CN103113974B - 一种环保型不锈钢拉伸油及其制备方法 - Google Patents

一种环保型不锈钢拉伸油及其制备方法 Download PDF

Info

Publication number
CN103113974B
CN103113974B CN201310066674.7A CN201310066674A CN103113974B CN 103113974 B CN103113974 B CN 103113974B CN 201310066674 A CN201310066674 A CN 201310066674A CN 103113974 B CN103113974 B CN 103113974B
Authority
CN
China
Prior art keywords
environment
stainless steel
drawing oil
steel drawing
potassium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310066674.7A
Other languages
English (en)
Other versions
CN103113974A (zh
Inventor
张乃庆
吴启东
陈立坤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Yuanyuan Power Lubrication Technology Co.,Ltd.
Original Assignee
Shanghai Jinzhao Energy Saving Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Jinzhao Energy Saving Technology Co Ltd filed Critical Shanghai Jinzhao Energy Saving Technology Co Ltd
Priority to CN201310066674.7A priority Critical patent/CN103113974B/zh
Publication of CN103113974A publication Critical patent/CN103113974A/zh
Application granted granted Critical
Publication of CN103113974B publication Critical patent/CN103113974B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种环保型不锈钢拉伸油及其制备方法。该环保型不锈钢拉伸油，按重量百分比计由以下组分组成：聚乙二醇30-50%，尿素5-10%，磷酸钾盐1-2%，四硼酸钾1-2%，水余量；所述聚乙二醇采用平均分子量在1000-6000的聚乙二醇。该环保型不锈钢拉伸油的制备方法：按所述重量百分比称取各原料，把所称取的尿素、磷酸钾盐、四硼酸钾依次加入所称取的水中搅拌至无沉淀物，再加入所称取的聚乙二醇，继续搅拌至完全透明后包装即可。本发明的环保型不锈钢拉伸油具有很好的润滑性、冷却性和极压抗磨性，加工件表面光亮度好，同时加工工件只需清水就可洗净，节省了清洗剂的使用量；无硫、氯等对环境有害的添加剂成分，减少了对环境和工人的危害。

Description

一种环保型不锈钢拉伸油及其制备方法
技术领域
本发明属于金属加工技术领域，具体涉及一种环保型不锈钢拉伸油及其制备方法。
背景技术
不锈钢拉伸传统的工艺是采用矿物油或/和菜籽油加入大量的含氯或/和含硫成分的抗磨添加剂进行润滑、冷却，润滑剂的使用量大，不易清洗，会造成加工场所和环境的巨大污染。
发明内容
本发明的目的是克服现有技术的不足，提供一种在不锈钢拉伸工艺中适用的采用新配方工艺制备的环保型不锈钢拉伸油及其制备方法。
为实现上述目的，本发明采用如下了技术方案：
一种环保型不锈钢拉伸油，按重量百分比计由以下组分组成：
Figure BDA00002874653600011
所述的聚乙二醇采用平均分子量在1000-6000的聚乙二醇，常用的商品编号有：PEG1000,PEG2000,PEG4000,PEG6000等，提供优异的润滑性能；
所述的尿素在不锈钢拉伸过程中可使表面更加光亮，同时对刀具和机床还有一定的防锈性；
所述的磷酸钾盐为磷酸二氢钾、磷酸氢二钾、磷酸钾中的一种或两种以上的混合物，极压抗磨性能优异；
所述的四硼酸钾极压抗磨性能好，同时还有防锈功能；
水可以让以上的固体物质互溶，同时增强冷却性。
上述环保型不锈钢拉伸油的制备方法：按所述重量百分比称取各原料，把所称取的尿素、磷酸钾盐、四硼酸钾依次加入所称取的水中搅拌至无沉淀物，再加入所称取的聚乙二醇，继续搅拌至溶液完全透明后即得环保型不锈钢拉伸油。
本发明的有益效果：
本发明与现有技术相比，具有很好的润滑性、冷却性和极压抗磨性，加工件表面光亮度好，同时加工工件只需清水就可洗净，节省了清洗剂的使用量；无硫、氯等对环境有害的添加剂成分，减少了对环境和工人的危害。
具体实施方式
下面结合实施例对本发明作进一步详细的说明：
实施例1
称取的5kg的尿素、1kg的磷酸钾、1kg的四硼酸钾依次加入称取的43kg水中搅拌至无沉淀物，再加入50kg的聚乙二醇PEG1000，继续搅拌至完全透明后包装即为一种环保型不锈钢拉伸油。
以上制备的环保型不锈钢拉伸油经检测理化指标为：
项目 基本数据 实验方法
外观 无色透明 目测
运动粘度40℃mm2/s 96 GB/T265
pH 9.2 SH/T0578
密度20℃kg/m3 1023 GB/T1884
四球极压试验PD kgf >500 GB/T12583
湿热实验（7天）级 1 GB/T2361
实施例2
称取的10kg的尿素、1kg的磷酸钾、1kg的磷酸二氢钾、2kg的四硼酸钾依次加入称取的56kg水中搅拌至无沉淀物，再加入30kg的聚乙二醇PEG6000，继续搅拌至完全透明后包装即为一种环保型不锈钢拉伸油。
以上制备的环保型不锈钢拉伸油经检测理化指标为：
项目 基本数据 实验方法
外观 无色透明 目测
运动粘度40℃mm2/s 128 GB/T265
pH 9.8 SH/T0578
密度20℃kg/m3 1022 GB/T1884
四球极压试验PB kgf >160 GB/T12583
实施例3
称取的8kg的尿素、1.5kg磷酸氢二钾、1.5kg的四硼酸钾依次加入称取的49kg水中搅拌至无沉淀物，再加入40kg的聚乙二醇PEG2000，继续搅拌至完全透明后包装即为一种环保型不锈钢拉伸油。
以上制备的环保型不锈钢拉伸油经检测理化指标为：
项目 基本数据 实验方法
外观 无色透明 目测
运动粘度40℃mm2/s 101 GB/T265
pH 9.5 SH/T0578
密度20℃kg/m3 1020 GB/T1884
四球磨斑直径mm 0.36 SH/T0762
实施例4
称取的6kg的尿素、1.2kg磷酸二氢钾、1.8kg的四硼酸钾依次加入称取的57kg水中搅拌至无沉淀物，再加入34kg的聚乙二醇PEG4000，继续搅拌至完全透明后包装即为一种环保型不锈钢拉伸油。
以上制备的环保型不锈钢拉伸油经检测理化指标为：
项目 基本数据 实验方法
外观 无色透明 目测
运动粘度40℃mm2/s 121 GB/T265
pH 9.1 SH/T0578
密度20℃kg/m3 1018 GB/T1884
铜片腐蚀（50℃，3h）级 1a GB/T5096

Claims (3)

1.一种环保型不锈钢拉伸油，其特征在于，按重量百分比计由以下组分组成：
聚乙二醇                          30-50%
尿素                               5-10%
磷酸钾盐                           1-2%
四硼酸钾                           1-2%
水                                 余量
所述聚乙二醇采用平均分子量在1000-6000的聚乙二醇。
2.如权利要求1所述的环保型不锈钢拉伸油，其特征在于，所述的磷酸钾盐为磷酸二氢钾、磷酸氢二钾、磷酸钾中的一种或两种以上的混合物。
3.一种如权利要求1-2中任一所述的环保型不锈钢拉伸油的制备方法，其特征在于：按所述重量百分比称取各原料，把所称取的尿素、磷酸钾盐、四硼酸钾依次加入所称取的水中搅拌至无沉淀物，再加入所称取的聚乙二醇，继续搅拌至溶液完全透明后即得。
CN201310066674.7A 2013-03-01 2013-03-01 一种环保型不锈钢拉伸油及其制备方法 Active CN103113974B (zh)