CN102898095A - 一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺 - Google Patents

一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺 Download PDF

Info

Publication number
CN102898095A
CN102898095A CN201210353940XA CN201210353940A CN102898095A CN 102898095 A CN102898095 A CN 102898095A CN 201210353940X A CN201210353940X A CN 201210353940XA CN 201210353940 A CN201210353940 A CN 201210353940A CN 102898095 A CN102898095 A CN 102898095A
Authority
CN
China
Prior art keywords
powder
weight
fineness
raw material
oyster shell
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201210353940XA
Other languages
English (en)
Other versions
CN102898095B (zh
Inventor
刘春梅
汪祖强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI BUYETIAN INTERLLIGENT DISPLAY TECHNOLOGY Co Ltd
Original Assignee
ANHUI BUYETIAN INTERLLIGENT DISPLAY TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI BUYETIAN INTERLLIGENT DISPLAY TECHNOLOGY Co Ltd filed Critical ANHUI BUYETIAN INTERLLIGENT DISPLAY TECHNOLOGY Co Ltd
Priority to CN201210353940.XA priority Critical patent/CN102898095B/zh
Publication of CN102898095A publication Critical patent/CN102898095A/zh
Application granted granted Critical
Publication of CN102898095B publication Critical patent/CN102898095B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺，其是由下述重量份的原料制得：贝壳粉26-28，硅酸盐水泥25-30，矾矿尾渣28-30，草木灰10-15，铁矾土3-5，磷石膏粉3-5，泥炭土1-2，耐火粘土1-2，纳米矿物改性混合粉2-4，壳聚糖0.5-1，生石灰1-2，浓度为25-35%的双氧水溶液6-9，水适量。本发明强度高、抗冲击性能好，容重低。

Description

一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺
技术领域
本发明涉及建筑材料领域，确切地说是一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺。
背景技术
轻质隔墙版的制备工艺是一种新型节能墙材料，它是一种外型象空心楼板一样的墙材，但是它两边有公母隼槽，安装时只需将板材立起，公、母隼涂上少量嵌缝砂浆后对拼装起来即可。它是由无害化磷石膏、轻质钢渣、磷石膏粉等多种工业废渣组成，经变频蒸汽加压养护而成。当前的隔墙板普遍存在墙板强度低，抗折、抗冲击较差，隔音效果、防水性能差等缺点。
发明内容
本发明的目的在于提供一种强度高、抗冲击性能好，并具有隔音、保温、防水优点的原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺。
上述目的通过以下方案实现：
一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺，其特征在于：
（1）配料：所述的轻质建筑用隔墙板是由下述重量份的原料制得：
贝壳粉26-28，硅酸盐水泥25-30，矾矿尾渣28-30，草木灰10-15，铁矾土3-5，磷石膏粉3-5，泥炭土1-2，耐火粘土1-2，纳米矿物改性混合粉2-4，壳聚糖0.5-1，生石灰1-2，浓度为25-35%的双氧水溶液6-9，水适量；
所述的纳米矿物改性混合粉由2-4重量份石英砂，5-8重量份海泡石粉、1-2重量份菱镁矿石粉混匀后，于700-800℃下烧损4-5小时，后研磨成纳米粉末，拌入相当于粉体重量1-2%的乙酰柠檬酸三乙酯、1-2%的氯化石蜡拌搅均匀，烘干，粉碎成粉末而得；
（2）按重量份取硅酸盐水泥，加适量水搅拌均匀，得水泥浆；
（3）将水泥浆与其余原料混匀，得浆料；
（4）将浆料投入墙板挤压成型机成型、切割、自然养护，即得；
所述的一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺，其特征在于：所述的矾矿尾渣细度为80-100目，所述的铁矾土细度为100-180目，所述的贝壳粉细度为80-100目，所述的泥炭土细度为80-180目，所述的耐火粘土细度为100-200目。
本发明的有益效果为：草木灰是植物体燃烧后的灰烬，取材容易，成本低廉。本发明强度高、抗冲击性能好，并具有隔音、保温、防水等优点，材料硬化干燥后的容重在300～600kg/m3的范围。
具体实施方式
实施例1：
一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺， 
（1）配料：所述的轻质建筑用隔墙板是由下述重量份（kg）的原料制得：
贝壳粉26，硅酸盐水泥30，矾矿尾渣30，草木灰15，铁矾土5，磷石膏粉5，泥炭土1，耐火粘土2，纳米矿物改性混合粉4，壳聚糖0.5，生石灰2，浓度为35%的双氧水溶液9，水适量；
所述的纳米矿物改性混合粉由2重量份石英砂，5重量份海泡石粉、1重量份菱镁矿石粉混匀后，于800℃下烧损5小时，后研磨成纳米粉末，拌入相当于粉体重量2%的乙酰柠檬酸三乙酯、1%的氯化石蜡拌搅均匀，烘干，粉碎成粉末而得；
（2）按重量份取硅酸盐水泥，加适量水搅拌均匀，得水泥浆；
（3）将水泥浆与其余原料混匀，得浆料；
（4）将浆料投入墙板挤压成型机成型、切割、自然养护，即得；
所述的矾矿尾渣细度为100目，所述的铁矾土细度为100目，所述的贝壳粉细度为100目，所述的泥炭土细度为180目，所述的耐火粘土细度为100目。
本实施例的容重为510Kg/m3 ，抗压强度为6.8MPa。     
实施例2：
一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺，
（1）配料：所述的轻质建筑用隔墙板是由下述重量份（kg）的原料制得：
建筑拆迁砖石垃圾粉10，贝壳粉28，硅酸盐水泥30，矾矿尾渣30，草木灰15，铁矾土3，磷石膏粉3，泥炭土1，耐火粘土1，纳米矿物改性混合粉2，壳聚糖1，生石灰1，浓度为35%的双氧水溶液6，水25；
所述的建筑拆迁砖石垃圾粉是将建筑拆迁砖石垃圾于800-900℃下煅烧4-6小时，后研磨，加入1-2％硬酯酸锌，1-2％双十八烷基胺、1-2%扩散剂MF、3-4%甲基硅油，混合烘干粉碎，过100-200目筛而得；
所述的纳米矿物改性混合粉由4重量份石英砂，5重量份海泡石粉、1重量份菱镁矿石粉混匀后，于800℃下烧损5小时，后研磨成纳米粉末，拌入相当于粉体重量2%的乙酰柠檬酸三乙酯、1%的氯化石蜡拌搅均匀，烘干，粉碎成粉末而得；
（2）按重量份取硅酸盐水泥，加适量水搅拌均匀，得水泥浆；
（3）将水泥浆与其余原料混匀，得浆料；
（4）将浆料投入墙板挤压成型机成型、切割、自然养护，即得；
所述的矾矿尾渣细度为80目，所述的铁矾土细度为180目，所述的贝壳粉细度为80目，所述的泥炭土细度为80目，所述的耐火粘土细度为200目。
本实施例的容重为500Kg/m3 ，抗压强度为6.2MPa。

Claims (2)

1.一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺，其特征在于：
（1）配料：所述的轻质建筑用隔墙板是由下述重量份的原料制得：
贝壳粉26-28，硅酸盐水泥25-30，矾矿尾渣28-30，草木灰10-15，铁矾土3-5，磷石膏粉3-5，泥炭土1-2，耐火粘土1-2，纳米矿物改性混合粉2-4，壳聚糖0.5-1，生石灰1-2，浓度为25-35%的双氧水溶液6-9，水适量；
所述的纳米矿物改性混合粉由2-4重量份石英砂，5-8重量份海泡石粉、1-2重量份菱镁矿石粉混匀后，于700-800℃下烧损4-5小时，后研磨成纳米粉末，拌入相当于粉体重量1-2%的乙酰柠檬酸三乙酯、1-2%的氯化石蜡拌搅均匀，烘干，粉碎成粉末而得；
（2）按重量份取硅酸盐水泥，加适量水搅拌均匀，得水泥浆；
（3）将水泥浆与其余原料混匀，得浆料；
（4）将浆料投入墙板挤压成型机成型、切割、自然养护，即得。
2.根据权利要求1所述的一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺，其特征在于：所述的矾矿尾渣细度为80-100目，所述的铁矾土细度为100-180目，所述的贝壳粉细度为80-100目，所述的泥炭土细度为80-180目，所述的耐火粘土细度为100-200目。
CN201210353940.XA 2012-09-21 2012-09-21 一种原料含有贝壳粉的轻质建筑用隔墙板材的制备工艺 Expired - Fee Related CN102898095B (zh)