CN102826821A - 一种地质聚合物基保温材料粘结剂 - Google Patents

一种地质聚合物基保温材料粘结剂 Download PDF

Info

Publication number
CN102826821A
CN102826821A CN2012103566430A CN201210356643A CN102826821A CN 102826821 A CN102826821 A CN 102826821A CN 2012103566430 A CN2012103566430 A CN 2012103566430A CN 201210356643 A CN201210356643 A CN 201210356643A CN 102826821 A CN102826821 A CN 102826821A
Authority
CN
China
Prior art keywords
insulating material
bonding agent
bonding
geopolymer
slag
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103566430A
Other languages
English (en)
Inventor
巢启
王新
崔学民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi Qili New Materials Science And Technology Co Ltd
Original Assignee
Guangxi Qili New Materials Science And Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi Qili New Materials Science And Technology Co Ltd filed Critical Guangxi Qili New Materials Science And Technology Co Ltd
Priority to CN2012103566430A priority Critical patent/CN102826821A/zh
Publication of CN102826821A publication Critical patent/CN102826821A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种地质聚合物基保温材料粘结剂。传统的保温材料粘贴剂存在着成本高、吸水率大、干燥速度慢、粘贴不牢等缺点，尤其是在自然条件下的日晒雨淋中，发生碳化反应，会逐渐影响保温材料粘结强度，容易造成保温板的大面积脱落，引起安全隐患。本发明由矿渣、粉煤灰、填料、有机粘结料、聚丙烯纤维和干粉水玻璃组成；具有制作简单、使用便利、粘结性好、强度高，克服传统粘贴剂粘贴不牢，易脱落等不足，本发明还具有和易性好、粘结强度高、耐水性好、粘合速度快、抗老化、耐撞击、耐潮湿、不易燃等特点。且具有一定的弹性，粘接厚度，硬化不流淌，适用于内外墙各种保温材料的粘接。

Description

一种地质聚合物基保温材料粘结剂
技术领域
本发明涉及的是一种地质聚合物基保温材料粘结剂，属于建筑材料领域。
背景技术
在建筑物的外墙墙面上粘贴保温材料，是建筑领域里一个节能减排的有效措施，因为这种措施效果明显，优点突出，政府已出台相关的政策以推广使用。但目前在公知技术中，把保温材料粘贴上墙面的粘贴剂普遍使用的都是硅酸盐水泥保温材料粘结剂，这种传统的粘贴剂存在着成本高、吸水率大、干燥速度慢、粘贴不牢等缺点，这种水泥基粘结剂的致命缺点是在自然条件下的日晒雨淋中，发生碳化反应，会逐渐影响保温材料粘结强度，容易造成保温板的大面积脱落，引起安全隐患。因此，寻求一种有效，安全，成本低，粘贴牢，保温板不脱落的粘贴剂，是保温材料使用技术进步的需要。
发明目的
本发明的目的就是提供一种地质聚合物基保温材料粘结剂，该粘结剂生产制作简单、使用便利、粘结性好、强度高，克服目前在建筑墙面上粘贴保温材料的粘贴不牢，易脱落等不足，通过本发明的地质聚合物基粘结剂可使保温材料能牢固地粘贴在建筑物墙面。
为实现上述目的，本发明采取了下述技术方案：一种地质聚合物基保温材料粘结剂，主要由下述重量百分比的原料制备而成：
矿渣30-54％、粉煤灰15-35％、填料16-33％、有机粘结料5-8％、聚丙烯纤维0.2-0.4％、干粉水玻璃7.5-10％；
所述的矿渣为细度100-600目的高炉水渣、100-600目的转炉钢渣中的任意一种或者上述两种以任意比例混合的混合物；
所述的粉煤灰为市售一级、二级粉煤灰中的任意一种或者上述两种以任意比例混合的混合物；
所述的填料由重质碳酸钙与石英砂组成，重质碳酸钙与石英砂的质量比是1-6∶1-5；
所述的有机粘结料为醋酸乙烯酯、高级脂肪酸乙烯脂类型的可再分散乳胶粉；
所述的聚丙烯纤维为0.5-2cm程度的高强聚丙烯束状纤维；
所述的干粉水玻璃为固体硅酸钠和固体硅酸钾的任意一种或者两种以任意比例混合的混合物；
上述原料的制备方法是：依次将上述原料于搅拌机中搅拌均匀即得。
本发明的使用方法是：进行施工时，以本发明与水的重量比100∶10-40的比例，加水搅拌均匀后即可施工。
采取上述措施的本发明，具有和易性好、粘结强度高、耐水性好、粘合速度快、抗老化、耐撞击、耐潮湿、耐碳化性好等特点。且具有一定的弹性，粘接厚度，硬化不流淌，适用于内外墙各种保温材料的粘接。本发明具有以下优点；(1)用工业矿渣作为建筑用无机胶凝材料替代了硅酸盐水泥，固化速度快、强度高、可塑性好、耐酸碱、耐冻融，耐化学介质；(2)使用干粉水玻璃作为激发剂，避免了施工现场添加液态水玻璃时计量不便带来的随意性；(3)采用工业矿渣和粉煤灰为原料，来源丰富，既消除了环境污染，又节约了能源。
具体实施方式
实施例1
本发明的地质聚合物基粘结剂的组分及配方一：
  组份   配方(重量％)
  矿渣   36.5
  粉煤灰   30
  填料   20
  有机粘结料(可再分散乳胶粉)   5
  聚丙烯纤维   0.3
  干粉水玻璃   8.2
  合计   100
制备及施工方法：
把填料加入到搅拌机中，开始搅拌；
把矿渣和粉煤灰加入搅拌机中；
把有机粘结料、聚丙烯纤维和干粉水玻璃加入搅拌机；
搅拌均匀后，制得本发明产品，装袋或放入仓库备用。
施工时，按照水灰比26∶100的比例，加水搅拌均匀后再施工。
实施例2
本发明的地质聚合物基粘结剂的组分及配方二：
  组份   配方(重量％)
  矿渣   33
  粉煤灰   20
  填料   30
  有机粘结料(可再分散乳胶粉)   7
  聚丙烯纤维   0.4
  干粉水玻璃   9.6
  合计   100
制备方法与实施例1相同。
施工时，按照水灰比23∶100的比例，加水搅拌均匀后再施工。
实施例3
本发明的地质聚合物基粘结剂的组分及配方三：
  组份   配方(重量％)
  矿渣   30
  粉煤灰   23.2
  填料   33
  有机粘结料(可再分散乳胶粉)   5.5
  聚丙烯纤维   0.3
  干粉水玻璃   8
  合计   100
制备方法与实施例1相同。
施工时，按照水灰比31∶100的比例，加水搅拌均匀后再施工。
实施例4
本发明的地质聚合物基粘结剂的组分及配方四：
  组份   配方(重量％)
  矿渣   40.2
  粉煤灰   23.5
  填料   18
  有机粘结料(可再分散乳胶粉)   8
  聚丙烯纤维   0.3
  干粉水玻璃   10
  合计   100
制备方法与实施例1相同。
施工时，按照水灰比28∶100的比例，加水搅拌均匀后再施工。
实施例5
本发明的地质聚合物基粘结剂的组分及配方五：
  组份   配方(重量％)
  矿渣   33.35
  粉煤灰   25
  填料   25
  有机粘结料(可再分散乳胶粉)   6.5
  聚丙烯纤维   0.35
  干粉水玻璃   9.8
  合计   100
制备方法与实施例1相同。
施工时，按照水灰比33∶100的比例，加水搅拌均匀后再施工。
本发明产品的主要技术性能如下表：
Figure BSA00000781581700051

Claims (1)

1.一种地质聚合物基保温材料粘结剂，其特征在于所述粘贴剂主要由下述重量百分比的原料制备而成：
矿渣30-54％、粉煤灰15-35％、填料16-33％、有机粘结料5-8％、聚丙烯纤维0.2-0.4％、干粉水玻璃7.5-10％；
所述的矿渣为细度100-600目的高炉水渣、100-600目的转炉钢渣中的任意一种或者上述两种以任意比例混合的混合物；
所述的粉煤灰为市售一级、二级粉煤灰中的任意一种或者上述两种以任意比例混合的混合物；
所述的填料由重质碳酸钙与石英砂组成，重质碳酸钙与石英砂的质量比是1-6∶1-5；
所述的有机粘结料为醋酸乙烯酯、高级脂肪酸乙烯脂类型的可再分散乳胶粉；
所述的聚丙烯纤维为0.5-2cm程度的高强聚丙烯束状纤维；
所述的干粉水玻璃为固体硅酸钠和固体硅酸钾的任意一种或者两种以任意比例混合的混合物。 
CN2012103566430A 2012-09-21 2012-09-21 一种地质聚合物基保温材料粘结剂 Pending CN102826821A (zh)