CN102978601A - 电机定子硒钢片表面除锈皮膜化成剂及制备方法 - Google Patents
电机定子硒钢片表面除锈皮膜化成剂及制备方法 Download PDFInfo
- Publication number
- CN102978601A CN102978601A CN 201210518097 CN201210518097A CN102978601A CN 102978601 A CN102978601 A CN 102978601A CN 201210518097 CN201210518097 CN 201210518097 CN 201210518097 A CN201210518097 A CN 201210518097A CN 102978601 A CN102978601 A CN 102978601A
- Authority
- CN
- China
- Prior art keywords
- acid
- mass concentration
- motor stator
- preparation
- selenium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种电机定子硒钢片表面除锈皮膜化成剂,如下质量百分比的组分构成:质量浓度为50%的氟锆酸0.1~0.5%,质量浓度为65%的硝酸0.1~0.3%,质量浓度为55%的植酸0.1~0.5%,柠檬酸0.6~1.6%,质量浓度为50%的氢氟酸0.05~0.1%,常温钢铁表面处理剂10~18%,钼酸钠0.05~0.15%,碳酸氢铵1~3%,三乙醇胺2~8%,聚乙二醇1~4%及水余量。先将计算称量的水加入到反应釜中,然后依次将常温钢铁表面处理剂、氟锆酸、硝酸、植酸、氢氟酸、柠檬酸、钼酸钠、碳酸氢铵、三乙醇胺、聚乙二醇依次徐徐加入到反应釜中,每加一种原料连续搅拌至少10min以上,最后搅拌至溶液呈浅绿色透明液体。
Description
技术领域
本发明涉及一种金属转化处理剂及制备方法,尤其是一种操作简单、利于环保、可提高工件表面与喷涂涂层之间的附着力、提高喷涂涂层耐腐蚀性的电机定子硒钢片表面除锈皮膜化成剂及制备方法。
背景技术
金属构件表面因油垢、浮锈、重锈、氧化皮及焊接高温氧化物等,因此在喷涂涂装等工艺处理前,都要求将上述油锈皮等清除掉,且大多通过磷酸盐转化处理,使其表面生成一层具有一定粗糙度、多孔性、吸附性的磷酸盐转化膜,以增强工件表面耐腐性、提高工件表面与涂层间或其他有机表面处理层间的附着力。目前,电机定子硒钢片表面除锈皮膜化处理后的表面经常出现锈蚀,尽管表面再喷涂一层有机硅绝缘漆,但是由于锈蚀的存在,严重影响喷涂层的结合力而造成漆层剥落,严重影响电机定子的使用性能。
发明内容
本发明是为了解决现有技术所存在的上述技术问题,提供一种操作简单、利于环保、可提高工件表面与喷涂涂层之间的附着力、提高喷涂涂层耐腐蚀性的电机定子硒钢片表面除锈皮膜化成剂及制备方法。
本发明的技术解决方案是:一种电机定子硒钢片表面除锈皮膜化成剂,其特征在于由如下质量百分比的组分构成:质量浓度为50%的氟锆酸0.1~0.5%,质量浓度为65%的硝酸0.1~0.3%,质量浓度为55%的植酸0.1~0.5%,柠檬酸0.6~1.6%,质量浓度为50%的氢氟酸0.05~0.1%,常温钢铁表面处理剂10~18%,钼酸钠0.05~0.15%,碳酸氢铵1~3%,三乙醇胺2~8%,聚乙二醇1~4%及水余量。
一种上述电机定子硒钢片表面除锈皮膜化成剂的制备方法,其特征在于按如下步骤进行:先将计算称量的水加入到反应釜中,开动搅拌器,控制转速为80转/分,然后依次将计算称量的常温钢铁表面处理剂、氟锆酸、硝酸、植酸、氢氟酸、柠檬酸、钼酸钠、碳酸氢铵、三乙醇胺、聚乙二醇依次徐徐加入到反应釜中,每加一种原料连续搅拌至少10min以上,最后搅拌至溶液呈浅绿色透明液体。
本发明可在电机定子硒钢片喷涂涂装前,通过擦拭的简单操作方法,在常温下除去电机定子硒钢片表面的灰尘、油污等,并在电机定子硒钢片表面形成转化膜,具有除油、除锈、钝化等功能。操作简单、利于环保、可提高电机定子硒钢片表面与喷涂涂层之间的附着力、提高喷涂涂层的耐腐蚀性能。
具体实施方式
实施例1:
原料及质量百分比如下:质量浓度为50%的氟锆酸0.1%,质量浓度为65%的硝酸0.3%,质量浓度为55%的植酸0.1%,柠檬酸1.6%,质量浓度为50%的氢氟酸0.05%,常温钢铁表面处理剂18%,钼酸钠0.05%,碳酸氢铵3%,三乙醇胺2%,聚乙二醇(M=400)4%及水余量。
制备方法按如下步骤进行:先将计算称量的水加入到反应釜中,开动搅拌器,控制转速为80转/分,然后依次将计算称量的常温钢铁表面处理剂、氟锆酸、硝酸、植酸、氢氟酸、柠檬酸、钼酸钠、碳酸氢铵、三乙醇胺、聚乙二醇依次徐徐加入到反应釜中,每加一种原料连续搅拌至少10min以上,最后搅拌至溶液呈浅绿色透明液体。
原料中的常温钢铁表面处理为大连三达奥克化学股份有限公司公开销售的产品,产品型号是SP-12。
实施例2:
原料及生产方法均同实施例1,其原料质量百分比如下:质量浓度为50%的氟锆酸0.5%,质量浓度为65%的硝酸0.1%,质量浓度为55%的植酸0.5%,柠檬酸0.6%,质量浓度为50%的氢氟酸0.1%,常温钢铁表面处理剂10%,钼酸钠0.15%,碳酸氢铵1%,三乙醇胺8%,聚乙二醇(M=400)1%及水余量。
实施例3:
原料及生产方法均同实施例1,其原料质量百分比如下:质量浓度为50%的氟锆酸0.3%,质量浓度为65%的硝酸0.2%,质量浓度为55%的植酸0.3%,柠檬酸1.0%,质量浓度为50%的氢氟酸0.08%,常温钢铁表面处理剂14%,钼酸钠0.10%,碳酸氢铵2%,三乙醇胺5%,聚乙二醇(M=400)3%及水余量。
使用时,按体积比为1:1将本发明实施例1、实施例2或实施例3加水配制工作液,人工用抹布蘸工作液擦拭硒钢片工件表面,除掉锈迹以后生成一薄层浅灰色锌系化成皮膜层,再用热风吹干表面即可。
Claims (2)
1. 一种电机定子硒钢片表面除锈皮膜化成剂,其特征在于由如下质量百分比的组分构成:质量浓度为50%的氟锆酸0.1~0.5%,质量浓度为65%的硝酸0.1~0.3%,质量浓度为55%的植酸0.1~0.5%,柠檬酸0.6~1.6%,质量浓度为50%的氢氟酸0.05~0.1%,常温钢铁表面处理剂10~18%,钼酸钠0.05~0.15%,碳酸氢铵1~3%,三乙醇胺2~8%,聚乙二醇1~4%及水余量。
2.一种如权利要求1所述电机定子硒钢片表面除锈皮膜化成剂的制备方法,其特征在于按如下步骤进行:先将计算称量的水加入到反应釜中,开动搅拌器,控制转速为80转/分,然后依次将计算称量的常温钢铁表面处理剂、氟锆酸、硝酸、植酸、氢氟酸、柠檬酸、钼酸钠、碳酸氢铵、三乙醇胺、聚乙二醇依次徐徐加入到反应釜中,每加一种原料连续搅拌至少10min以上,最后搅拌至溶液呈浅绿色透明液体。