进行聚合反应,聚合反应结束后,静置反应30min,静置反应结束后即为硝酸钙聚合体。
所述的一种多用途助磨剂多功能复合助磨分散剂配伍原料:由对不同非金属矿,金属矿具有助磨分散功能的助磨分散剂组成,其原料组成为:十二胺、十二烷基多苷、分散剂M-13、海藻酸钠。
所述的一种多用途助磨剂磁化水采用自来水或地下水经过磁化装置处理后得到。磁化装置的磁场强度为250-300mT,水流速度为0.3m-0.5m/s,磁化时间为25-30s。
本发明的一种多用途助磨剂的有益效果是:一是指甲酸钙、亚硝酸钠、三乙醇胺复合后,形成甲酸钙聚合体,可极大提高水泥各龄期的强度,比单独加入三乙醇胺的效果要好的多;由于采用不同助磨分散功能的助磨分散剂进行多相复合,扩大了助磨剂的应用范围与功能范围;由于采用磁化水为分散载体,提高了助磨剂的活性与应用效果。二是适用于球磨机、碾磨、振动磨等磨矿机的干磨、湿磨等。提高磨机效率20-35%,适用于提高水泥各龄期强度,降低水泥熟料加入量,提高水泥混合材掺入量和提高水泥磨机台时产量的水泥生产中使用。提高有效矿物的产率和利用率。
具体实施方式:
实施例1:
取甲酸钙聚合体:25%
十二胺:10%
十二烷基多苷:5%
分散剂M-13:10%
海藻酸钠:15%
磁化水:35%
实施例2:
取甲酸钙聚合体:30%
十二胺:5%
十二烷基多苷:8%
分散剂M-13:15%
海藻酸钠:7%
磁化水:35%
在室温条件下生产加工。以下均按质量百分数加入。启动搅拌机后,先将35%磁化水加入到搅拌罐中,加入25-30%甲酸钙聚合体后,加入5-10%十二胺和5-8%十二烷基多苷,待搅拌、溶解、混合均匀后,加入10-15%的分散剂M-13,搅拌、溶解、混合均匀后加入7-15%海藻酸钠,搅拌、溶解、全部混合均匀后静置反应30min,滤出沉淀物的溶液即为多用途助磨剂成品。
用剂量:在硅酸盐水泥磨机中使用,加剂量为0.1%,在其它非金属矿、金属矿磨机中使用,视不同磨矿物、不同磨机,加剂量为0.1-0.3%。
Claims (5)
1.一种多用途助磨剂,其特征在于由质量配比化工原料:甲酸钙聚合体:25-30%,多功能复合助磨分散剂:35-40%,磁化水:35%混溶后组成液体状多功能助磨剂。
2.如权利要求1所述的一种多用途助磨剂,其特征在于甲酸钙聚合体,多功能复合助磨分散剂、磁化水等在使用前提前制备,包括下述步骤:(1)、甲酸钙聚合体配伍与生产工艺:配伍:甲酸钙:25%,亚硝酸钠:23%,三乙醇胺:15%,磁化水:37。
3.如权利要求2所述的一种多用途助磨剂,其特征在于甲酸钙聚合体生产工艺:是在加热罐中加入自来水或地下水,升温至90-95℃,加入甲酸钙搅拌、溶解、混均,加入亚硝酸钠搅拌、溶解、混均,加入三乙醇胺,维持90-95℃,连续搅拌2-3h进行聚合反应,聚合反应结束后,静置反应30min,静置反应结束后即为硝酸钙聚合体。
4.如权利要求1所述的一种多用途助磨剂,其特征在于多功能复合助磨分散剂配伍原料:由对不同非金属矿,金属矿具有助磨分散功能的助磨分散剂组成,其原料组成为:十二胺、十二烷基多苷、分散剂M-13、海藻酸钠。
5.如权利要求1所述的一种多用途助磨剂,其特征在于磁化水采用自来水或地下水经过磁化装置处理后得到。磁化装置的磁场强度为250-300mT,水流速度为0.3m-0.5m/s,磁化时间为25-30s。