CN102995261A - Natural thermal effect composite fabric knitting fabric and knitting method thereof - Google Patents
Natural thermal effect composite fabric knitting fabric and knitting method thereof Download PDFInfo
- Publication number
- CN102995261A CN102995261A CN2012105712893A CN201210571289A CN102995261A CN 102995261 A CN102995261 A CN 102995261A CN 2012105712893 A CN2012105712893 A CN 2012105712893A CN 201210571289 A CN201210571289 A CN 201210571289A CN 102995261 A CN102995261 A CN 102995261A
- Authority
- CN
- China
- Prior art keywords
- fabric
- yarn
- natural
- model
- knitting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a knitting method of a natural thermal effect composite fabric knitting fabric. The knitting method is characterized in that wool fiber blended yarns, kam ammonia wrapped yarns and modal are selected to perform interweaving, composite ribs combining plain stitch and rib stitch are adopted, the plain stitch adopts the modal to perform knitting, the rib stitch adopts biological fine-drawn wool/ mucilage glue/ kapok blended yarns to perform knitting, and the three-layer composite tissue is knitted. The inner surface of the fabric is a comfortable warm-keeping surface, the outer surface of the fabric is a moisture-absorption heat-dissipation warm-keeping surface, and the middle surface of the fabric is a high-elastic comfortable layer formed by wrapped yarns. By means of the knitting method, the elasticity of the fabric is improved, and multifunctional effects of moisture absorption, heat dissipation and the like of the wool, kapok and multi-fiber blended interwoven fabric can be fully achieved. The natural thermal effect composite knitting fabric is knitted by means of selection of raw materials and reasonable organization structures and has the advantages of being light, thin, fashionable, good in breathability and capable of absorbing moisture and dissipating heat naturally.
Description
Technical field
The invention belongs to the textile product technical field, relate to the improvement of knit product and production technology thereof, is a kind of natural thermogenetic effect composite material knit goods and weaving method thereof specifically.
Background technology
Along with weather turns warm, people pursue from the past for insulation garment heating and thick and heavyly ask that warming to change into frivolous and warming be main, principle according to Heat-moisture Comfort, select rational raw material, institutional framework and arrangement processing, design fabric frivolous, natural moisture absorption heating, and be aided with functional treatment, be a direction of current cold-proof underwear development.
At present, the research and comparison of Japan aspect hygroscopic heating fibers is ripe, American-European countries following closely, and the synthetic fiber weaving process with moisture absorption heating function has no report at home, domesticly only the moisture absorption heating synthetic fiber of external production have been done Preliminary Applications, but many research to use all be the spinning that is conceived to the heat generating fiber take synthetic fiber such as acrylic fibers, terylene as carrier, weave, dyeing and finishing processing method.
Therefore, how mainly to utilize multiple moisture absorption heating natural fabric and artificial fibre reasonably combined, adopt new reasonable fabric tissue, study and improve ripe weaving process, the mutual supplement with each other's advantages of bringing into play multiple fiber is the technical problem that needs to be resolved hurrily at present.
Summary of the invention
The problem and shortage that the present invention exists for solving prior art, and provide a kind of natural thermogenetic effect composite material knit goods and weaving method thereof, selection and rational institutional framework and weaving process route by raw material, produce natural thermogenetic effect knit fabric, have frivolous, natural moisture absorption heating, breathe freely, the effect of fashion, make product reach the specification requirement of moisture absorption heating knitted underwear inherent quality.
The objective of the invention is to be achieved through the following technical solutions: a kind of natural thermogenetic effect composite material knit goods, it is characterized in that: select the fleece fibre blended spinning yarn to interweave with bright and beautiful ammonia wrapped yarn and model, the compound rib that adopts plain stitch to be combined with rib stitch, rib stitch adopts the model braiding, biological drawing-down wool/viscose glue/kapok blended yarn braiding is adopted in plain stitch, braiding becomes three layers of complex tissue, the fabric inner face is close skin thermal surface, the fabric outside is moisture absorption heating insulation face, the high-elastic comfort liner that forms for wrapped yarn in the middle of the fabric.Not only improve the elasticity of fabric, and given full play to the multi-functional effects such as moisture absorption heating of wool, kapok and multifilament blended interwoven fabric.Hydrophily and warmth retention property is good, and the soft fiber one side of pressing close to skin as underwear, with the fiber of the wet comfortableness excellence of the heat outside as underwear.
To improvement of the technical scheme: described blended yarn is drawing-down wool/viscose glue/kapok 14.8tex blended yarn, and described model is the 14.8tex model.
A kind of weaving method of natural thermogenetic effect composite material knit goods, it is characterized in that: select the fleece fibre blended spinning yarn to interweave with bright and beautiful ammonia wrapped yarn and model, the compound rib that adopts plain stitch to be combined with rib stitch, rib stitch adopts the model braiding, biological drawing-down wool/viscose glue/kapok blended yarn braiding is adopted in plain stitch, braiding becomes three layers of complex tissue, the fabric inner face is close skin thermal surface, the fabric outside is moisture absorption heating insulation face, the high-elastic comfort liner that forms for wrapped yarn in the middle of the fabric.Not only improve the elasticity of fabric, and given full play to the multi-functional effects such as moisture absorption heating of wool, kapok and multifilament blended interwoven fabric.Hydrophily and warmth retention property is good, and the soft fiber one side of pressing close to skin as underwear, with the fiber of the wet comfortableness excellence of the heat outside as underwear.
To improvement of the technical scheme: described blended yarn is drawing-down wool/viscose glue/kapok 14.8tex blended yarn, and described model is the 14.8tex model.
To further improvement in the technical proposal: adopt the two-sided large circle machine braiding of JH-P4U2, the mode of entrying: 1F/5F penetrates drawing-down wool/viscose glue/kapok 14.8tex blended yarn; 2F/6F penetrates bright and beautiful ammonia wrapped yarn; 3F/4F/7F/8F penetrates model 14.8tex.
To further improvement in the technical proposal: in the weaving process parameter, hundred needlework are long: 1F/5F is 240 ± 2mm, and 2F/6F is 220 ± 2mm, and 3F/4F/7F/8F is 270 ± 2mm; Blank weight per square meter: 210 ± 2.5g/m
2, light base: 230 ± 10g/m
2Fabric is vertical close: 62 ± 1 lines/5cm; Lower machine fabric width: (90cm * 2) ± 2.5cm.
To further improvement in the technical proposal: present the style that the surface is rough, the inside is fine and smooth for making fabric panel, use three belts when adjustment of tonicity, the tension force of surperficial yarn is controlled at 2.5-3.5g; In be the looping stretch yarn, tension force is controlled at 3.5-4.5g; The inside yarn is 2 the tunnel and all weaves plain stitch that will control yarn feed quantity well, tension force is controlled at 4.5-5.5g.
The present invention compared with prior art has the following advantages and good effect: the present invention is by selection and rational institutional framework and the weaving process route of raw material, produce natural thermogenetic effect knit fabric, and have frivolous, natural moisture absorption heating, breathe freely, the effect of fashion.
(1) by drawing-down wool and kapok, viscose blended yarn and bright and beautiful ammonia wrapped yarn, model are interweaved, make the collocation of multiple fiber reasonable combination, give full play on the basis of natural moisture absorption heating effect of product and reach best cost performance.
(2) unique design, optimum selecting three-layer complex tissue, it is warming to produce fabric unilateralis skin, another side moisture absorption heating insulation, the high-elastic comfortable effect of middle wrapped yarn, product integral body have moisture transported permeable, emitting far-infrared, produce negative oxygen ion, the multi-functional effect of ANTIPILLING.
(3) for reach better frivolous, natural moisture absorption heating, breathe freely, the effect of fashion, preferred fleece fibre blended spinning yarn interweaves with bright and beautiful ammonia wrapped yarn and model, the compound rib that adopts plain stitch to be combined with rib stitch, rib stitch adopts the model braiding, biological drawing-down wool/viscose glue/kapok blended yarn braiding is adopted in plain stitch, not only improve the elasticity of fabric, and given full play to the multi-functional effects such as moisture absorption heating of wool, kapok and multifilament blended interwoven fabric.
Knit goods of the present invention reaches the specification requirement of moisture absorption heating knitted underwear inherent quality, and the various functions index all surpassed existing Product Level, and natural thermogenetic effect is obvious.Therefore, knit goods of the present invention is a kind of high value added product that integrates function and environmental protection, and to improving product specification, it is significant to increase economic benefit.
Description of drawings
Fig. 1 is the knitting needle Pareto diagram that adopts in the knit goods production technology of the present invention;
Fig. 2 is the cam chart that adopts in the knit goods production technology of the present invention;
Fig. 3 is the structural representation of the natural thermogenetic effect composite material of the present invention knit goods.
The specific embodiment
Below in conjunction with drawings and Examples the present invention is described in further detail.
Referring to Fig. 3, the embodiment of a kind of natural thermogenetic effect composite material knit goods of the present invention, select the fleece fibre blended spinning yarn to interweave with bright and beautiful ammonia wrapped yarn and model, the compound rib that adopts plain stitch to be combined with rib stitch, rib stitch adopts the model braiding, biological drawing-down wool/viscose glue/kapok blended yarn braiding is adopted in plain stitch, braiding becomes three layers of complex tissue, fabric inner face 3 is close skin thermal surface, fabric outside 1 is moisture absorption heating insulation face, the high-elastic comfort liner 2 that forms for wrapped yarn in the middle of the fabric.Not only improve the elasticity of fabric, and given full play to the multi-functional effects such as moisture absorption heating of wool, kapok and multifilament blended interwoven fabric.Hydrophily and warmth retention property is good, and the soft fiber one side 3 of pressing close to skin as underwear, with the fiber of the wet comfortableness excellence of the heat outside 1 as underwear.
Above-mentioned blended yarn is drawing-down wool/viscose glue/kapok 14.8tex blended yarn, and described model is the 14.8tex model.
The embodiment of a kind of natural thermogenetic effect composite material knit goods of the present invention and weaving method thereof, select the fleece fibre blended spinning yarn to interweave with bright and beautiful ammonia wrapped yarn and model, the compound rib that adopts plain stitch to be combined with rib stitch, rib stitch adopts the model braiding, biological drawing-down wool/viscose glue/kapok blended yarn braiding is adopted in plain stitch, braiding becomes three layers of complex tissue (seeing Fig. 3), fabric inner face 3 is close skin thermal surface, fabric outside 1 is moisture absorption heating insulation face, the high-elastic comfort liner 2 that forms for wrapped yarn in the middle of the fabric.Not only improve the elasticity of fabric, and given full play to the multi-functional effects such as moisture absorption heating of wool, kapok and multifilament blended interwoven fabric.Hydrophily and warmth retention property is good, and the soft fiber one side 3 of pressing close to skin as underwear, with the fiber of the wet comfortableness excellence of the heat outside 1 as underwear.
Above-mentioned blended yarn is drawing-down wool/viscose glue/kapok 14.8tex blended yarn, and above-mentioned model is the 14.8tex model.
Concrete knit goods weaving process is as follows:
Knitting needle is arranged and is seen Fig. 1, and triangle arrangement is seen Fig. 2.
Adopt the two-sided large circle machine braiding of JH-P4U2, the mode of entrying: 1F/5F penetrates drawing-down wool/viscose glue/kapok 14.8tex blended yarn; 2F/6F penetrates bright and beautiful ammonia wrapped yarn; 3F/4F/7F/8F penetrates Modal14.8tex.
In the weaving process parameter, hundred needlework are long: 1F/5F is 240 ± 2mm, and 2F/6F is 220 ± 2mm, and 3F/4F/7F/8F is 270 ± 2mm; Blank weight per square meter: 210 ± 2.5g/m
2, light base: 230 ± 10g/m
2Fabric is vertical close: 62 ± 1 lines/5cm; Lower machine fabric width: (90cm * 2) ± 2.5cm.
For making fabric panel present the style that the surface is rough, the inside is fine and smooth, when adjustment of tonicity, use three belts, the tension force of surperficial yarn is controlled at 2.5-3.5g; In be the looping stretch yarn, tension force is controlled at 3.5-4.5g; The inside yarn is 2 the tunnel and all weaves plain stitch that will control yarn feed quantity well, tension force is controlled at 4.5-5.5g.
Key problem in technology of the present invention:
(1) arranges yarn according to machine in the requirement of technique, prevent the wrong yarn of fabric.
(2) fabric style is that the surface is rough, and the inside is fine and smooth, so use three belts when adjustment of tonicity.The tension force of surface yarn wants large, is controlled at about 3g; In be stretch yarn, tension force is controlled at about 4g; The inside yarn is 2 the tunnel all to weave plain stitch, control its yarn feed quantity well, and tension force is controlled at about 5g.
The physical index of knit goods of the present invention reaches outside the current standard requirement through test, and the various functions index is also tested, and its its functional attributes test result sees the following form:
Show by upper table: the various functions index of knit goods of the present invention has all far surpassed existing Product Level and natural thermogenetic effect is obvious, therefore, this knit goods is a kind of high value added product that integrates function and environmental protection, to improving product specification, it is significant to increase economic benefit.
The above only is preferred embodiment of the present invention, is not to be the restriction of the present invention being made other form, and any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the equivalent embodiment of equivalent variations.But every technical solution of the present invention content that do not break away to any simple modification, equivalent variations and remodeling that above embodiment does, still belongs to the protection domain of technical solution of the present invention according to technical spirit of the present invention.
Claims (8)
1. natural thermogenetic effect composite material knit goods, it is characterized in that: select the fleece fibre blended spinning yarn to interweave with bright and beautiful ammonia wrapped yarn and model, the compound rib that adopts plain stitch to be combined with rib stitch, rib stitch adopts the model braiding, biological drawing-down wool/viscose glue/kapok blended yarn braiding is adopted in plain stitch, and braiding becomes three layers of complex tissue, and the fabric inner face is close skin thermal surface, the fabric outside is moisture absorption heating insulation face, the high-elastic comfort liner that forms for wrapped yarn in the middle of the fabric.
2. according to natural thermogenetic effect composite material knit goods claimed in claim 1, it is characterized in that described blended yarn is drawing-down wool/viscose glue/kapok 14.8tex blended yarn, described model is the 14.8tex model.
3. the weaving method of a natural thermogenetic effect composite material knit goods, it is characterized in that, select the fleece fibre blended spinning yarn to interweave with bright and beautiful ammonia wrapped yarn and model, the compound rib that adopts plain stitch to be combined with rib stitch, rib stitch adopts the model braiding, biological drawing-down wool/viscose glue/kapok blended yarn braiding is adopted in plain stitch, braiding becomes three layers of complex tissue, the fabric inner face is close skin thermal surface, the fabric outside is moisture absorption heating insulation face, the high-elastic comfort liner that forms for wrapped yarn in the middle of the fabric.
4. according to the weaving method of a kind of natural thermogenetic effect composite material knit goods claimed in claim 3, it is characterized in that described blended yarn is drawing-down wool/viscose glue/kapok 14.8tex blended yarn, described model is the 14.8tex model.
5. according to claim 3 or 4 described a kind of natural thermogenetic effect composite material knit goods and weaving method thereof, it is characterized in that, adopt the two-sided large circle machine braiding of JH – P4U2, the mode of entrying: 1F/5F penetrates drawing-down wool/viscose glue/kapok 14.8tex blended yarn; 2F/6F penetrates bright and beautiful ammonia wrapped yarn; 3F/4F/7F/8F penetrates model 14.8tex.
6. according to the weaving method of a kind of natural thermogenetic effect composite material knit goods claimed in claim 5, it is characterized in that in the weaving process parameter, hundred needlework are long: 1F/5F is 240 ± 2mm, and 2F/6F is 220 ± 2mm, and 3F/4F/7F/8F is 270 ± 2mm; Blank weight per square meter: 210 ± 2.5 g/ ㎡, light base: 230 ± 10 g/ ㎡; Fabric is vertical close: 62 ± 1 lines/5cm; Lower machine fabric width: (90cm * 2) ± 2.5cm.
7. according to the weaving method of claim 3 or 4 described a kind of natural thermogenetic effect composite material knit goodss, it is characterized in that, for making fabric panel present the style that the surface is rough, the inside is fine and smooth, when adjustment of tonicity, use three belts, the tension force of surperficial yarn is controlled at 2.5-3.5g; In be the looping stretch yarn, tension force is controlled at 3.5-4.5g; The inside yarn is 2 the tunnel and all weaves plain stitch that will control yarn feed quantity well, tension force is controlled at 4.5-5.5g.
8. according to the weaving method of a kind of natural thermogenetic effect composite material knit goods claimed in claim 6, it is characterized in that, for making fabric panel present the style that the surface is rough, the inside is fine and smooth, when adjustment of tonicity, use three belts, the tension force of surperficial yarn is controlled at 2.5-3.5g; In be the looping stretch yarn, tension force is controlled at 3.5-4.5g; The inside yarn is 2 the tunnel and all weaves plain stitch that will control yarn feed quantity well, tension force is controlled at 4.5-5.5g.