CN102911434A - 一种ldpe改性聚丙烯管及其制备方法 - Google Patents
一种ldpe改性聚丙烯管及其制备方法 Download PDFInfo
- Publication number
- CN102911434A CN102911434A CN 201210398866 CN201210398866A CN102911434A CN 102911434 A CN102911434 A CN 102911434A CN 201210398866 CN201210398866 CN 201210398866 CN 201210398866 A CN201210398866 A CN 201210398866A CN 102911434 A CN102911434 A CN 102911434A
- Authority
- CN
- China
- Prior art keywords
- ldpe
- modified polypropene
- parts
- tube
- cis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种LDPE改性聚丙烯管及制备方法,由下列质量比组成:PP100;填充剂30;LDPE15-30;抗氧剂0.6-1;顺丁橡胶10;辅助抗氧剂0.5;相容剂3;该聚丙烯管稳定性优异,而且工艺简单,成本低廉;使用本发明制作的管材,无毒,电绝缘性优秀,吸水性很低,化学抗性也优秀;适用于水管,上水管等,无刺激性气味;该管材具有耐热,耐酸碱,耐寒,高硬度等优点,会得到广泛使用,并不断替代现有材料。
Description
技术领域
本发明涉及高分子材料领域,尤其涉及一种LDPE改性聚丙烯管及其制备方法。
背景技术
聚丙烯管具有耐腐蚀、强度高、抗渗漏、内阻小、抗拉、抗弯、造价低、寿命长、安装维修方便等特点,广泛应用于石油、化工、电力、纺织、冶金、制药、造纸、食品、矿山、垃圾处理、建筑等行业。
而随着人性化理念的普及,及新型和谐社会的构成,不断改进聚丙烯管的韧性和强度,以达到消费者的需要是非常必要的。
现有的聚丙烯管材,主要采用在聚丙烯管材上镀铝,中国专利CN 2738073Y公开了一种在聚丙烯材料管件的外表面上加有真空镀铝层方法,但是考虑到以上方法工艺复杂,成本太高,现有技术就显得略有不足。
发明内容
本发明提供一种LDPE改性聚丙烯管,解决现有聚丙烯管材中镀铝工艺的操作复杂,成本高,加工中有气味易挥发等技术问题。
本发明采用以下技术方案:
LDPE改性聚丙烯管,由下列原料组成,以质量份数表示法为:
PP 100;
填充剂 30;
LDPE 15-30;
抗氧剂 0.6-1;
顺丁橡胶 10;
辅助抗氧剂 0.5;
相容剂 3。
其中,所述PP采用531PH或M030中的一种,M030熔体流动速率:0.3g/10min,缺口冲击强度:68拉伸强度:28.4MPa;531PH熔体流动速率:0.3g/10min密度:0.905g/cm3缺口冲击强度:7拉伸强度:30MPa断裂伸长率:600%。
所述填充剂采用碳酸钙,所述碳酸钙规格600-1000目。
所述抗氧剂为1010或DLTP中的一种或多种混合物。
所述辅助抗氧剂采用亚磷酸酯AT-168或1500中的一种或多种混合物。
所述相容剂采用PE-g-MAH。
LDPE改性聚丙烯管的制备方法为:
第一步:先将顺丁橡胶在双辊混炼机上塑炼;
第二步:按照上文所述质量分数比称取各种原料,PP、填充剂、LDPE、抗氧剂、辅助抗氧剂和相容剂,将上述原料加入到塑炼后的顺丁橡胶中混炼3-5分钟,使各种成分分散均匀;
第三步:将第二步混合后的物料粗碎后挤出、造粒,然后在单螺杆挤出机中成型,挤出机温度设置为:供料段150-170℃,压缩段170-190℃,计量段190-210℃,口模210-230℃,螺杆转速36r/min,牵引速度0.52m/min。
作为本发明的一种优选技术方案:填充剂选择碳酸钙,无毒、无臭、无刺激性,pH值为8.0~8.6,相对密度为2.7~2.9,对塑料制品尺寸的稳定性有很大作用,能提高制品的硬度,还可以提高制品的表面光泽和表面平整性,在一般塑料制品中添加碳酸钙耐热性可以提高。
作为本发明的一种优选技术方案:选择的LDPE,无毒,软化点较低,柔韧性、抗冲击韧性和耐低温性很好,电绝缘性优秀,吸水性很低,几乎不吸水,化学稳定性优秀,如对酸、碱、盐、有机溶剂都较稳定。
作为本发明的一种优选技术方案:选择的抗氧剂1010和DLTP,抗抽出能力强,挥发性低,相容性好,无味,可与其它种类的添加剂,如辅助抗氧剂(硫醚,亚磷酸酯)等混合使用。
作为本发明的一种优选技术方案:顺丁橡胶选择型号为9000,具有高弹性,滞后损失和生热小,低温、填充和模内流动性好,耐磨和耐挠曲性能优异等优点。
作为本发明的一种优选技术方案:辅助抗氧剂选择亚磷酸酯具有无苯、热分解温度高,不易分解,具有耐水解性、耐热性和耐候性。
本发明使用的所有原料均为共知的已有,使用方法和功能均为已有技术。
本发明所述一种LDPE改性聚丙烯管采用以上技术方案与现有技术相比,具有以下技术效果:1、该聚丙烯管稳定性优异,而且工艺简单,成本低廉;2、使用本发明制作的管材,无毒,电绝缘性优秀,吸水性很低,化学抗性也优秀;3、适用于水管,上水管等,无刺激性气味;4、该管材具有耐热,耐酸碱,耐寒,高硬度等优点,会得到广泛使用,并不断替代现有材料。
具体实施方式
以下通过实施例更加详细地阐述本发明的内容。
实施例1:
第一步:按照下文所述质量分数比称取各种原料
PP M030,赢德塑胶原料有限公司 100;
填充剂碳酸钙 上海一环化工有限公司 30;
LDPE 通富塑胶贸易有限公司 15-30;
抗氧剂1010 上海畅圆贸易有限公司 0.4-0.5;
顺丁橡胶 BR9000,瑞洋橡胶化工有限公司 10;
抗氧剂DLTP 淄博爱鑫塑料有限公司 0.2-0.5;
辅助抗氧剂亚磷酸酯 集信商贸有限公司 0.5;
相容剂PE-g-MAH 德庭化工贸易有限公司 3;
第二步:将顺丁橡胶BR9000在双辊混炼机上塑炼;
第三步:按照上文所述质量分数比称取各种原料,PP、填充剂、LDPE、抗氧剂、辅助抗氧剂和相容剂,将上述原料加入到第二步塑炼后的顺丁橡胶中混炼3-5分钟,使各种成分分散均匀;
第四步:将第三步混合后的物料粗碎后挤出、造粒,然后在单螺杆挤出机中成型,挤出机温度设置为:供料段150-170℃,压缩段170-190℃,计量段190-210℃,口模210-230℃,螺杆转速36r/min,牵引速度0.52m/min。
上述实施例只是用于对本发明的内容进行阐述,而不是限制,因此在与本发明的权利要求书相当的含义和范围内的任何改变,都应该认为是包括在权利要求书的范围内。
Claims (7)
1.一种LDPE改性聚丙烯管,其特征在于:其组成成份以质量份数表示法为:
PP 100;
填充剂 30;
LDPE 15-30;
抗氧剂 0.6-1;
顺丁橡胶 10;
辅助抗氧剂 0.5;
相容剂 3。
2.根据权利要求1所述的一种LDPE改性聚丙烯管,其特征在于:所述PP采用531PH或M030中的一种,M030熔体流动速率:0.3g/10min,缺口冲击强度:68拉伸强度:28.4MPa;531PH熔体流动速率:0.3g/10min密度:0.905g/cm3缺口冲击强度:7拉伸强度:30MPa断裂伸长率:600%。
3.根据权利要求1所述的一种LDPE改性聚丙烯管,其特征在于:所述填充剂采用碳酸钙,所述碳酸钙规格600-1000目。
4.根据权利要求1所述的一种LDPE改性聚丙烯管,其特征在于:所述抗氧剂为1010或DLTP中的一种或多种混合物。
5.根据权利要求1所述的一种LDPE改性聚丙烯管,其特征在于:所述辅助抗氧剂采用亚磷酸酯AT-168或1500中的一种或多种混合物。
6.根据权利要求1所述的一种LDPE改性聚丙烯管,其特征在于:所述相容剂采用PE-g-MAH。
7.一种制备权利要求1所述LDPE改性聚丙烯管的方法,其特征在于步骤为:
第一步:先将顺丁橡胶在双辊混炼机上塑炼;
第二步:按照上文所述质量分数比称取各种原料,PP、填充剂、LDPE、抗氧剂、辅助抗氧剂和相容剂,将上述原料加入到塑炼后的顺丁橡胶中混炼3-5分钟,使各种成分分散均匀;
第三步:将第二步混合后的物料粗碎后挤出、造粒,然后在单螺杆挤出机中成型,挤出机温度设置为:供料段150-170℃,压缩段170-190℃,计量段190-210℃,口模210-230℃,螺杆转速36r/min,牵引速度0.52m/min。