CN103114494A - 一种阻燃纸及其制备方法 - Google Patents

一种阻燃纸及其制备方法 Download PDF

Info

Publication number
CN103114494A
CN103114494A CN2013100202600A CN201310020260A CN103114494A CN 103114494 A CN103114494 A CN 103114494A CN 2013100202600 A CN2013100202600 A CN 2013100202600A CN 201310020260 A CN201310020260 A CN 201310020260A CN 103114494 A CN103114494 A CN 103114494A
Authority
CN
China
Prior art keywords
paper
flame retardant
papers
fire retardant
ludox
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013100202600A
Other languages
English (en)
Inventor
乔英杰
赵红
张晓红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Harbin Engineering University
Original Assignee
Harbin Engineering University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Harbin Engineering University filed Critical Harbin Engineering University
Priority to CN2013100202600A priority Critical patent/CN103114494A/zh
Publication of CN103114494A publication Critical patent/CN103114494A/zh
Pending legal-status Critical Current

Abstract

本发明提供的是一种阻燃纸及其制备方法。以质量比为35-75份的硅酸铝纤维、5-45份的胶黏剂为原料。硅酸铝纤维经除渣后进行打浆处理5-30min，再与胶黏剂混合后倒入疏解器800-3000rad疏解，用造纸成型器进行抄造，抽真空干燥，形成纸页。本发明采用硅酸铝纤维复合纸代替植物纤维和传统阻燃剂复合制备阻燃包装纸，环保、阻燃效果好。避免了阻燃包装纸制备中使用有毒物质、污染环境，阻燃效果不好等问题。

Description

一种阻燃纸及其制备方法
技术领域
本发明涉及的是一种阻燃纸。本发明也涉及一种阻燃纸的制备方法。
背景技术
众所周知，“纸里包不住火”。纸一般是由植物纤维抄造而成，植物纤维是有机物，易燃。纸品的易燃性限制了制品的适用范围。纸易燃，经过特殊处理，可达到不燃，使纸品的应用范围增大。目前阻燃包装纸可用于以下几个方面：面层贴合材料、填芯材料、微波炉食品加热袋、电器的包装材料、礼宾、花筒纸质包装品、灯笼纸质等方面[1、李超等，镁铝水滑石制备阻燃纸的研究，中华纸业，2011(1)]
已有的阻燃包装纸存在的阻燃剂使用有毒物质、溴污染环境阻燃效果不好等问题[2、逄锦江等，硅酸铝纤维作为造纸填料的可能性的探讨，中国造纸，2010(4)]。
发明内容
本发明目的是提供一种据偶良好的隔热性能的阻燃纸。本发明的目的还在于提供一种产品的隔热性能好，环境污染小的阻燃纸的制备方法。
本发明的目的是这样实现的：
本发明的阻燃纸是由质量比为35-75份的硅酸铝纤维，5-45份的胶黏剂制成。
所述的胶黏剂为玉米淀粉、硅溶胶或者是质量比为5-40:5-30的玉米淀粉与硅溶胶的混合物。
所述的硅溶胶为聚合氯化铝或硅酸钠。
本发明的阻燃纸是采用这样的方法来制备的：
硅酸铝纤维经除渣后进行打浆处理5-30min，再与胶黏剂混合后倒入疏解器800-3000rad疏解，用造纸成型器进行抄造，抽真空干燥，形成纸页。
本发明采用硅酸铝纤维代替植物纤维和阻燃剂制备阻燃包装纸。在制备的过程中，采用玉米淀粉（羧甲基纤维素）、硅溶胶（聚合氯化铝、硅酸钠）或硅溶胶（聚合氯化铝、硅酸钠）与玉米淀粉（羧甲基纤维素）复配混合物为胶黏剂。
本发明与现有技术相比，具有以下明显的优势和有益效果：
a.无机胶黏剂耐高温，但在常温下胶黏效果不如有机胶黏剂，为了保证阻燃包装纸在常温下的力学性能，不能影响在高温下的阻燃性能，有机胶黏剂的使用量降到4%-20%。
b.本发明的阻燃包装纸可应用在面层贴合材料中，硅酸铝纤维阻燃纸复合在阻燃壁纸或装饰贴面纸中间，遇明火或高温时阻燃，能减少火灾损失，甚至可以阻止火灾的发生。将硅酸铝纤维阻燃包装纸贴在瓦楞纸板面纸与芯纸的中间，既不影响瓦楞纸板的适印性，又起到阻燃的效果。
本发明续燃时间和阴燃时间8.5s和3.4s，比用镁铝水滑石体系续燃时间和灼燃时间1.5s和4.1s效果好。
具体实施方式
下面举例对本发明做更详细的描述：
实施例1：
以硅酸铝纤维75份为原料将硅酸铝纤维棉首先进行打浆5min，以25份的质量比为12:7的硅溶胶与玉米淀粉的混合物为胶黏剂，硅酸铝纤维与胶黏剂混合后倒入疏解器900rad疏解，用造纸用成型器进行抄造，后抽真空干燥，形成纸页。
复合阻燃纸试样有部分成分快速燃烧，有明火烧过的部分有炭化，但阻燃纸内有部分未燃烧，无炭化长度，续燃时间8.1S，阴燃时间2.2S，复合阻燃纸试样没有燃烧的痕迹，点火后，在纸张上有火焰烟熏过的痕迹，被火焰烧过的地方比没烧过的地方要软。
实施例2：
以硅酸铝纤维70份为原料首先进行打浆10min，以30份的质量比为14:9的硅溶胶与玉米淀粉的混合物为胶黏剂30，混合后倒入疏解器800rad疏解，用造纸用成型器进行抄造，后抽真空干燥，形成纸页。
复合阻燃纸试样有部分成分快速燃烧，有明火烧过的部分有炭化，但阻燃纸内有部分未燃烧，无炭化长度，续燃时间8.4S，阴燃时间2.7S，复合阻燃纸试样没有燃烧的痕迹，点火后，在纸张上有火焰烟熏过的痕迹，被火焰烧过的地方比没烧过的地方要软。
实施例3：
以硅酸铝纤维棉65份为原料首先进行打浆15min，以35份的质量比为13:8的硅溶胶与玉米淀粉的混合物为胶黏剂，混合后倒入疏解器1000rad疏解，用造纸用成型器进行抄造，后抽真空干燥，形成纸页。复合阻燃纸试样有部分成分快速燃烧，有明火烧过的部分有炭化，但阻燃纸内有部分未燃烧，无炭化长度，续燃时间8.6S，阴燃时间2.4S，复合阻燃纸试样没有燃烧的痕迹，点火后，在纸张上有火焰烟熏过的痕迹，被火焰烧过的地方比没烧过的地方要软。
实施例4：
以硅酸铝纤维棉73份为原料首先进行打浆20min，以27份的质量比为16:13硅溶胶与玉米淀粉的混合物为胶黏剂，混合后倒入疏解器1500rad疏解，用造纸用成型器进行抄造，后抽真空干燥，形成纸页。复合阻燃纸试样有部分成分快速燃烧，有明火烧过的部分有炭化，但阻燃纸内有部分未燃烧，无炭化长度，续燃时间8.1S，阴燃时间3.2S，复合阻燃纸试样没有燃烧的痕迹，点火后，在纸张上有火焰烟熏过的痕迹，被火焰烧过的地方比没烧过的地方要软。
实施例5：
以硅酸铝纤维棉60份%为原料首先进行打浆25min，以40份的质量比为17:14的硅溶胶与玉米淀粉的混合物为胶黏剂，混合后倒入疏解器2000rad疏解，用造纸专用成型器进行抄造，后抽真空干燥，形成纸页。复合阻燃纸试样有部分成分快速燃烧，有明火烧过的部分有炭化，但阻燃纸内有部分未燃烧，无炭化长度，续燃时间9.1S，阴燃时间2.6S，复合阻燃纸试样没有燃烧的痕迹，点火后，在纸张上有火焰烟熏过的痕迹，被火焰烧过的地方比没烧过的地方要软。

Claims (6)

1.一种阻燃纸，其特征是由质量比为35-75份的硅酸铝纤维，5-45份的胶黏剂制成。
2.根据权利要求1所述的阻燃纸，其特征是：所述的胶黏剂为玉米淀粉、硅溶胶或者是质量比为5-40:5-30的玉米淀粉与硅溶胶的混合物。
3.根据权利要求3所述的阻燃纸，其特征是：所述的硅溶胶为聚合氯化铝或硅酸钠。
4.一种如权利要求1所述的阻燃纸的制备方法，其特征是：硅酸铝纤维经除渣后进行打浆处理5-30min，再与胶黏剂混合后倒入疏解器800-3000rad疏解，用造纸成型器进行抄造，抽真空干燥，形成纸页。
5.根据权利要求4所述的阻燃纸的制备方法，其特征是：所述的胶黏剂为玉米淀粉、硅溶胶或者是质量比为5-40:5-30的玉米淀粉与硅溶胶的混合物。
6.根据权利要求5所述的阻燃纸，其特征是：所述的硅溶胶为聚合氯化铝或硅酸钠。
CN2013100202600A 2013-01-18 2013-01-18 一种阻燃纸及其制备方法 Pending CN103114494A (zh)