CN102875912A - 一种由废旧电器类聚苯乙烯材料制备的高性能聚苯乙烯合金及其制备方法和应用 - Google Patents
一种由废旧电器类聚苯乙烯材料制备的高性能聚苯乙烯合金及其制备方法和应用 Download PDFInfo
- Publication number
- CN102875912A CN102875912A CN2012103281915A CN201210328191A CN102875912A CN 102875912 A CN102875912 A CN 102875912A CN 2012103281915 A CN2012103281915 A CN 2012103281915A CN 201210328191 A CN201210328191 A CN 201210328191A CN 102875912 A CN102875912 A CN 102875912A
- Authority
- CN
- China
- Prior art keywords
- electrical equipment
- waste electrical
- preparation
- equipment class
- polystyrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
性质 | 方法 | 单位 | 数据 |
比重 | ASTM D792 | — | 1.16 |
模收缩 | ASTM D955 | % | 0.2~0.4 |
拉伸强度 | ASTM D638 | Kgf/c㎡ | 420 |
弯曲强度 | ASTM D790 | Kgf/c㎡ | 550 |
延伸率 | ASTM D638 | % | 40 |
弯曲模数 | ASTM D790 | Kgf/c㎡ | 11500 |
缺口冲击强度(1/8")(23℃) | ASTM D256 | Kg·㎝/㎝ | 9.2 |
热变形温度 | ASTM D648 | ℃ | 80 |
耐燃性 | UL94 | (1/8") | V0 |
干燥温度 | — | ℃ | 70 |
干燥时间 | — | HR | 4 |
熔融温度 | — | ℃ | 190~230 |
建议模温 | — | ℃ | 50 |
性质 | 方法 | 单位 | 数据 |
比重 | ASTM D792 | — | 1.16 |
模收缩 | ASTM D955 | % | 0.2~0.4 |
拉伸强度 | ASTM D638 | Kgf/c㎡ | 420 |
弯曲强度 | ASTM D790 | Kgf/c㎡ | 550 |
延伸率 | ASTM D638 | % | 40 |
弯曲模数 | ASTM D790 | Kgf/c㎡ | 11000 |
缺口冲击强度(1/8")(23℃) | ASTM D256 | Kg·㎝/㎝ | 9 |
热变形温度 | ASTM D648 | ℃ | 80 |
耐燃性 | UL94 | (1/8") | V0 |
干燥温度 | — | ℃ | 70 |
干燥时间 | — | HR | 4 |
熔融温度 | — | ℃ | 190~230 |
建议模温 | — | ℃ | 50 |
Claims (8)