CN102909494B - 一种铜基钎料的粘结剂 - Google Patents
一种铜基钎料的粘结剂 Download PDFInfo
- Publication number
- CN102909494B CN102909494B CN201210467305.4A CN201210467305A CN102909494B CN 102909494 B CN102909494 B CN 102909494B CN 201210467305 A CN201210467305 A CN 201210467305A CN 102909494 B CN102909494 B CN 102909494B
- Authority
- CN
- China
- Prior art keywords
- binder
- solder
- binding agent
- good
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种铜基钎料的粘结剂,属于钎焊技术领域。其组成与质量份数为:工业白油7-9份;分子量为200~300的聚乙烯醇8-10份;硅油1-2份。本钎料具有熔点低,接头强度高,耐热性、耐腐蚀性和流动性好的优点。本发明对铜基钎料具有很好的侵润性和粘结力,与铜基钎料、钎剂混合后,所得的钎料膏具有较好的流动性,并且成型容易,钎焊时粘结剂在350-500℃时的温度下能迅速分解,无残留,并能保持成形坯的形状;具有成本低,效果好,钎焊强度高的优点。
Description
技术领域
本发明属于钎焊技术领域,具体地说,涉及一种粘结剂,更具体地说,涉及一种铜基钎料的粘结剂。
背景技术
粘结剂是钎料和钎剂的载体,它的作用是把钎料和钎剂有机的结合为一体,使钎料和钎剂按所涉及的比例均匀混合起来,把钎料和钎剂混合成具有合适粘度的膏状的钎料膏,能够均匀细腻地涂覆并固化在钎焊部位,从而保证钎缝质量的稳定性。
粘结剂应满足的要求有:(1)对碳钢具有很好的侵润性和粘结力,能使钎料膏具有良好的可塑性,或是使得钎料粉末具有较好的流动性;(2)混合和成型时形状稳定;(3)脱脂初期具有一定的强度;(4)分解特性好,加热到一定温度能全部分解,无残留;(5)成本低。选择粘结剂主要考虑金属粉末和粘结剂混合的流变特性和粘结剂的脱脂特性。不同的粉末和工艺对应不同的粘结剂,一般来说,粘结剂的添加量应少于金属粉末的量。对于铜基钎料,需要特殊的粘结剂,因此针对铜基钎料找出最有效的组合,理想的粘结剂对粉末具有较好的润湿性,短时间内能均匀混合成喂料,成形性好且稳定,在脱脂过程中不受气氛的限制,在一定温度下都能分解、并且无残留,保持成形坯不变形。
常用的粘结剂主要有醇类,胺类物质如聚乙烯醇、正葵醇、三乙醇胺等,以及硅油。首选的是聚乙烯醇,它是一种有机高分子化合物,在高温下溶于水,具有很强的粘性。因此,他可以作为粘结剂使用。但是,在铜基钎料的钎料膏中加入聚乙烯醇,加热时产生气体不易释放,而且,它必须在高温下和水混合,室温时成固体状,不便于钎料膏的生产。其他粘结剂同意铜基钎料组成的钎料膏都可以成膏状,且粘性较强,长时间保存钎料膏不变质,但其缺点也很明显,在加热到400~500℃时放出大量的烟雾,并且已经焦化,撕开钎焊连接面发现含有大量的残渣,接头强度低,因此不适用作铜基钎料的粘结剂。而我们意外的发现低分子量的聚乙烯醇和合适的油料搭配作为粘结剂使用有良好的效果。
中国专利号:200880103131.5,公开日2010年07月21日,公开了一份名称为钎焊用焊剂、钎焊膏组合物及钎焊方法的专利文件,该发明提供一种钎焊用焊剂,可以在抑制焊剂残渣的粘附性、确保高可靠性的同时,减少软熔时的挥发量而实现环境负担小的钎焊。作为解决该问题的途径,该发明的钎焊用焊剂是含有基质树脂、活化剂及溶剂的钎焊用焊剂,作为所述溶剂,含有在20℃以上为液状的有机酸酐及在20℃以上为液状的多元醇,并且在将所述有机酸酐的酸值设为AV(mgKOH/g),将其含量设为WA(g),将所述多元醇的羟基值设为OHV(mgKOH/g),将其含量设为WOH(g)时,则满足AV×WA∶OHV×WOH=1∶0.4~0.6。其中还提到了钎焊膏组合物,但是该专利的钎焊膏组合物没有采用粘结剂,钎焊膏组合物涂覆并固化在钎焊部位时存在不够均匀细腻的缺点,无法保证钎缝质量的稳定性。
中国专利申请号:201210247812.7,公开日2012年11月07日,公开了一份名称为一种醇溶性铜焊膏的专利文件,该发明公开了一种醇溶性铜焊膏,焊膏的组成物及重量百分比为:a)铜基合金钎料粉末:50~86%;b)硼化物与氟化物复合钎剂:0~25%;c)醇溶性高分子化合物类粘合剂:3~10%;d)醇类溶剂:10~30%;e)辅助助剂:0.05~1%。该发明在进行钎焊时还是存在涂覆并固化在钎焊部位不够均匀细腻的缺点,钎缝质量的稳定性差,钎焊接头含有大量的残渣,接头强度低。
发明内容
要解决的问题
针对现有技术铜基钎料的粘结剂钎焊时焊缝有大量的残渣,接头强度低的问题,本发明提供一种铜基钎料的粘结剂。
技术方案
为解决上述问题,本发明采用的技术方案如下。
一种铜基钎料的粘结剂,其组成与质量份数为:
工业白油7-9份;
分子量为200~300的聚乙烯醇8-10份;
硅油1-2份。
优选的,其组成与质量份数为:
工业白油8份;
分子量为200~300的聚乙烯醇9份;
硅油1份。
有益效果
相比于现有技术,本发明具有如下有益效果:
(1)本发明采用工业白油、分子量为200~300的聚乙烯醇和硅油搭配,并且给出了合理的比例范围,适合作为铜基钎料的粘结剂,对铜基钎料具有较好的润湿性,短时间内能均匀混合成喂料,成形性好且稳定,在脱脂过程中不受气氛的限制,在350-500℃时的温度下能迅速分解、无残留,并能保持成形坯的形状;
(2)本发明给出了工业白油8份、分子量为200~300的聚乙烯醇9份和硅油1份的最佳组合比例,对铜基钎料具有很好的侵润性和粘结力,与铜基钎料、钎剂混合后,所得的钎料膏具有较好的流动性,并且成型容易,钎焊时粘结剂迅速分解,无残留,不产生钎焊残渣缺陷;
(3)本发明作为铜基钎料的粘结剂,成本低,效果好,焊缝强度高。
具体实施方式
下面结合具体实施例对本发明进行详细描述。
实施例1
一种铜基钎料的粘结剂,其组成与质量份数为:
工业白油8份;
分子量为200~300的聚乙烯醇9份;
硅油1份。
使用时将铜基钎料、钎剂与本发明混合,所得的钎料膏具有较好的流动性,具有很好的侵润性和粘结力,并且成型容易;钎焊时粘结剂在350℃时迅速分解,无残留,不产生钎焊残渣缺陷。
实施例2
一种铜基钎料的粘结剂,其组成与质量份数为:
工业白油7份;
分子量为200~300的聚乙烯醇8份;
硅油1份。
粘结剂的分解温度为500℃。
实施例3
一种铜基钎料的粘结剂,其组成与质量份数为:
工业白油9份;
分子量为200~300的聚乙烯醇10份;
硅油2份。
粘结剂的分解温度为430℃。
Claims (2)
1.一种铜基钎料的粘结剂,其特征在于,其组成与质量份数为:
工业白油7-9份;
分子量为200~300的聚乙烯醇8-10份;
硅油1-2份。
2.根据权利要求1所述的一种铜基钎料的粘结剂,其特征在于,其组成与质量份数为:
工业白油8份;
分子量为200~300的聚乙烯醇9份;
硅油1份。