CN105839393A - Multifunctional multielement textile finishing agent - Google Patents
Multifunctional multielement textile finishing agent Download PDFInfo
- Publication number
- CN105839393A CN105839393A CN201510568057.6A CN201510568057A CN105839393A CN 105839393 A CN105839393 A CN 105839393A CN 201510568057 A CN201510568057 A CN 201510568057A CN 105839393 A CN105839393 A CN 105839393A
- Authority
- CN
- China
- Prior art keywords
- weight percentage
- finishing agent
- textile finishing
- multifunctional
- fatty acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a polyester and pure cotton fabric functional textile finishing agent. The finishing agent is a multifunctional multielement textile finishing agent by compounding of the following components: 8-10% (weight percentage) of dimethyl siloxane, 20-30% (weight percentage) of nanoscale zinc oxide powder, 7-10% of diamino-modified silicone oil (weight percentage), 2-4% (weight percentage) of fatty acid monoglyceride, 1-3% (weight percentage) of white oil, 1-3% (weight percentage) of stearic acid, and 50-61% (weight percentage) of deionized water. The technical key points of the multifunctional multielement textile finishing agent lie in that: first, nanotechnology zinc oxide powder is introduced into a textile finishing process to produce excellent function, and second, active matters various design required functional active matters are employed for compounding, so that the active matters can coordinate to give play to respective functions so as to achieve the respective functions required by the design.
Description
Technical field
The field that the present invention relates to is the technical field during fabric finishing.The most formulated
Multifunctional multicomponent fabric finishing agent.
Background technology
The fabric finishing agent class that Present Domestic dyeing system is applied, is single finishing auxiliaries with performance, even if
The finishing auxiliaries of bacteria resistance function occurs, has been also adopted by that chemosynthesis is antibacterial, press down mould raw material, even if this raw material serves mycete
Inhibitory action but human body is simultaneously also created damaging effect, do not meet health care requirement.Another person, the most generally makes
Finishing auxiliaries to playing soft effect after textile finishing, but lack smooth body-sensing, its function is more single.Put before this
We conducted the R&D work of multifunctional multicomponent fabric finishing agent, the preferable achievement of existing acquirement.
Summary of the invention
It is an object of the invention to the situation of the dyeing and finishing auxiliaries used for current dyeing, it is provided that one makes fabric pass through
Printing and dyeing i.e. acquire a certain degree of fluffy softness, smooth after arranging, obtain again when wearing fungi-proofing presses down mould function, simultaneously to people
Body skin is without the dyeing and finishing auxiliaries of the multifunctional multicomponent effect of any toxic action.
For reaching above-mentioned purpose, the present invention adopts the following technical scheme that
Introduce nano raw material technology, with nanoscale zinc powder, dimethyl siloxane, methylsiloxane, fatty acid monoglyceride, white
Oil stearic acid, deionized water etc. are raw material, become multifunctional multicomponent fabric finishing agent through Recompounded multielement.
Recipe ratio used: (calculated in weight percent)
Oxide powder and zinc: (particle diameter is 20-30nm) 3-5%
Dimethyl siloxane: 8-10%
Amido silicon oil: 7-10%
Fatty acid monoglyceride 2-4%
Fatty acid diacylglycerol: 2-4%
White oil 1-3%
Stearic acid 1-3%
Deionized water 50-61%
The technology of the present invention product, fabric is provided simultaneously with softness, mycostatic nature smooth, antibacterial after this Product organization.The most prominent
Go out is that this inventive technique product introduces nanotechnology raw material, can not only antibacterial press down mould, protects skin health, overcomes tradition
Antibacterial press down the harm to skin health of the mould auxiliary agent, thus build the mankind and biotic environment.
Example 1:
Oxide powder and zinc (20-30nm) 4%
Dimethicone: 9%
Amido silicon oil: 8%
Fatty acid monoglyceride: 3%
Fatty acid diacylglycerol: 3%
White oil: 3%
Stearic acid: 2%
Deionized water: 68%
Example 2:
Oxide powder and zinc (20-30nm) 4%
Dimethicone: 10%
Amido silicon oil: 3%
Fatty acid monoglyceride: 3%
Fatty acid diacylglycerol: 3%
White oil: 2%
Stearic acid: 1%
Deionized water: 68%
Product preparation process of the present invention (step is carried out in the following order)
Prepare pluralism complex:
(1) first stearic acid, white oil and part deionized water it is mixed heating 80 degree by proportional quantity, within 10 minutes, is sufficiently stirred for equal
Even.
(2) add appropriate deionized water after quantitative fatty acid Dan Ganzi and fatty acid diacylglycerol being puddled and heat 80 degree,
Stir.
(3) quantitative dimethicone and amido silicon oil are mixed, stir stand-by.
(4) quantitative oxide powder and zinc is mixed with appropriate deionized water fully stir evenly stand-by.
(5) residue deionized water is all added in the double sweet sub-ester solution of the most solvent fatty acid monoglyceride and fatty acid stir
Again the most solvent white oil and stearic acid mixed solution are added in above-mentioned mixed solution after mixing uniformly, then high-speed stirred is after 10 minutes
Become conventional speeds stirring, be slowly added to aforementioned silicone oil mixed liquor while stirring, after stirring 10 minutes, add the most solvent oxidation
Zinc solution, stirs 10 minutes.Then the above-mentioned milky product made stands ight 200 eye mesh screen filter, remove
Filtrate multifunctional multicomponent fabric finishing agent after micro residue thing.
Using method:
In mechanization equipment for dyeing and finishing, add enough tap waters on request, be subsequently adding the fabric needing dyeing and finishing.Intensification limit, limit adds
Enter by the total amount of fabric 3% than adding, multifunctional multicomponent fabric finishing agent, dyeing and finishing 20 minutes at a temperature of 60-70 degree.
Claims (4)
- Product the most of the present invention is a kind of multifunctional multicomponent fabric finishing agent.
- 2. and introduce nanoscale raw material technology.
- 3. with double amido silicon oils, stearic acid fatty acid monoglyceride, fatty acid diacylglycerol, particle diameter 30nm level oxide powder and zinc, white oil, nothing Ionized waters etc. are raw material, form through Recompounded multielement.
- 4. use proportioning raw materials (calculated in weight percent) content is:Nanoscale zinc powder (particle diameter 20-30nm) 3-5%Dimethyl siloxane 8-10%Double amido silicon oil 7-10%Fatty acid monoglyceride 2-4%White oil 1-3%Stearic acid 1-3%Deionized water 50-61%.