CN103059769A - 胶合板调胶树脂 - Google Patents
胶合板调胶树脂 Download PDFInfo
- Publication number
- CN103059769A CN103059769A CN 201110332166 CN201110332166A CN103059769A CN 103059769 A CN103059769 A CN 103059769A CN 201110332166 CN201110332166 CN 201110332166 CN 201110332166 A CN201110332166 A CN 201110332166A CN 103059769 A CN103059769 A CN 103059769A
- Authority
- CN
- China
- Prior art keywords
- powder
- bark
- stirs
- adds
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种酚醛树脂,具体涉及一种胶合板调胶树脂及其加工工艺,属化工技术领域。该加工工艺采用落叶松树皮作为填充剂,这种树皮容易粉碎和研磨成树皮粉。落叶松树皮粉质轻,密度低,含有大量单宁成分,它与密度高,渗透性大的矿物粉混合使用,可以有效改善矿物粉分层沉淀等问题,使调胶后树脂粘度稳定,活性期长。同时减少了面粉的用量,在提高胶合板胶粘度的同时,降低了生产成本。
Description
技术领域
本发明涉及一种酚醛树脂,具体涉及一种胶合板调胶树脂及其加工工艺,属化工技术领域。
背景技术
目前,在建筑材料市场上,各种类型的胶合板用途广泛,对于胶合板用的胶,大多采用面粉和矿物粉两种成分复合作为增充剂与低毒树脂混合,树脂容易产生分层和沉淀,只有面粉增量剂占总增充剂量的60%以上,才能满足生产工艺对胶活性期的要求,没有分层和沉淀。面粉用量过多,会加大填料成本。而林区有大量落叶松林,采伐剥皮后有大量落叶松树皮,这种树皮容易粉碎和研磨成树皮粉。落叶松树皮粉质轻,密度低,含有大量单宁成分,它与密度高,渗透性大的矿物粉混合使用,可以改善矿物粉分层沉淀等问题。
发明内容
本发明的目的是为克服上述现有技术的不足之处,提供一种胶合板调胶树脂及其加工工艺,该胶包括有填充剂、增量剂和稀释剂,所述的填充剂包括矿物粉、落叶松树皮粉、面粉。其中落叶松树皮粉和面粉用量比例增高,树脂的初粘度也随增高。由于落叶松树皮粉密度低,在含水率低时与树脂的混溶性较差,只有使其含水率达较高水平,才能与树脂很好混合,否则会浮在胶液表面,经长时间搅拌才能与胶混合均匀。均匀分散在胶液中的树皮粉对矿物粉起到了悬浮的作用,防止了矿物粉的沉淀与分层,加入适量面粉增量剂的应用,对调节胶的初粘度,提高树脂活性期起到了重要作用。
本发明是以如下技术方案实现的:一种胶合板调胶树脂,其特征是:该胶包括有填充剂、增量剂和稀释剂,所述的填充剂包括矿物粉、落叶松树皮粉、面粉,其重量份分别为:70、20、10,矿物粉为白色粉状的二氧化氮、二氧化硅,PH值为8.5-9.5;落叶松树皮粉含水率为9.4%。
一种胶合板调胶树脂加工工艺,其特征是:包括如下步骤:
(1)树皮粉加温,含水率达50%,加入总量1/2的酚醛树脂,搅拌均匀;
(2)面粉加水搅拌均匀,加入矿物粉搅拌均匀,加入总量1/2的酚醛树脂,搅拌均匀;
(3)将步骤(1)、(2)的物料合并再搅拌均匀,即得成品。
本发明的优点是:该加工工艺采用落叶松树皮作为填充剂,这种树皮容易粉碎和研磨成树皮粉。落叶松树皮粉质轻,密度低,含有大量单宁成分,它与密度高,渗透性大的矿物粉混合使用,可以有效改善矿物粉分层沉淀等问题,使调胶后树脂粘度稳定,活性期长。同时减少了面粉的用量,在提高胶合板胶粘度的同时,降低了生产成本。
具体实施方式
实施例、
该胶包括有填充剂、增量剂和稀释剂,所述的填充剂包括矿物粉、落叶松树皮粉、面粉,其重量份分别为:70、20、10,矿物粉为白色粉状的二氧化氮、二氧化硅,PH值为8.5-9.5;落叶松树皮粉含水率为9.4%。
一种胶合板调胶树脂加工工艺,其特征是:包括如下步骤:
(1)树皮粉加温,含水率达50%,加入总量1/2的酚醛树脂,搅拌均匀;
(2)面粉加水搅拌均匀,加入矿物粉搅拌均匀,加入总量1/2的酚醛树脂,搅拌均匀;
(3)将步骤(1)、(2)的物料合并再搅拌均匀,即得成品。
Claims (2)
1.一种胶合板调胶树脂,其特征是:该胶包括有填充剂、增量剂和稀释剂,所述的填充剂包括矿物粉、落叶松树皮粉、面粉,其重量份分别为:70、20、10,矿物粉为白色粉状的二氧化氮、二氧化硅,PH值为8.5-9.5;落叶松树皮粉含水率为9.4%。
2.一种胶合板调胶树脂加工工艺,其特征是:包括如下步骤:
(1)树皮粉加温,含水率达50%,加入总量1/2的酚醛树脂,搅拌均匀;
(2)面粉加水搅拌均匀,加入矿物粉搅拌均匀,加入总量1/2的酚醛树脂,搅拌均匀;
(3)将步骤(1)、(2)的物料合并再搅拌均匀,即得成品。