CN102911465B - 一种高阻燃耐火电力电缆料及其制备方法 - Google Patents

一种高阻燃耐火电力电缆料及其制备方法 Download PDF

Info

Publication number
CN102911465B
CN102911465B CN201210346188.6A CN201210346188A CN102911465B CN 102911465 B CN102911465 B CN 102911465B CN 201210346188 A CN201210346188 A CN 201210346188A CN 102911465 B CN102911465 B CN 102911465B
Authority
CN
China
Prior art keywords
compound
rubber
cable material
high flame
power supply
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210346188.6A
Other languages
English (en)
Other versions
CN102911465A (zh
Inventor
赵家玉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou poly Electronics Co., Ltd.
Original Assignee
TONGLING CITY TONGDU SPECIAL CABLE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING CITY TONGDU SPECIAL CABLE CO Ltd filed Critical TONGLING CITY TONGDU SPECIAL CABLE CO Ltd
Priority to CN201210346188.6A priority Critical patent/CN102911465B/zh
Publication of CN102911465A publication Critical patent/CN102911465A/zh
Application granted granted Critical
Publication of CN102911465B publication Critical patent/CN102911465B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高阻燃耐火电力电缆料及其制备方法，其组成原料的重量份为：混合料A：聚烯烃弹性体10-20、甲基乙烯基硅橡胶20-30、氯丁橡胶20-30、马来酸酐接枝PE 10-20、半补强炭黑1-3、改性蒙脱石粉40-60、异氰酸酯1-3、促进剂C-15E86 1.5-2.5、硬脂酸锌1-3、双硬脂酸甘油酯3-4、氢氧化镁10-20和烟片胶1-3；混合料B：丙烯酸酸橡胶30-40、甲基乙烯基硅橡胶10-20、三元乙丙橡胶20-30、丁腈橡胶20-30、聚-4-甲基-1-戊烯0.3-0.5、2-硫醇基苯骈咪唑2-4、交联剂TAC 2-3、抗氧剂DLTP 1-3、氢氧化铝25-35和硼酸锌1-3。本发明制备方法简单，组成原料配方合理，性能大大提高，拉伸强度、断裂延伸率、老化后的拉伸强度保持率及断裂伸出保持率，冲击脆化温度能同时获得优异的性能。

Description

一种高阻燃耐火电力电缆料及其制备方法
技术领域
本发明涉及一种高阻燃耐火电力电缆料及其制备方法，属于电缆料技术领域。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，随着电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视，电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，同时随着通讯事业、汽车工业和计算机工业的发展，特别是船用导线、汽车用线、高温仪表电缆、石油钻井平台电缆等许多场合，当然高阻燃耐火电力电缆料也是必不可少的。
发明内容
本发明的目的是提供一种高阻燃耐火电力电缆料及其制备方法，本发明制备方法简单，组成原料配方合理，性能大大提高，拉伸强度、断裂延伸率、老化后的拉伸强度保持率及断裂伸出保持率，冲击脆化温度能同时获得优异的性能。
为实现上述目的本发明的采用如下技术方案：
高阻燃耐火电力电缆料，其组成原料的重量份为：
混合料A：聚烯烃弹性体10-20、甲基乙烯基硅橡胶20-30、氯丁橡胶20-30、马来酸酐接枝PE  10-20、半补强炭黑1-3、改性蒙脱石粉40-60、异氰酸酯1-3、促进剂C-15E86  1.5-2.5、硬脂酸锌1-3、双硬脂酸甘油酯3-4、氢氧化镁10-20和烟片胶1-3；
混合料B：丙烯酸酸橡胶30-40、甲基乙烯基硅橡胶10-20、三元乙丙橡胶20-30、丁腈橡胶20-30、聚-4-甲基-1-戊烯0.3-0.5、2-硫醇基苯骈咪唑2-4、交联剂 TAC  2-3、抗氧剂DLTP  1-3、氢氧化铝25-35和硼酸锌1-3。
高阻燃耐火电力电缆料，其组成原料的重量份为：
混合料A：聚烯烃弹性体15、甲基乙烯基硅橡胶25、氯丁橡胶25、马来酸酐接枝PE  15、半补强炭黑2、改性蒙脱石粉50、异氰酸酯2、促进剂C-15E86  2、硬脂酸锌2、双硬脂酸甘油酯3.5、氢氧化镁15和烟片胶2；
混合料B：丙烯酸酸橡胶35、甲基乙烯基硅橡胶15、三元乙丙橡胶25、丁腈橡胶25、聚-4-甲基-1-戊烯0.4、2-硫醇基苯骈咪唑3、交联剂 TAC  2.5、抗氧剂DLTP  2、氢氧化铝30和硼酸锌2。
高阻燃耐火电力电缆料的制备方法，包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；将混合料A、B的原料分别在温度110-125℃在密炼4-6分钟后，密炼后再在温度170-190℃下混炼20-30分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在133-138℃，最后在140-150℃下塑炼3-5分钟，出料。
所述的聚烯烃弹性体为POE0201,通用级,埃克森美孚公司制造。
所述的改性蒙脱石粉制备方法为先用13-18%盐酸浸泡蒙脱石1-2小时，静置，澄清，离心，固体用水洗至中性，烘干后，加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀，烘干，粉碎得到。
本发明的优点：
本发明制备方法简单，组成原料配方合理，性能大大提高，拉伸强度、断裂延伸率、老化后的拉伸强度保持率及断裂伸出保持率，冲击脆化温度能同时获得优异的性能。
具体实施方式
实施例1：高阻燃耐火电力电缆料，其组成原料的重量份为：
混合料A：聚烯烃弹性体15、甲基乙烯基硅橡胶25、氯丁橡胶25、马来酸酐接枝PE  15、半补强炭黑2、改性蒙脱石粉50、异氰酸酯2、促进剂C-15E86  2、硬脂酸锌2、双硬脂酸甘油酯3.5、氢氧化镁15和烟片胶2；
混合料B：丙烯酸酸橡胶35、甲基乙烯基硅橡胶15、三元乙丙橡胶25、丁腈橡胶25、聚-4-甲基-1-戊烯0.4、2-硫醇基苯骈咪唑3、交联剂 TAC  2.5、抗氧剂DLTP  2、氢氧化铝30和硼酸锌2。
高阻燃耐火电力电缆料的制备方法，包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；将混合料A、B的原料分别在温度110-125℃在密炼4-6分钟后，密炼后再在温度170-190℃下混炼20-30分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在133-138℃，最后在140-150℃下塑炼3-5分钟，出料。
所述的聚烯烃弹性体为POE0201,通用级,埃克森美孚公司制造。
所述的改性蒙脱石粉制备方法为先用13-18%盐酸浸泡蒙脱石1-2小时，静置，澄清，离心，固体用水洗至中性，烘干后，加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀，烘干，粉碎得到。
    本发明制得的高阻燃耐火电力电缆料性能：
    拉伸强度为16.5-19Mpa，断裂伸出率为250-300%，老化后拉伸强度保持率（120℃，96h） 85%，老化后断裂伸出保持率（120℃，96h）75%，冲击脆化温度-37℃--45℃。单根垂直燃烧试验，续燃时间为7-9秒，烧焦端距上夹具下缘距离为280-320毫米；成束燃烧试验，炭化长度为0.7 -1.3米。

Claims (4)

1.一种高阻燃耐火电力电缆料，其特征在于其组成原料的重量份为：
混合料A：聚烯烃弹性体10-20、甲基乙烯基硅橡胶20-30、氯丁橡胶20-30、马来酸酐接枝PE  10-20、半补强炭黑1-3、改性蒙脱石粉40-60、异氰酸酯1-3、促进剂C-15E86  1.5-2.5、硬脂酸锌1-3、双硬脂酸甘油酯3-4、氢氧化镁10-20和烟片胶1-3；
混合料B：丙烯酸酯橡胶30-40、甲基乙烯基硅橡胶10-20、三元乙丙橡胶20-30、丁腈橡胶20-30、聚-4-甲基-1-戊烯0.3-0.5、2-硫醇基苯并咪唑2-4、交联剂 TAC  2-3、抗氧剂DLTP  1-3、氢氧化铝25-35和硼酸锌1-3；
所述的改性蒙脱石粉制备方法为先用13-18%盐酸浸泡蒙脱石1-2小时，静置，澄清，离心，固体用水洗至中性，烘干后，加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀，烘干，粉碎得到。
2.根据权利要求1所述的高阻燃耐火电力电缆料，其特征在于其组成原料的重量份为：
混合料A：聚烯烃弹性体15、甲基乙烯基硅橡胶25、氯丁橡胶25、马来酸酐接枝PE  15、半补强炭黑2、改性蒙脱石粉50、异氰酸酯2、促进剂C-15E86  2、硬脂酸锌2、双硬脂酸甘油酯3.5、氢氧化镁15和烟片胶2；
混合料B：丙烯酸酯橡胶35、甲基乙烯基硅橡胶15、三元乙丙橡胶25、丁腈橡胶25、聚-4-甲基-1-戊烯0.4、2-硫醇基苯并咪唑3、交联剂 TAC  2.5、抗氧剂DLTP  2、氢氧化铝30和硼酸锌2。
3.一种如权利要求1或2所述的高阻燃耐火电力电缆料的制备方法，其特征在于包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；将混合料A、B的原料分别在温度110-125℃下密炼4-6分钟，密炼后再在温度170-190℃下混炼20-30分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在133-138℃，最后在140-150℃下塑炼3-5分钟，出料。
4.根据权利要求1或2所述的高阻燃耐火电力电缆料，其特征在于：所述的聚烯烃弹性体为POE0201,通用级,埃克森美孚公司制造。
CN201210346188.6A 2012-09-18 2012-09-18 一种高阻燃耐火电力电缆料及其制备方法 Expired - Fee Related CN102911465B (zh)