CN102153719B - 热芯盒呋喃树脂 - Google Patents

热芯盒呋喃树脂 Download PDF

Info

Publication number
CN102153719B
CN102153719B CN 201110067012 CN201110067012A CN102153719B CN 102153719 B CN102153719 B CN 102153719B CN 201110067012 CN201110067012 CN 201110067012 CN 201110067012 A CN201110067012 A CN 201110067012A CN 102153719 B CN102153719 B CN 102153719B
Authority
CN
China
Prior art keywords
parts
furan resin
value
mass percent
regulating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201110067012
Other languages
English (en)
Other versions
CN102153719A (zh
Inventor
辛杰
尹俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHIYAN YUN COUNTY ZHUBANG CHEMICAL CO Ltd
Original Assignee
SHIYAN YUN COUNTY ZHUBANG CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHIYAN YUN COUNTY ZHUBANG CHEMICAL CO Ltd filed Critical SHIYAN YUN COUNTY ZHUBANG CHEMICAL CO Ltd
Priority to CN 201110067012 priority Critical patent/CN102153719B/zh
Publication of CN102153719A publication Critical patent/CN102153719A/zh
Application granted granted Critical
Publication of CN102153719B publication Critical patent/CN102153719B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提出了热芯盒呋喃树脂，按质量份由甲醛375±5份、尿素85±5份、苯酚100±5份、糠醇600±5份、丙三醇50±5份、山梨醇20±5，经过如下步骤制成：（1）、将苯酚、甲醛、尿素投入反应釜中，用质量百分比浓度为30%的氢氧化钠水溶液，调节pH值为8.5～9.0，在80～95℃反应60～80分钟；（2）、加入糠醇，用质量百分比浓度为10%的盐酸水溶液，调节pH值为4.5-4.8，在90～98℃反应90～110分钟；（3）、用质量百分比浓度为30%的氢氧化钠水溶液调节pH值为7.0，然后真空脱水，加入丙三醇、山梨醇，相互混合均匀，冷却至50℃以下，放料。本发明的固化温度在160-170℃，通过降低固化温度既节能降耗，又改善了生产工人的工作环境，提高了铸件精度。

Description

热芯盒呋喃树脂
技术领域
本发明属于一种铸造用中温固化的热芯盒呋喃树脂。
背景技术
随着我国铸造业的迅猛发展，呋喃树脂砂工艺的大量采用，铸造用呋喃树脂现已成为铸造业不可缺少的主力胶粘剂，现市场使用的呋喃树脂主要是热芯盒和自硬两类，目前的热芯盒呋喃树脂需要在230℃以上高温才能固化而满足使用要求，导致了工作现场温度太高，生产工人工作环境差，同时，还有所制芯、型存在热变形现象而影响铸件精度，自硬砂存在着固化时间太长（一般需要24小时），且型、芯强度低，不利于搬运等缺陷。
发明内容
本发明提出了在160-170℃温度时固化的热芯盒呋喃树脂，不但节能降耗，也给生产工人创造了良好的工作环境，同时有利于提高铸件精度。
为此，本发明的技术方案是：热芯盒呋喃树脂，其特征在于：按质量份由甲醛375±5份、尿素85±5份、苯酚100±5份、糠醇600±5份、丙三醇50±5份、山梨醇20±5，经过如下步骤制成：
（1）、将计量好的苯酚、甲醛、尿素投入反应釜中，用质量百分比浓度为30%的氢氧化钠水溶液，调节pH值为8.5～9.0，然后升温，在80～95℃的温度范围内反应60～80分钟；
（2）、加入计量好的糠醇，用质量百分比浓度为10%的盐酸水溶液，调节pH值为4.5-4.8，然后升温，在90～98℃的温度范围内反应90～110分钟；
（3）、用质量百分比浓度为30%的氢氧化钠水溶液调节pH值为7.0，然后真空脱水，加入计量好的丙三醇、山梨醇，相互混合均匀，冷却至50℃以下，放料。
有益效果：本发明采用了丙三醇和山梨醇后，改变了树脂的分子结构，使得树脂在受热和固化剂的作用下更易形成梯形分子结构而固化，本发明的固化温度在160-170℃，通过降低固化温度既节能降耗，又改善了生产工人的工作环境，减轻了所制芯、型存在的热变形现象，提高了铸件精度。
具体实施方式
实施例1：热芯盒呋喃树脂，由甲醛375kg、尿素85 kg、苯酚100 kg、糠醇600 kg、丙三醇50 kg、山梨醇20 kg，经过如下步骤制成：
（1）、将计量好的苯酚、甲醛、尿素投入反应釜中，用质量百分比浓度为30%的氢氧化钠水溶液，调节pH值为8.5，然后升温，在80～85℃的温度范围内反应70分钟；
（2）、加入计量好的糠醇，用质量百分比浓度为10%的盐酸水溶液，调节pH值为4.5，然后升温，在90～95℃的温度范围内反应100分钟；
（3）、用质量百分比浓度为30%的氢氧化钠水溶液调节pH值为7.0，然后真空脱水，加入计量好的丙三醇、山梨醇，相互混合均匀，冷却至50℃以下，放料。
实施例2：热芯盒呋喃树脂，由甲醛375kg、尿素85 kg、苯酚100 kg、糠醇600 kg、丙三醇50 kg、山梨醇20 kg，经过如下步骤制成：
（1）、将计量好的苯酚、甲醛、尿素投入反应釜中，用质量百分比浓度为30%的氢氧化钠水溶液，调节pH值为9.0，然后升温，在90～95℃的温度范围内反应60分钟；
（2）、加入计量好的糠醇，用质量百分比浓度为10%的盐酸水溶液，调节pH值为4.5，然后升温，在95～98℃的温度范围内反应110分钟；
（3）、用质量百分比浓度为30%的氢氧化钠水溶液调节pH值为7.0，然后真空脱水，加入计量好的丙三醇、山梨醇，相互混合均匀，冷却至50℃以下，放料。
热芯盒呋喃树脂的技术标准和本发明的检验结果对比如下表:
                                                 
Figure 811363DEST_PATH_IMAGE001
 

Claims (1)

1.热芯盒呋喃树脂，其特征在于：按质量份由甲醛375±5份、尿素85±5份、苯酚100±5份、糠醇600±5份、丙三醇50±5份、山梨醇20±5，经过如下步骤制成：
（1）、将计量好的苯酚、甲醛、尿素投入反应釜中，用质量百分比浓度为30%的氢氧化钠水溶液，调节pH值为8.5～9.0，然后升温，在80～95℃的温度范围内反应60～80分钟；
（2）、加入计量好的糠醇，用质量百分比浓度为10%的盐酸水溶液，调节pH值为4.5-4.8，然后升温，在90～98℃的温度范围内反应90～110分钟；
（3）、用质量百分比浓度为30%的氢氧化钠水溶液调节pH值为7.0，然后真空脱水，加入计量好的丙三醇、山梨醇，相互混合均匀，冷却至50℃以下，放料。
CN 201110067012 2011-03-21 2011-03-21 热芯盒呋喃树脂 Expired - Fee Related CN102153719B (zh)