CN102965590A - 一种改性硬质合金及其制备 - Google Patents

一种改性硬质合金及其制备 Download PDF

Info

Publication number
CN102965590A
CN102965590A CN201210471436XA CN201210471436A CN102965590A CN 102965590 A CN102965590 A CN 102965590A CN 201210471436X A CN201210471436X A CN 201210471436XA CN 201210471436 A CN201210471436 A CN 201210471436A CN 102965590 A CN102965590 A CN 102965590A
Authority
CN
China
Prior art keywords
graphene
preparation
parts
hard alloy
carbon dust
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201210471436XA
Other languages
English (en)
Other versions
CN102965590B (zh
Inventor
高熠辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hechi Technical Market Management Office
Original Assignee
WUXI CHANG'AN GENERAL METAL PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI CHANG'AN GENERAL METAL PRODUCT CO Ltd filed Critical WUXI CHANG'AN GENERAL METAL PRODUCT CO Ltd
Priority to CN201210471436.XA priority Critical patent/CN102965590B/zh
Publication of CN102965590A publication Critical patent/CN102965590A/zh
Application granted granted Critical
Publication of CN102965590B publication Critical patent/CN102965590B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种改性硬质合金，由以下重量份的组分制备完成：石墨烯：0.1-0.8份，碳粉：0.2-0.5份，Si：0.1-0.3份，Ti：0.1-0.8份，P：0-0.01份，Cr：1-2份，Ni：3-8份，Mo：0.5-2份，Fe：100-200份。本发明的改性硬质合金的硬度远远大于普通合金或金属的硬度，其制备方法非常简单，特别适于工业化生产。

Description

一种改性硬质合金及其制备
技术领域
本发明涉及一种合金材料，具体地，涉及一种改性硬质合金及其制备。
背景技术
硬质合金是由难熔金属的硬质化合物和粘结金属通过粉末冶金工艺制成的一种合金材料。硬质合金具有硬度高、耐磨、强度和韧性较好、耐热、耐腐蚀等一系列优良性能，特别是它的高硬度和耐磨性，即使在500℃的温度下也基本保持不变，在1000℃时仍有很高的硬度，广泛用作工业切削刀具、矿山钻头、耐磨件、精密零件等。传统硬质合金工业制
备方法主要以粉末冶金方法为主，将碳化物与金属粘结剂混合压制成型，经过烧结形成致
密合金。因此硬质合金的工业原料大量使用碳化物，其制备方法主要是为固相烧结反应制
备法，是一种耗时、耗能的制备方法。直接以金属粉末或者氧化物作为原料，在烧结过程
中一次完成碳化和烧结致密化过程，将大大缩短工艺流程，降低能耗，提高效率。目前的发明专利公开了一种硬质合金，但是以传统金属粉末与碳粉混合制备硬质合金由于原料颗粒过大，碳粉难以有效形成在金属粉末外面包裹结构，碳化反应不均匀导致组织缺陷偏析严重，极大制约着这种方法思路的实施。纳米技术的发展给硬质合金行业带来了新的发展思路，推动了高性能超细硬质合金的制备技术的发展。
发明内容
本发明要解决的技术问题是克服现有的缺陷，提供了一种改性硬质合金，该硬质合金的硬度远远大于普通合金或金属的硬度。
为了解决上述技术问题，本发明提供了如下的技术方案：
一种改性硬质合金，由以下重量份的组分制备完成：
石墨烯：0.1-0.8份，碳粉 ：0.2-0.5份，Si ：0.1-0.3份，Ti ：0.1-0.8份，P：0-0.01份， Cr ：1-2份，Ni ：3-8份，Mo ：0.5-2份，Fe：100-200份。
具体地，由以下重量份的组分制备完成：
石墨烯：0.3-0.6份，碳粉 ：0.3-0.5份，Si ：0.1-0.3份，Ti ：0.3-0.6份，P：0-0.005份， Cr ：1-2份，Ni ：5-7份，Mo ：0.8-1.5份，Fe：120-180份。
具体地，由以下重量份的组分制备完成：
石墨烯：0.5份，碳粉 ：0.4份，Si ：0.2份，Ti ：0.5份，P：0.002份， Cr ：2份，Ni ：6份，Mo ： 1份，Fe：100份。
改性硬质合金的制备方法，包括以下步骤：
将石墨烯均匀分散于有机溶剂中形成分散液，再与其他原料粉末混合形成硬质合金原料，将该混合料进行熔融，冷却为铸锭后，研磨为细粉，干燥、造粒，再次熔融，得到所需产品。
本发明具有以下有益效果：
采用高活性石墨烯与金属粉末作为制备硬质合金的原料，在烧结过程中一步实现碳化和烧结，具有高效快捷的特点，尤其是采用氧化石墨烯作为添加成分，利用其表面带有的大量含氧基团以及易分散、高活性的特点，将其良好分散在乙醇等介质中形成分散液再进行添加，能有效克服传统碳粉添加均一性差的不足；利用石墨烯具有巨大的表面积，且为超薄柔韧片状结构的特点，使之通过简单物理吸附包裹在金属原料粉末表面，进而在后续球磨过程中实现与金属粉末的良好复合和嵌入，在基体中的良好分散，从而实现在后续烧结过程中使组织均匀，降低烧结缺陷；石墨烯在后续烧结过程中迅速被还原，并与基体硬质合金发生反应，调节硬质合金中的碳含量，由于其具有比传统石墨粉高得多的活性，因此能够使硬质合金基体碳含量更加均匀，改善组织均一性；利用石墨烯所具有优异的综合力学性能以及兼具的超高力学强度和柔韧性等特点，以残余石墨烯发挥增强增韧作用，实现对硬质合金力学性能的提升。
具体实施方式
实施例1
一种改性硬质合金，由以下重量份的组分制备完成：
石墨烯：0.1份，碳粉 ：0.2份，Si ：0.1份，Ti ：0.1份， Cr ：1份，Ni ：3份，Mo ：0.5份，Fe：100份。
改性硬质合金的制备方法，包括以下步骤：
将石墨烯均匀分散于有机溶剂中形成分散液，再与其他原料粉末混合形成硬质合金原料，将该混合料进行熔融，冷却为铸锭后，研磨为细粉，干燥、造粒，再次熔融，得到所需产品。
实施例2
一种改性硬质合金，由以下重量份的组分制备完成：
石墨烯： 0.8份，碳粉 ： 0.5份，Si ： 0.3份，Ti ： 0.8份，P： 0.01份， Cr ： 2份，Ni ： 8份，Mo ： 2份，Fe： 200份。
改性硬质合金的制备方法，包括以下步骤：
将石墨烯均匀分散于有机溶剂中形成分散液，再与其他原料粉末混合形成硬质合金原料，将该混合料进行熔融，冷却为铸锭后，研磨为细粉，干燥、造粒，再次熔融，得到所需产品。
实施例3
一种改性硬质合金，其特征在于，由以下重量份的组分制备完成：
石墨烯：0.5份，碳粉 ：0.4份，Si ：0.2份，Ti ：0.5份，P：0.002份， Cr ：2份，Ni ：6份，Mo ： 1份，Fe：100份。
改性硬质合金的制备方法，包括以下步骤：
将石墨烯均匀分散于有机溶剂中形成分散液，再与其他原料粉末混合形成硬质合金原料，将该混合料进行熔融，冷却为铸锭后，研磨为细粉，干燥、造粒，再次熔融，得到所需产品。
采用高活性石墨烯与金属粉末作为制备硬质合金的原料，在烧结过程中一步实现碳化和烧结，具有高效快捷的特点，尤其是采用氧化石墨烯作为添加成分，利用其表面带有的大量含氧基团以及易分散、高活性的特点，将其良好分散在乙醇等介质中形成分散液再进行添加，能有效克服传统碳粉添加均一性差的不足；利用石墨烯具有巨大的表面积，且为超薄柔韧片状结构的特点，使之通过简单物理吸附包裹在金属原料粉末表面，进而在后续球磨过程中实现与金属粉末的良好复合和嵌入，在基体中的良好分散，从而实现在后续烧结过程中使组织均匀，降低烧结缺陷；石墨烯在后续烧结过程中迅速被还原，并与基体硬质合金发生反应，调节硬质合金中的碳含量，由于其具有比传统石墨粉高得多的活性，因此能够使硬质合金基体碳含量更加均匀，改善组织均一性；利用石墨烯所具有优异的综合力学性能以及兼具的超高力学强度和柔韧性等特点，以残余石墨烯发挥增强增韧作用，实现对硬质合金力学性能的提升。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (4)

1.一种改性硬质合金，其特征在于，由以下重量份的组分制备完成：
石墨烯：0.1-0.8份，碳粉 ：0.2-0.5份，Si ：0.1-0.3份，Ti ：0.1-0.8份，P：0-0.01份， Cr ：1-2份，Ni ：3-8份，Mo ：0.5-2份，Fe：100-200份。
2.根据权利要求1 所述的改性硬质合金，其特征在于，由以下重量份的组分制备完成：
石墨烯：0.3-0.6份，碳粉 ：0.3-0.5份，Si ：0.1-0.3份，Ti ：0.3-0.6份，P：0-0.005份， Cr ：1-2份，Ni ：5-7份，Mo ：0.8-1.5份，Fe：120-180份。
3.根据权利要求1 所述的改性硬质合金，其特征在于，由以下重量份的组分制备完成：
石墨烯：0.5份，碳粉 ：0.4份，Si ：0.2份，Ti ：0.5份，P：0.002份， Cr ：2份，Ni ：6份，Mo ： 1份，Fe：100份。
4.权利要求1-3之一所述的改性硬质合金的制备方法，包括以下步骤：
将石墨烯均匀分散于有机溶剂中形成分散液，再与其他原料粉末混合形成硬质合金原料，将该混合料进行熔融，冷却为铸锭后，研磨为细粉，干燥、造粒，再次熔融，得到所需产品。
CN201210471436.XA 2012-11-20 2012-11-20 一种改性硬质合金及其制备 Expired - Fee Related CN102965590B (zh)