CN102911439B - Fire-resistant control cable material for ships and method for preparing same - Google Patents
Fire-resistant control cable material for ships and method for preparing same Download PDFInfo
- Publication number
- CN102911439B CN102911439B CN201210346183.3A CN201210346183A CN102911439B CN 102911439 B CN102911439 B CN 102911439B CN 201210346183 A CN201210346183 A CN 201210346183A CN 102911439 B CN102911439 B CN 102911439B
- Authority
- CN
- China
- Prior art keywords
- parts
- compound
- control cable
- cable material
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a fire-resistant control cable material for ships and a method for preparing the fire-resistant control cable material. The fire-resistant control cable material comprises the following raw materials by weight: a mixture A and a mixture B; the mixture A comprises 10-20 parts of polyolefin elastomer, 20-30 parts of ethylene-propylene-diene monomer rubber, 20-30 parts of high-density polyethylene resin, 10-20 parts of chlorinated polyethylene, 1-3 parts of semi-reinforcing carbon black, 40-60 parts of modified sepiolite powder, 1-3 parts of magnesium oxide, 1.5-2.5 parts of a promoting agent which is the DTDM, 1-3 parts of zinc stearate, 3-4 parts of ethylene bis-stearamide, and 1-3 parts of dibutyl phthalate; and the mixture B comprises 10-20 parts of polyolefin elastomer, 20-30 parts of nitrile rubber, 20-30 parts of PVC resin powder, 10-20 parts of acrylate rubber, 1-3 parts of 2-mercaptobenzothiazole, 2-3 parts of DCP (dicumyl peroxide), 1-3 parts of antioxidant 1010, 1-3 parts of talc powder and 1-3 parts of zinc borate. The method for preparing the fire-resistant control cable material is simple, the fire-resistant control cable material has excellent electrical properties, the formula of the raw materials is reasonable, and the prepared cable material is environmentally friendly and has hot oil resistance, fire resistance and thermal oxidative aging properties.
Description
Technical field
The present invention relates to a kind of fireproof control cable material peculiar to vessel and preparation method thereof, belong to CABLE MATERIALS technical field.
Background technology
Along with developing rapidly of economy, electric wire is at industry-by-industry, in field, be all widely used, along with the frequent generation of electrical fire accident, the fire-retardant problem of electric wire causes the attention of countries in the world gradually, when cable fire, discharge a large amount of smog and poisonous, corrosive gas is Hazard Factor in fire, people's safe escape and fire-fighting work in fire, are hindered, make lives and properties suffer heavy losses, simultaneously along with communication career, the development of automotive industry and computer industry, particularly wire peculiar to vessel, line for cars, high temperature instrument cable, many occasions such as oil drilling platform cable, certain fireproof control cable material peculiar to vessel is also absolutely necessary.
Summary of the invention
The object of this invention is to provide a kind of fireproof control cable material peculiar to vessel and preparation method thereof, preparation method of the present invention is simple, electrical property excellence, and constitutive material formula is reasonable, not only environmental protection of the CABLE MATERIALS making, has the performances such as well heat-resisting, resistivity against fire and thermo oxidative aging.
The following technical scheme of employing of the present invention for achieving the above object:
Fireproof control cable material peculiar to vessel, the weight part of its constitutive material is:
Compound A: polyolefin elastomer 10-20, terpolymer EP rubber 20-30, high-density polyethylene resin 20-30, chlorinatedpolyethylene 10-20, semi-reinforcing hydrocarbon black 1-3, modified meerschaum powder 40-60, magnesium oxide 1-3, vulkacit D TDM 1.5-2.5, Zinic stearas 1-3, the two hard esteramides 3-4 of ethylene group and dibutyl phthalate 1-3;
Compound B: polyolefin elastomer 10-20, paracril 20-30, polyvinyl chloride resin powder 20-30, acrylic elastomer 10-20,2-thiol group benzimidazolyl 1-3, dicumyl peroxide DCP 2-3, antioxidant 1010 1-3, talcum powder 30-40 and zinc borate 1-3.
Fireproof control cable material peculiar to vessel, the weight part of its constitutive material is:
Compound A: polyolefin elastomer 15, terpolymer EP rubber 25, high-density polyethylene resin 25, chlorinatedpolyethylene 15, semi-reinforcing hydrocarbon black 2, modified meerschaum powder 50, magnesium oxide 2, vulkacit D TDM 2, Zinic stearas 2, the two hard esteramides 3.5 of ethylene group and dibutyl phthalate 2;
Compound B: polyolefin elastomer 15, paracril 25, polyvinyl chloride resin powder 25, acrylic elastomer 15,2-thiol group benzimidazolyl 2, dicumyl peroxide DCP 2.5, antioxidant 1010 2, talcum powder 35-40 and zinc borate 2.
The preparation method of fireproof control cable material peculiar to vessel, comprises the following steps:
(1) first take respectively all raw materials of compound A, B by the weight part of constitutive material; By the raw material of compound A, B respectively at temperature 100-120 ℃ after banburying 5-7 minute, mixing 25-35 minute at temperature 170-190 ℃ again after banburying, obtains respectively compound A and compound B;
(2) mix compound A and compound B, mixing 10-15 minute at temperature 170-190 ℃, then carries out high-energy radiation, is respectively cross-linking radiation under 10-12KW, 8-9Mev electron beam at power and energy, and irradiation dose is 180-230Gy, extrudes and makes material.
Described polyolefin elastomer is POE7467, injection grade, and du pont company manufactures.
Described modified meerschaum powder, preparation method thereof, for first using 15-20% salt acid soak sepiolite 1-2 hour, leaves standstill, clarification, centrifugal, solid washes with water to neutrality, after oven dry, add that to be equivalent to the vinyltriethoxysilane agitating of solid weight 3-5% even, dry, be ground into powder.
Advantage of the present invention:
Preparation method of the present invention is simple, electrical property excellence, and constitutive material formula is reasonable, and not only environmental protection of the CABLE MATERIALS making has the performances such as well heat-resisting, resistivity against fire and thermo oxidative aging.
Embodiment
embodiment 1:fireproof control cable material peculiar to vessel, the weight part of its constitutive material is:
Compound A: polyolefin elastomer 15, terpolymer EP rubber 25, high-density polyethylene resin 25, chlorinatedpolyethylene 15, semi-reinforcing hydrocarbon black 2, modified meerschaum powder 50, magnesium oxide 2, vulkacit D TDM 2, Zinic stearas 2, the two hard esteramides 3.5 of ethylene group and dibutyl phthalate 2;
Compound B: polyolefin elastomer 15, paracril 25, polyvinyl chloride resin powder 25, acrylic elastomer 15,2-thiol group benzimidazolyl 2, dicumyl peroxide DCP 2.5, antioxidant 1010 2, talcum powder 35 and zinc borate 2.
The preparation method of fireproof control cable material peculiar to vessel, comprises the following steps:
(1) first take respectively all raw materials of compound A, B by the weight part of constitutive material; By the raw material of compound A, B respectively at temperature 100-120 ℃ after banburying 5-7 minute, mixing 25-35 minute at temperature 170-190 ℃ again after banburying, obtains respectively compound A and compound B;
(2) mix compound A and compound B, mixing 10-15 minute at temperature 170-190 ℃, then carries out high-energy radiation, is respectively cross-linking radiation under 10-12KW, 8-9Mev electron beam at power and energy, and irradiation dose is 180-230Gy, extrudes and makes material.
Described polyolefin elastomer is POE7467, injection grade, and du pont company manufactures; Described modified meerschaum powder, preparation method thereof, for first using 15-20% salt acid soak sepiolite 1-2 hour, leaves standstill, clarification, centrifugal, solid washes with water to neutrality, after oven dry, add that to be equivalent to the vinyltriethoxysilane agitating of solid weight 3-5% even, dry, be ground into powder.
the fireproof control cable material property energy peculiar to vessel that the present invention makes:
Use temperature 170-190 ℃, 220 ℃ of maximum operation (service) temperatures, stretching strength retentivity 75-78%, conservation rate 73-75% is stretched out in fracture, changes in hardness+23,185 ℃ of bendings are qualified.Tensile strength is 15.3-18Mpa, oxygen index 30-38.5%, and smoke density is 69-75, testing vertical flammability is by UL-94V0 level, volume specific resistance 7.4 × 10
14ohm. centimetre, the heat ageing test of 136 ℃ × 168 hours can be passed through.
Claims (4)
1. a fireproof control cable material peculiar to vessel, is characterized in that the weight part of its constitutive material is:
Compound A: polyolefin elastomer 10-20, terpolymer EP rubber 20-30, high-density polyethylene resin 20-30, chlorinatedpolyethylene 10-20, semi-reinforcing hydrocarbon black 1-3, modified meerschaum powder 40-60, magnesium oxide 1-3, vulkacit D TDM 1.5-2.5, Zinic stearas 1-3, the two hard esteramides 3-4 of ethylene group and dibutyl phthalate 1-3;
Compound B: polyolefin elastomer 10-20, paracril 20-30, polyvinyl chloride resin powder 20-30, acrylic elastomer 10-20,2 mercapto benzimidazole 1-3, dicumyl peroxide DCP 2-3, antioxidant 1010 1-3, talcum powder 30-40 and zinc borate 1-3;
Described modified meerschaum powder, preparation method thereof, for first using 15-20% salt acid soak sepiolite 1-2 hour, leaves standstill, clarification, centrifugal, solid washes with water to neutrality, after oven dry, add that to be equivalent to the vinyltriethoxysilane agitating of solid weight 3-5% even, dry, be ground into powder.
2. fireproof control cable material peculiar to vessel according to claim 1, is characterized in that the weight part of its constitutive material is:
Compound A: polyolefin elastomer 15, terpolymer EP rubber 25, high-density polyethylene resin 25, chlorinatedpolyethylene 15, semi-reinforcing hydrocarbon black 2, modified meerschaum powder 50, magnesium oxide 2, vulkacit D TDM 2, Zinic stearas 2, the two hard esteramides 3.5 of ethylene group and dibutyl phthalate 2;
Compound B: polyolefin elastomer 15, paracril 25, polyvinyl chloride resin powder 25, acrylic elastomer 15,2 mercapto benzimidazole 2, dicumyl peroxide DCP 2.5, antioxidant 1010 2, talcum powder 35 and zinc borate 2.
3. a preparation method for fireproof control cable material peculiar to vessel as claimed in claim 1 or 2, is characterized in that comprising the following steps:
(1) first take respectively all raw materials of compound A, B by the weight part of constitutive material; By the raw material of compound A, B, respectively at temperature 100-120 ℃ of banburying 5-7 minute, mixing 25-35 minute at temperature 170-190 ℃ again after banburying, obtains respectively compound A and compound B;
(2) mix compound A and compound B, mixing 10-15 minute at temperature 170-190 ℃, then carries out high-energy radiation, is respectively cross-linking radiation under 10-12KW, 8-9Mev electron beam at power and energy, and irradiation dose is 180-230Gy, extrudes and makes material.
4. fireproof control cable material peculiar to vessel according to claim 1 and 2, is characterized in that: described polyolefin elastomer is POE7467, injection grade, and du pont company manufactures.