CN103289415B - 一种含有改性甲基乙烯基硅橡胶的电缆护套料及其制备方法 - Google Patents

一种含有改性甲基乙烯基硅橡胶的电缆护套料及其制备方法 Download PDF

Info

Publication number
CN103289415B
CN103289415B CN201310162487.9A CN201310162487A CN103289415B CN 103289415 B CN103289415 B CN 103289415B CN 201310162487 A CN201310162487 A CN 201310162487A CN 103289415 B CN103289415 B CN 103289415B
Authority
CN
China
Prior art keywords
modified methyl
vinylsiloxane rubber
methyl vinylsiloxane
rubber
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310162487.9A
Other languages
English (en)
Other versions
CN103289415A (zh
Inventor
董后友
姜树海
张传海
董伟
肖明枝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hubei Xin Hai letter Chemical Co., Ltd.
Original Assignee
ANHUI GREEN ECOLOGICAL POLYMER MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI GREEN ECOLOGICAL POLYMER MATERIALS TECHNOLOGY Co Ltd filed Critical ANHUI GREEN ECOLOGICAL POLYMER MATERIALS TECHNOLOGY Co Ltd
Priority to CN201310162487.9A priority Critical patent/CN103289415B/zh
Publication of CN103289415A publication Critical patent/CN103289415A/zh
Application granted granted Critical
Publication of CN103289415B publication Critical patent/CN103289415B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有改性甲基乙烯基硅橡胶的电缆护套料及其制备方法，其组成原料为：改性甲基乙烯基硅橡胶、耐冲击性聚苯乙烯、碳酸钙、硅藻土、氮化铝、促进剂DM、促进剂TMTD、双(二辛氧基焦磷酸酯基)乙撑钛酸酯、蓖麻油酸钙、二苯胺、柠檬酸三丁酯和磷酸三甲苯酯；本发明采用改性甲基乙烯基硅橡胶作为主料，通过对甲基乙烯基硅橡胶的改性，机械性能大大幅提高，较好的力学性能，具有低烟、无卤、高绝缘电阻的特性，同时在原料中采用碳酸钙作为补强剂，硅藻土和氮化铝作为填料。

Description

一种含有改性甲基乙烯基硅橡胶的电缆护套料及其制备方法
技术领域
本发明涉及一种电缆护套料，具体涉及一种含有改性甲基乙烯基硅橡胶的电缆护套料及其制备方法。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视，电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，同时随着通讯事业、汽车工业和计算机工业的发展，对电缆护套料的质量要求日益增加，本发明提供一种含有改性甲基乙烯基硅橡胶的电缆护套料及其制备方法。
发明内容
本发明的目的在于提供一种含有改性甲基乙烯基硅橡胶的电缆护套料及其制备方法。
本发明采用如下技术方案：
含有改性甲基乙烯基硅橡胶的电缆护套料，其组成原料的重量份为：改性甲基乙烯基硅橡胶88-95、耐冲击性聚苯乙烯17-23、碳酸钙2.5-3.5、硅藻土30-35、氮化铝8.0-9.0、促进剂DM  1.6-1.8、促进剂TMTD  1.1-1.3、双(二辛氧基焦磷酸酯基)乙撑钛酸酯2.8-3.5、蓖麻油酸钙1.8-2.2、二苯胺0.8-1.2、柠檬酸三丁酯3.5-4.5和磷酸三甲苯酯6.5-8.5。
含有改性甲基乙烯基硅橡胶的电缆护套料，其组成原料的重量份为：改性甲基乙烯基硅橡胶92、耐冲击性聚苯乙烯20、碳酸钙3.0、硅藻土32、氮化铝8.5、促进剂DM  1.7、促进剂TMTD  1.2、双(二辛氧基焦磷酸酯基)乙撑钛酸酯3.2、蓖麻油酸钙2.0、二苯胺1.0、柠檬酸三丁酯4.0和磷酸三甲苯酯7.5。
含有改性甲基乙烯基硅橡胶的电缆护套料的制备方法，包括以下步骤：
（1）改性甲基乙烯基硅橡胶的制备：
配方（重量份）：甲基乙烯基硅橡胶23-28、明矾粉17-19、二甲苯 25-30、2,2′- 硫代双(4- 特辛基苯酚)1.7-1.9、顺丁烯二酸酐2.2-2.4、2,6二叔丁基对甲酚4.8-5.5、二茂铁1.0-1.2和交联剂 TAIC  0.7-0.9；
制备方法如下：
a：按组成原料的重量份将甲基乙烯基硅橡胶、二甲苯、顺丁烯二酸酐在100-120℃下搅拌反应3-5小时；
b：在步骤（a）中按重量份加入明矾粉和2,2′- 硫代双(4- 特辛基苯酚)在155-165℃下搅拌反应1-2小时；
c：在步骤（b）中加入2,6二叔丁基对甲酚、二茂铁和交联剂 TAIC在170-180℃下搅拌反应1.0-2.0小时，最后蒸馏除去二甲苯溶剂，得到改性甲基乙烯基硅橡胶；
（2）按组成原料的重量份称取步骤（1）的改性甲基乙烯基硅橡胶和其他剩余各原料，常温下低速搅拌5-8分钟，使得混合均匀，然后在温度50-70℃混炼35-45分钟，出料。
本发明的有益效果：
本发明采用改性甲基乙烯基硅橡胶作为主料，通过对甲基乙烯基硅橡胶的改性，机械性能大大幅提高，较好的力学性能，具有低烟、无卤、高绝缘电阻的特性，同时在原料中采用碳酸钙作为补强剂，硅藻土和氮化铝作为填料。
具体实施方式
实施例1：含有改性甲基乙烯基硅橡胶的电缆护套料，其组成原料的重量（kg）为：改性甲基乙烯基硅橡胶92、耐冲击性聚苯乙烯20、碳酸钙3.0、硅藻土32、氮化铝8.5、促进剂DM  1.7、促进剂TMTD  1.2、双(二辛氧基焦磷酸酯基)乙撑钛酸酯3.2、蓖麻油酸钙2.0、二苯胺1.0、柠檬酸三丁酯4.0和磷酸三甲苯酯7.5。
含有改性甲基乙烯基硅橡胶的电缆护套料的制备方法，包括以下步骤：
（1）改性甲基乙烯基硅橡胶的制备：
配方（kg）：甲基乙烯基硅橡胶25、明矾粉18、二甲苯 28、2,2′- 硫代双(4- 特辛基苯酚)1.8、顺丁烯二酸酐2.3、2,6二叔丁基对甲酚5.2、二茂铁1.1和交联剂 TAIC  0.8；
制备方法如下：
a：按组成原料的重量份将甲基乙烯基硅橡胶、二甲苯、顺丁烯二酸酐在110℃下搅拌反应4小时；
b：在步骤（a）中按重量份加入明矾粉和2,2′- 硫代双(4- 特辛基苯酚)在160℃下搅拌反应1-2小时；
c：在步骤（b）中加入2,6二叔丁基对甲酚、二茂铁和交联剂 TAIC在175℃下搅拌反应1.5小时，最后蒸馏除去二甲苯溶剂，得到改性甲基乙烯基硅橡胶；
（2）按组成原料的重量份称取步骤（1）的改性甲基乙烯基硅橡胶和其他剩余各原料，常温下低速搅拌7分钟，使得混合均匀，然后在温度60℃混炼40分钟，出料。
通过本发明的实施例1制得的电缆料性能数据：
序号 项目名称 单位 测试值
1 抗张强度 Mpa 7.9
2 断裂伸长率 % 548
3 200℃，,240h老化后抗张强度 Mpa 7.35
4 200℃，,240h老化后断裂伸长率 % 530
5 20℃体积电阻率 Ω·m 8.95×1012
6 相对介电常数 / 3.3
7 1000℃×90min高温下绝缘电阻 MΩ 1.4

Claims (2)

1.一种含有改性甲基乙烯基硅橡胶的电缆护套料，其特征在于其组成原料的重量份为：改性甲基乙烯基硅橡胶88-95、耐冲击性聚苯乙烯17-23、碳酸钙2.5-3.5、硅藻土30-35、氮化铝8.0-9.0、促进剂DM  1.6-1.8、促进剂TMTD  1.1-1.3、双(二辛氧基焦磷酸酯基)乙撑钛酸酯2.8-3.5、蓖麻油酸钙1.8-2.2、二苯胺0.8-1.2、柠檬酸三丁酯3.5-4.5和磷酸三甲苯酯6.5-8.5；
该电缆护套料的制备方法，其特征在于包括以下步骤：
（1）改性甲基乙烯基硅橡胶的制备：
配方以重量份计：甲基乙烯基硅橡胶23-28、明矾粉17-19、二甲苯 25-30、2,2′- 硫代双(4- 特辛基苯酚)1.7-1.9、顺丁烯二酸酐2.2-2.4、2,6二叔丁基对甲酚4.8-5.5、二茂铁1.0-1.2和交联剂 TAIC  0.7-0.9；
改性甲基乙烯基硅橡胶的制备方法如下：
a：按组成原料的重量份将甲基乙烯基硅橡胶、二甲苯、顺丁烯二酸酐在100-120℃下搅拌反应3-5小时；
b：在步骤（a）中按重量份加入明矾粉和2,2′- 硫代双(4- 特辛基苯酚)在155-165℃下搅拌反应1-2小时；
c：在步骤（b）中加入2,6二叔丁基对甲酚、二茂铁和交联剂 TAIC在170-180℃下搅拌反应1.0-2.0小时，最后蒸馏除去二甲苯溶剂，得到改性甲基乙烯基硅橡胶；
（2）按组成原料的重量份称取步骤（1）的改性甲基乙烯基硅橡胶和其他剩余各原料，常温下低速搅拌5-8分钟，使得混合均匀，然后在温度50-70℃混炼35-45分钟，出料。
2.根据权利要求1所述的含有改性甲基乙烯基硅橡胶的电缆护套料，其特征在于其组成原料的重量份为：改性甲基乙烯基硅橡胶92、耐冲击性聚苯乙烯20、碳酸钙3.0、硅藻土32、氮化铝8.5、促进剂DM  1.7、促进剂TMTD  1.2、双(二辛氧基焦磷酸酯基)乙撑钛酸酯3.2、蓖麻油酸钙2.0、二苯胺1.0、柠檬酸三丁酯4.0和磷酸三甲苯酯7.5。
CN201310162487.9A 2013-05-06 2013-05-06 一种含有改性甲基乙烯基硅橡胶的电缆护套料及其制备方法 Active CN103289415B (zh)