CN102921878B - 一种覆膜砂及其制备方法 - Google Patents

一种覆膜砂及其制备方法 Download PDF

Info

Publication number
CN102921878B
CN102921878B CN201210458471.8A CN201210458471A CN102921878B CN 102921878 B CN102921878 B CN 102921878B CN 201210458471 A CN201210458471 A CN 201210458471A CN 102921878 B CN102921878 B CN 102921878B
Authority
CN
China
Prior art keywords
sand
parts
curing agent
additive
order
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210458471.8A
Other languages
English (en)
Other versions
CN102921878A (zh
Inventor
侯广怀
曹岳山
季建国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sinotruk Jinan Power Co Ltd
China National Heavy Duty Truck Group Jinan Power Co Ltd
Original Assignee
China National Heavy Duty Truck Group Jinan Power Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China National Heavy Duty Truck Group Jinan Power Co Ltd filed Critical China National Heavy Duty Truck Group Jinan Power Co Ltd
Priority to CN201210458471.8A priority Critical patent/CN102921878B/zh
Publication of CN102921878A publication Critical patent/CN102921878A/zh
Application granted granted Critical
Publication of CN102921878B publication Critical patent/CN102921878B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种覆膜砂及其制备方法，由下列重量份比的原料制成：50～100目焙烧石英砂40份，40～70目莫来石高温焙烧砂30份，50～100目铬铁矿砂30份，酚醛树脂2份，固化剂2份，添加剂1份。将焙烧石英砂、莫来石高温焙烧砂、铬铁矿砂混合加热、干混，然后依次加入酚醛树脂、固化剂、添加剂混匀，卸砂冷却。本发明制得的覆膜砂具有较高的耐火度和热化学稳定性、具有较高的热抗拉强度和热抗弯强度、良好的溃散性和低发气性。

Description

一种覆膜砂及其制备方法
技术领域
本发明涉及铸造用覆膜砂及其制备方法，特别是一种适用于大功率（10升、12升）柴油发动机缸体毛坯铸造生产中，热芯盒法生产水套砂芯用的特种覆膜砂。
背景技术
近年来，由于重型汽车发展速度很快，大功率柴油发动机产量也大幅度提高，为提高发动机缸体铸件质量和降低生产成本，要求铸造生产水套砂芯用覆膜砂必须具有较高的耐火度和热化学稳定性、具有较高的热抗拉强度和热抗弯强度、良好的溃散性和低发气性。
发明内容
本发明的目的是提供一种具有较高的耐火度和热化学稳定性、具有较高的热抗拉强度和热抗弯强度、良好的溃散性和低发气性的覆膜砂及其制备方法。
本发明采取的技术方案为：
一种覆膜砂，由下列重量份比的原料制成：50～100目焙烧石英砂40份，40～70目莫来石高温焙烧砂30份，50～100目铬铁矿砂30份，酚醛树脂2份，固化剂0.3份，添加剂1份。
所述的添加剂为重量比为1:1的石墨粉和氧化铁粉，两者均在200目以下的。
所述的固化剂为：质量浓度为50%的乌洛托品水溶液。
所述的覆膜砂的制备方法，包括步骤如下：
（1）将焙烧石英砂、莫来石高温焙烧砂、铬铁矿砂混合；
（2）将混合好的材料加热到150-160℃；
（3）将材料加入到转速为200r/min高速混砂机，干混5-10秒；
（4）向混料中加入酚醛树脂继续混30-35秒，再加入固化剂混45-50秒；
（5）加入添加剂混15-20秒，卸砂，破碎筛分，风冷至40℃以下，储存。
本发明的有益效果是：本发明制得的覆膜砂具有较高的耐火度和热化学稳定性、具有较高的热抗拉强度和热抗弯强度、良好的溃散性和低发气性。使用该特种覆膜砂进行热芯盒法生产水套砂芯用于发动机缸体毛坯铸造生产，提高了铸件成品率和质量。使用普通覆膜砂生产水套砂芯用于发动机缸体毛坯铸造生产，水套砂芯造成的废品一般为10-15%，使用本发明特种覆膜砂水套砂芯造成的废品降为1%以下。
具体实施方式
下面结合实施例进一步说明。
实施例1
称量原料：50目焙烧石英砂（市场可购买，生产厂家：内蒙古通辽市大林型砂有限公司）40份，40目莫来石高温焙烧砂（市场可购买，生产厂家：河南省禹州大禹耐火材料有限公司）30份，50目铬铁矿砂30份，酚醛树脂2份，固化剂（质量浓度为50%的乌洛托品水溶液）0.3份，添加剂（重量比为1:1的石墨粉和氧化铁粉）1份。
选择一台高速转子混砂机；按照组分的重量份配料，将50目焙烧石英砂，40目莫来石高温焙烧砂，50目铬铁矿砂加入高速混砂机混合1分钟，将混合好的材料倒入加热炉加热到150℃；再选择一台高速转子混砂机；将加热后的混合料加入到高速混砂机干混5秒；加入酚醛树脂混30秒；再加入固化剂混45秒；加入添加剂混15秒；卸砂；将混好的砂子利用振动筛破碎筛分，利用冷却器风冷至40℃以下；储存。
实施例2
称量原料：100目焙烧石英砂40份，70目莫来石高温焙烧砂30份，100目铬铁矿砂30份，酚醛树脂2份，固化剂0.3份，添加剂1份。
选择一台高速转子混砂机；按照组分的重量份配料，将100目焙烧石英砂，70目莫来石高温焙烧砂，100目铬铁矿砂加入高速混砂机混合1分钟，将混合好的材料倒入加热炉加热到150℃；再选择一台高速转子混砂机；将加热后的混合料加入到高速混砂机干混5秒；加入酚醛树脂混30秒；再加入固化剂混45秒；加入添加剂混15秒；卸砂；将混好的砂子利用振动筛破碎筛分，利用冷却器风冷至40℃以下；储存。

Claims (1)

1.一种覆膜砂，其特征是，它由下列重量份比的原料制成：50～100目焙烧石英砂40份，40～70目莫来石高温焙烧砂30份，50～100目铬铁矿砂30份，酚醛树脂2份，固化剂0.3份，添加剂1份；所述的添加剂为重量比为1:1的石墨粉和氧化铁粉，两者均在200目以下的；
所述的固化剂为：质量浓度为50％的乌洛托品水溶液；
其制备方法为：
(1)将焙烧石英砂、莫来石高温焙烧砂、铬铁矿砂混合；
(2)将混合好的材料加热到150-160℃；
(3)将材料加入到转速为200r/min高速混砂机，干混5-10秒；
(4)向混料中加入酚醛树脂继续混30-35秒，再加入固化剂混45-50秒；
(5)加入添加剂混15-20秒，卸砂，破碎筛分，风冷至40℃以下，储存。
CN201210458471.8A 2012-11-14 2012-11-14 一种覆膜砂及其制备方法 Active CN102921878B (zh)