CN101858036B - Solvent method fiber treatment oil solution - Google Patents
Solvent method fiber treatment oil solution Download PDFInfo
- Publication number
- CN101858036B CN101858036B CN2010101930921A CN201010193092A CN101858036B CN 101858036 B CN101858036 B CN 101858036B CN 2010101930921 A CN2010101930921 A CN 2010101930921A CN 201010193092 A CN201010193092 A CN 201010193092A CN 101858036 B CN101858036 B CN 101858036B
- Authority
- CN
- China
- Prior art keywords
- solution
- fiber
- leomin
- solvent method
- oil solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a solvent method fiber treatment oil solution, which comprises the following ingredients in parts by weight: 30-80 parts of Leomin WG solution, 15-50 parts of Leomin OR solution and 5-20 parts of Leomin AN solution. The oil solution of the invention can satisfy fiber oiling on raw materials of wood pulp, bamboo pulp and cotton pulp produced by the solvent method. The oil solution has only three components; the preparation is more convenient so as to reduce labor intensity of oil-making workers; and the oil solution is economic and practical. The oil solution of the invention has excellent effect on improving fiber smoothness and softness and improves good cohesive property and antistatic property of the fiber.
Description
Technical field
The present invention relates to a kind of fiber treatment oil solution, relate in particular to a kind of solvent method fiber treatment oil solution.
Background technology
Finish is a kind of lubricant that uses in fiber production and the process in the textile industry, and it mainly rises and regulates the fibre frictoin characteristic, prevents or eliminate accumulation of static electricity, gives characteristics such as fiber smooth, soft, makes fiber smoothly through spinning, operations such as manufacturing.The effect of finish is to guarantee under certain condition and improves fibre manufacturing technique and carry out smoothly, and improves the performance of fiber, to improve the value of fibre.The staple fibre that traditional viscose process is produced, finish is owing to lack special component, and the ratio between component and the component is unreasonable, and what have is only applicable to wool type fiber, can not be applicable to cotton type and medium length type; What have is only applicable to xylon, and can not be applicable to cotton fiber and bamboo fibre; Traditional viscose process is joined the finish component of finish needs more than 4 kinds, have in addition surpass kind more than 10.Because the finish component is unreasonable, it is level and smooth to satisfy fiber, softness, obvolvent, multiple performance demands such as antistatic.
Summary of the invention
Technical problem to be solved by this invention provides a kind of solvent method fiber treatment oil solution; Can satisfy solvent method and produce the oiling of staple fibre that wood pulp, bamboo pulp, cotton pulp are raw material, have good raising fiber smooth, soft effect, improve good coherent and the antistatic behaviour of fiber.
For solving the problems of the technologies described above, the present invention realizes through following technical scheme:
A kind of solvent method fiber treatment oil solution is become by the following raw materials in parts by weight array: 30～80 parts of LeominWG solution, 15～50 parts of Leomin OR solution, 5～20 parts of Leomin AN solution.
Described Leomin WG solution is a kind of nonionic surface active agent of nitrogenous fatty acid polyethylene glycol ester class, and manufacturer is Clariant International Ltd, and the active ingredient mass concentration is 30%.Acting as of this raw material: can make this invention have good smooth, soft property, it mainly is through reducing friction, increase film strength, protection fiber surface, be in complete isolation between the fiber thereby make, improving smooth, soft property thereby play.
Described Leomin OR solution is a kind of nonionic surface active agent of fatty acid polyethylene glycol ester class, and manufacturer is Clariant International Ltd, and the active ingredient mass concentration is 90%.Have good increase fiber and the coherent between the fiber, it mainly is through infiltration, absorption and the mutual adhesive attraction of self to fiber, and the fiber coherent is improved.
Described Leomin AN solution is a kind of organic phosphate, and manufacturer is ClariantInternational Ltd, and the active ingredient mass concentration is 85%.Have good antistatic performance, as highly effective antistatic agent, it promotes discharge process through the fiber surface electric charge is flowed rapidly.
Leomin WG solution, Leomin OR solution and Leomin AN solution are taken by weighing in proportion, mix, can make solvent method fiber treatment oil solution of the present invention.
When fiber oils operation, the above-mentioned solvent method fiber treatment oil solution of the present invention that makes is added in the proper amount of deionized water, mix, make the emulsion of active ingredient mass concentration 10～30%.Adopt conventional spray process that above-mentioned emulsion is directly sprayed on the fiber again.The oil active ingredient mass concentration of circulating slot finish of fiber is controlled between 0.5～3.5%, and the spray circular flow that oils is controlled at 0.5～5m
3/ h, 50～60 ℃ of temperature.
This patent finish can satisfy solvent method and produce the oiling of staple fibre that wood pulp, bamboo pulp, cotton pulp are raw material, and applicability is very strong.
This patent finish is only formed needs three kinds, all needed more than 4 kinds in the past, even wanting more than ten kinds of having.Adopt the present invention, more convenient during preparation, alleviated the labour intensity of oil man, and economical and practical.
The specific embodiment
Embodiment 1
Present embodiment carries out oiling treatment to the wood pulp fluff dimension that solvent method production is produced.
Take by weighing 6 kilograms of Leomin WG solution successively, 10 kilograms of Leomin OR solution, 1 kilogram of Leomin AN solution.
Above-mentioned Leomin WG solution, Leomin OR solution and Leomin AN solution stirring are mixed, can make solvent method fiber treatment oil solution of the present invention.
The above-mentioned solvent method fiber treatment oil solution of the present invention that makes is added in the proper amount of deionized water, mixes, modulate the emulsion of active ingredient mass concentration 30%.
Adopt conventional spray process that above-mentioned emulsion is directly sprayed on the wood pulp fluff dimension of above-mentioned solvent method production production again.The oil effective mass concentration of circulating slot finish of fiber is controlled at 1.0%, and the spray circular flow that oils is controlled at 1.5m
3/ h,, 55 ℃ of temperature.
Detect finished fiber oil-containing 0.20% according to GB/T 6504-2008.
Adopt industry method in common, measure the coefficient of kinetic friction μ of back wood pulp fluff dimension that oil metal
d(F/M) be 0.245cm.min
-1
Embodiment 2
Present embodiment carries out oiling treatment to the bamboo pulp staple fibre of solvent method production.
Take by weighing 16 kilograms of Leomin WG solution successively, 3 kilograms of Leomin OR solution, 4 kilograms of Leomin AN solution.
The above-mentioned solvent method fiber treatment oil solution of the present invention that makes is added in the proper amount of deionized water, mixes, modulate the emulsion of active ingredient mass concentration 25%.
Adopt conventional spray process that above-mentioned emulsion is directly sprayed on the bamboo pulp staple fibre of above-mentioned solvent method production again.The oil effective mass concentration of circulating slot finish of fiber is controlled at 1.5%, and the spray circular flow that oils is controlled at 2.5m
3/ h, 60 ℃ of temperature.
Detect finished fiber oil-containing 0.25% according to GB/T 6504-2008.
Adopt industry method in common, measure the coefficient of kinetic friction μ of back bamboo pulp staple fibre that oil metal
d(F/M) be 0.222cm.min
-1
Embodiment 3
Present embodiment carries out oiling treatment to the cotton pulp staple fibre of solvent method production.
Take by weighing 11 kilograms of Leomin WG solution successively, 6.5 kilograms of Leomin OR solution, 2.5 kilograms of Leomin AN solution.
The above-mentioned solvent method fiber treatment oil solution of the present invention that makes is added in the proper amount of deionized water, mixes, modulate the emulsion of active ingredient mass concentration 15%.
Adopt conventional spray process that above-mentioned emulsion is directly sprayed on the cotton pulp staple fibre of above-mentioned solvent method production again.The oil effective mass concentration of circulating slot finish of fiber is controlled at 2.0%, and the spray circular flow that oils is controlled at 4.0m
3/ h,, 50 ℃ of temperature.
Detect finished fiber oil-containing 0.25% according to GB/T 6504-2008.
Adopt industry method in common, measure the coefficient of kinetic friction μ of back cotton pulp staple fibre that oil metal
d(F/M) be 0.228cm.min
-1
Solvent method fiber treatment oil solution of the present invention compares with general oil solution, to the coefficient of kinetic friction μ of metal
d(F/M) less, can improve fiber smoothness, form oil film at fiber surface, reduce the frictional force between the fiber; Have good antistatic performance, weaving after add man-hour, tow disperses, and to produce lousiness broken end phenomenon few; Improve the holding of fiber, can avoid when spinning bar to do stretching inhomogeneous, yarn strength is low.For the spinnability of fiber and road processing afterwards provide great convenience.
Claims (1)
1. a solvent method fiber treatment oil solution is characterized in that, is become by the following raw materials in parts by weight array: 30～80 parts of Leomin WG solution, 15～50 parts of Leomin OR solution, 5～20 parts of Leomin AN solution.