CN101250812B - Xanthochromia-resistance dacron afterprocessing oil solution and manufacturing method thereof - Google Patents

Xanthochromia-resistance dacron afterprocessing oil solution and manufacturing method thereof Download PDF

Info

Publication number
CN101250812B
CN101250812B CN 200810061144 CN200810061144A CN101250812B CN 101250812 B CN101250812 B CN 101250812B CN 200810061144 CN200810061144 CN 200810061144 CN 200810061144 A CN200810061144 A CN 200810061144A CN 101250812 B CN101250812 B CN 101250812B
Authority
CN
China
Prior art keywords
agent
oil
xanthochromia
afterprocessing
component
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 200810061144
Other languages
Chinese (zh)
Other versions
CN101250812A (en
Inventor
朱建成
孙燕琳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongkun Group Co Ltd
Original Assignee
Tongkun Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongkun Group Co Ltd filed Critical Tongkun Group Co Ltd
Priority to CN 200810061144 priority Critical patent/CN101250812B/en
Publication of CN101250812A publication Critical patent/CN101250812A/en
Application granted granted Critical
Publication of CN101250812B publication Critical patent/CN101250812B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses terylene afterprocessing oil agent for preventing xanthochromia, which is mainly formed by smoothing agent, emulsifying agent, cleaning agent and addition agent, and is characterized in that weight percentage of each component is smoothing agent 85%-90%, emulsifying agent 5%-10%, cleaning agent 2%-4% and addition agent 1%-1.5%. According to the weight percentage of each component, the method for preparation is that firstly packing emulsifying agent and cleaning agent with precise measure into an autoclave to heat from 50 DEG C to 80 DEG C, secondly packing smoothing agent into the autoclave to mix for 40-60 min, thirdly charging addition agent to mix homogeneously, and then cooling, filtering and packaging. The terylene after-processing oil agent for preventing xanthochromia has the advantages that interfacial force is low, permeability and diffusibility are good, the applying oil process is quick and homogeneous, the volume for applying oil is easy to be controlled, after-processing is smooth and has no imperfect effect on weave process and causticity component, and the invention is easy for washing and not influence on coloration and topical finish, and is good in cohesion property and forming of silk can, high in oil film strength, and strong in ability of preventing xanthochromia, thereby being favorable to store silks.

Description

Xanthochromia-resistance dacron afterprocessing oil solution and manufacture method thereof
Technical field
The present invention relates to a kind of process technology of synthetic fiber, particularly a kind of Xanthochromia-resistance dacron afterprocessing oil solution and manufacture method thereof.
Background technology
At present, production and the manufacturing of processing finish behind the terylene mainly are to adopt 5 #White oil, 32 #Machinery oil and certain emulsifying agent, antistatic additive and additive compound form, and at high temperature season, terylene thread is subjected under solar radiation or the hot environment easily to occur xanthochromia, and the quality of silk is had certain impact.
Summary of the invention
The objective of the invention is provides a kind of stable performance for the deficiency that solves above-mentioned technology, satisfies processing request behind the terylene thread, the Xanthochromia-resistance dacron afterprocessing oil solution of Effective Raise terylene thread period of storage and external quality and manufacture method thereof.
In order to achieve the above object, a kind of Xanthochromia-resistance dacron afterprocessing oil solution provided by the invention, mainly formed by smooth agent, emulsifying agent, detergent, additive, the percentage by weight that it is characterized in that each component is: smooth agent 85% to 90%, emulsifying agent 5% to 10%, detergent 2% to 4%, additive 1% to 1.5%.
Described smooth agent is the technical white oil of three hydrogenation, the mixture of one or more in the unit alcohol aliphatic alcohol ester.The effect of smooth agent can keep between fiber and the fiber, the suitable coefficient of friction between fiber and other contact components, the cohesive force of increase fiber, the unwinding when being conducive to the fiber winding shaping and weaving.
Described emulsifying agent is polyoxyethylene nonylphenol ether, oleic acid polyoxyethylene, C 12-14One or more mixtures of alcohol polyoxyethylene ether, sorbitan fatty acid ester.The effect of emulsifying agent is that with the various components in the finish, particularly emulsified object smooth agent reaches balance by physical and chemical process, makes finish become in use even, transparent, stable oily liquid, and is not stratified, labile acid.
Described detergent is one or more the mixture in coconut oil alkanolamide, the polyoxyethylene nonylphenol ether.The effect of detergent is to make finish after guaranteeing the associated uses of terylene thread in rear processing and the process of weaving cotton cloth, and is convenient to the dyeing factory washing, is beneficial to carrying out smoothly of dyeing, does not form the phenomenons such as oil mark, uneven dyeing.
Described additive be methyl-silicone oil and prevent splash agent, one or more the mixture in the organic acid.The adding of additive can guarantee the goodish penetrability of finish, fiber is oiled smoothly and meets the requirements of oil mass, prevents that simultaneously finish is splashed on the ground, affects the board health, can also guarantee the stability of using and storing of finish.
A kind of Xanthochromia-resistance dacron afterprocessing oil solution provided by the invention can be smooth agent 88% especially: wherein 15 of three hydrogenation #White oil 80%, Ethylhexyl stearate 8%; Emulsifying agent 8%: wherein polyoxyethylene nonylphenol ether 6%, C 12-14Alcohol polyoxyethylene ether 2%; Detergent 2%: wherein the coconut oil alkanolamide 2%; Additive 2%: methyl-silicone oil 0.5% prevents splash agent 1.5%.
A kind of Xanthochromia-resistance dacron afterprocessing oil solution provided by the invention can be smooth agent 90%: select 10 of three hydrogenation especially #White oil; Emulsifying agent 6%: select sorbitan fatty acid ester 4%, polyoxyethylene nonylphenol ether 2%; Detergent 2%: select Nonyl pheno-10 ether; Additive 2%: select methyl-silicone oil 1%, prevent splash agent 1%.
The manufacture method of Xanthochromia-resistance dacron afterprocessing oil solution of the present invention is: by the percentage by weight of each component, first with emulsifying agent, the detergent suction reactor of accurate measurement, being heated to 50 ℃ to 80 ℃ stirs, again with in the smooth agent suction reactor, stir after 40 minutes to 60 minutes, add additive, rear cooling stirs, filter packing.
The resulting a kind of Xanthochromia-resistance dacron afterprocessing oil solution of the present invention compared with prior art has following distinguishing feature and good effect:
1, surface tension is low, and the diffusion performance is good, can evenly oil rapidly, upper oil mass easy to control; 2, rear processing is smooth and easy, and weaving process has no adverse effects, and can wash easily, does not affect dyeing and rear arrangement; 3, coherent is good, and film strength is high, and the silk cylinder is shaped; 4, non-corrosiveness composition, all without corrosion, anti-yellowing change ability is strong, and is favourable to the storage of silk to people and equipment.
Xanthochromia-resistance dacron afterprocessing oil solution of the present invention is applicable to the production line of POY, DTY two step method.Meet DTY processing oil tanker oiling method, can satisfy that POY adds that DTY when playing reels smoothly and the smooth unwinding processing request of DTY when weaving.Between the megathermal period, guarantee that the storage of DTY silk is subjected to solar radiation and not flavescence simultaneously.Use through the Duo Jia chemical fibre factory, reaction is good.
The specific embodiment
The invention will be further described by reference to the accompanying drawings below by embodiment.
Embodiment:
A kind of Xanthochromia-resistance dacron afterprocessing oil solution that the present embodiment provides, mainly be comprised of smooth agent, emulsifying agent, detergent, additive, the percentage by weight of each component is: smooth agent 85% to 90%, emulsifying agent 5% to 10%, detergent 2% to 4%, additive 1% to 1.5%.
A kind of Xanthochromia-resistance dacron afterprocessing oil solution and manufacture method thereof that the present embodiment is described, by weight percentage first, determine the ratio of each component:
Embodiment 1 prescription forms:
Smooth agent 88%: wherein 15 #White oil (three hydrogenation) 80%, Ethylhexyl stearate 8%;
Emulsifying agent 8%: wherein polyoxyethylene nonylphenol ether 6%, C 12-14Alcohol polyoxyethylene ether 2%;
Detergent 2%: wherein the coconut oil alkanolamide 2%;
Additive 2%: methyl-silicone oil 0.5% prevents splash agent 1.5%.
Embodiment 2 prescriptions form:
Smooth agent 90%: select 10 #White oil (three hydrogenation);
Emulsifying agent 6%: select sorbitan fatty acid ester 4%, polyoxyethylene nonylphenol ether 2%;
Detergent 2%: select Nonyl pheno (10) ether;
Additive 2%: select methyl-silicone oil 1%, prevent splash agent 1%.
After the described ratio batching of above-mentioned two embodiment, the manufacture method of its Xanthochromia-resistance dacron afterprocessing oil solution is:
With emulsifying agent, detergent suction reactor, open and stir, be warmed up to about 60 ℃.Stir, again with smooth agent suction reactor, maintain the temperature at about 60 ℃, stirred 45 minutes, add at last additive, stirred 15 minutes, stir and finish, be cooled to about 30 ℃, blowing filters, and it is namely good to pack.
According to percentage of the present invention when the Xanthochromia-resistance dacron afterprocessing oil solution produced of manufacture method can reach following quality index:
1, outward appearance (25 ℃): colourless to faint yellow transparent oily liquid
2, pH value (1% aqueous solution, 25 ℃): 6.0 to 8.0
3, active constituent content (%, 〉=): 98.5
4, kinematic viscosity (40 ± 0.1 ℃, m 2/ s): (8~15) * 10 -6

Claims (2)

1. an Xanthochromia-resistance dacron afterprocessing oil solution mainly is comprised of smooth agent, emulsifying agent, detergent, additive, it is characterized in that the percentage by weight of each component is: smooth agent 88%: wherein 15 of three hydrogenation #White oil 80%, Ethylhexyl stearate 8%; Emulsifying agent 8%: wherein polyoxyethylene nonylphenol ether 6%, C 12-14Alcohol polyoxyethylene ether 2%; Detergent 2%: wherein the coconut oil alkanolamide 2%; Additive 2%: methyl-silicone oil 0.5% prevents splash agent 1.5%.
2. the manufacture method of an Xanthochromia-resistance dacron afterprocessing oil solution, after it is characterized in that percentage by weight by each component takes by weighing, first with emulsifying agent, the detergent suction reactor of accurate measurement, being heated to 50 ℃ to 80 ℃ stirs, again with in the smooth agent suction reactor, stir after 40 minutes to 60 minutes, add additive, the rear cooling that stirs is filtered, packing, wherein, the percentage by weight of each component is: smooth agent 85% to 90%, emulsifying agent 5% to 10%, detergent 2% to 4%, additive 1% to 1.5%.
CN 200810061144 2008-03-12 2008-03-12 Xanthochromia-resistance dacron afterprocessing oil solution and manufacturing method thereof Expired - Fee Related CN101250812B (en)