CN102824716B - 一种扑灭铀金属自燃的灭火剂的制备方法 - Google Patents
一种扑灭铀金属自燃的灭火剂的制备方法 Download PDFInfo
- Publication number
- CN102824716B CN102824716B CN201210357331.1A CN201210357331A CN102824716B CN 102824716 B CN102824716 B CN 102824716B CN 201210357331 A CN201210357331 A CN 201210357331A CN 102824716 B CN102824716 B CN 102824716B
- Authority
- CN
- China
- Prior art keywords
- powder
- uranium
- uranium metal
- chloride
- crucible
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种扑灭铀金属自燃的灭火剂的制备方法,包括以下步骤: 分别取氯化钠、氯化钾和氯化钡放置于烘箱中,在120℃下烘3个小时;按质量百分比为20%、25%、55%的比例称取经步骤烘干后的氯化钠、氯化钾和氯化钡三组分,混合并研磨、搅拌;将步骤的混合物放入坩埚,并将坩埚置于马弗炉中,在650℃的温度下煅烧4小时;马弗炉冷却后,将煅烧后得到的晶体从中取出,粉碎晶体,得到粉末;
Description
技术领域
本发明属于一种灭火剂的制备方法,具体为一种用于扑灭铀金属自燃的灭火剂的制备方法。
背景技术
在金属铀的加工与物料处理过程中,容易产生碎渣、粉末以及剥落的垢皮等细碎的金属铀屑。金属铀易被氧化,且粉末状金属铀的比表面积大,与空气接触很容易自燃。现有技术除了等待燃烧的铀火自然熄灭,尚没有有效的措施灭铀火。由于铀屑自燃的情况发生频繁,并且铀屑燃烧时,所产生的大量的气溶胶以及相当高的热量极大的危害工作人员健康和工作环境的安全,若不及时扑灭铀火,可能使火势扩散,造成较大的损失。
金属铀的自燃属于金属火灾,目前国内外没有专用于扑灭铀火的灭火剂的生产,也没有系统、完整的扑灭铀自燃的方法,本技术领域现有的研究成果提供了可能的灭火剂配方,但未解决可行的制备方法。
发明内容
为了解决上述技术问题,本发明提供了一种扑灭铀金属自燃的灭火剂的制备方法。
本发明一种扑灭铀金属自燃的灭火剂的制备方法的技术方案为:一种扑灭铀金属自燃的灭火剂的制备方法,包括以下步骤:
分别取氯化钠、氯化钾和氯化钡放置于烘箱中,在120℃下烘3个小时;
按质量百分比为20%、25%、55%的比例依次称取经步骤烘干后的氯化钠、氯化钾和氯化钡三组分,混合并研磨、搅拌;
将步骤的混合物放入坩埚,并将坩埚置于马弗炉中,在650℃的温度下煅烧4小时;
停止煅烧,待马弗炉冷却后,将煅烧后得到的晶体从中取出,釆用超微粉碎机粉碎晶体,得到细度为40μm的粉末;
在粉碎后的粉末中加入硬脂酸镁,搅拌均匀,制得灭火剂;
将制得的灭火剂干粉充装于灭火器中,充装压力为0.8MPa,充装气体为氩气。
所述硬脂酸镁与步骤(4)粉末的质量比为1:19。
釆用本发明的制备方法,在最低共熔点550℃时,析出氯化钠、氯化钾和氯化钡的最低共熔混合物,最低共熔混合物具有特殊的致密结构,性质均匀。
铀金属自燃时,使用充装的灭火器在远距离喷射燃烧中的铀金属表面,当灭火剂粉末与灼烧的铀屑或铀粉末表面接触,在铀金属表面的高温作用下达到低共熔点时,粉末被熔化,形成一个较为致密的玻璃状覆盖层,将燃烧的铀金属表面与周围空气隔开,使燃烧窒息,从而达到了快速的灭火效果。
具体实施方式
下面,结合实施例对本发明一种扑灭铀金属自燃的灭火剂的制备方法做进一步说明。
分别取氯化钠、氯化钾和氯化钡放置于烘箱中,在120℃下烘3个小时,通过烘干工艺去除原料中的水分和结晶水;
按质量百分比为20%、25%、55%比例依次称取经步骤烘干后的氯化钠、氯化钾和氯化钡三组分,混合并研磨、搅拌,研磨使混合原料达到均匀的粒度,搅拌使混合原料达到均匀的混合度;
将步骤的混合物放入坩埚,并将坩埚置于马弗炉中,在650℃的温度下煅烧4小时,当坩埚中混合物的温度达到最低共熔点550℃时,析出最低共熔混合物晶体;
停止煅烧,待马弗炉冷却后,将煅烧后得到的晶体从中取出,釆用超微粉碎机粉碎晶体,得到细度为40μm的粉末;
在粉碎后的粉末中加入硬脂酸镁干燥剂,硬脂酸镁干燥剂与最低共熔混合物的质量比为1:19,搅拌均匀,制得灭火剂;
釆用通用的1千克干粉灭火器金属罐作为容器,氩气作为灭火剂粉末的驱动气体,将1千克步骤(5)的灭火剂粉末放入金属罐内,再将氩气充入容器至容器内压力达到0.8MPa后密封充装口。
铀金属自燃时,使用充装的灭火器在远距离喷射燃烧中的铀金属表面。当灭火剂粉末与灼烧的铀屑或铀粉末表面接触时,在铀金属表面的高温作用下达到低共熔点时,粉末被熔化,形成一个较为致密的玻璃状覆盖层 将燃烧的铀金属表面与周围空气隔幵,使燃烧窒息,从而达到了快速的灭火效果。
Claims (1)
1.一种扑灭铀金属自燃的灭火剂的制备方法,包括以下步骤:
(1)分别取氯化纳、氯化钾和氯化钡放置于烘箱中,在120℃下烘3小时;
(2)按质量百分比为20%、25%、55%的比例依次称取经步骤(1)烘干后的氯化纳、氯化钾和氯化钡三组分,混合并研磨、搅拌;
(3)将步骤(2)的混合物放入坩锅,并将坩锅置于马弗炉中,在650℃的温度下煅烧4小时;
(4)停止煅烧,待马弗炉冷却后,将煅烧后得到的晶体从中取出,采用超微粉碎机粉碎晶体,得到细度为40μm的粉末;
(5)在粉碎后的粉末中加入硬脂酸镁,搅拌均匀,制得灭火剂;
(6)将制得的灭火剂干粉充装于灭火器中,充装压力为0.8MPa,充装气体为氩气;
(7)所述的硬脂酸镁与步骤(4)粉末的质量比为1:19。