CN102977422A - 一种耐油耐腐蚀橡胶 - Google Patents
一种耐油耐腐蚀橡胶 Download PDFInfo
- Publication number
- CN102977422A CN102977422A CN 201210566018 CN201210566018A CN102977422A CN 102977422 A CN102977422 A CN 102977422A CN 201210566018 CN201210566018 CN 201210566018 CN 201210566018 A CN201210566018 A CN 201210566018A CN 102977422 A CN102977422 A CN 102977422A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- oilproof
- oil
- resistant rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐油耐腐蚀橡胶,由以下重量份的成分组成:天然橡胶30~60;沥青2~5;硬脂酸镁10~15;酞菁化合物5~10;氧化锌10~20;铜粉5~10;46号机械油1~5;导电炭黑20~40;松香1~5。本发明与现有技术相比,用此橡胶配方生产出的耐油橡胶具有良好的耐油性、耐热性、气密性。
Description
技术领域
本发明涉及一种耐油耐腐蚀橡胶。
背景技术
正常汽车使用的油缸密封件的使用的橡胶对橡胶的耐油、耐热、气密性都有一定的要求,现有的橡胶往往达不到要求,其耐油性能只能达到10%。
发明内容
针对现有技术存在的不足,本发明所要解决的技术问题是,提供一种耐油性能达到8-10% 的耐油耐腐蚀橡胶。
为解决上述技术问题,本发明所采取的技术方案是:一种耐油耐腐蚀橡胶,由以下重量份的成分组成:
天然橡胶 30~60;
沥青 2~5;
硬脂酸镁 10~15;
酞菁化合物 5~10;
氧化锌 10~20;
铜粉 5~10;
46号机械油 1~5;
导电炭黑 20~40;
松香 1~5。
本发明耐油耐腐蚀橡胶的优点是:本发明与现有技术相比,用此橡胶配方生产出的耐油橡胶具有良好的耐油性、耐热性、气密性。
具体实施方式
下面结合具体实施例对本发明做进一步详细说明;
一种耐油耐腐蚀橡胶,由以下重量份的成分组成:
天然橡胶 30~60;
沥青 2~5;
硬脂酸镁 10~15;
酞菁化合物 5~10;
氧化锌 10~20;
铜粉 5~10;
46号机械油 1~5;
导电炭黑 20~40;
松香 1~5。
当然,上述说明并非是对本发明的限制,本发明也并不限于上述举例,本技术领域的普通技术人员,在本发明的实质范围内,作出的变化、改型、添加或替换,都应属于本发明的保护范围。
Claims (1)
1.一种耐油耐腐蚀橡胶,其特征在于,由以下重量份的成分组成:
天然橡胶 30~60;
沥青 2~5;
硬脂酸镁 10~15;
酞菁化合物 5~10;
氧化锌 10~20;
铜粉 5~10;
46号机械油 1~5;
导电炭黑 20~40;
松香 1~5。