CN102850039B - Micro powder polished brick and its processing method - Google Patents
Micro powder polished brick and its processing method Download PDFInfo
- Publication number
- CN102850039B CN102850039B CN201110180786.6A CN201110180786A CN102850039B CN 102850039 B CN102850039 B CN 102850039B CN 201110180786 A CN201110180786 A CN 201110180786A CN 102850039 B CN102850039 B CN 102850039B
- Authority
- CN
- China
- Prior art keywords
- powder
- brick
- starting material
- micro powder
- feldspar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a micro powder polished brick and its processing method. The brick is prepared from (by weight part) Guangdong ball clay 21-35, Hunan low-temperature sand 23-37, potash feldspar 13-27, pagodastone 3-9, Hebei soil 1-5, Yantai feldspar 3-17 and calcined kaolin 1-5. The processing method includes finely selecting raw materials, removing iron, preparing materials, ball milling, processing micro powder, forming, drying, sintering, polishing, sorting and packaging. The brick has high density, good glossiness and strong antifouling capability; and during use, it has low water absorption rate, good antifouling resistance, strong aging resistance, easy cleaning and maintenance, good corrosion resistance and good durability.
Description
Technical field
The present invention relates to a kind of building and ornament materials, particularly a kind of micro powder polished brick and working method thereof.
Background technology
Along with improving constantly of living standards of the people and aesthetic conceptions, share of market high-quality, multi-functional building material product increases gradually, and production development tends to diversification, fashion-orientation, environment protection health gradually.Natural marble had once won people's favor with its abundant color, but its a large amount of exploitations, have brought very large destruction to environment, as natural marble Gao Bisheng, to the load larrying member of the building higher requirement of having deducted a percentage itself, in addition, find after deliberation most of natural stone beautiful in colour, its radioactivity is very strong, have a strong impact on health of people, and lithotome is to form under normal pressure, in its structure, there is more bubble, so product impermeabilisation weak effect.Therefore, client needs decorative effect, glossiness identical with lithotome, but radiation is low, and property indices is all better than the product innovation of lithotome, though the polished tile of the natural-like stone occurring on market approaches to a certain extent lithotome on decorative effect, but still exist a certain distance ，Ge enterprise to think always, constantly carry out technical renovation and exploration, expectation acquisition all directions performance is better, the product of lower-cost natural-like stone.
Summary of the invention
For the weak point existing in the problems referred to above, the invention provides that a kind of to have density high, micro powder polished brick and the working method thereof of the feature such as glossiness is good.
For achieving the above object, the invention provides a kind of micro powder polished brick, described brick face is made according to parts by weight scope by following raw materials according: Guangdong ball clay 21～35, Hunan low temperature sand 23～37, potassium felspar sand 13～27, agalmatolite 3～9, Hebei soil 1～5, Yantai feldspar 3～17, calcined kaolin 1～5.
Described brick face is made according to parts by weight scope by following raw materials according: Guangdong ball clay 24～31, Hunan low temperature sand 27～33, potassium felspar sand 17～23, agalmatolite 5～7, Hebei soil 2～4, Yantai feldspar 6～11, calcined kaolin 2～3.
Described brick face is made according to weight part numerical value by following raw materials according: Guangdong ball clay 28, Hunan low temperature sand 30, potassium felspar sand 20, agalmatolite 6, Hebei soil 3, Yantai feldspar 10, calcined kaolin 3.
In addition, the present invention also provides a kind of working method of micro powder polished brick simultaneously, comprises the following steps:
A, picking of raw material: starting material carry out block-by-block picking after entering factory, remove the starting material with impurity;
B, deironing: starting material are broken into fine powder by the deironing of high deironing device automated cycle;
C, batching: starting material are proportionally mixed;
D, ball milling: the starting material of having filled a prescription enter to add water after ball mill and be ground to 250 order mud;
E, powder process: the spray-dried tower of ground mud is made half dry-pressing granular powder material;
F, micro mist processing: particle powder is polished into ultra tiny powder through special-purpose powder beater;
G, moulding: through special machinery cloth, become different patterns by great tonnage press compression moulding different colours micro mist;
H, dry: drying kiln is got rid of moisture;
I, burn till: roller kiln high-temperature roasting, the temperature of firing is 1200 ℃;
J, polishing: automatic polishing machinery is thrown to horizontal surface firing product surface, 90 ° of luminance brightness >;
K, pick: product selecting pattern and grade after polishing.
Compared with prior art, the present invention has the following advantages:
Micro powder polished brick provided by the invention, brick face is made according to parts by weight scope by following raw materials according: Guangdong ball clay 21～35, Hunan low temperature sand 23～37, potassium felspar sand 13～27, agalmatolite 3～9, Hebei soil 1～5, Yantai feldspar 3～17, calcined kaolin 1～5.The working method of above-mentioned micro powder polished brick comprises picking of raw material, deironing, batching, ball milling, powder process, micro mist processing, moulding, is dried, burns till, polishing, pick and packing.The present invention is by selecting raw material, proportioning and suitable complete processing, obtained the brick body that density is high, glossiness good, stain resistance is strong, it in use has, and water-intake rate is low, didirtresistance good, ageing resistance is strong, easy cleaning and maintenance and have the feature of good corrosion resistance, durable.
Embodiment
The invention provides a kind of micro powder polished brick, brick face is made according to parts by weight scope by following raw materials according: Guangdong ball clay 21～35, Hunan low temperature sand 23～37, potassium felspar sand 13～27, agalmatolite 3～9, Hebei soil 1～5, Yantai feldspar 3～17, calcined kaolin 1～5.
The working method of above-mentioned micro powder polished brick, comprises the following steps:
A, picking of raw material: starting material carry out block-by-block picking after entering factory, remove the starting material with impurity;
B, deironing: starting material are broken into fine powder by the deironing of high deironing device automated cycle;
C, batching: starting material are proportionally mixed;
D, ball milling: the starting material of having filled a prescription enter to add water after ball mill and be ground to 250 order mud;
E, powder process: the spray-dried tower of ground mud is made half dry-pressing granular powder material;
F, micro mist processing: particle powder is polished into ultra tiny powder through special-purpose powder beater;
G, moulding: through special machinery cloth, become different patterns by great tonnage press compression moulding different colours micro mist;
H, dry: drying kiln is got rid of moisture;
I, burn till: roller kiln high-temperature roasting, the temperature of firing is 1200 ℃;
J, polishing: automatic polishing machinery is thrown to horizontal surface firing product surface, 90 ° of luminance brightness >;
K, pick: product selecting pattern and grade after polishing.
Embodiment 1
The invention provides a kind of micro powder polished brick, brick face is made according to parts by weight scope by following raw materials according: Guangdong ball clay 24～31, Hunan low temperature sand 27～33, potassium felspar sand 17～23, agalmatolite 5～7, Hebei soil 2～4, Yantai feldspar 6～11, calcined kaolin 2～3.
The working method of above-mentioned micro powder polished brick, comprises the following steps:
A, picking of raw material: starting material carry out block-by-block picking after entering factory, remove the starting material with impurity;
B, deironing: starting material are broken into fine powder by the deironing of high deironing device automated cycle;
C, batching: starting material are proportionally mixed;
D, ball milling: the starting material of having filled a prescription enter to add water after ball mill and be ground to 250 order mud;
E, powder process: the spray-dried tower of ground mud is made half dry-pressing granular powder material;
F, micro mist processing: particle powder is polished into ultra tiny powder through special-purpose powder beater;
G, moulding: through special machinery cloth, become different patterns by great tonnage press compression moulding different colours micro mist;
H, dry: drying kiln is got rid of moisture;
I, burn till: roller kiln high-temperature roasting, the temperature of firing is 1200 ℃;
J, polishing: automatic polishing machinery is thrown to horizontal surface firing product surface, 90 ° of luminance brightness >;
K, pick: product selecting pattern and grade after polishing.
Embodiment 2
The invention provides a kind of micro powder polished brick, brick face is made according to weight part numerical value by following raw materials according: Guangdong ball clay 28, Hunan low temperature sand 30, potassium felspar sand 20, agalmatolite 6, Hebei soil 3, Yantai feldspar 10, calcined kaolin 3.
The working method of above-mentioned micro powder polished brick, comprises the following steps:
A, picking of raw material: starting material carry out block-by-block picking after entering factory, remove the starting material with impurity;
B, deironing: starting material are broken into fine powder by the deironing of high deironing device automated cycle;
C, batching: starting material are proportionally mixed;
D, ball milling: the starting material of having filled a prescription enter to add water after ball mill and be ground to 250 order mud;
E, powder process: the spray-dried tower of ground mud is made half dry-pressing granular powder material;
F, micro mist processing: particle powder is polished into ultra tiny powder through special-purpose powder beater;
G, moulding: through special machinery cloth, become different patterns by great tonnage press compression moulding different colours micro mist;
H, dry: drying kiln is got rid of moisture;
I, burn till: roller kiln high-temperature roasting, the temperature of firing is 1200 ℃;
J, polishing: automatic polishing machinery is thrown to horizontal surface firing product surface, 90 ° of luminance brightness >;
K, pick: product selecting pattern and grade after polishing.
Only as described above, be only preferred embodiment of the present invention, such as professional who are familiar with this art. after understanding technique means of the present invention, natural energy, according to actual needs, is changed under instruction of the present invention.Therefore all equal variation and modifications of doing according to the present patent application the scope of the claims, once should still remain within the scope of the patent.
Claims (4)
1. a micro powder polished brick, it is characterized in that, described brick face is made according to parts by weight scope by following raw materials according: Guangdong ball clay 21～35, Hunan low temperature sand 23～37, potassium felspar sand 13～27, agalmatolite 3～9, Hebei soil 1～5, Yantai feldspar 3～17, calcined kaolin 1～5.
2. micro powder polished brick as claimed in claim 1, it is characterized in that, described brick face is made according to parts by weight scope by following raw materials according: Guangdong ball clay 24～31, Hunan low temperature sand 27～33, potassium felspar sand 17～23, agalmatolite 5～7, Hebei soil 2～4, Yantai feldspar 6～11, calcined kaolin 2～3.
3. micro powder polished brick as claimed in claim 1 or 2, it is characterized in that, described brick face is made according to weight part numerical value by following raw materials according: Guangdong ball clay 28, Hunan low temperature sand 30, potassium felspar sand 20, agalmatolite 6, Hebei soil 3, Yantai feldspar 10, calcined kaolin 3.
4. the working method of micro powder polished brick as claimed in claim 1, is characterized in that, comprises the following steps:
A, picking of raw material: starting material carry out block-by-block picking after entering factory, remove the starting material with impurity;
B, deironing: starting material are broken into fine powder by the deironing of high deironing device automated cycle;
C, batching: starting material are proportionally mixed;
D, ball milling: the starting material of having filled a prescription enter to add water after ball mill and be ground to 250 order mud;
E, powder process: the spray-dried tower of ground mud is made half dry-pressing granular powder material;
F, micro mist processing: particle powder is polished into ultra tiny powder through special-purpose powder beater;
G, moulding: through special machinery cloth, become different patterns by great tonnage press compression moulding different colours micro mist;
H, dry: drying kiln is got rid of moisture;
I, burn till: roller kiln high-temperature roasting, the temperature of firing is 1200 ℃;
J, polishing: automatic polishing machinery is thrown to horizontal surface firing product surface, 90 ° of luminance brightness >;
K, pick: product selecting pattern and grade after polishing.