CN102974953B - Tin-copper-cobalt (Sn-Cu-Co) lead-free solder containing ferrum (Fe) and neodymium (Nd) - Google Patents
Tin-copper-cobalt (Sn-Cu-Co) lead-free solder containing ferrum (Fe) and neodymium (Nd) Download PDFInfo
- Publication number
- CN102974953B CN102974953B CN201210544352.4A CN201210544352A CN102974953B CN 102974953 B CN102974953 B CN 102974953B CN 201210544352 A CN201210544352 A CN 201210544352A CN 102974953 B CN102974953 B CN 102974953B
- Authority
- CN
- China
- Prior art keywords
- lead
- percent
- solder
- free brazing
- brazed seam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides tin-copper-cobalt (Sn-Cu-Co) lead-free solder containing ferrum (Fe) and neodymium (Nd), and the solder belongs to a braze welding material in the fields of metal materials and metallurgy. Chemical components (in mass percentage) are as follows: 0.3 percent to 1.5 percent of Cu, 0.05 percent to 2.5 percent of Co, 0.002 percent to 0.1 percent of Fe, and 0.01 percent to 0.2 percent of Nd, and the rest is Sn. The solder has good moistening performance, can effectively suppress the growth of the thickness of chemicals among brazing seam interface metal, so that the reliability of a braze welding connector is greatly improved, and the solder can be used for wave soldering, reflow soldering and other soldering methods in the electronic industry.
Description
Technical field
The present invention relates to a kind of Sn-Cu-Co lead-free brazing containing Fe and Nd, belong to the brazing material of class of metal materials and field of metallurgy.Being mainly used in assembling and the encapsulation of electron trade components and parts, is that a kind of brazing property (as wettability) is good, the novel green of solder joint (brazed seam) good mechanical performance, environment-friendly type lead-free solder.
Background technology
Along with RoHS(The Restriction of the Use of certain Hazardous Substance in Electrical and Electronic Equipment) the coming into force of instruction, research and development lead-free brazing is the focus of electron trade technical staff research with the problem of alternative tin-lead solder always.Lead-free brazing representative at present has the alloy systems such as Sn-Ag-Cu, Sn-Zn, Sn-Cu, Sn-Cu-Ni, has his own strong points, but compares with tin-lead solder, still has a certain distance in solder cost, solder fusing point etc.Sn-Cu-Ni brazing filler metal is owing to having good combination property, moderate, has a good application prospect, and wave-soldering has started application.But in use find, along with the prolongation of time, between the brazed seam interface metal of Sn-Cu-Ni solder, the thickness of compound has the trend progressively increasing, thicken, and thus may reduce " reliability " of soldered fitting.Therefore, this problem that Sn-Cu-Ni solder exists, still needs Improvement.
The basis of the external Sn-Cu-Ni solder of recent year have developed " lead-free brazing containing cerium " (Chinese invention patent, CN1792539), " a kind of anti-molten copper tin copper lead free brazing material alloy " (Chinese invention patent, CN102554490A), " a kind of SAC cobalt lead-free brazing " (Chinese invention patent, CN102091882A) and " containing V, the Sn-Cu-Ni lead-free brazing of Nd and Ge " (Chinese invention patent, the Sn-Cu of multiple " multi-element alloy system " such as CN101885119A), Sn-Cu-Ni solder, the Sn-Cu of they and binary or ternary, Sn-Cu-Ni alloy phase makes moderate progress than in some performance, but the grown in thickness of compound between brazed seam interface metal, the research aspect thickened not yet relates to, therefore, for Sn-Cu, " reliability " problem of Sn-Cu-Ni solder brazing joint, still need further research, improve.This invention " the Sn-Cu-Co lead-free brazing containing Fe and Nd ", namely completes under this technical background.
Summary of the invention
The object of this invention is to provide and a kind of there is good wettability, effectively can suppress the growth of compound thickness between brazed seam interface metal, thus improve " reliability " of soldered fitting widely and be applicable to the Sn-Cu-Co series leadless solder of the welding methods such as electron trade wave-soldering and reflow welding.
To achieve the object of the present invention, the Sn-Cu-Co lead-free brazing containing Fe and Nd of the present invention, the chemical composition determined after optimizing by mass percent proportioning is: the Cu of 0.3 ~ 1.5%; the Co of 0.05 ~ 2.5%; the Fe of 0.002 ~ 0.1%, the Nd of 0.01 ~ 0.2%, surplus is Sn; Wherein the addition mass ratio of Co and Fe meets Co ︰ Fe=24 ~ 26 ︰ 1.
Conventional method is adopted to prepare solder; namely commercially available tin slab, neodymium metal, cathode copper, ferrocobalt is used; various raw metal proportioning on demand, adds commercially available " coverture " determined through optimal screening or adopts " inert gas " protection to carry out smelting, casting, can obtain bar during smelting.By extruding, drawing, namely obtain a material (also scaling powder can be added, make " flux-cored wire ").Pb element is as " impurity element " in the raw material such as tin slab, cathode copper, overall control, within the scope of the wt.% of Pb≤0.1, meets the regulation (specifying Pb≤0.1wt.% in standard) of National Standard of the People's Republic of China GB/T 20422-2006 " lead-free brazing " to meet.
Consider that neodymium metal fusing point is high and be very easily oxidized, also neodymium metal can be smelted into intermediate alloy in advance according to need of production, add with the form of Sn-Nd, to ensure the accuracy of neodymium metal composition in solder.
Solder even tissue of the present invention, is easy to be processed into various shape, as strip, bar-shaped, thread, soldered ball, to adapt to the needs of different working condition.
Accompanying drawing explanation
Fig. 1 does not add the Sn-Cu-Co brazed seam interface topography of Fe and Nd;
Fig. 2 adds the Sn-Cu-Co brazed seam interface topography of Fe and Nd;
The Sn-Nd intermetallic compound that Fig. 3 is formed when adding 0.25% Nd;
The relation curve (in figure, ordinate " IMC " is the english abbreviation of general " intermetallic compound " in the industry, lower same) of Fig. 4 Sn-0.3 Cu-2.5Co and Sn-0.3 Cu-2.5 Co-0.1 Fe-0.2Nd timeliness 1200 hours rear interface intermetallic compound gross thickness and aging time;
The relation curve of Fig. 5 Sn-1.1Cu-0.25 Co and Sn-1.1Cu-0.25 Co-0.01 Fe-0.12 Nd timeliness 1200 hours rear interface intermetallic compound gross thickness and aging time;
The relation curve of Fig. 6 Sn-1.0Cu-0.2 Co and Sn-1.0Cu-0.2 Co-0.008 Fe-0.05Nd timeliness 1200 hours rear interface intermetallic compound gross thickness and aging time;
The relation curve of Fig. 7 Sn-0.8 Cu-0.5Co and Sn-0.8 Cu-0.5Co-0.02 Fe-0.02Nd timeliness 1200 hours rear interface intermetallic compound gross thickness and aging time;
The relation curve of Fig. 8 Sn-1.5Cu-0.05Co and Sn-1.5Cu-0.05Co-0.002 Fe-0.01Nd timeliness 1200 hours rear interface intermetallic compound gross thickness and aging time.
Specific embodiments
Compared with studying, creativeness of the present invention was in the past:
1) found effectively to suppress the Fe element that between brazed seam interface metal, compound thickness increases.
In process of the test of the present invention, research finds, Fe joins in Sn-Cu-Co lead-free brazing, effectively can suppress the growth rate of compound thickness between Sn-Cu-Co lead-free brazing brazed seam interface metal.Further research finds, if add Fe and Nd element simultaneously, the inhibitory action of Fe to the growth rate of compound thickness " between the brazed seam interface metal " of Sn-Cu-Co lead-free brazing is more remarkable.
Research in the past is unanimously thought, adding of Fe element, will the wettability of " deterioration " Sn-Pb solder and lead-free brazing significantly.Therefore, be no matter GB/T 3131-2001 " tin-lead solder " or GB/T 20422-2006 " lead-free brazing ", all using Fe element as " impurity element ", require to control its content within 0.02%.
In the present invention, research finds, when Fe joins in Sn-Cu-Co lead-free brazing, although the wettability of solder can be worsened, and, can by adding rare earth element nd " counteracting " its negative effect simultaneously.Even if when the addition of Fe reaches 0.1% (having exceeded GB/T 3131-2001 " tin-lead solder ", GB/T 20422-2006 " lead-free brazing " standard gauge definite value 5 times), still there is good wettability containing the Sn-Cu-Co lead-free brazing of Fe and Nd.But adding the Fe of 0.002 ~ 0.1%, to the inhibitory action that compound thickness between brazed seam interface metal increases, is but very significant (see accompanying drawing 4 ~ Fig. 8).As can be seen from Fig. 4 ~ Fig. 8, with the addition of the Sn-Cu-Co lead-free brazing of Fe and Nd element, between brazed seam interface metal, the prolongation of compound gross thickness and aging time is (in test, generally acknowledge in the industry and carry out analog component service time with aging time) although be all the relation of " grow up, thickening ", but compound gross thickness is all less than the gross thickness of the Sn-Cu-Co lead-free brazing not adding Fe and Nd element between the Sn-Cu-Co lead-free brazing brazed seam interface metal that with the addition of Fe and Nd element.Illustrate and add Fe and Nd element, really have and suppress the effect that between brazed seam interface metal, compound thickness increases, thus the risk causing crack initiation because of growing up of intermetallic compound, grow up, finally make solder joint (brazed seam) ftracture can be reduced, improve the reliability of solder joint (brazed seam).
Because existing research is unanimously generally acknowledged, along with the prolongation of solder joint working time (as: components and parts service time), between brazed seam interface metal, compound thickness constantly can increase (thickening), intermetallic compound can constantly be grown up, thus Joint Strength can be made to decline gradually, finally cause solder joint to destroy or lost efficacy.Therefore, Chinese scholars is found by large quantity research, Ni or Co element is added in Sn-Cu lead-free brazing, have and suppress the effect that between brazed seam interface metal, compound thickness increases, thus the risk causing crack initiation because of growing up of intermetallic compound, grow up, finally make solder joint (brazed seam) ftracture can be reduced, improve the reliability of solder joint (brazed seam).
Present inventor studies discovery, and Fe and Co or Ni element belong to the VIIIth race's element in " periodic table of elements " together, chemically analyze in theory, and Fe should tool and the same or analogous effect of Co or Ni element.Therefore, found by lot of experiments, the addition (mass percent) of Fe, 0.002 ~ 0.1% time, really has and suppresses the effect that between brazed seam interface metal, compound thickness increases.
2) verification experimental verification the interpolation scope of preferred Co and Fe and proportionate relationship
Find that Fe joins to suppressing the affecting laws that between brazed seam interface metal, compound thickness increases in Sn-Cu-Co lead-free brazing by " Sequential designed experiment " method, and tentatively determined interpolation scope and the proportionate relationship of Co and Fe.Namely in the addition (mass percent) of Fe in the scope of 0.002 ~ 0.1%, when the addition mass ratio of Co and Fe meets Co ︰ Fe=25 ︰ 1, neoteric lead-free brazing has good solder joint (or brazed seam) " reliability ".Effectively can suppress the growth of compound thickness between brazed seam interface metal, thus the risk causing crack initiation because of growing up of intermetallic compound, grow up, finally make solder joint (brazed seam) ftracture can be reduced, improve the reliability of solder joint (brazed seam).
Size due to weld thickness is little, and (intermetallic compound thickness is at micron order, general between several micron to tens microns), measure error is large, therefore, existing research means can't assess exactly Co ︰ Fe actual ratio (such as, during Co ︰ Fe=24 ︰ 1 or Co ︰ Fe=26 ︰ 1, whether Fe will significantly die down to the inhibitory action that in Sn-Cu-Co lead-free brazing, between brazed seam interface metal, compound thickness increases), therefore, " optimization " proportion that the present invention provides proposes according to the experiment interpolation scope of " Sequential designed experiment " method.
3) the interpolation scope of rare earth element nd is optimized
Compared with the lead-free brazing of existing interpolation rare earth element, in the alloy system that the present invention relates to, " favourable " interpolation scope of rare earth element nd is very narrow, only in 0.01 ~ 0.2% scope.Other many lead-free brazing containing rare earth element unlike, can 0.001% be low to moderate, up to 1%.Primary Study shows, adding of iron, due effect is not had when making rare earth element nd be less than 0.01%, and after the addition of Nd is greater than 0.2%, the appearance of " rare-earth phase ", under the existence condition of Fe, can have a negative impact (see accompanying drawing 3 to neoteric solder wetting performance, after the addition of Nd reaches 0.25%, " rare-earth phase " that occur in Sn-0.3Cu-2.5Ni-0.1 Fe-0.25Nd lead-free brazing).
According to the quality proportioning of " the Sn-Cu-Co lead-free brazing containing Fe and Nd " of the present invention, describe the specific embodiment of the present invention as follows.
embodiment one
Containing a Sn-Cu-Co lead-free brazing of Fe and Nd, by mass percent proportioning, its composition is: the Cu of 0.3%, the Co of 2.5%, the Fe of 0.1%, the Nd of 0.2%, and surplus is Sn.
" the Sn-Cu-Co lead-free brazing containing Fe and Nd " solidus temperature that mentioned component proportioning obtains is at about 228 DEG C, and liquidus temperature is about 246 DEG C (all considering test error).Coordinate commercially available RMA brazing flux on copper plate, have excellent wettability, brazed seam tensile strength reaches 40MPa ± 10MPa.
Fig. 4 shows, and timeliness is after 1200 hours, and the Sn-Cu-Co lead-free brazing that with the addition of Fe and Nd is less by about 30% than compound gross thickness between the lead-free brazing brazed seam interface metal of not adding Fe and Nd, illustrates that the reliability of solder joint (brazed seam) is significantly improved.
embodiment two
Containing a Sn-Cu-Co lead-free brazing of Fe and Nd, by mass percent proportioning, its composition is: the Cu of 1.1%, the Co of 0.25%, the Fe of 0.01%, the Nd of 0.12%, and surplus is Sn.
" the Sn-Cu-Co lead-free brazing containing Fe and Nd " solidus temperature that mentioned component proportioning obtains is at about 228 DEG C, and liquidus temperature is about 240 DEG C (all considering test error).Coordinate commercially available RMA brazing flux on copper plate, have excellent wettability, brazed seam tensile strength reaches 40MPa ± 10MPa.
Fig. 5 shows, and timeliness is after 1200 hours, and the Sn-Cu-Co lead-free brazing that with the addition of Fe and Nd is less by about 30% than compound gross thickness between the lead-free brazing brazed seam interface metal of not adding Fe and Nd, illustrates that the reliability of solder joint (brazed seam) is significantly improved.
embodiment three
Containing a Sn-Cu-Co lead-free brazing of Fe and Nd, by mass percent proportioning, its composition is: the Cu of 1.0%, the Co of 0.2%, the Fe of 0.008%, the Nd of 0.05%, and surplus is Sn.
" the Sn-Cu-Co lead-free brazing containing Fe and Nd " solidus temperature that mentioned component proportioning obtains is at about 228 DEG C, and liquidus temperature is about 240 DEG C (all considering test error).Coordinate commercially available RMA brazing flux on copper plate, have excellent wettability, brazed seam tensile strength reaches 40MPa ± 10MPa.
Fig. 6 shows, and timeliness is after 1200 hours, and the Sn-Cu-Co lead-free brazing that with the addition of Fe and Nd is less by about 30% than compound gross thickness between the lead-free brazing brazed seam interface metal of not adding Fe and Nd, illustrates that the reliability of solder joint (brazed seam) is significantly improved.
embodiment four
Containing a Sn-Cu-Co lead-free brazing of Fe and Nd, by mass percent proportioning, its composition is: the Cu of 0.8%, the Co of 0.5%, the Fe of 0.02%, the Nd of 0.02%, and surplus is Sn.
" the Sn-Cu-Co lead-free brazing containing Fe and Nd " solidus temperature that mentioned component proportioning obtains is at about 226 DEG C, and liquidus temperature is about 245 DEG C (all considering test error).Coordinate commercially available RMA brazing flux on copper plate, have excellent wettability, brazed seam tensile strength reaches 40MPa ± 10MPa.
Fig. 7 shows, and timeliness is after 1200 hours, and the Sn-Cu-Co lead-free brazing that with the addition of Fe and Nd is less by about 30% than compound gross thickness between the lead-free brazing brazed seam interface metal of not adding Fe and Nd, illustrates that the reliability of solder joint (brazed seam) is significantly improved.
embodiment five
Containing a Sn-Cu-Co lead-free brazing of Fe and Nd, by mass percent proportioning, its composition is: the Cu of 1.5%, the Co of 0.05%, the Fe of 0.002%, the Nd of 0.01%, and surplus is Sn.
" the Sn-Cu-Co lead-free brazing containing Fe and Nd " solidus temperature that mentioned component proportioning obtains is at about 230 DEG C, and liquidus temperature is about 248 DEG C (all considering test error).Coordinate commercially available RMA brazing flux on copper plate, have excellent wettability, brazed seam tensile strength reaches 40MPa ± 10MPa.
Fig. 8 shows, and timeliness is after 1200 hours, and the Sn-Cu-Co lead-free brazing that with the addition of Fe and Nd is less by about 30% than compound gross thickness between the lead-free brazing brazed seam interface metal of not adding Fe and Nd, illustrates that the reliability of solder joint (brazed seam) is significantly improved.
Claims (2)
1., containing a Sn-Cu-Co lead-free brazing of Fe and Nd, it is characterized in that: composition by mass percent proportioning is: the Cu of 0.3 ~ 1.5%, the Co of 0.05 ~ 2.5%, the Fe of 0.002 ~ 0.1%, the Nd of 0.01 ~ 0.2%, surplus is Sn; Wherein the addition mass ratio of Co and Fe meets Co ︰ Fe=24 ~ 26 ︰ 1.
2. the Sn-Cu-Co lead-free brazing containing Fe and Nd according to claim 1, is characterized in that: the optimum addition mass ratio of Co and Fe meets Co ︰ Fe=25 ︰ 1.