CN102912359A - 一种金属铁表面除锈的方法 - Google Patents

一种金属铁表面除锈的方法 Download PDF

Info

Publication number
CN102912359A
CN102912359A CN2012103582452A CN201210358245A CN102912359A CN 102912359 A CN102912359 A CN 102912359A CN 2012103582452 A CN2012103582452 A CN 2012103582452A CN 201210358245 A CN201210358245 A CN 201210358245A CN 102912359 A CN102912359 A CN 102912359A
Authority
CN
China
Prior art keywords
iron
metallic
strongthener
oxide compound
surface derusting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103582452A
Other languages
English (en)
Inventor
史昊东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2012103582452A priority Critical patent/CN102912359A/zh
Publication of CN102912359A publication Critical patent/CN102912359A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种金属铁表面除锈的方法，是用浓度百分比为40-50％的稀磷酸配制铁的氧化物和增强材料浆料，并将该浆料涂覆于待处理金属表面；用低压蒸汽加热待处理金属表面。

Description

一种金属铁表面除锈的方法
技术领域
本发明属于金属表面除锈技术领域，特别是指一种金属铁表面除锈的方法。
背景技术
铁及铁合金作为最常用的材料遍及国民经济建设的各个领域，但金属在自然环境中的腐蚀现象也相当严重，每年铁的腐蚀损失就高达几百亿，在一些领域，腐蚀情况更加严重，因此铁及铁合金的除锈和防腐蚀处理技术为当前最重要的课题之一。
针对铁及铁合金的腐蚀问题，目前主要有三种解决方式，第一种是涂覆防腐涂料，第二种是采用电镀耐腐蚀金属，第三种采用合金方式来解决，但对于大多数铁合金也需要进行防腐蚀处理。对于第一种和第二种处理方式，在进行防腐处理前要进行除锈处理，即用除锈剂去除金属表面的锈蚀或氧化层，再涂覆防腐蚀材料或电镀，这种方式增加了成本和操作工艺。
发明内容
本发明的目的在于克服现有技术的不足，提供一种除锈方法，该方法能够根据各领域中的铁及铁合金的腐蚀特点，在有效除锈的同时实现了抗腐蚀效果。
本发明是通过以下技术方案实现的：
一种金属表面除锈的方法，其包括以下步骤：
1)、用浓度百分比为40-50％的稀磷酸配制铁的氧化物和增强材料浆料，并将该浆料涂覆于待处理金属表面；
2)、用低压蒸汽加热待处理金属表面，加热温度为80-120℃，加热时间为10-20分钟；
3)、将加热后的金属置于25-35℃的温度范围内36-200小时；
4)、将经过处理后的金属表面进行其它方式的防腐处理或直接使用。
所述稀磷酸同铁的氧化物及增强材料和重量比为1∶1。
所述步骤1)中的涂覆厚度为0.5-1mm。
所述铁的氧化物为三氧化二铁或四氧化三铁中的一种或两种组合。
所述铁的氧化物同增强材料的重量比为1.5∶1-1∶1。
所述增强材料为粉煤灰或硅酸钙粉末。
所述铁的氧化物和增强材料粉末的粒径为0.5-10μm。
本发明的有益效果是：
通过本发明的技术方案，不需要去除铁表面的氧化层或锈层，因此不会造成铁厚度的损失，并且将铁表面的锈及氧化层直接转变为耐腐蚀防护层。
具体实施方式
以下通过具体实施例来详细描述本发明的技术方案。
一种金属铁表面除锈的方法，其包括以下步骤：
1)、用浓度百分比为40-50％的稀磷酸配制铁的氧化物和增强材料浆料，所述铁的氧化物为三氧化二铁或四氧化三铁中的一种或两种组合，所述增强材料为粉煤灰或硅酸钙粉末，所述铁的氧化物和增强材料粉末的粒径为0.5-10μm；所述铁的氧化物同增强材料的重量比为1.5∶1-1∶1；所述稀磷酸同铁的氧化物及增强材料和重量比为1∶1。并将该浆料涂覆于待处理金属表面；涂覆厚度为0.5-1mm。
2)、用低压带磷酸蒸汽加热待处理金属表面，加热温度为80-120℃，加热时间为10-20分钟；所述低压蒸汽是指压力低于1MPa的蒸汽；加热时间的选择依金属的最后用途及所应用的环境来确定，因为加热的时间越长，最后形成的耐腐蚀层越厚，但一般情况下以48小时为最佳时间，因为防腐蚀层过厚会导致耐腐蚀层变脆，反而降低耐腐蚀效果。
3)、将加热后的金属置于25-35℃的温度范围内36-200小时；
4)、将经过处理后的金属表面进行其它方式的防腐处理或直接使用。
在本发明的技术方案中，关于稀磷酸溶液的浓度并无特别区别，在本技术要求范围内均能实现本发明的目的。
例用本技术方案对三块铁板进行处理，其中一块为有氧化层铁板，一块为有锈铁板，一块为表面经去除氧化层处理的铁板，将这三块铁板的一面均经相同条件用上述方式进行处理，并均于25-35℃的温度范围内140小时后，放置于25℃，8％盐溶液中60天后观察，经本技术方案处理一面的铁板没有变化，而没有经本技术方案处理的一面腐蚀现象相当明显。

Claims (7)

1.一种金属铁表面除锈的方法，其特征在于：包括以下步骤：
1)、用浓度百分比为40-50％的稀磷酸配制铁的氧化物和增强材料浆料，并将该浆料涂覆于待处理金属表面；
2)、用低压蒸汽加热待处理金属表面，加热温度为80-120℃，加热时间为10-20分钟；
3)、将加热后的金属置于25-35℃的温度范围内36-200小时；
4)、将经过处理后的金属表面进行其它方式的防腐处理或直接使用。
2.根据权利要求1所述的金属铁表面除锈的方法，其特征在于：所述稀磷酸同铁的氧化物及增强材料和重量比为1∶1。
3.根据权利要求1所述的金属铁表面除锈的方法，其特征在于：所述步骤1)中的涂覆厚度为0.5-1mm。
4.根据权利要求1所述的金属铁表面除锈的方法，其特征在于：所述铁的氧化物为三氧化二铁或四氧化三铁中的一种或两种组合。
5.根据权利要求1所述的金属铁表面除锈的方法，其特征在于：所述铁的氧化物同增强材料的重量比为1.5∶1-1∶1。
6.根据权利要求1所述的金属铁表面除锈的方法，其特征在于：所述增强材料为粉煤灰或硅酸钙粉末。
7.根据权利要求1或5所述的金属铁表面除锈的方法，其特征在于：所述铁的氧化物和增强材料粉末的粒径为0.5-10μm。
CN2012103582452A 2012-09-21 2012-09-21 一种金属铁表面除锈的方法 Pending CN102912359A (zh)