CN102943335A - 一种导电抗紫外线面料及其加工工艺 - Google Patents

一种导电抗紫外线面料及其加工工艺 Download PDF

Info

Publication number
CN102943335A
CN102943335A CN201210382912.0A CN201210382912A CN102943335A CN 102943335 A CN102943335 A CN 102943335A CN 201210382912 A CN201210382912 A CN 201210382912A CN 102943335 A CN102943335 A CN 102943335A
Authority
CN
China
Prior art keywords
warp thread
uvioresistant
conduction
weft yarn
behind
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210382912.0A
Other languages
English (en)
Inventor
洪桂焕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaoxing County Kwong Fung Printing & Dyeing Co Ltd
Original Assignee
Shaoxing County Kwong Fung Printing & Dyeing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shaoxing County Kwong Fung Printing & Dyeing Co Ltd filed Critical Shaoxing County Kwong Fung Printing & Dyeing Co Ltd
Priority to CN201210382912.0A priority Critical patent/CN102943335A/zh
Publication of CN102943335A publication Critical patent/CN102943335A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种导电抗紫外线面料，它是以金属丝包覆纱(21S棉+68D金属丝)为经纱(1)、抗紫外纱与棉组成的低捻度复合丝为纬纱(2)，经纱(1)和纬纱(2)互相垂直织造而成。本发明具有优异的导电、抗紫外线等性能。

Description

一种导电抗紫外线面料及其加工工艺
技术领域
本发明公开了一种导电抗紫外线面料及其加工工艺，属于合成纤维与复合纱的复合物技术领域。
技术背景
金属(不锈钢)纤维是经过多次拉伸，集束拉伸，熔融纺丝，切削或须晶等过程，把不锈钢做成直径4-16μm的纤维材料(长丝或短纤)，相当柔软，然后混入常规纺织材料，做成防静电织物。这类织物最早是由日本精线公司研制开发成功的。混有不锈钢导电纤维的导电纱，具有很好的耐热、耐化学腐蚀性，导电性能良好，不受酸、碱和其他化学药品的影响，染色可采用常规方法，由于织物中不锈钢纤维含量较低，完全不影响织物的外观和手感。
在织物中只要添加很少量的导电纤维，就能达到静电驱散的要求。适用于耐高温屏蔽防电磁波辐射之针织布、机织布、高温输送带、消除静电带、防电磁波辐射布料的织造原材料。
抗紫外纱线是在PET纤维的纺丝过程中，将耐高温的抗紫外纺丝母粒均匀的加入到PET纺丝熔体中，在纤维冷却成形后，纳米级的抗紫外剂均匀地分布在纤维表面和内部。与传统的后整理法或涂层法相比，具有抗紫外作用持久、永不消褪的特点。经多次的洗涤及烘干对纤维及织物的抗紫外功能基本无影响。
发明内容
本发明的目的是提供一种导电抗紫外线面料。
为实现上述目的，本发明采用了以下技术方案：
一种导电抗紫外线面料，以金属丝包覆纱(21S棉+68D金属丝)为经纱、抗紫外纱与棉组成的低捻度复合丝为纬纱，经纱和纬纱互相垂直织造而成。
所述经纱的密度为415根/10cm，纬纱的密度为325根/10cm。
本发明导电抗紫外线面料及其加工工艺，包括如下步骤：
(1)经纱经自动络筒机络筒后，再经倍捻、定型、整经、穿经工序；
(2)经纱经自动络筒机络筒后，再经倍捻、定型、并合、倒筒工序；
(3)将经上述加工工序的经纱与纬纱一起织造成坯布，而在整个织造过程中，应控制好长丝纤维的张力；
(4)将织造好的坯布经翻布、精练、脱水开幅、预定型、碱减量、染色、脱水开幅、柔软定型这几道工序后整理工序后完成整个加工工艺。
所述步骤(4)中的染色工序，采取分段升温的染色过程，升温到90℃保温30min，然后以1.5℃/min的速率升温到112-122℃，保温45min后降温，开注入清水、皂洗剂，升温至95℃清洗15min。
本发明的有益效果是，以导电纤维及抗紫外纱为原料，增强了面料的导电、抗紫外线等性能，并赋予面料柔软、滑爽的手感，使此面料具有更佳的透气透湿性和穿着舒适性。
具体实施方案
下面通过具体实施例对本发明作进一步说明：
表1：染色工序中保温45min的温度值
 实施例1   实施例2   实施例3   实施例4  实施例5
  温度(℃)  112   115   117   119  122
本发明导电抗紫外线面料，它是以金属丝包覆纱(21S棉+68D金属丝)为经纱、抗紫外纱与棉组成的低捻度复合丝为纬纱，织造而成。
经纱经自动络筒机络筒后，经倍捻、定型、整经、穿经工序；
纬纱经自动络筒机络筒后，经倍捻、定型、并合、倒筒工序；
所述经纱的密度为415根/10cm，纬纱的密度为325根/10cm。
本发明导电抗紫外线面料及其加工工艺，包括如下步骤：
(1)经纱经自动络筒机络筒后，再经倍捻、定型、整经、穿经工序；
(2)经纱经自动络筒机络筒后，再经倍捻、定型、并合、倒筒工序；
(3)将经上述加工工序的经纱与纬纱一起织造成坯布，而在整个织造过程中，应控制好长丝纤维的张力；
(4)将织造好的坯布经翻布、精练、脱水开幅、预定型、碱减量、染色、脱水开幅、柔软定型这儿道工序后整理工序后完成整个加工工艺。
所述步骤(4)中的染色工序，采取分段升温的染色过程，升温到90℃保温30min，然后以1.5℃/min的速率升温到112-122℃，保温45min后降温，并注入清水、皂洗剂，升温至95℃清洗15min。

Claims (4)

1.一种导电抗紫外线面料，其特征在于，它是以金属丝包覆纱(21S棉+68D金属丝)为经纱(1)、抗紫外纱与棉组成的低捻度复合丝为纬纱(2)，经纱(1)与纬纱(2)互相垂直织造而成。
2.根据权利要求1所述的一种导电抗紫外线面料，其特征在于，所述经纱(1)的密度为415根/10cm，纬纱(2)的密度为325根/10cm。
3.一种加工权利要求1所述的导电抗紫外线面料的工艺，其特征在于包括如下步骤：
(1)经纱经自动络筒机络筒后，再经倍捻、定型、整经、穿经工序；
(2)经纱经自动络筒机络筒后，再经倍捻、定型、并合、倒筒工序；
(3)将经上述加工工序的经纱与纬纱一起织造成坯布，而在整个织造过程中，应控制好长丝纤维的张力；
(4)、将织造好的坯布经翻布、精练、脱水开幅、预定型、碱减量、染色、脱水开幅、柔软定型这几道工序后整理工序后完成整个加工工艺。
4.按照权利要求2所述导电抗紫外线面料的工艺，其特征在于：所述步骤(4)中的染色工序，采取分段升温的染色过程，升温到90℃保温30min，然后以1.5℃/min的速率升温到112-122℃，保温45min后降温，并注入清水、皂洗剂，升温至95℃清洗15min。
CN201210382912.0A 2012-09-27 2012-09-27 一种导电抗紫外线面料及其加工工艺 Pending CN102943335A (zh)