CN102934687A - 果蔬保鲜剂的制备方法 - Google Patents
果蔬保鲜剂的制备方法 Download PDFInfo
- Publication number
- CN102934687A CN102934687A CN 201210446850 CN201210446850A CN102934687A CN 102934687 A CN102934687 A CN 102934687A CN 201210446850 CN201210446850 CN 201210446850 CN 201210446850 A CN201210446850 A CN 201210446850A CN 102934687 A CN102934687 A CN 102934687A
- Authority
- CN
- China
- Prior art keywords
- magnesium aluminate
- drying
- fresh
- aluminate
- keeping agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种高效果蔬保鲜剂的制备方法：包括如下步骤：①制备铝酸镁载体颗粒将氯化镁晶体于60-80℃的铝酸钠水溶液，调节pH值为8-10，生成凝胶过滤，水洗经干燥后制得铝酸镁粉末；将铝酸镁粉末同粘合料一起研磨、成型、干燥后，再经600℃高温烧制成一定形状的颗粒，即铝酸镁载体颗粒；②制备保鲜剂成品将制得的铝酸镁载体颗粒添加到3%的高锰酸钾溶液中，煮沸30分钟，经固液分离、干燥后得到保鲜剂成品。本发明铝酸镁载体优于传统的沸石、活性炭载体。1.吸附能力强，且对高锰酸钾氧化乙烯有较好的催化作用。2．载体中添加强氧化剂，使保鲜剂具有吸附和氧化乙烯的双重作用，提高保鲜效率。3．用磷酸作黏合剂，成型效果好。
Description
技术领域
本发明涉及于家用果蔬保鲜或密封包装果蔬保鲜。
背景技术
现在的果蔬保鲜剂大多是适合于大型冷冻库的果蔬保鲜剂，家庭使用会造成浓度高，用量大，容易造成不必要的污染。开发适合于家庭用的果蔬保鲜剂也有必要。
发明内容
本发明提供一种适合于家庭使用、安全、高效的果蔬保鲜剂的制备方法。
一种高效果蔬保鲜剂的制备方法：包括如下步骤
①制备铝酸镁载体颗粒
将氯化镁晶体于60---80℃的铝酸钠水溶液，调节pH值为8-10，生成凝胶过滤，水洗经干燥后制得铝酸镁粉末；
将铝酸镁粉末同粘合料一起研磨、成型、干燥后，再经600℃高温烧制成一定形状的颗粒，即铝酸镁载体颗粒；
②制备保鲜剂成品
将制得的铝酸镁载体颗粒添加到3%的高锰酸钾溶液中，煮沸30分钟，经固液分离、干燥后得到保鲜剂成品。
粘合料为磷酸。
铝酸镁载体颗粒和2-4%的高锰酸钾溶液固、液混合比例为100g： 500ml。
本发明的有益效果是：
1．铝酸镁载体优于传统的沸石、活性炭载体。吸附能力强，且对高锰酸钾氧化乙烯有较好的催化作用。
2．载体中添加强氧化剂，使保鲜剂具有吸附和氧化乙烯的双重作用，提高保鲜效率。
3．用磷酸作黏合剂，成型效果好。
具体实施方式
实施例一
1、制备铝酸镁载体颗粒
将氯化镁晶体于60---80℃的铝酸钠水溶液，调节pH值为8，生成凝胶（MgO/Al2O3摩尔比为2-6，Na2O/Al2O3摩尔比为2-3）过滤，水洗经干燥后制得铝酸镁粉末。
将铝酸镁粉末同粘合料一起研磨、成型、干燥后，再经600℃高温烧制成一定形状的颗粒，即铝酸镁载体颗粒。其中，粘合料用磷酸。
②制备保鲜剂成品
将制得的铝酸镁载体颗粒添加到２%的高锰酸钾溶液中，煮沸30分钟，经固液分离、干燥后得到保鲜剂成品。
实施例二
1、制备铝酸镁载体颗粒
将氯化镁晶体于70℃的铝酸钠水溶液，调节pH值为9，生成凝胶（MgO/Al2O3摩尔比为2-6，Na2O/Al2O3摩尔比为2-3）过滤，水洗经干燥后制得铝酸镁粉末。
将铝酸镁粉末同粘合料一起研磨、成型、干燥后，再经600℃高温烧制成一定形状的颗粒，即铝酸镁载体颗粒。其中，粘合料用磷酸。
②制备保鲜剂成品
将制得的铝酸镁载体颗粒添加到３%的高锰酸钾溶液中，煮沸30分钟，经固液分离、干燥后得到保鲜剂成品。
实施例三
1、制备铝酸镁载体颗粒
将氯化镁晶体于80℃的铝酸钠水溶液，调节pH值为１０，生成凝胶（MgO/Al2O3摩尔比为2-6，Na2O/Al2O3摩尔比为2-3）过滤，水洗经干燥后制得铝酸镁粉末。
将铝酸镁粉末同粘合料一起研磨、成型、干燥后，再经600℃高温烧制成一定形状的颗粒，即铝酸镁载体颗粒。其中，粘合料用磷酸。
②制备保鲜剂成品
将制得的铝酸镁载体颗粒添加到４%的高锰酸钾溶液中，煮沸30分钟，经固液分离、干燥后得到保鲜剂成品。
本发明还可以有其它实施方式，凡采用同等替换或等效变换形成的技术方案，均落在本发明要求保护的范围之内。
Claims (3)
1. 一种高效保鲜剂的制备方法：包括如下步骤
①制备铝酸镁载体颗粒
将氯化镁晶体于60---80℃的铝酸钠水溶液，调节pH值为8-10，生成凝胶过滤，水洗经干燥后制得铝酸镁粉末；
将铝酸镁粉末同粘合料一起研磨、成型、干燥后，再经600℃高温烧制成一定形状的颗粒，即铝酸镁载体颗粒；
②制备保鲜剂成品
将制得的铝酸镁载体颗粒添加到2-4%的高锰酸钾溶液中，煮沸30分钟，经固液分离、干燥后得到保鲜剂成品。
2.如权利要求1或2所述的制备方法，其特征为：所述的粘合料为磷酸。
3.如权利要求1或2所述的制备方法，其特征为：所述的铝酸镁载体颗粒和2-4%的高锰酸钾溶液固、液混合比例为100g： 500ml。