CN102875046B - 一种菱镁水泥用高效粉体型缓凝剂 - Google Patents
一种菱镁水泥用高效粉体型缓凝剂 Download PDFInfo
- Publication number
- CN102875046B CN102875046B CN201210408722.1A CN201210408722A CN102875046B CN 102875046 B CN102875046 B CN 102875046B CN 201210408722 A CN201210408722 A CN 201210408722A CN 102875046 B CN102875046 B CN 102875046B
- Authority
- CN
- China
- Prior art keywords
- parts
- powder type
- type retarder
- raw material
- magnesite cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明是一种菱镁水泥用高效粉体缓凝剂,是由石膏粉、氯化锌、硼酸钠、硫酸钙和粉煤灰按照一定比例混合,经过粉磨、均化后得到的均匀粉体,其添加量为菱镁水泥用原料氧化镁的0.6~1.2%。本发明优异效果是:1)本粉体缓凝剂能够显著延缓菱镁水泥的凝结时间,尤其在夏季高温生产时,通过延缓凝结时间,使制品充分水化完全,防止制品裂缝,降低菱镁水泥次品率;2)本粉体缓凝剂相较于现有水剂型缓凝剂缓凝时间提高10%,并且粉体缓凝剂较好的解决了产品在使用安全和运输安全方面存在的隐患。
Description
技术领域
本发明涉及化工材料技术领域,具体地说是一种菱镁水泥用高效粉体型缓凝剂。
背景技术
菱镁水泥主要是由活性MgO与调和剂溶液(MgCl2溶液)拌合而成,得到一种碱式氯化镁固化体,外表和强度似波特兰水泥,故称之为氯氧镁水泥,又叫菱镁水泥。其优点是:制品不需要潮湿养护;强度增长快,抗折、抗压强度高;弱碱性、低腐蚀性;对有机和无机材料或纤维具有较好的胶结性等特点广泛应用于各类板材(包括:防火板、保温板、装饰板、门芯板),大型器械及产品的包装箱,农业温室大棚支架,市政大小型工艺品,各类养殖棚舍,沼气池,通风管道、波瓦等。
菱镁水泥具有硬化快、强度高的特点,尤其在夏季高温(25℃~40℃)生产时硬化更快,往往来不及成型已经硬化,给生产操作带来困难;菱镁水泥水化时会放出大量的热量,当夏天温度高时生产出的菱镁制品的温度甚至达到80℃,当制品温度过高时生产的制品将不再是5.1.8相,而是非常不稳定的 9.1.5相,而且强度不高;同时温度过高时生产的菱镁水泥会出现返卤、变形、强度不高等问题。
所以在夏季高温生产时通常在菱镁水泥中加入缓凝剂,目的是为了分散制品水化热量,延长水泥的水化硬化时间,使新拌菱镁水泥料浆能在较长时间内保持塑性,从而调节新拌水泥的凝结时间。
发明内容
本发明的技术任务是解决现有技术的不足,提供一种菱镁水泥用高效粉体型缓凝剂。
本发明的技术方案是按以下方式实现的,菱镁水泥用高效粉体型缓凝剂是由以下重量配比的原料制成:
石膏粉20~35份、氯化锌15~30份、硼酸钠5~25份、硫酸钙20~30份、粉煤灰4~15份;
制备方法如下:
按重量配比称取各原料混合搅拌均匀,加入粉磨机,粉磨成细度在150目~200目的粉体,再经过均化设备进一步均化得到成品。
所述的缓凝剂是由以下重量配比的原料制成:
石膏粉25~30份、氯化锌20~25份、硼酸钠15~20份、硫酸钙22~26份、
粉煤灰7~12份。
所述的缓凝剂,是由以下重量配比的原料制成:
石膏粉28份、氯化锌23份、硼酸钠8份、硫酸钙24份、粉煤灰10份。
本发明的菱镁水泥用高效粉体型缓凝剂具有以下突出的有益效果:能够显著延长菱镁水泥的凝集时间,经过试验验证,本发明粉体缓凝剂相较于现有水剂型缓凝剂缓凝时间提高10份以上。本发明的缓凝剂产品具有很好的市场应用价值,适合广泛推广。
具体实施方式
实施例1
本发明的菱镁水泥用高效粉体型缓凝剂是由以下重量配比的原料制成:
石膏粉20份、氯化锌15份、硼酸钠5份、硫酸钙20份、粉煤灰4份;
制备方法如下:
按重量配比称取各原料混合搅拌均匀,加入粉磨机,粉磨成细度在150目~200目的粉体,再经过均化设备进一步均化得到成品;
实施例2
本发明的菱镁水泥用高效粉体型缓凝剂是由以下重量配比的原料制成:
石膏粉35份、氯化锌30份、硼酸钠25份、硫酸钙30份、粉煤灰15份;
制备方法与实施例1相同;
实施例3
本发明的菱镁水泥用高效粉体型缓凝剂是由以下重量配比的原料制成:
石膏粉25份、氯化锌20份、硼酸钠15份、硫酸钙22份、粉煤灰7份;
制备方法与实施例1相同;
实施例4
本发明的菱镁水泥用高效粉体型缓凝剂是由以下重量配比的原料制成:
石膏粉30份、氯化锌25份、硼酸钠20份、硫酸钙26份、粉煤灰12份;
制备方法与实施例1相同;
实施例5
本发明的菱镁水泥用高效粉体型缓凝剂是由以下重量配比的原料制成:
石膏粉28份、氯化锌23份、硼酸钠12份、硫酸钙29份、粉煤灰8份;
实施例6:
本发明的菱镁水泥用高效粉体型缓凝剂是由以下重量配比的原料制成:
石膏粉33份、氯化锌21份、硼酸钠 16份、硫酸钙26份、粉煤灰4份;
实施例7:
本发明的菱镁水泥用高效粉体型缓凝剂是由以下重量配比的原料制成:
石膏粉30份、氯化锌22份、硼酸钠14份、硫酸钙28份、粉煤灰6份;
实施效果:
按照如下配比制备菱镁标准试块:
称取轻烧氧化镁450g,标准砂1350g,卤水450 g(卤水浓度为1.22g/cm3),加入实施例1-4制备的粉体缓凝剂,添加量为轻烧氧化镁的1%,即4.5g。试验温度为27℃。通过测定菱镁水泥的初凝时间查看应用效果,详见表1:
表1 缓凝效果对比试验
样品 | 空白试验 | 水剂型缓凝剂 | 实施例1 | 实施例2 | 实施3 | 实施4 |
添加量份 | 0 | 0.7 | 0.8 | 0.9 | 1 | 1.2 |
缓凝时间(min) | 45 | 140 | 153 | 149 | 155 | 160 |
通过以上试验对比可以看出,本粉体型缓凝剂加入菱镁水泥后能够显著延缓菱镁水泥的初凝时间,相较于现在应用的水剂型缓凝剂缓凝时间也提高了10份以上,以施例3效果最为显著。
本发明的缓凝剂尤其在夏季生产时,给生产操作足够时间,同时减少制品因固化时间短放热快产生的裂纹。
除本发明的说明书公开的技术特征外均为本专业技术人员的公职技术。
Claims (3)
1.一种菱镁水泥用高效粉体型缓凝剂,其特征在于,是由以下重量配比的原料制成:
石膏粉20~35份、氯化锌15~30份、硼酸钠5~25份、硫酸钙20~30份、粉煤灰4~15份;
制备方法如下:
按重量配比称取各原料混合搅拌均匀,加入粉磨机,粉磨成细度在150目~200目的粉体,再经过均化设备进一步均化得到成品。
2.根据权利要求1所述的缓凝剂,其特征在于是由以下重量配比的原料制成:
石膏粉25~30份、氯化锌20~25份、硼酸钠15~20份、硫酸钙22~26份、粉煤灰7~12份。
3.根据权利要求1所述的缓凝剂,其特征在于是由以下重量配比的原料制成:
石膏粉28份、氯化锌23份、硼酸钠8份、硫酸钙24份、粉煤灰10份。