CN102828068A - 锌铝合金丝 - Google Patents

锌铝合金丝 Download PDF

Info

Publication number
CN102828068A
CN102828068A CN2012103156440A CN201210315644A CN102828068A CN 102828068 A CN102828068 A CN 102828068A CN 2012103156440 A CN2012103156440 A CN 2012103156440A CN 201210315644 A CN201210315644 A CN 201210315644A CN 102828068 A CN102828068 A CN 102828068A
Authority
CN
China
Prior art keywords
alloy wire
aluminum alloy
zinc
zinc aluminum
impurity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103156440A
Other languages
English (en)
Inventor
张新华
张若煜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Shaoxing
Original Assignee
University of Shaoxing
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Shaoxing filed Critical University of Shaoxing
Priority to CN2012103156440A priority Critical patent/CN102828068A/zh
Publication of CN102828068A publication Critical patent/CN102828068A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种锌铝合金丝，属于锌铝合金丝生产的技术领域，包含有以下重量百分比的组分：铝10-45%，总量不超过0.03%的杂质，余量为锌。本发明锌铝合金丝具有强度高（大于110N/mm2）、延伸性好（断后延伸率28%以上）、导电性能好（电阻率低于50mΩ·mm2/m）、熔点高（固相线380℃）的优点。本发明锌铝合金丝具有更大的粘附强度和耐蚀性，其抗腐蚀效果更好，施工性能更为优越。

Description

锌铝合金丝
技术领域
本发明公开一种锌铝合金丝，属于锌铝合金丝生产的技术领域。
背景技术
锌铝合金是国际上近几年来开发的一种新型材料，主要应用于金属表面的热喷涂工艺。同纯锌丝和纯铝丝相比，锌铝合金丝具有更大的粘附强度和耐蚀性，其抗腐蚀效果更好，施工性能更为优越。锌铝合金涂层作为阳极保护，可使钢铁构件的寿命延长5－10倍，因而广泛地应用于舰船、水利工程、铁路桥梁、地下金属管道的防腐。
锌铝合金丝，主要用作金属化薄膜电容器端面喷涂金属材料（简称喷金料）。随着金属化薄膜电容器本身的发展，对喷金料不断提出新的要求，致使当前的锌铝合金丝已无法适应这些要求，本案由此产生。
发明内容
本发明的目的是提供一种抗腐蚀效果更好的锌铝合金丝。
为达到上述目的，本发明所采用的技术方案为：
    一种锌铝合金丝，包含有以下重量百分比的组分：铝10-45%，总量不超过0.03%的杂质，余量为锌。
    所述铝为35%，总量不超过0.03%的杂质，余量为锌。
所述杂质为铁0.002-0.01%、锡＜0.001%、铅＜0.003%、铜＜0.01%。
所述杂质为铁0.002-0.01%、锡＜0.001%、铜＜0.01%。
所述杂质为铁0.002-0.01%、铅＜0.01%、铜＜0.01%。
本发明锌铝合金丝具有强度高（大于110N/mm2）、延伸性好（断后延伸率28%以上）、导电性能好（电阻率低于50mΩ·mm2/m）、熔点高（固相线380℃）的优点。本发明锌铝合金丝具有更大的粘附强度和耐蚀性，其抗腐蚀效果更好，施工性能更为优越。
具体实施方式
    以下结合实施例对本发明进行进一步的说明，但本发明并不受以下实施例所限制。
    实施例1
    本发明锌铝合金丝，包含有以下重量百分比的组分：铝35%，总量不超过0.03%的杂质，余量为锌。
     其中，杂质为铁0.008%、锡0.0006%、铅0.001%、铜0.008%。
本发明锌铝合金丝的制造工艺，包括如下步骤：
（1）选料；
（2）在熔融状态的锌液中加入铝块进行充分混合熔炼后，再进行铸锻，铸锻时连铸炉的温度为500℃；液高200mm；冷却水压为0.2MPa；
（3）挤压；
（4）时效；
（5）拉伸：退火炉温200℃，时间4小时，拉伸速度为800mm/s；
（6）时效；
（7）成品包装。
实施例2
    本发明锌铝合金丝，包含有以下重量百分比的组分：铝10%，总量不超过0.03%的杂质，余量为锌。
其中，杂质为铁0.01%、锡0.0005%、铜0.0075%。
本发明锌铝合金丝的制造工艺，包括如下步骤：
（1）选料；
（2）在熔融状态的锌液中加入铝块进行充分混合熔炼后，再进行铸锻，铸锻时连铸炉的温度为600℃；液高300mm；冷却水压为0.4MPa；
（3）挤压；
（4）时效；
（5）拉伸：退火炉温400℃，时间2小时，拉伸速度为2000mm/s；
（6）时效；
（7）成品包装。
实施例3
    本发明锌铝合金丝，包含有以下重量百分比的组分：铝45%，总量不超过0.03%的杂质，余量为锌。
其中，杂质为铁0.006%、铅0.003%、铜0.008%。
本发明锌铝合金丝的制造工艺，包括如下步骤：
（1）选料；
（2）在熔融状态的锌液中加入铝块进行充分混合熔炼后，再进行铸锻，铸锻时连铸炉的温度为550℃；液高250mm；冷却水压为0.3MPa；
（3）挤压；
（4）时效；
（5）拉伸：退火炉温300℃，时间3小时，拉伸速度为1500mm/s；
（6）时效；
（7）成品包装。 
上述实施例仅用于解释说明本发明的发明构思，而非对本发明权利保护的限定，凡利用此构思对本发明进行非实质性的改动，均应落入本发明的保护范围。

Claims (5)

1.一种锌铝合金丝，其特征在于包含有以下重量百分比的组分：铝10-45%，总量不超过0.03%的杂质，余量为锌。
2.如权利要求1所述的锌铝合金丝，其特征在于：所述铝为35%，总量不超过0.03%的杂质，余量为锌。
3.如权利要求1或2所述的锌铝合金丝，其特征在于：所述杂质为铁0.002-0.01%、锡＜0.001%、铅＜0.003%、铜＜0.01%。
4.如权利要求1或2所述的锌铝合金丝，其特征在于：所述杂质为铁0.002-0.01%、锡＜0.001%、铜＜0.01%。
5.如权利要求1或2所述的锌铝合金丝，其特征在于：所述杂质为铁0.002-0.01%、铅＜0.01%、铜＜0.01%。
CN2012103156440A 2012-08-31 2012-08-31 锌铝合金丝 Pending CN102828068A (zh)