CN103044644B - 铸造用高强度环保型呋喃树脂及制备方法 - Google Patents
铸造用高强度环保型呋喃树脂及制备方法 Download PDFInfo
- Publication number
- CN103044644B CN103044644B CN201210479889.7A CN201210479889A CN103044644B CN 103044644 B CN103044644 B CN 103044644B CN 201210479889 A CN201210479889 A CN 201210479889A CN 103044644 B CN103044644 B CN 103044644B
- Authority
- CN
- China
- Prior art keywords
- furfuryl alcohol
- furan resin
- minutes
- preparation
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种高强度环保型呋喃树脂及制备方法。其特征是原料重量百分比,糠醇50%,甲醛25%,尿素10%;辅助材料10%,增强剂1%,氨水0.5%,盐酸0.5%,糖类下脚料3%。(1)先将糠醇与增强剂在40℃温度下改性反应20分钟后放料备用。(2)当尿素、甲醛通过碱性PH10,温度98℃,保温反应50分钟,然后加入已改性的糠醇、总量1/2再调PH4.2—4.5,缓慢升温(半小时)到105℃反应1.5小时。中间不需脱水即可冷却到85℃,调PH7.0放料。加辅助材料10%,氨水0.5%,糖类下脚料3%。再加入已改性糠醇1/2保温反应30分钟吹风过滤冷却40℃放料。
Description
技术领域
本发明涉及一种铸造用呋喃树脂,尤其是高强度环保型呋喃树脂,属化工原料领域。
背景技术
随着我国铸造业的迅速发展,树脂砂工艺被广泛运用,其需求量正在不断增加。目前使用的呋喃树脂主要以甲醛、尿素和糠醇为主要原料合成,虽然其铸造性能较好,但在使用过程中会散发醛、酚等有害气体,不仅污染环境,而且还影响操作工人的身体健康。
发明内容
本发明的目的是克服现有技术的不足,提供一种适用于各种铸件,方法独特,可实现无游离甲醛、不需脱水、糠醇独立改性反应、产品两用、高强度环保型呋喃树脂及制备方法。其在铸造使用过程中无甲醛散发,不仅有利于保护环境,而且有利于工人身体健康。
本发明的技术解决方案是:
1.铸造用高强度环保型呋喃树脂的原料配方:
原料重量百分比,糠醇50%,甲醛25%,尿素10%;辅助材料10%,增强剂1%,氨水0.5%,盐酸0.5%,糖类下脚料3%。
2. 铸造用高强度环保型呋喃树脂制备方法:
将制造过程分为两步:
(1)先将糠醇与增强剂在40℃温度下改性反应20分钟后放料备用。
(2)当尿素、甲醛通过碱性PH10,温度98℃,保温反应50分钟,然后加入已改性的糠醇、总量1/2再调PH4.2—4.5,缓慢升温(半小时)到105℃反应1.5小时。中间不需脱水即可冷却到85℃,调PH7.0放料。加辅助材料10%,氨水0.5%,糖类下脚料3%。再加入已改性糠醇1/2保温反应30分钟吹风过滤冷却40℃放料。其树脂具有粘度低,游离甲醛在0.01%左右。不含酚;强度高,比一般树脂加入量少15%-20%,可节约生产成本。
本发明的有益效果是:
1. 本发明生产效率高,工艺简单,绿色环保:在合成过程中先将糠醇与增强剂在40℃温度下改性反应,当尿醛通过碱性PH10反应后,再加入已改性的糠醇加入调PH4.2—4.5,不需脱水,通过辅助材料与甲醇进一步反应,使产品中不含游离甲醛,不仅有利于保护环境,而且有利于工人身体健康。
2. 本发明的配方科学,产品强度高,用途范围广:本发明提供原料配方独特,其产品强度高,可作自硬型和热芯盒两种方法使用。
具体实施方式
1.铸造用高强度环保型呋喃树脂的原料配方:
原料重量百分比,糠醇50%,甲醛25%,尿素10%;辅助材料10%,增强剂1%,氨水0.5%,盐酸0.5%,糖类下脚料3%。
2. 铸造用高强度环保型呋喃树脂制备方法:
将制造过程分为两步:
(1)先将糠醇与增强剂在40℃温度下改性反应20分钟后放料备用。
(2)当尿素、甲醛通过碱性PH10,温度98℃,保温反应50分钟,然后加入已改性的糠醇、再调PH4.2—4.5,缓慢升温(半小时)到105℃反应1.5小时。中间不需脱水即可冷却到85℃,调PH7.0放料。加辅助材料10%,氨水0.5%,糖类下脚料3%。加入改性糠醇1/2保温反应30分钟冷却40℃吹风过滤放料。其树脂具有粘度低,游离甲醛在0.01%左右。不含酚;强度高,比一般树脂加入量少15%-20%,可节约生产成本。
Claims (1)
1.一种高强度环保型呋喃树脂的制备方法,其特征是:
(1)高强度环保型呋喃树脂的原料重量百分比:糠醇50%,甲醛25%,尿素10%;辅助材料10%,增强剂1%,氨水0.5%,盐酸0.5%,糖类下脚料3%。
(2)高强度环保型呋喃树脂的制备方法:先将糠醇与增强剂在40℃温度下改性反应20分钟后放料备用;当尿素、甲醛通过碱性pH10,温度98℃,保温反应50分钟,然后加入已改性的糠醇,总量1/2再调pH4.2—4.5,缓慢升温到105℃反应1.5小时;冷却到85℃,调pH7.0放料;加辅助材料10%,氨水0.5%,糖类下脚料3%;再加入已改性糠醇1/2保温反应30分钟,吹风过滤冷却40℃放料。