CN102994877A - 金属陶瓷摩擦材料 - Google Patents
金属陶瓷摩擦材料 Download PDFInfo
- Publication number
- CN102994877A CN102994877A CN 201210395830 CN201210395830A CN102994877A CN 102994877 A CN102994877 A CN 102994877A CN 201210395830 CN201210395830 CN 201210395830 CN 201210395830 A CN201210395830 A CN 201210395830A CN 102994877 A CN102994877 A CN 102994877A
- Authority
- CN
- China
- Prior art keywords
- parts
- friction material
- ceramic friction
- wear
- metal ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种金属陶瓷摩擦材料,由如下重量份的原料组成:铁40-60份、铜2-10份、铝2-8份、镍1-5份、蓝晶石2-6份、氮化硼1-5份、抗磨剂5-15份、鳞片石墨1-5份。该金属陶瓷摩擦材料具有高强度、高模量、耐高温特点,呈现出摩擦系数稳定,磨损率低的优点,还具有较好的抗冲击强度,对偶磨损较小,大大提高了使用寿命。
Description
技术领域
本发明涉及摩擦材料领域,特别是涉及一种金属陶瓷摩擦材料。
背景技术
摩擦材料是一种应用在动力机械上,依靠摩擦作用来执行制动和传动功能的部件材料。它主要包括制动器衬片(刹车片)和离合器面片(离合器片)。刹车片用于制动,离合器片用于传动。任何机械设备与运动的各种车辆都必须要有制动或传动装置。摩擦材料是这种制动或传动装置上的关键性部件,它最主要的功能是通过摩擦来吸收或传递动力,如离合器片传递动力,制动片吸收动能。它们使机械设备与各种机动车辆能够安全可靠地工作。所以说摩擦材料是一种应用广泛又甚关键地材料。
然而现有的摩擦材料普遍存在强度较差、产品磨损量大、噪音严重、抗冲击强度较差。
发明内容
本发明主要解决的技术问题是提供一种强度高、耐磨性能好,能够大幅度改善刹车片的力学、物理及摩擦磨损性能,使用寿命长的金属陶瓷摩擦材料。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种金属陶瓷摩擦材料,由如下重量份的原料组成:铁40-60份、铜2-10份、铝2-8份、镍1-5份、蓝晶石2-6份、氮化硼1-5份、抗磨剂5-15份、鳞片石墨1-5份。
在本发明一个较佳实施例中,进一步包括短切钢纤维5-15份。
在本发明一个较佳实施例中,所述抗磨剂为极压抗磨剂,包括钼1-5份、碳3-10份、磷1-3份。
本发明的有益效果是:本发明金属陶瓷摩擦材料具有高强度、高模量、耐高温特点,呈现出摩擦系数稳定,磨损率低的优点,还具有较好的抗冲击强度,对偶磨损较小,大大提高了使用寿命。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括:
一种金属陶瓷摩擦材料,由如下重量份的原料组成:铁40-60份、铜2-10份、铝2-8份、镍1-5份、蓝晶石2-6份、氮化硼1-5份、抗磨剂5-15份、鳞片石墨1-5份。
本发明进一步包括短切钢纤维5-15份。短切钢纤维可以进一步提高该金属陶瓷摩擦材料的机械性能,比无钢纤维的摩擦材料具有更好的耐磨性、更合理和稳定的摩擦系数,对对偶磨损也很小。
蓝晶石是一种新型耐火材料,属于高铝矿物,抗化学腐蚀性能强、热震机械强度大,受热膨胀不可逆等。
氮化硼耐腐蚀、耐热性、电绝缘性好,提高了该摩擦材料的综合性能。
所述抗磨剂为极压抗磨剂,包括钼1-5份、碳3-10份、磷1-3份。当金属表面承受很高的负荷时,大量的金属表面直接接触,产生大量的热,而抗磨剂形成的膜也被破坏,不再起保护金属表面的作用,极压抗磨剂能与金属表面起化学反应生成化学反应膜,起润滑作用,防止金属表面擦伤,甚至熔焊。极压抗磨剂防止金属表面在高负荷条件下发生烧结、卡咬、刮伤,可防止或减少金属表面在中等负荷条件下的磨损。实际应用中,通常将不同种类的极压抗磨剂按一定比例混合使用性能更好。
鳞片石墨是天然晶质石墨,其形似鱼磷状,属六方晶系,呈层状结构,具有良好的耐高温、导电、导热、润滑、可塑及耐酸碱等性能。
实施例1:
一种金属陶瓷摩擦材料,由如下重量份的原料组成:铁40份、铜2份、铝2份、镍1份、蓝晶石2份、氮化硼1份、钼1份、碳3份、磷1份、鳞片石墨1份、短切钢纤维5份。
实施例2:
一种金属陶瓷摩擦材料,由如下重量份的原料组成:铁60份、铜10份、铝8份、镍5份、蓝晶石6份、氮化硼5份、钼3份、碳10份、磷2份、鳞片石墨5份、短切钢纤维15份。
实施例3:
一种金属陶瓷摩擦材料,由如下重量份的原料组成:铁50份、铜5份、铝6份、镍3份、蓝晶石3份、氮化硼2份、钼3份、碳5份、磷3份、鳞片石墨3份、短切钢纤维10份。
与现有技术相比,本发明金属陶瓷摩擦材料具有高强度、高模量、耐高温特点,呈现出摩擦系数稳定,磨损率低的优点,还具有较好的抗冲击强度,对偶磨损较小,大大提高了使用寿命。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (3)
1.一种金属陶瓷摩擦材料,其特征在于,由如下重量份的原料组成:铁40-60份、铜2-10份、铝2-8份、镍1-5份、蓝晶石2-6份、氮化硼1-5份、抗磨剂5-15份、鳞片石墨1-5份。
2.根据权利要求1所述的金属陶瓷摩擦材料,其特征在于:进一步包括短切钢纤维5-15份。
3.根据权利要求1所述的金属陶瓷摩擦材料,其特征在于:所述抗磨剂为极压抗磨剂,包括钼1-5份、碳3-10份、磷1-3份。