CN103121806A - 一种砌筑、抹灰砂浆塑化剂和制法 - Google Patents
一种砌筑、抹灰砂浆塑化剂和制法 Download PDFInfo
- Publication number
- CN103121806A CN103121806A CN2013100473547A CN201310047354A CN103121806A CN 103121806 A CN103121806 A CN 103121806A CN 2013100473547 A CN2013100473547 A CN 2013100473547A CN 201310047354 A CN201310047354 A CN 201310047354A CN 103121806 A CN103121806 A CN 103121806A
- Authority
- CN
- China
- Prior art keywords
- mortar
- water
- fluidizer
- rosin
- plastering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种砌筑、抹灰砂浆塑化剂和制法。该塑化剂成分和重量比为松香:氢氧化钠:聚乙烯醇:水为8-12:1:8-12:80-120。其配方科学合理，制法简单，成本低。所述的塑化剂会使砂浆内产生无数小气泡，增加水泥体积，减少砂粒之间的摩擦力，它可改善水泥砂浆性能，增加砂浆和易性，保水性；同时，提高砂浆砌筑、抹灰的功效；还减少落地灰；节约水泥，不用石灰膏，保护环境；还能起到扩散水泥，乳化发泡作用。克服起壳、开裂等通病。在加气混凝土，普通混凝土低面打底或面层使用也有很好效果。按照中国国家标准对加入本发明塑化剂的建筑砂浆进行检测。结果表明，本发明的塑化剂完全符合上述的标准的规定。
Description
技术领域
本发明涉及一种砌筑、抹灰砂浆塑化剂和制法，属于建筑领域。
背景技术
传统的建筑砂浆一般的都现场拌制，施工和易性差、粘结力低、收缩大、耐久性差，用于内外墙施工易开裂、渗漏、空鼓、脱落等。尤其是要加入大量的石灰，不但增加人工成本还污染环境。后来，广泛使用塑化剂。但是还要使用的石灰膏或石灰粉。仍然有污染环境的问题，并且，成本较高，不为施工单位所接受。
发明内容
为了解决已有技术存在的问题，为此，本发明提供一种砌筑、抹灰砂浆塑化剂和制法。提供一种新型的塑化剂，取代传统的石灰膏和石灰粉。在水泥、粉煤灰配制的水泥砂浆基础之上，内掺于砌筑砂浆之中，使其和易性和保水性满足混合砂浆的技术要求。并且使其配制的混合砂浆各项技术性能指标优于传统的混合砂浆各项性能指标。
本发明提供的一种砌筑、抹灰砂浆塑化剂的成分和重量比为松香:氢氧化钠: 聚乙烯醇:水为8-12:1: 8-12:80-120；所述的松香，工业用一级品;氢氧化钠，工业级。
本发明提供的一种砌筑、抹灰砂浆塑化剂的制法如下：按松香:氢氧化钠:水的重量比为8-12:1: 10-15,将水、氢氧化钠加入水浴锅中加热到60℃，再将粒径为1mm的松香粉末均匀加入；按聚乙烯醇:水的重量比为8-12:70-105，加入聚乙烯醇和水，待松香全部溶解，成为浅黄色稠体，继续沸煮2个小时，浓缩成暗棕色的膏状体。
用法：（1）按塑化剂与水的重量比为1:10，将本发明提供的一种砌筑、抹灰砂浆塑化剂用水稀释，得到稀释的塑化剂；（2）按砂浆重量与稀释的塑化剂的重量比为1000:0.2-0.3，把稀释的塑化剂加入到砂浆中，搅拌均匀，即可使用。
有益效果：本发明提供的一种砌筑、抹灰砂浆塑化剂及制法。该塑化剂是由有机高聚物和无机化学外加剂复合的引气型粉状或液体外加剂，属阴离子活性材料。配方科学合理，效果独特，成本低。
本发明提供的一种砌筑、抹灰砂浆塑化剂可降低溶液表面张力，经加水搅拌产生封闭而微小的气泡。 塑化剂搅拌砂浆产生的微泡稳定性好，其微泡间距一般在0.25—2.5mm，这样使水泥水化反应充分，改善了砂浆的和易性。塑化剂的制备过程，在于它的浓缩时间与浓缩倍数，这样就决定在施工过程中的塑化剂的稀释和加入量。
本发明提供的一种砌筑、抹灰砂浆塑化剂可分散水泥颗粒，增加水泥体积，减少砂粒之间的摩擦力。该塑化剂的各种物理力学性能进行分析表明，该塑化剂具有良好的和易性、稠度和保水性，能更有效的提高建筑工程质量，克服传统混合砂浆的缺点，使砌筑砂浆更易施工操作，薄层施工时可延长操作，厚层施工时，具有良好的抗流挂性，粘结强度高，不易开裂。
本发明提供的一种砌筑、抹灰砂浆塑化剂可提高砂浆砌筑、抹灰的功效；还减少落地灰；节约水泥，不用石灰膏或石灰粉；在保证质量的前提下，还可以掺入粉煤灰，既废物利用，又有降低成本；克服了起壳、开裂等通病。在加气混凝土，普通混凝土低面打底或面层使用也收到很好的效果。在砌筑中使用，其饱满度提高。硬化后具有抗冻、减水、防渗、耐久、抗裂，保温、隔热等作用。
具体实施方式
实施例1 一种砌筑、抹灰砂浆塑化剂。该塑化剂的成分和重量比为松香:氢氧化钠: 聚乙烯醇:水=10:1: 10:90；所述的松香，工业用一级品;氢氧化钠，工业级。
本发明提供的一种砌筑、抹灰砂浆塑化剂的制法如下：
按松香:氢氧化钠:水的重量比为10:1:10,将水、氢氧化钠加入水浴锅中加热到60℃，再将粒径为1mm的松香粉末均匀加入；按聚乙烯醇:水的重量比为10:80，加入聚乙烯醇和水，待松香全部溶解，成为浅黄色稠体，继续沸煮2个小时，浓缩成暗棕色的膏状体。
用法：（1）按塑化剂与水的重量比为1:10，将本发明提供的砌筑、抹灰砂浆塑化剂用水稀释，得到稀释的塑化剂；（2）按本发明塑化剂的配比重量是水泥+粉煤灰重量的1-3‰，把稀释的塑化剂加入到砂浆中，搅拌均匀，即可使用。
实施例2 一种砌筑、抹灰砂浆塑化剂。该塑化剂的成分和重量比为松香:氢氧化钠: 聚乙烯醇:水=8:1: 12:80；所述的松香，工业用一级品;氢氧化钠，工业级。
本发明提供的一种砌筑、抹灰砂浆塑化剂的制法如下：按松香:氢氧化钠:水的重量比为8:1: 10,将水、氢氧化钠加入水浴锅中加热到60℃，再将粒径为1mm的松香粉末均匀加入；按聚乙烯醇:水的重量比为12:70，加入聚乙烯醇和水，待松香全部溶解，成为浅黄色稠体，继续沸煮2个小时，浓缩成暗棕色的膏状体。其余的同实施例1
实施例3 一种砌筑、抹灰砂浆塑化剂。该塑化剂的成分和重量比为松香:氢氧化钠: 聚乙烯醇:水=12:1: 8:120；所述的松香，工业用一级品;氢氧化钠，工业级。
本发明提供的一种砌筑、抹灰砂浆塑化剂的制法如下：按松香:氢氧化钠:水的重量比为12:1: 15,将水、氢氧化钠加入水浴锅中加热到60℃，再将粒径为1mm的松香粉末均匀加入；按聚乙烯醇:水的重量比为8:105，加入聚乙烯醇和水，待松香全部溶解，成为浅黄色稠体，继续沸煮2个小时，浓缩成暗棕色的膏状体。其余的同实施例1
对于实施例1 制得的塑化剂 进行了检测。见表1和表2。
表1
注：表1中，本发明塑化剂的配比重量范围是水泥+粉煤灰重量和的1-3‰。
表2
注：表2中，本发明塑化剂的配比重量范围同表1。
表1是按照中国国家标准:砌筑砂浆配合比设计程CJG98-2000的规定，对加入本发明的塑化剂的砌筑砂浆进行检测的的结果。表2是按照中国国家标准: 建筑砂浆基本性能试验方法标准JGJ/T70-2009的规定，对加入本发明的塑化剂的建筑砂浆进行检测的的结果。可以看出，本发明的塑化剂完全符合上述的标准的规定，满足现代建筑施工的需要。
Claims (2)
1.一种砌筑、抹灰砂浆塑化剂，其特征在于，成分和重量比为松香:氢氧化钠: 聚乙烯醇:水为8-12:1: 8-12:80-120；所述的松香，工业用一级品;氢氧化钠，工业级。
2.如权利要求1所述的一种砌筑、抹灰砂浆塑化剂的制法，其特征在于，步骤和条件如下：按松香:氢氧化钠:水的重量比为8-12:1: 10-15,将水、氢氧化钠加入水浴锅中加热到60℃，再将粒径为1mm的松香粉末均匀加入；按聚乙烯醇:水的重量比为8-12:70-105，加入聚乙烯醇和水，待松香全部溶解，成为浅黄色稠体，继续沸煮2个小时，浓缩成暗棕色的膏状体。