CN102925083A - 一种水性热熔胶及其制备方法 - Google Patents
一种水性热熔胶及其制备方法 Download PDFInfo
- Publication number
- CN102925083A CN102925083A CN2011102362041A CN201110236204A CN102925083A CN 102925083 A CN102925083 A CN 102925083A CN 2011102362041 A CN2011102362041 A CN 2011102362041A CN 201110236204 A CN201110236204 A CN 201110236204A CN 102925083 A CN102925083 A CN 102925083A
- Authority
- CN
- China
- Prior art keywords
- parts
- hour
- melten gel
- emulsifying agent
- hot melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种水性热熔胶,由以下重量比的组分构成:去离子水50份,保护胶体0.1份,乳化剂2-2.5份,苯乙烯10-20份,丙烯酸分酯单体35-30份,化学纯过硫酸铵0.3份;化学纯碳酸氢钠0.15份;分子量调节剂0.2份,消泡剂0.1-0.5份;氨水0.4-0.6份、改性树脂1-3份、增稠剂0.1-0.5份。其具有常温下液态、无毒不燃、干燥快、粘接强度高、节省电力和热能、使用方便等优点。
Description
技术领域
本发明涉及一种胶粘剂,具体涉及一种水性热熔胶及其制备方法。
背景技术
胶粘剂大致分为水基型胶、溶剂型胶及热熔胶三大类。水基型胶无毒不燃,生产工艺较易控制,应用广泛,但干燥速度慢,粘接强度低是其缺陷;溶剂型胶的粘接强度高,干燥速度快,但因为使用苯、甲苯、二甲苯等有毒有害化学成分,易污染环境,严重危害人体健康,即使无三苯,改用其它溶剂,也存在易燃、易爆,安全隐患多等缺点;目前市售的热熔胶是固态的,包装运输容易,无毒无害,热熔后粘接强度高,性能好,但由于其是固态的,加温热熔温度要求较高(通常为160℃-180℃),电力消耗大,且由固态变为流动态,粘度高,导致涂布量较高,增加使用成本,在长时间的加温下,导致胶体树脂热劣化和炭化,严重影响粘接力和外观,且成膜后胶膜耐温性差。
发明内容
为克服上述各种胶的技术问题,本发明提供了一种以水为溶剂,以多元单体经共聚得到的水性热熔胶及其制备方法。
所述的水性热熔胶由以下重量比例的组分组成:去离子水50份,保护胶体0.1份,乳化剂2-2.5份,苯乙烯10-20份,丙烯酸分酯单体35-30份,化学纯过硫酸铵0.3份;化学纯碳酸氢钠0.15份;分子量调节剂0.2份,消泡剂(DF-1311)0.1-0.5份;氨水0.4-0.6份、改性树脂1-3份、增稠剂0.1-0.5份。
所述的乳化剂为阴、非离子复配,复配比例为1:2。
制备上述水性热熔胶的方法包括以下步骤:
1)、取1.5份去离子水溶解0.15份过硫酸铵,配成过硫酸铵溶液待用;取1份去离子水溶解碳酸氢钠,配成碳酸氢钠溶液待用。
2)、将18份去离子水加入预乳化罐中,加入乳化剂1-1.25份搅匀,在900转/分钟下投入计量丙烯酸酯单体及苯乙烯,半小时后预乳化液乳白均匀后备用。
3)、在聚合釜中投入29.5份去离子水,搅拌条件下加入保护胶体、乳化剂1-1.25份、过硫酸铵0.15份和碳酸氢钠0.075份、分子量调节剂0.2份搅匀,加入5%的预乳化液后继续搅拌并开始升温,65℃-67℃时罐内液料出现兰光,温度逐步升高至87℃-89℃,而后回落至85℃时,保温半小时。
4)、种子聚合结束后保持85℃,平行滴加预乳化液,预先配好的过硫酸铵溶液与碳酸氢钠溶液,3-4小时滴完,滴加完毕85℃保温半小时后,逐步升温至90℃,继续保温1-1.5小时后,降温。
5)、降温至60℃以下时,另取5份去离子水稀释0.4-0.6份氨水后调整PH值7-8,加入消泡剂,改性树脂,增稠剂,使粘度达到要求,即可得到水性热熔胶。
所述的步骤4)中碳酸氢钠溶液比过硫酸铵溶液提前15分钟滴完。
本发明具有以下有益效果:通过本工艺及配方获得的水性热熔胶具有常温下液态、水性胶的无毒不燃等优点,更加快了干燥速度,提高了粘接强度,应用范围广泛;使用温度只要95℃-98℃,大量节省电力和热能,粘度可调,可以喷,浸,淋,滚涂,使用方便,降低了使用成本。
具体实施方式
实施例一
1)、取1.5份去离子水溶解0.15份过硫酸铵,配成过硫酸铵溶液待用;取1份去离子水溶解0.075份碳酸氢钠,配成碳酸氢钠溶液待用。
2)、将18份去离子水加入预乳化罐中,加入1-1.25份乳化剂搅匀,在900转/分钟下投入计量丙烯酸酯单体及苯乙烯,半小时后预乳化液乳白均匀后备用。
3)、在聚合釜中投入29.5份去离子水,搅拌条件下加入保护胶体、1份的乳化剂、过硫酸铵0.15份和碳酸氢钠0.075份、分子量调节剂0.2份搅匀,加入5%的预乳化液后继续搅拌并开始升温,65℃时罐内液料出现兰光,温度逐步升高至87℃,而后回落至85℃,保温半小时。
4)、种子聚合结束后保持85℃,平行滴加预乳化液,预先配好的过硫酸铵溶液与碳酸氢钠溶液,3小时滴完,滴加完毕85℃保温半小时后逐步升温至90℃,继续保温1小时后,降温。
5)、降温至60℃以下时,另取5分去离水稀释0.4份氨水后调整PH值7,加入消泡剂,改性树脂,增稠剂,使粘度达到要求,即可得到水性热熔胶。
实施例二
1)、取1.5份去离子水溶解0.15份过硫酸铵,配成过硫酸铵溶液待用;取1份去离子水溶解0.075份碳酸氢钠,配成碳酸氢钠溶液待用。
2)、将18份去离子水加入预乳化罐中,加入1.25份乳化剂搅匀,在900转/分钟下投入计量丙烯酸酯单体及苯乙烯,半小时后预乳化液乳白均匀后备用。
3)、在聚合釜中投入29.5份去离子水,搅拌条件下加入保护胶体、1.25份的乳化剂、过硫酸铵0.15份和碳酸氢钠0.075份、分子量调节剂0.2份搅匀,加入5%的预乳化液后继续搅拌并开始升温,67℃时罐内液料出现兰光,温度逐步升高至89℃,而后回落至85℃,保温半小时。
4)、种子聚合结束后保持85℃,平行滴加预乳化液,预先配好的过硫酸铵溶液与碳酸氢钠溶液,4小时滴完,滴加完毕85℃保温半小时后逐步升温至90℃,继续保温1.5小时后,降温。
5)、降温至60℃以下时,用氨水调整PH值8,加入消泡剂,改性树脂,增稠剂,使粘度达到要求,即可得到水性热熔胶。
Claims (4)
1.一种水性热熔胶,其特征在于:由以下重量比例的组分组成:去离子水50份,保护胶体0.1份,乳化剂2-2.5份,苯乙烯10-20份,丙烯酸分酯单体35-30份,化学纯过硫酸铵0.3份;化学纯碳酸氢钠0.15份;分子量调节剂0.2份,消泡剂(DF-1311)0.1-0.5份;氨水0.4-0.6份、改性树脂1-3份、增稠剂0.1-0.5份。
2.如权利要求1所述的一种水性热熔胶,其特征在于:所述的乳化剂为阴、非离子复配,复配比例为1∶2。
3.一种制备权利要求1所述水性热熔胶的方法,其特征在于:包括以下步骤:
1)、取1.5份去离子水溶解0.15份过硫酸铵,配成过硫酸铵溶液待用;取1份去离子水溶解碳酸氢钠,配成碳酸氢钠溶液待用。
2)、将18份去离子水加入预乳化罐中,加入乳化剂1-1.25份搅匀,在900转/分钟下投入计量丙烯酸酯单体及苯乙烯,半小时后预乳化液乳白均匀后备用。
3)、在聚合釜中投入29.5份去离子水,搅拌条件下加入保护胶体、乳化剂1-1.25份、过硫酸铵0.15份和碳酸氢钠0.075份、分子量调节剂0.2份搅匀,加入5%的预乳化液后继续搅拌并开始升温,65℃-67℃时罐内液料出现兰光,温度逐步升高至87℃-89℃,而后回落至85℃时,保温半小时。
4)、种子聚合结束后保持85℃,平行滴加预乳化液,预先配好的过硫酸铵溶液与碳酸氢钠溶液,3-4小时滴完,滴加完毕85℃保温半小时后,逐步升温至90℃,继续保温1-1.5小时后,降温。
5)、降温至60℃以下时,另取5份去离子水稀释0.4-0.6份氨水后调整PH值7-8,加入消泡剂,改性树脂,增稠剂,使粘度达到要求,即可得到水性热熔胶。
4.如权利要求3所述的制备水性热熔胶的方法,其特征在于:所述的步骤4)中碳酸氢钠溶液比过硫酸铵溶液提前15分钟滴完。