CN102851878A - 海藻纤维可吸收医用辅料及其制作工艺 - Google Patents

海藻纤维可吸收医用辅料及其制作工艺 Download PDF

Info

Publication number
CN102851878A
CN102851878A CN2012103595683A CN201210359568A CN102851878A CN 102851878 A CN102851878 A CN 102851878A CN 2012103595683 A CN2012103595683 A CN 2012103595683A CN 201210359568 A CN201210359568 A CN 201210359568A CN 102851878 A CN102851878 A CN 102851878A
Authority
CN
China
Prior art keywords
auxiliary material
acupuncture
medical auxiliary
net
alginate fibre
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103595683A
Other languages
English (en)
Other versions
CN102851878B (zh
Inventor
夏延致
王斌
魏立
姜明
鞠海虹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zibo Nachl Biological Technology Co ltd
Qingdao University
Original Assignee
ZIBO NAIQIER TEXTILE TECHNOLOGY DEVELOPMENT CO LTD
Qingdao University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZIBO NAIQIER TEXTILE TECHNOLOGY DEVELOPMENT CO LTD, Qingdao University filed Critical ZIBO NAIQIER TEXTILE TECHNOLOGY DEVELOPMENT CO LTD
Priority to CN201210359568.3A priority Critical patent/CN102851878B/zh
Publication of CN102851878A publication Critical patent/CN102851878A/zh
Application granted granted Critical
Publication of CN102851878B publication Critical patent/CN102851878B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种海藻纤维可吸收医用辅料及其制作工艺，属于医用辅料领域。所述的海藻纤维可吸收医用辅料，其特征在于，该辅料采用海藻纤维和聚乳酸纤维针刺混纺，以重量百分比计，织物中各原料组分的含量为：海藻纤维70～100％，聚乳酸纤维0～30%。本发明提供了一种亲肤抑菌、吸湿透气、安全环保的海藻聚乳酸可吸收医用辅料及其制作工艺。

Description

海藻纤维可吸收医用辅料及其制作工艺
技术领域
本发明涉及一种海藻纤维可吸收医用辅料及其制作工艺，属于医用辅料领域。 
背景技术
医用敷料是用以覆盖伤口或其他损害的医用材料，传统方式对伤口的处理主要是用纱布覆盖来吸收创面的渗出液和防止脏东西的侵入而引起感染，但是这种方式因不能保湿和粘连创面，更换时易再次损伤创口而引起剧烈疼痛。现在已经出现了一些用新材料新方法制成的敷料，但还没有一种使用的是纯天然可吸收安全可靠的材料。 
发明内容
本发明要提供一种亲肤抑菌、吸湿透气、安全环保的海藻聚乳酸可吸收医用辅料及其制作工艺。 
所述的海藻纤维可吸收医用辅料，其特征在于，该辅料采用海藻纤维和聚乳酸纤维针刺混纺，以重量百分比计，织物中各原料组分的含量为：海藻纤维：70~100％，聚乳酸纤维0~30%。 
权利要求1所述的医用辅料的制作工艺，其特征在于，由以下步骤制得：纤维开松—混合—梳理—成网—叠网—合并预针刺—主针刺—后整理—切边—检验-成品。 
所述的合并预针刺和主针刺针刺深度范围为3-7mm；针刺频率为300-600次/分。 
所述的后整理在100~130℃下整理成卷。 
所述的混合时间为40~50分钟，混合时摇臂的转速为40转/分。 
所述的成网工艺参数：锡林转速，200-350转/分；斩刀，摆动次数在600-700次/分。 
纤维成网后，进入合并预针刺和主针刺工序，针刺深度一般范围为3-7mm。 
后整理是，利用针刺使纤维缠结成布，再对无纺布进行后道压光、热定型，在120℃温度下对其进行定型，使无纺布表面自然形成一层膜，再经检验，最后卷曲成卷。 
本发明提供的医用辅料充分利用海藻纤维的特性，具有亲肤抑菌、吸湿透气、安全环保的特点，既能快速吸收伤口的渗出液，又能避免创面脱水，具有一定的保湿性，同时还能避免与创口粘连，大大减少更换时的痛苦，使创口能尽快愈合。提供的制备方法，充分结合所用纤维的特性，使所用纤维能针刺成型，并且其成品率较高。 
具体实施方式
以下结合实施例对本发明做进一步描述。 
实施例1 
所述的海藻纤维可吸收医用辅料，以重量百分比计，海藻纤维为70%，聚乳酸纤维为30%； 
并由以下步骤制得：纤维开松—混合—梳理—成网—叠网—合并预针刺—主针刺—后整理—切边—检验—成品。其中针刺的范围是7mm，针刺频率为600次/分，混合时间为50分钟，混合时摇臂的转速为40转/分。锡林转速350转/分；斩刀摆动次数在700次/分，后整理温度为130℃。 
经检验，所制得的医用辅料： 
Figure BDA00002184935300021
Figure 20121035956831000021
实施例2 
所述的海藻纤维可吸收医用辅料，以重量百分比计，海藻纤维为100%，聚乳酸纤维为0%； 
并由以下步骤制得：纤维开松—混合—梳理—成网—叠网—合并预针刺—主针刺—后整理—切边—检验—成品。其中针刺的范围是3mm，针刺频率为300次/分，为40分钟，混合时摇臂的转速为40转/分。锡林转速，200转/分；斩刀，摆动次数在600次/分，后整理温度为100℃。 
经检验，所制得的医用辅料： 
Figure BDA00002184935300032
Figure 20121035956831000022
实施例3 
所述的海藻纤维可吸收医用辅料，以重量百分比计，海藻纤维为99%，聚乳酸纤维为1%； 
并由以下步骤制得：纤维开松—混合—梳理—成网—叠网—合并预针刺—主针刺—后整理—切边—检验—成品。其中针刺的范围是6mm，针刺频率为400次/分，混合时间为45分钟，混合时摇臂的转速为40转/分。锡林转速300转/分；斩刀,摆动次数在650次/分，后整理温度为125℃。 
经检验，所制得的医用辅料： 
Figure BDA00002184935300042
实施例4 
所述的海藻纤维可吸收医用辅料，以重量百分比计，海藻纤维为85%，聚乳酸纤维为15%； 
并由以下步骤制得：纤维开松—混合—梳理—成网—叠网—合并预针刺—主针刺—后整理—切边—检验—成品。其中针刺的范围是4mm，针刺频率为500 次/分，混合时间为45分钟，混合时摇臂的转速为40转/分。锡林转速250转/分；斩刀摆动次数在650次/分，后整理温度为120℃。 
经检验，所制得的医用辅料 
Figure BDA00002184935300051
实施例5：所述的海藻纤维可吸收医用辅料，以重量百分比计，海藻纤维为95%，聚乳酸纤维为5%；并由以下步骤制得：纤维开松—混合—梳理—成网—叠网—合并预针刺—主针刺—后整理—切边—检验—成品。其中针刺的范围是6mm，针刺频率为550为50分钟，混合时摇臂的转速为40转/分。锡林转速350转/分；斩刀摆动次数在600次/分，后整理温度为120℃。 
经检验，所制得的医用辅料： 
Figure 3

Claims (6)

1.一种海藻纤维可吸收医用辅料，其特征在于，该辅料采用海藻纤维和聚乳酸纤维针刺混纺，以重量百分比计，织物中各原料组分的含量为：海藻纤维：70~100％，聚乳酸纤维0~30%。
2.一种权利要求1所述的医用辅料的制作工艺，其特征在于，由以下步骤制得：纤维开松—混合—梳理—成网—叠网—合并预针刺—主针刺—后整理—切边—检验—成品。
3.根据权利要求2所述的制备工艺，其特征在于，所述的合并预针刺和主针刺针刺深度范围为3-7mm；针刺频率为300-600次/分。
4.根据权利要求2所述的制备工艺，其特征在于，所述的后整理在100~130℃下整理成卷。
5.根据权利要求2所述的制备工艺，其特征在于，所述的混合时间为40~50分钟，混合时摇臂的转速为40转/分。
6.根据权利要求2所述的制备工艺，其特征在于，所述的成网工艺参数：锡林转速，200-350转/分；斩刀，摆动次数在600-700次/分。
CN201210359568.3A 2012-09-24 2012-09-24 海藻纤维可吸收医用辅料及其制作工艺 Expired - Fee Related CN102851878B (zh)