CN102978910A - Acrylic fiber oiling agent - Google Patents
Acrylic fiber oiling agent Download PDFInfo
- Publication number
- CN102978910A CN102978910A CN2012105054102A CN201210505410A CN102978910A CN 102978910 A CN102978910 A CN 102978910A CN 2012105054102 A CN2012105054102 A CN 2012105054102A CN 201210505410 A CN201210505410 A CN 201210505410A CN 102978910 A CN102978910 A CN 102978910A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic fiber
- oiling agent
- surface active
- diethanol amine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an acrylic fiber oiling agent. The acrylic fiber oiling agent comprises the following components in parts by weight: 13-20 parts of fatty acid polyalcohol non-ionic surfactant, 3-8 parts of cationic surface active agent, 2-5 parts of triethanolamine, 1-3 parts of coconut acyl diethanol amine, 2-4 parts of fatty alcohol polyoxyethylene ether, 3-7 parts of castor oil polyoxyethylene ester and the balance being water. The acrylic fiber oiling agent is reasonable in formula, has a good using effect, and can be well applied to the market.
Description
Technical field
The present invention relates to field of textiles, particularly relate to a kind of polyacrylic fibre oil.
Background technology
The same with most of synthetic fiber, acrylic fibers are a kind of hydrophobic fibers, in spinning process and spinning, wool spinning with weave etc. in the rear process, friction between the fiber and will produce static with the friction of machinery, the cohesiveness of the appropriateness that the shortage natural fabric has between fiber in addition, thereby easily cause around roller, loose, flyings etc. the processing of fiber being carried out smoothly.So in the spinning technique of acrylic fibers, the important step that is absolutely necessary that oils of fiber.But the shortcomings such as it is bad that there is the effect that oils in polyacrylic fibre oil commonly used at present, expensive.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, preferably polyacrylic fibre oil of a kind of result of use is provided.
A kind of polyacrylic fibre oil is comprised of each component of following weight portion:
13 ~ 20 parts of fatty polyol type non-ionic surface active agents;
3 ~ 8 parts of cationic surfactants;
2 ~ 5 parts of triethanolamines;
1 ~ 3 part of coconut acyl diethanol amine;
2 ~ 4 parts of fatty alcohol-polyoxyethylene ether;
3 ~ 7 parts of castor oil polyoxyethylene esters;
Water surplus.
In the preferred embodiment of the invention, a kind of polyacrylic fibre oil is comprised of each component of following weight portion:
13 parts of fatty polyol type non-ionic surface active agents;
8 parts of cationic surfactants;
2 parts of triethanolamines;
3 parts of coconut acyl diethanol amine;
2 parts of fatty alcohol-polyoxyethylene ether;
7 parts of castor oil polyoxyethylene esters;
Water surplus.
In the preferred embodiment of the invention, a kind of polyacrylic fibre oil is comprised of each component of following weight portion:
20 parts of fatty polyol type non-ionic surface active agents;
3 parts of cationic surfactants;
5 parts of triethanolamines;
1 part of coconut acyl diethanol amine;
2 parts of fatty alcohol-polyoxyethylene ether;
7 parts of castor oil polyoxyethylene esters;
Water surplus.
Above-mentioned polyacrylic fibre oil, prescription is reasonable, and result of use is better, can be applied to preferably market.
The specific embodiment
For technological means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below in conjunction with the specific embodiment, further set forth the present invention.
Embodiment 1
A kind of polyacrylic fibre oil is comprised of each component of following weight portion:
15 parts of fatty polyol type non-ionic surface active agents;
7 parts of cationic surfactants;
4 parts of triethanolamines;
2 parts of coconut acyl diethanol amine;
2 parts of fatty alcohol-polyoxyethylene ether;
7 parts of castor oil polyoxyethylene esters;
Water surplus.
The polyacrylic fibre oil of this embodiment, excellent performance oils evenly, and film strength is high.This polyacrylic fibre oil can be given the good antistatic behaviour of acrylic fibers, flexibility, and suitable flatness, coherent are soft, smooth with the acrylic fibers of its production, and gloss is bright, and moderate, the good spinnability of frictional coefficient of fiber can be passed through each procedure of textile mills smoothly.Polyacrylic fibre oil can improve the product quality of acrylic fibers greatly.
Embodiment 2
A kind of polyacrylic fibre oil is comprised of each component of following weight portion:
13 parts of fatty polyol type non-ionic surface active agents;
8 parts of cationic surfactants;
2 parts of triethanolamines;
3 parts of coconut acyl diethanol amine;
2 parts of fatty alcohol-polyoxyethylene ether;
7 parts of castor oil polyoxyethylene esters;
Water surplus.
Embodiment 3
A kind of polyacrylic fibre oil is comprised of each component of following weight portion:
20 parts of fatty polyol type non-ionic surface active agents;
3 parts of cationic surfactants;
5 parts of triethanolamines;
1 part of coconut acyl diethanol amine;
2 parts of fatty alcohol-polyoxyethylene ether;
7 parts of castor oil polyoxyethylene esters;
Water surplus.
Above-mentioned polyacrylic fibre oil, prescription is reasonable, and result of use is better, can be applied to preferably market.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes specification of the present invention and accompanying drawing content to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (3)
1. a polyacrylic fibre oil is characterized in that, is comprised of each component of following weight portion:
13 ~ 20 parts of fatty polyol type non-ionic surface active agents;
3 ~ 8 parts of cationic surfactants;
2 ~ 5 parts of triethanolamines;
1 ~ 3 part of coconut acyl diethanol amine;
2 ~ 4 parts of fatty alcohol-polyoxyethylene ether;
3 ~ 7 parts of castor oil polyoxyethylene esters;
Water surplus.
2. polyacrylic fibre oil according to claim 1 is characterized in that, is comprised of each component of following weight portion:
13 parts of fatty polyol type non-ionic surface active agents;
8 parts of cationic surfactants;
2 parts of triethanolamines;
3 parts of coconut acyl diethanol amine;
2 parts of fatty alcohol-polyoxyethylene ether;
7 parts of castor oil polyoxyethylene esters;
Water surplus.
3. polyacrylic fibre oil according to claim 1 is characterized in that, is comprised of each component of following weight portion:
20 parts of fatty polyol type non-ionic surface active agents;
3 parts of cationic surfactants;
5 parts of triethanolamines;
1 part of coconut acyl diethanol amine;
2 parts of fatty alcohol-polyoxyethylene ether;
7 parts of castor oil polyoxyethylene esters;
Water surplus.